Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

Effect of phosphogypsum on saline-alkalinity and aggregate stability of bauxite residue

A column experiment was conducted to investigate the effect of phosphogypsum (PG) on the saline- alkalinity, and aggregate stability of bauxite residue. Results showed that: with increasing leaching time, the concentrations of saline-alkali ions decreased while the concentration increased in bauxite residue leachate; compared with CK (control group) treatment, pH, electric conductivity (EC), exchangeable sodium percentage (ESP), sodium absorption ratio (SAR), and exchangeable Na⁺ content of bauxite residue were reduced following PG treatment; average particle sizes in aggregates following CK and PG treatments were determined to be 155 and 193 nm, respectively. SR-μCT test results also confirmed that bauxite residue following PG treatment acquired larger aggregates and larger pore diameter. These results indicate that the PG treatment could significantly modulate the saline-alkalinity, and simultaneously enhance aggregate stability of bauxite residue, which provides a facile approach to reclaim bauxite residue disposal areas.     

Spectral radiance reconstruction from trichromatic camera responses based on orthogonal test and regularized algorithm

Reconstruction of spectral information based on multi‐channel image system is a significant problem in color reproduction, detection, and recognition. A spectral radiance reconstruction from trichromatic digital camera responses is researched in this article. The mapping relationship between the trichromatic imaging system response and the incident spectral radiance is analyzed. Then, in order to remove the ill‐posedness of the problem, a regularized constraint solution model of spectral radiance reconstruction matrix is established. And the spectral radiance can be reconstructed by spectral radiance reconstruction matrices and trichromatic imaging system response. Finally, the spectral radiance reconstruction matrix is estimated by the system radiometric calibration experiment. The input radiance is offered by a LCD display. A 3‐factor and 9‐level orthogonal test is designed for the calibration experiment, and a test set of 24 colors is used for precision analysis. The results show that the average relative mean error of our method is 8.69%, it is lower than that of Wiener filtering method by 2.84%. The method can reconstruct spectral radiance information effectively.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

高分子材料导热性能影响因素研究进展

介绍了高分子材料导热性能影响因素研究进展，重点阐释了聚合物基体的结构特性（链结构、分子间相互作用、取向、结晶度等）、导热填料（种类、含量、形态、尺寸等）以及制备方法等对高分子材料导热性能的影响。     

BS960E高强钢激光-电弧复合焊接头氢脆行为研究

氢脆具有很强的微观组织敏感性,威胁着各类高强结构材料的安全服役.采用激光-电弧复合焊工艺对BS960E型高强钢进行焊接,并对接头在原位电化学充氢的条件下进行慢应变速率(10-5s-1)拉伸试验,结合微观组织和断裂特征进行分析并对接头的氢脆行为进行研究.结果 表明,焊接热循环所形成的富马氏体中的细晶区可以使接头表现出一定的氢脆敏感性,马氏体较大的氢扩散系数和较低的氢溶解度以及氢在晶界上的快速扩散是引起接头对氢脆敏感的主要原因,通过控制焊接工艺参数可抑制焊接热循环所引起的马氏体转变量,能够降低BS960E型高强钢激光-电弧复合焊接头的氢脆敏感性.     

Performance analysis of bit error rate of data link system under pulse LFM interference in time-varying rayleigh channel

Wireless Networks - In such mobile platforms as ships and aircraft, the detection and reconnaissance devices are near to the communication facilities. When working at the same time, they will...     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.