镁砂加入量对铝镁质摆动流嘴预制件性能的影响

以电熔刚玉、烧结刚玉、刚玉细粉、尖晶石微粉(<5μm)、氧化铝微粉(<2μm)、铝酸钙水泥(Secar 71)、电熔镁砂细粉为主要原料,制备了镁砂加入质量分数分别为1.5%、2.5%、3.5%的铝镁浇注料.测定1 500℃3 h处理后试样的体积密度、显气孔率、强度和加热永久线变化率,并在1 500℃3 h条件下进行抗高炉渣侵蚀试验.结果表明:随着镁砂加入量的增加,材料烧后的显气孔率增大,强度降低,抗高炉渣侵蚀性能下降.这主要是电熔镁砂在高温下与氧化铝反应生成尖晶石产生体积膨胀所至,因此,镁砂的加入质量分数以2.5%为宜.     

蓝晶石粒度对刚玉-莫来石材料性能的影响

以粒度为2～1mm和1～0.5mm的M60莫来石为骨料,以电熔白刚玉粉以及粒度分别为0.8～0.355mm、0.355～0.088mm和<0.088mm的蓝晶石为基质料,以少量二氧化硅微粉和苏州土为结合剂,制成36mm×36mm的试样,在110℃干燥24h后,分别在1200℃、1300℃、1400℃和1500℃保温3h煅烧,然后测定烧后试样的线变化率、显气孔率、体积密度和耐压强度。结果表明:(1)对于在各温度下煅烧后的试样,添加粒度<0.088mm蓝晶石的试样烧后线变化率和显气孔率较添加粒度>0.088mm蓝晶石的小,体积密度和耐压强度较添加粒度>0.088mm蓝晶石的大;(2)当添加粒度<0.088mm的蓝晶石时,随着煅烧温度的升高,试样的烧后线变化率、显气孔率、体积密度和耐压强度变化较小;当添加粒度>0.088mm的蓝晶石时,随着煅烧温度的升高,试样的烧后线变化率和显气孔率迅速增大,体积密度和耐压强度迅速减小。     

2MgO·TiO2的固相反应合成与烧结

在2MgO.TiO2的热力学计算基础上,将97电熔镁砂(<0.088 mm)和钛白粉(<0.044 mm)按n(MgO):n(TiO2)=2:1的配比共磨并预烧(1 000℃保温3 h)后,将预烧料破碎并预压造粒,成型为44 mm×44 mm的试样,然后在1 250~1 700℃(间隔50℃)共10个温度点下分别煅烧5 h。对煅烧后的试样进行XRD和SEM分析以及显气孔率、体积密度、常温耐压强度的测定,在此基础上研究了2MgO.TiO2的合成与烧结。结果表明:以97电熔镁砂和钛白粉为原料,按n(MgO):n(TiO2)=2:1配料,在1 400℃保温5 h就可以合成高含量的2MgO.TiO2,但合成2MgO.TiO2的烧结温度应控制在1 650℃保温5 h。     

以矾土碎矿和煤矸石合成莫来石均质料

采用Ⅰ等高铝矾土碎矿、Ⅱ等高铝矾土碎矿分别与煤矸石配合,并加入活性Al2O3调整m(Al2O3)/m(SiO2),按照矾土基莫来石均质熟料w(Al2O3)=68%～72%的要求,共配成6个混合料,将混合料湿磨至粒度≤0.044mm以均化化学成分,经成型、干燥后分别在1550℃、1600℃、1650℃和1700℃煅烧3h,冷却后测定其显气孔率和体积密度,以确定它们的烧结温度。结果表明:均质料的烧结温度为1700℃;在1700℃烧结制成的矾土基莫来石均质熟料的Al2O3含量为68%～72%,显气孔率<2.5%,体积密度≥2.75g·cm-3,其莫来石晶体发育良好,构成网络结构。同时,还将部分试样分别在800℃、1000℃、1200℃、1300℃、1400℃、1500℃、1600℃、1650℃和1700℃保温3h,测量其烧后线收缩率和显气孔率,并用XRD分析其相组成,据此分析试样在不同温度下所发生的反应。结果表明,试样在1000～1700℃加热过程中的变化可分为3个阶段:1000～1200℃的一次莫来石形成阶段,1200～1500℃的二次莫来石化阶段,以及1500～1700℃的液相烧结阶段。     

电熔镁砂加入量对Al2O3-SiC-C浇注料性能的影响

以电熔棕刚玉颗粒(粒度为5~3 mm、3~1 mm,≤1 mm)、电熔白刚玉细粉(≤0.088 mm)、SiC颗粒(≤1 mm)和细粉(≤0.088 mm)、电熔镁砂细粉(≤0.088 mm)、活性α-Al2O3微粉、SiO2微粉、Si粉和球状沥青为主要原料,以纯铝酸钙水泥为结合剂,配制成电熔镁砂细粉加入量(质量分数)分别为0、3%、6%、9%、12%的出铁沟用Al2O3-SiC-C浇注料,经振动成型、养护、脱模、110℃24 h烘干后,分别于1 100℃3 h、1 450℃3 h热处理,测定处理后试样的体积密度、显气孔率、烧后线变化率、抗折强度、抗高炉渣侵蚀性和抗氧化性,并分析其物相组成和显微结构。结果表明:随着电熔镁砂加入量的增加,试样的显气孔率提高,体积密度、抗折强度和抗氧化性降低,抗渣性变化不大;1 450℃3 h处理后试样物相主要由3C-SiC、6H-SiC、刚玉、方镁石以及反应生成的尖晶石和莫来石组成,且随着电熔镁砂加入量的增加,尖晶石和莫来石的生成量也增加;在侵蚀面附近,刚玉颗粒边缘生成了厚度约80μm的尖晶石层。     

微孔富镁尖晶石对低碳MgO-C材料性能的影响

分别以微孔富镁尖晶石(5~3和3~1 mm)和电熔镁砂(5~3和3~1 mm)为粗骨料,以<1 mm的电熔镁砂为细骨料,以镁砂粉(≤0.088 mm)、鳞片石墨粉(≤0.088 mm)、金属铝粉(≤0.074 mm)为细粉,以酚醛树脂为结合剂,制备了w(C)=6%的两种低碳MgO-C材料,经220和1 500℃(埋焦炭)热处理后,测定其显气孔率、常温耐压强度、常温抗折强度、加热永久线变化率、抗热震性和抗渣性。结果表明:1)用微孔富镁尖晶石骨料取代普通低碳MgO-C材料中的部分镁砂骨料后,经220和1 500℃热处理后试样的显气孔率均比普通低碳MgO-C试样的大,体积密度均比普通低碳MgO-C试样的小;220℃固化后试样的强度比普通低碳MgO-C试样的小,但1 500℃热处理后试样的强度比普通低碳MgO-C试样的大;1 500℃热处理后试样的加热永久线变化率比普通低碳MgO-C试样的小。2)使用微孔富镁尖晶石骨料代替电熔镁砂骨料能有效提高低碳MgO-C材料的抗热震性,但对低碳MgO-C材料的抗侵蚀性不利。     

电熔白刚玉细粉对RH炉用刚玉质浇注料性能的影响

为进一步提高RH炉用刚玉质浇注料的抗热震性,以烧结刚玉为骨料,烧结刚玉粉、活性氧化铝微粉和铝酸钙水泥(Secar 71)为基质,用电熔白刚玉粉替代基质中烧结刚玉粉,研究了电熔白刚玉加入量对RH炉浇注料1 600℃烧后体积密度、显气孔率、线变化、常温抗折强度、常温耐压强度以及抗热震性能的影响,并用SEM对试样进行显微结构分析。结果表明:随着电熔白刚玉粉加入量的增加,试样的体积密度、热震次数逐渐增加,显气孔率、线变化率逐渐减小,这与试样中生成的六铝酸钙量有关。当电熔白刚玉粉替代量为20%(w)时,试样的抗热震性最好。     

不同添加剂加入量对Al_2O_3-SiC-C砖性能影响

为进一步提高Al_2O_3-SiC-C砖的性能,以≤5mm的均化矾土料、≤5mm的板状刚玉、≤1mm的碳化硅、0.044mm的α-Al_2O_3微粉和≤0.154mm的石墨等为原料,以酚醛树脂为结合剂制备了Al_2O_3-SiC-C不烧砖。研究了电熔镁砂粉、叶蜡石粉或红柱石粉的加入量(w)皆分别为1%、2%和3%时对试样各项性能的影响,并采用国标对220℃保温24h后试样的各项性能进行检测。结果表明:在Al_2O_3-SiC-C砖中添加少量电熔镁砂粉、红柱石粉、叶蜡石粉可提高试样的高温抗折强度和抗热震性能,加入1%(w)电熔镁砂粉的试样高温抗折强度最大,加入1%(w)红柱石粉的试样抗热震性最好;添加1%(w)电熔镁砂粉可减少熔渣对均化矾土的侵蚀,明显提高试样的抗渣侵蚀性能。综合考虑,加入1%(w)电熔镁砂粉的试样性能最佳。     

TiO2加入量对MgO-TiO2熟料性能和显微结构的影响

以w(MgO)=96.14%的轻烧氧化镁和w(TiO2)>99.0%的分析纯TiO2为原料,分别加入质量分数0、5%、10%、15%、20%的TiO2,混合均匀,压制成型为30 mm×5 mm的试样,分别在1 500和1 600℃保温3 h烧结,制备得到MgO-TiO2熟料,并研究了熟料的体积密度、显气孔率、抗水化性能、物相组成和显微结构。结果表明:由于TiO2和MgO间的固溶和尖晶石反应,使得方镁石晶粒逐渐长大,反应过程中生成的Mg2TiO4分布在方镁石晶粒周围,降低了试样的显气孔率,提高了熟料的抗水化性能;TiO2添加量为5%(w)时熟料最致密,继续增加时,由于生成的Mg2TiO4体积膨胀,显气孔率有所增大;随着煅烧温度升高,熟料致密度提高,当温度为1 600℃时,能够获得抗水化性能良好的致密熟料。     

活性MgO和铝酸钙水泥结合刚玉-尖晶石浇注料性能对比

为改善刚玉-尖晶石浇注料的性能，以板状刚玉、活性氧化铝、烧结镁砂细粉为主要原料，分别以活性MgO和铝酸钙水泥(CAC)为结合剂制备了刚玉-尖晶石浇注料，对比了二者对1 600℃煅烧3 h后试样的显气孔率、烧后线变化率、常温抗折强度、常温耐压强度和抗CaO-Al₂O₃-Fe₂O₃-SiO₂(CAFS)渣侵蚀性能的影响。结果表明：经1 600℃热处理后，与CAC结合的刚玉-尖晶石浇注料相比，活性MgO结合的刚玉-尖晶石浇注料的常温抗折强度和常温耐压强度较低，但其体积稳定性、对CAFS渣的抗侵蚀性和抗渗透性显著提高。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

Sapindaceae,cyanolipids, and bugs

Scentless plant bugs (Heteroptera: Rhopalidae) are so named because adults of the Serinethinae have vestigial metathoracic scent glands. Serinethines are seed predators of Sapindales, especially Sapindaceae that produce toxic cyanolipids. In two serinethine species whose ranges extend into the southern United States,Jadera haematoloma andJ. sanguinolenta, sequestration of host cyanolipids as glucosides renders these gregarious, aposematic insects unpalatable to a variety of predators. The blood glucoside profile and cyanogenesis ofJadera varies depending on the cyanolipid chemistry of hosts, and adults and larvae fed golden rain tree seeds (Koelreuteria paniculata) excrete the volatile lactone, 4-methyl-2(5H)-furanone, to which they are attracted.Jadera fed balloon vine seeds (Cardiospermum spp.) do not excrete the attractive lactone. Loss of the usual heteropteran defensive glands in serinethines may have coevolved with host specificity on toxic plants, and the orientation ofJadera to a volatile excretory product could be an adaptive response to save time.Mention of a commercial product does not consititute an endorsement by the USDA.     

Insect antifeedant properties of anthranoids from the genusVismia

Vismiones and ferruginins, representatives of a new class of lypophilic anthranoids from the genusVismia were found to inhibit feeding in larvae of species ofSpodoptera, Heliothis, and inLocusta migratoria.     

2008～2009年世界塑料工业进展

收集了2008年7月～2009年6月世界塑料工业的相关资料,介绍了2008～2009年国外塑料工业的发展情况,提供了世界塑料产量、消费量及全球各类树脂的需求量及产能情况。按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)、通用热固性树脂(酚醛、聚氨酯、环氧树脂、不饱和聚酯树脂)不同品种的顺序,对树脂的产量、消费量、供需状况及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等技术作了详细介绍。     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。