缓凝剂与聚羧酸减水剂对硫铝酸盐水泥流动性和强度的影响

为改善掺聚羧酸减水剂(PC)的硫铝酸盐水泥(CSA)浆体的流动度和经时损失,并保证其施工时间,本文将PC与缓凝剂柠檬酸(CA)或葡萄糖酸钠(SG)复掺到CSA净浆或胶砂试件中,测试了浆体的流动度、凝结时间和各龄期胶砂试件的抗压强度,并采用紫外-可见光分光光度计和X-射线衍射仪分别测试PC减水剂在自制硫铝酸盐水泥上的吸附量和减水剂、缓凝剂对水化产物的影响.研究结果表明:随着CA或SG掺量的提高,浆体30 min流动度有大幅度的增长;初凝和终凝时间均有不同程度的延长;PC吸附量随CA掺量升高而减小,但随SG掺量升高而增大:随缓凝剂掺量提高,各龄期胶砂试件的抗压强度略有下降,且SG较CA导致的强度降低幅度更大.     

超细矿渣在水泥砂浆中的应用研究

在普通硅酸盐水泥砂浆中加入济钢产超细矿渣,研究不同掺量的超细矿渣对水泥浆体凝结时间及胶砂流动度、强度的影响.实验结果表明:随着掺量的提高,水泥浆体的初凝时间延长,终凝时间缩短;胶砂流动度随超细矿渣掺量的增大而减小;随超细矿渣掺量的增大,水泥胶砂的3d和28 d强度提高,当质量分数掺量为30％时,水泥砂浆28 d的抗折、抗压强度达到最大,分别达到9.65 MPa和68.44 MPa.     

外掺氧化镁膨胀剂对水泥净浆流变特性及胶砂强度的影响

研究了氧化镁膨胀剂在不同掺量下对水泥浆体流变特性和胶砂强度的影响规律。研究结果表明:外掺氧化镁膨胀剂,会降低水泥浆体流动度,增大浆体的剪切粘度,提高浆体的屈服应力和塑性粘度;掺氧化镁膨胀剂胶砂3d龄期的抗压强度稍低于不掺氧化镁膨胀剂的胶砂,7d、28d时抗压强度高于不掺氧化镁膨胀剂的胶砂,当掺量为6%时,抗压强度较不掺氧化镁膨胀剂的胶砂增加了10%左右;3d、7d龄期时掺氧化镁膨胀剂组的胶砂抗折强度要低于不掺氧化镁膨胀剂组,而28d龄期抗折强度明显高于不掺氧化镁膨胀剂组。     

沸石粉对硫铝酸盐水泥水化行为的影响机理研究

研究了沸石粉对硫铝酸盐水泥浆体流动度、凝结时间和抗压强度的影响规律,并通过自收缩、电阻率和XRD测试分析了沸石粉在硫铝酸盐水泥水化行为中的作用机理。结果表明,掺入沸石粉后水泥浆体的流动度明显降低,凝结时间显著延长,且延长时间随掺量的增大呈先增大后减小的趋势。当沸石粉掺量为5%~15%(质量分数)时,硬化水泥浆体的1 d、3 d、7 d抗压强度均有显著提高;沸石粉掺量为10%时,水泥浆体3 d、7 d、28 d的强度增长幅度最大,和空白组相比,分别增长了21.6%、13.9%和5.4%。掺入沸石粉后水泥浆体的24 h电阻率显著增大,硬化浆体的7 d自收缩减小,且在相同龄期时,硬化浆体的自收缩随沸石粉掺量的增大而减小。XRD分析显示沸石粉的掺入能有效促进硫铝酸盐水泥的水化,有利于1 d、3 d和28 d龄期内钙矾石的形成。     

三乙醇胺对水泥流变性能和水化的影响

采用标准稠度用水量、凝结时间、流变性能、力学强度、XRD、SEM等手段,研究不同掺量的三乙醇胺对水泥流变性能和水化的影响.掺0.15％ TEA后,水泥10 min和30 min的塑性粘度、屈服应力均降低,增加了水泥浆体的流动性,延长了水泥的凝结时间.掺0.20％ TEA对水泥具有促凝作用,促进了水泥的水化,10 min和30 min的塑性粘度、屈服应力均增大,降低了水泥浆体的流动性.随TEA掺量增加,减少了水泥标准稠度用水量,促进了水化产物AFt的生成,提高了水泥净浆强度.     

速凝剂与石灰石粉对水泥浆体性能的影响

通过不同掺量的速凝剂和石灰石粉对水泥浆体凝结时间、流动度、粘度、胶砂强度和水化进程的影响研究,探讨速凝剂与石灰石粉共同作用下对水泥浆体性能的影响。结果表明:石灰石粉能够提高水泥净浆的流动度和粘度,并且其流动度和粘度损失随着石灰石粉掺量的增加而增大。速凝剂掺量为5%时,石灰石粉掺量为5%,水泥的凝结时间进一步缩短,水泥胶砂3 d、7 d和28 d的抗压强度略有提高,当石灰石粉超过5%时,水泥的凝结时间随着石灰石粉掺量的增加反而延长,水泥的胶砂抗折、抗压强度随着石灰石粉掺量的增加而降低。水泥水化初始期和加速期的水化放热速率随着速凝剂掺量的增加而增加,掺加速凝剂后,水化加速期提前10 h,同时石灰石粉也能够提高水泥水化初始期和加速期的水化放热速率。掺加速凝剂后,水泥水化放热量反而降低了一半,但是加入石灰石粉后,水泥水化放热量增加。     

–10℃条件下氯化钙溶液对硫铝酸盐水泥性能的影响EI北大核心CSCD

研究了–10℃条件下氯化钙冷溶液拌合冷硫铝酸盐水泥所获得浆体的凝结硬化及试样的强度发展、物相组成、显微结构和氯离子含量。结果表明:分别采用16%(质量分数)、28%氯化钙冷溶液拌合的浆体存在明显而持续的水化温升过程,证实了该条件下水泥水化的启动与持续进行;提高溶液浓度,浆体达到水化温升最高温度对应的时间延长,从16%时约90 min延长至28%时约150min。采用16%氯化钙冷溶液拌合,浆体凝结硬化快、试样抗压强度高(初凝和终凝时间分别为15min和24 min,1 d和28 d抗压强度分别为41.0 MPa和85.2 MPa);而采用28%氯化钙冷溶液拌合,浆体凝结硬化慢、试样抗压强度低(初凝和终凝时间分别为85 min和155 min,1 d和28 d抗压强度分别为24.3 MPa和57.7 MPa)。溶液浓度16%时,水化产物主要为钙矾石,以针棒状晶体存在,试样中结合氯离子含量极低;而溶液浓度28%时,水化产物主要为F盐,以花瓣形六方板状晶体存在,试样中含有0.95%左右结合氯离子。–10℃条件下采用同处于负温环境的氯化钙冷溶液拌合冷硫铝酸盐水泥可实现冷物料拌合,防止浆体结冰,保证水泥持续水化,其中16%~20%氯化钙溶液拌合时可以获得较短凝结时间和较高强度。     

铁尾矿粉、砂泥粉对水泥-减水剂体系工作性能的影响

为揭示铁尾矿粉和天然河砂中砂泥粉对水泥净浆体系的影响规律,分别测试了聚羧酸减水剂（ PCA）和萘系减水剂（ FDN）与两类粉体双掺后水泥浆动电电位和流变参数。结果表明：铁尾矿粉与砂泥粉对水泥-减水剂体系工作性能的影响存在显著差异。在PCA-水泥浆与铁尾矿粉或砂泥粉的双掺体系中,含铁尾矿粉水泥浆动电电位及塑性粘度变化率明显低于含砂泥粉水泥浆体系,铁尾矿粉对水泥浆流动性影响较小;采用FDN时,含砂泥粉的水泥浆体系流动性能优于掺铁尾矿粉的水泥浆体系;当水泥浆体系中粉体外掺量达到7％时,浆体塑性粘度显著增加,浆体体系流动性较差。     

废水泥浆对水泥胶砂性能的影响

研究了废水泥浆澄清液、浆体以及干燥后的粉体三种状态的废水泥浆对水泥胶砂流动度以及抗压强度的影响。采用澄清液取代自来水会增大水泥胶砂的流动性,且不会导致抗压强度明显降低;采用水泥浆体,流动度均大于基准组,但抗压强度波动较大;采用废浆粉末取代水泥会导致流动度明显下降,且抗压强度大幅下降。     

热活化和机械活化对拜耳法赤泥性能影响

为提高赤泥基碱激发胶凝材料的力学性能,分别通过焙烧和机械研磨对赤泥基复合粉体进行活化处理.结果表明,600℃煅烧180 min制备的胶砂试件28 d抗压强度最大,为27.0 MPa,对比未煅烧处理的赤泥粉体混合物,抗压强度提高了15.3％.机械研磨300 s制备的胶砂试件28 d抗压强度最小,为20.2 MPa,比研磨60 s制备的试件抗压强度降低了16.8％.热活化可以提高碱激发材料的强度但需要控制煅烧温度,赤泥本身较细不需要研磨活化处理.     

底座连接口特征参数对显示器后壳注塑质量的影响分析

在Moldflow分析软件的基础上,对显示器后壳进行仿真研究,以翘曲变形量为质量指标,结合控制变量法进行单因素变动实验,保持注射工艺参数不变,研究显示器后壳底座连接口对制品翘曲变形的影响。对数据进行图表分析,结果表明显示器后壳尺寸定位68.58 cm(27英寸)时,底座连接口选用圆形,连接口位置距离底边26 mm,尺寸为直径21 mm的时候模具翘曲表现更好。     

The role of the symmetry and the flexibility of the anion on the characteristics of the nanostructures and the viscosities of ionic liquids☆

The transport properties of ionic liquids (ILs) are crucial properties in view of their applications in electrochem-ical devices. One of the most important advantages of ILs is that their chemical–physical properties and conse-quently their bulk performances can be well tuned by optimizing the chemical structures of their ions. This will require elucidating the structural features of the ions that fundamentally determine the characteristics of the nanostructures and the viscosities of ILs. Here we showed for the first time that the“rigidity”, the order, and the compactness of the three-dimensional ionic networks generated by the anions and the cation head groups determine the formation and the sizes of the nanostructures in the apolar domains of ILs. We also found that the properties of ionic networks are governed by the conformational flexibility and the symmetry of the anion and/or the cation head group. The thermal stability of the nanostructures of ILs was shown to be con-trolled by the sensitivity of the conformational equilibrium of the anion to the change of temperature. We showed that the viscosity of ILs is strongly related to the symmetry and the flexibility of the constitute ions rather than to the size of the nanostructures of ILs. Therefore, the characteristics of the nanostructures and the viscosities of ILs, especially the thermal stability of the nanostructures, can be fine-tuned by tailoring the symmetry and the conformational flexibility of the anion.     

浅谈设备的性能与操作对胎面压出质量的影响

简要介绍了胎面压出的工作原理及工艺过程，对设备的配置及操作对胎面压出质量的影响进行了分析，并对压出过程中常见的质量缺陷、造成的原因以及解决措施提出了自己的见解。     

Investigation of the effects of fatty acids on the compressive strength of the concrete and the grindability of the cement

In cement industry, a great energy consumption has been observed during grinding of clinker. To reduce this consumption, some waste products have been used as grinding aids.In this investigation, the effects of sunflower oil (SO), oleic acid (OA), stearic acid (SA), myristic acid (MA) and lauric acid (LA) on the fineness and strength of the cement have been examined. These aids were added into clinker in certain ratios based on the cement clinker weight and the grinding has been done for a definite time at the same condition.All of the fatty acids used increased the fineness as compared with the cement without the grinding additives. SO and OA decreased the strength significantly, LA decreased it to a lesser extent and SA increased it definitely according to the common cement. But MA did not alter the strength of the cement as much as SA. In addition, the covering of the balls influences the grinding of cement clinker unfavourably.     

煤粉流动性对GSP气化炉气力输送的影响研究

针对GSP气化装置煤粉气力输送在试车阶段出现的煤粉锁斗下料不畅、发料罐输送性能不佳等问题,从原料煤性质和工业装置的改进方面出发,通过煤粉的流动性参数的测量与研究,分析出现上述工程问题可能的内在原因,并提出工业装置改进方法,为保证GSP煤粉气力输送工业装置的正常运行提供解决办法。     

关于建立火炸药安全数据库的探讨

由反映火炸药及其制品的危险性能和用于对它们的生产、储运系统进行安全评价数学模型出发,探讨了如何建立一个全面、实用的火炸药安全评估数据库。通过对此数据库内容、数据表示方法、数据搜索方法以及建立步骤的讨论,明确了该数据库的使用对象和主要功能。     

Effect of the drafting force on the strength of the bottom of the spinneret

In spinning basalt fibres, the drafting force is in the same range as in spinning of glass fibres. The effect of the drafting force can not be considered in the calculation for the strength and rigidity of the bottom of the spinneret. __________ Translated from Khimicheskie Volokna, No. 5, pp. 47–50, September–October, 2007.