Al2O3/Cr3C2/(W,Ti)C陶瓷材料的力学性能及微观结构

用热压烧结工艺在1 700℃,28 MPa保温保压30 min及N2气氛条件下,制备了添加不同含量Cr3C2和(W,Ti)C颗粒的Al2O3/CraC2/(W,Ti)C复合陶瓷材料.对复合陶瓷的力学性能进行测试.用环境扫描电镜、透射电镜和能谱分析仪对复合陶瓷的显微结构进行观察.结果表明与纯Al2O3相比,70Al2O3/10Cr3C2/20(W,Ti)C复合陶瓷材料的显微组织更均匀细化,具有良好的综合力学性能,其断裂韧性自纯Al2Oa陶瓷的4.0 MPa·m1/2提高到8.92 MPa·m1/2.分析发现其内部位错机制、纳米颗粒的淀析、裂纹扩展路径偏转、沿晶断裂、韧窝及解理撕裂等是材料断裂韧性提高的主要原因.     

双相Sialon材料的研究

研究了工艺条件、化学组成、显微结构与材料性能的关系，制备了双相Sialon材料。该材料室温抗折强度、断裂韧性分别达到624MPa、4MPa·m1／2，硬度达到Hv2000左右。其最佳烧结温度为1550℃，1．5h。添加剂Y2O3、Al2O3和AlN的最佳含量分别为10％、5％、5％。     

热处理温度对MgO--MgAl_2O_4--ZrO_2共晶材料力学性能的影响

以分析纯的MgO、活性α--Al2O3、电熔单斜ZrO2和电熔镁砂为原料,研究了热处理温度对MgO--MgAl2O4--ZrO2共晶材料力学性能和热震稳定性的影响。结果表明:随热处理温度从1 650℃提高到1 740℃,MgO--MgAl2O4--ZrO2共晶体的生成比例逐渐增加,材料断裂韧性、断裂表面能、高温抗折强度和抗热震稳定性逐渐提高。经过1 740℃热处理后,MgO--MgAl2O4--ZrO2共晶材料的力学性能明显改善,其断裂韧性、断裂表面能、高温抗折强度分别为MgO--Al2O4--ZrO2非共晶材料的1.65倍、2.04倍、5.91倍,MgO--ZrO2材料的1.49倍、1.72倍、2.22倍。MgO--MgAl2O4--ZrO2共晶材料因能吸收裂纹并阻止裂纹扩展而具备优异的抗热震稳定性能,其抗热震稳定性参数Rst值和R′′′′值分别为MgO--MgAl2O4--ZrO2非共晶材料的1.29倍、1.81倍,MgO--ZrO2材料的1.50倍、3.29倍。     

SiCw掺杂GdPO4的相组成和断裂韧性

GdPO4 是一种极具应用潜力的热障涂层材料，但其断裂韧性有待进一步提升。本 文在 GdPO4 中掺杂 SiCw，研究了二者的高温相容性以及反应产物相组成，探究了 SiCw 掺杂量 对断裂韧性的影响。研究结果表明，掺杂有 SiCw 的 GdPO4 在高温下发生两相反应：SiCw 掺杂 量为 10 mol% 时，反应产物为 Gd9.33(SiO4)6O2和 SiO2；掺杂量为 20 mol% 时，反应产物为 SiO2、 Gd2Si2O7和 Gd9.33(SiO4)6O2；更高掺杂量 (30 mol%) 时，反应产物基本为 Gd2Si2O7。反应形成 的新相对 GdPO4 有较明显的增韧作用。当 SiCw 掺杂 10 mol% 时，复合材料的断裂韧性比纯 GdPO4提高 20% 左右，达到 1.37 MPa·m1/2 ± 0.1 MPa·m1/2。韧化机理在于新形成的第二相有助 于降低裂纹尖端扩展驱动力且产生细晶强化。此外，反应形成的 Gd9.33(SiO4)6O2 具有较低的热 导率，有利于涂层材料的隔热性能。     

多晶YAG陶瓷的制备及力学性能

本实验采用共沉淀方法制备YAG微粉 ,Al和Y元素分布均匀 ,在 90 0℃煅烧 2h即可全部转变为YAG粉体 ,无过渡相 .15 0 0℃热压 1h可获得致密烧结体 ,其抗弯强度为 2 45MPa ,断裂韧性为 2 .0MPa·m1 /2 ,晶粒大小为 3～ 6μm ;14 0 0℃放电等离子烧结 5min可获得相对密度为 93 %的烧结体 ,其抗弯强度为 3 4 8MPa,断裂韧性为 2 .1MPa·m1 /2 ,晶粒大小为 1～ 2 μm .     

高聚物粘结炸药平面应变断裂韧度实验研究

介绍了高聚物粘结炸药平面应变断裂韧度 K1c的测试方法 ,对三种高聚物粘结炸药 JOB- 90 0 3、JO- 915 9、JB- 90 14在常温下的K1c值进行了测试。测试结果分别为 :0 .2 4± 0 .0 1MPa·m1/ 2、0 .17± 0 .0 1MPa· m1/ 2、0 .37± 0 .0 1MPa·m1/ 2 ,显示出 JB- 90 14具有相对较强的抗裂纹扩展能力。文章同时讨论了三种高聚物粘结炸药 K1c值与其常规力学性能如拉伸应力应变曲线、蠕变曲线测试结果的一致性 ,还从材料组成的角度 ,分析揭示了 JB- 90 14具有较大 K1c值的主要原因在于 JB- 90 14所用粘结剂为 F2 314     

掺碳SiC颗粒对MoSi_2复合材料性能的影响

研究分析了掺碳SiCp/MoSi2 复合材料的相组成、室温和高温力学性能、高温抗氧化性能、耐磨性能以及电阻率 .结果表明 :(SiCp+C) /MoSi2 复合材料主要由MoSi2 ,α -SiCp,Mo5Si3和 β -SiC组成 .材料的密度和相对密度分别为 5.1 2 g/cm3和 91 % ;Vickers硬度 ,抗弯强度和断裂韧性分别为 1 2 .2GPa ,530MPa和 7.2MPa·m1 / 2 ;80 0℃的Vickers硬度为 8.0GPa ,1 2 0 0℃和 1 40 0℃的抗压强度分别为 560MPa和1 60MPa .材料的抗氧化性能优良 .在Al2 O3和SiC磨盘上表现出优异的耐磨性能 .电阻率为 40 .2 μΩ·cm .与非增强MoSi2 相比 ,材料的各种力学性能有大幅度的提高     

多孔SiC基耐火材料的热震损伤

本文从抗热震性是材料的力学和热学性能的综合反映这观点出发,研究了SiC基耐火材料的组分-显微结构-力学性能之间的关系,从而剖析材料的抗热震能力。首先,探讨了粘土结合剂含量不同的三种SiC基材料的强度随热震温差△T的增大而下降的趋势;多次热震导致的强度衰减规律;分析了材料的热震裂纹扩展行为;确定了该系列材料具有“准静态热震裂纹扩展”的属性,亦即其抗热震能力主要由“裂纹稳定性系数”R_(at)-[γf/Eα~2]~(1/2)来表征;从而说明断裂功rf的提高,是改善该系列材料抗热震性的最重要的力学因素。在系统实验的基础上得出:在600℃≤△T≤1000℃的热震温差范围内,材料的强度不仅随着温差△T的增大而下降,亦随着热震次数的增多而衰减。因此,这是热震损伤问题较为突出的阶段,当△T≥1000℃,由于SiC颗粒间界的铝硅酸盐在高温下出现了粘滞态的玻璃相,在淬冷瞬间吸收了部分能量,削弱了热震裂纹的扩展趋势,相应缓和了材料的热震损伤倾向。     

BaNb_2O_6/Al_2O_3复相陶瓷的制备及力学性能

为研究功能材料对结构陶瓷微观结构和力学性能的影响,将铁电相BaNb2O6引入到Al2O3陶瓷中,分别采用无压和热压烧结技术于1350℃制备BaNb2O6/Al2O3复相陶瓷,对其物相组成、微观结构和力学性能进行了研究。结果表明:BaNb2O6与Al2O3经过高温烧结能够稳定共存,BaNb2O6的加入促进了Al2O3陶瓷的烧结。BaNb2O6加入量为10%(体积分数)时,1350℃无压烧结和热压烧结制备的BaNb2O6/Al2O3复相陶瓷的致密度、抗弯强度和断裂韧性分别为94.6%、214MPa、2.28 MPa m1/2和99.3%、332 MPa、3.55MPa m1/2。当裂纹扩展遇到BaNb2O6晶粒时发生穿晶断裂,但在晶粒内部出现裂纹偏转,说明铁电相BaNb2O6晶粒内部的微观结构有助于陶瓷的强韧化。     

Fabrication and Mechanical Property of BaNb2O6/Al2O3 Composite Ceramics

为研究功能材料对结构陶瓷微观结构和力学性能的影响,将铁电相 BaNb2O6引入到 Al2O3陶瓷中,分别采用无压和热压烧结技术于 1350 ℃制备 BaNb2O6/Al2O3复相陶瓷,对其物相组成、微观结构和力学性能进行了研究。结果表明：BaNb2O6与 Al2O3经过高温烧结能够稳定共存,BaNb2O6的加入促进了 Al2O3陶瓷的烧结。BaNb2O6加入量为 10%（体积分数）时,1350 ℃无压烧结和热压烧结制备的 BaNb2O6/Al2O3复相陶瓷的致密度、抗弯强度和断裂韧性分别为 94.6%、214MPa、2.28 MPa m1/2和 99.3%、332 MPa、3.55MPa m1/2。当裂纹扩展遇到 BaNb2O6晶粒时发生穿晶断裂,但在晶粒内部出现裂纹偏转,说明铁电相 BaNb2O6晶粒内部的微观结构有助于陶瓷的强韧化。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。