Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

Matrix Manipulation of Directly-Synthesized PbS Quantum Dot Inks Enabled by Coordination Engineering

The direct-synthesis of conductive PbS quantum dot (QD) ink is facile, scalable, and low-cost, boosting the future commercialization of optoelectronics based on colloidal QDs. However, manipulating the QD matrix structures still is a challenge, which limits the corresponding QD solar cell performance. Here, for the first time a coordination-engineering strategy to finely adjust the matrix thickness around the QDs is presented, in which halogen salts are introduced into the reaction to convert the excessive insulating lead iodide into soluble iodoplumbate species. As a result, the obtained QD film exhibits shrunk insulating shells, leading to higher charge carrier transport and superior surface passivation compared to the control devices. A significantly improved power-conversion efficiency from 10.52% to 12.12% can be achieved after the matrix engineering. Therefore, the work shows high significance in promoting the practical application of directly synthesized PbS QD inks in large-area low-cost optoelectronic devices.     

Colossal dielectric response and relaxation behavior in novel system of Zr4+ and Nb5+ co-substituted CaCu3Ti4O12 ceramics

In this work, we developed a novel system of isovalent Zr⁴⁺ and donor Nb⁵⁺ co-doped CaCu₃Ti₄O₁₂ (CCTO) ceramics to enhance dielectric response. The influences of Zr⁴⁺ and Nb⁵⁺ co-substituting on the colossal dielectric response and relaxation behavior of the CCTO ceramics fabricated by a conventional solid-phase synthesis method were investigated methodically. Co-doping of Zr⁴⁺ and Nb⁵⁺ ions leads to a significant reduction in grain size for the CCTO ceramics sintered at 1060 °C for 10 h. XRD and Raman results of the CaCu₃Ti_3.8-xZr_xNb_0.2O₁₂ (CCTZNO) ceramics show a cubic perovskite structure with space group Im-3. The first principle calculation result exhibits a better thermodynamic stability of the CCTO structure co-doped with Zr⁴⁺ and Nb⁵⁺ ions than that of single-doped with Zr⁴⁺ or Nb⁵⁺ ion. Interestingly, the CCTZNO ceramics exhibit greatly improved dielectric constant (~10⁵) at a frequency range of 10²–10⁵ Hz and at a temperature range of 20–210 °C, indicating a giant dielectric response within broader frequency and temperature ranges. The dielectric properties of CCTZNO ceramics were analyzed from the viewpoints of defect-dipole effect and internal barrier layer capacitance (IBLC) model. Accordingly, the immensely enhanced dielectric response is primarily ascribed to the complex defect dipoles associated with oxygen vacancies by co-doping Zr⁴⁺ and Nb⁵⁺ ions into CCTO structure. In addition, the obvious dielectric relaxation behavior has been found in CCTZNO ceramics, and the relaxation process in middle frequency regions is attributed to the grain boundary response confirmed by complex impedance spectroscopy and electric modulus.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.     

Synthesis of succinic acid-based polyamide through direct solid-state polymerization method: Avoiding cyclization of succinic acid

Succinic acid is an important synthetic monomer but it is difficult to use it as a precursor for synthesizing high molecular weight polyamide, due to its tendency to perform intra-cyclization reaction at high temperature. In order to solve this problem, in this paper, the direct solid-state polymerization (DSSP) method with the initial reactant, nylon salt which was composed of 1, 5-diaminopentane, succinic acid, and terephthalic acid, was applied to synthesize the bio-based copolyamide PA 5T/54. In comparison with the conventional melting polymerization method, the DSSP method can prevent the cyclization reaction of succinic acid effectively due to the lower reacting temperature as well as the restriction effect of the nylon salt. As a result, the product fabricated by DSSP method has higher molecular weight and much lighter color from red to white. Therefore, the DSSP method is advantageous for the synthesis of the polymers or copolymers composed of the succinic acid as the monomer. Furthermore, the polymerization mechanism proposed in this work can serve as a guidance for the design of the molecular structure and control of the polymerization process.     

Enhanced thermal shrinkage behavior of phenolic-derived carbon aerogel-reinforced by HNTs with superior compressive strength performance

A novel carbon/m-HNTs composite aerogel was synthesized by introducing the modified halloysite nanotubes (m-HNTs) into phenolic (PR) aerogels through chemical grafting, followed with carbonization treatment. In order to explore the best proportion of HNTs to phenolic, the micromorphology of PR/m-HNTs were investigated by SEM before carbonization, confirming 10 wt% of m-HNTs is most beneficial to the porous network of aerogels. The interaction between PR and HNTs was studied by FTIR spectra, and microstructure evolution of the target product-carbon/m-HNTs composite aerogel were illustrated by SEM and TEM techniques. SEM patterns indicated that the carbon/m-HNTs aerogels maintain a stable porous structure at 1000 °C (carbonization temperature), while a ~20 nm carbon layer was formed around m-HNTs generating an integral unit through TEM analysis. Specific surface area and pore size distribution of composite aerogels were analyzed based on mercury intrusion porosimetry and N₂ adsorption–desorption method, the obtained results stayed around 500 m²g^?1 and 1.00 cm³g^?1 (pore volume) without significant discrepancy, compared with pure aerogel, showing the uniformity of pore size. The weight loss rate (26.76%) decreased greatly compared with pure aerogel, at the same time, the best volumetric shrinkage rate was only 30.83%, contributed by the existence of HNTs supporting the neighbor structure to avoid over-shrinking. The highest compressive strength reached to 4.43 MPa, while the data of pure aerogel was only 1.52 MPa, demonstrating the excellent mechanical property of carbon/m-HNTs aerogels.     

Enhanced the photocatalytic activity of B–C–N–TiO2 under visible light:Synergistic effect of element doping and Z-scheme interface heterojunction constructed with Ag nanoparticles

In order to enhance the photocatalytic activity of TiO₂ under visible light, Ag nanoparticles were introduced into tridoped B–C–N–TiO₂ (TT) catalyst by photoreduction deposition. Ag/B–C–N–TiO₂ (ATT) catalysts with the functions of reducing band gap and carrier recombination were prepared. At the same time, the effect of the amount of Ag on the photocatalytic performance of ATT catalyst was investigated. Through XRD, XPS, PL and other characterization methods, the (211)/(101)/Ag interface heterojunction mechanism similar to the traditional Z-scheme heterojunction was proposed. The intervention of Ag nanoparticles changed the P–N interface heterojunction between (211)/(101) to the (211)/(101)/Ag Z-scheme interface heterojunction. The results show that ATT catalyst exhibits the highest photocatalytic activity when the molar amount of Ag is 0.005% with the MB degradation rate of the ATT catalyst (0.01707 min^?1), which is 14.59 times of TiO₂ (0.00117 min^?1) and 2.02 times of TT (0.00847 min^?1). In addition, the four cycles efficiencies of ATT for MB degradation were all above 94.00%.This study reveals the possibility of construction of Z-scheme heterojunctions between precious metal nanoparticles and different interfaces of TiO₂, and provides a reference for the construction of Z-scheme interface heterojunctions.