高温合金800H的动态再结晶及其模型的建立

采用单道次热压缩实验分析了变形参数对高温高强合金800H热变形的影响。结果表明:初始晶粒尺寸越小、变形温度越高、变形速率越小,越容易出现动态再结晶现象;同样,在能够发生动态再结晶的情况下,变形量的增大促使动态再结晶充分进行;利用拟合得到了800H合金的动态再结晶激活能、临界变形量模型、再结晶动力学模型、再结晶运动学模型和再结晶晶粒尺寸模型。采用Deform-2D进行晶粒度模拟,仿真模拟结果与金相统计出的再结晶晶粒尺寸变化趋势一致,平均误差为4.5μm。极小的平均误差表明所建模型与实际情况相符合,可以用于预测800H合金热变形过程中再结晶的晶粒尺寸。     

CSP热轧TRIP钢动态再结晶行为研究

摘要：采用Gleeble-3500热模拟试验机,在温度为950~1150℃、应变速率为0.1~10s-1和变形量为65%的条件下研究了CSP热轧TRIP钢的动态再结晶行为,探讨了初始奥氏体晶粒尺寸对TRIP钢动态再结晶行为的影响。研究结果表明,初始奥氏体晶粒尺寸越小,变形温度越高,应变速率越慢时,TRIP钢中奥氏体越易发生动态再结晶。其中,粗晶试样（初始奥氏体晶粒尺寸为767.54μm）在1050~1150℃内变形时,将发生动态再结晶。其热变形激活能为361539.17J/mol,确定了Zener-Holloman参数与应变速率和温度的关系式,建立了动态再结晶临界应变模型、高温奥氏体流动应力模型和动态再结晶晶粒尺寸模型,理论模拟结果与试验结果吻合较好。     

904L不锈钢动态再结晶行为

采用单道次热压缩试验,研究了904L钢在不同变形温度、不同应变速率下的真应力-应变曲线以及组织形貌,阐明了热加工过程中热变形参数对其在变形过程中发生的动态再结晶行为及微观组织演变规律的影响,揭示了其相应的软化机制。结果表明:变形温度越高,流变应力越小,动态再结晶体积分数越高,晶粒尺寸越大;同温度下,变形速率越小,应力峰值越小,晶粒尺寸越大且晶界越平直化;904L钢的动态再结晶行为随着变形温度的升高,应变速率的减小,应变量的增大而进行得越充分且较高的变形温度有利于动态再结晶的进行。     

微合金化非调质钢C38N2动态再结晶行为

针对微合金化非调质钢热轧过程的变形特征,通过Gleeble-3800热模拟试验机研究了Nb-Ti-V非调质钢C38N2(/%:0.40C、0.52Si、1.42Mn、0.010P、0.047S、0.028V、0.025 Ti、0.022Nb)在950～1 150℃,变形速率0.1～10 s-1变形量60%,单道次压缩时的奥氏体动态再结晶过程,计算得出C38N2钢的动态再结晶晶粒尺寸模型和动态再结晶状态图。结果表明,C38N2钢变形温度越高,变形速率越低,则发生动态再结晶的储蓄能越小,动态再结晶越易发生。C38N2钢的动态再结晶激活能Q_d=294.905 kJ/mol。     

904L不锈钢动态再结晶行为

采用单道次热压缩试验,研究了904L钢在不同变形温度、不同应变速率下的真应力-应变曲线以及组织形貌,阐明了热加工过程中热变形参数对其在变形过程中发生的动态再结晶行为及微观组织演变规律的影响,揭示了其相应的软化机制。结果表明:变形温度越高,流变应力越小,动态再结晶体积分数越高,晶粒尺寸越大;同温度下,变形速率越小,应力峰值越小,晶粒尺寸越大且晶界越平直化;904L钢的动态再结晶行为随着变形温度的升高,应变速率的减小,应变量的增大而进行得越充分且较高的变形温度有利于动态再结晶的进行。     

热变形对40CrMnMo钢的晶粒尺寸影响规律研究

采用了MMS-200热力模拟机以40CrMnMo钢为实验对象进行了热压缩试验,研究了变形温度850℃～1150℃,变形量0.8,应变速率在0.01～10s~(-1)条件下实验钢的热变形行为。通过分析高温下变形参数对流变应力和奥氏体晶粒尺寸的影响,建立40CrMnMo钢的稳态动态再结晶晶粒尺寸模型。结果表明:变形温度为850℃～1150℃,实验钢在应变速率0.01～0.1s~(-1)下发生连续动态再结晶,应变速率1～10s~(-1)下发生动态回复。通过引入Zener-Hollomon(Z)参数表征变形参数对稳态动态再结晶晶粒尺寸的影响,建立了稳态再结晶晶粒尺寸的数学模型,得出提高应变速率或变形温度较低能使Z参数增大,峰值应力升高且动态再结晶晶粒减小。     

Custom 450高强度不锈钢的动态再结晶行为

摘要：为了探究Custom 450钢的动态再结晶行为,采用Gleeble 3800热模拟试验机,在变形温度为1050~1200℃和应变速率为0.01~10s-1的变形条件下开展了单道次等温压缩试验。研究结果显示,在变形温度为1050~1200℃和应变速率为1.0~10s-1的变形范围内,钢虽发生了完全的动态再结晶,但应力应变曲线未表现出明显的应力峰值;钢的动态再结晶的晶粒尺寸随着变形温度的升高和应变速率的降低逐渐增大,当应变速率为001s-1时,动态再结晶晶粒发生长大。采用双曲正弦函数构建了Cutom 450钢的热变形方程,并建立了钢的动态再结晶动力学、临界应变、峰值应变及动态再结晶晶粒尺寸与Zener Holloman参数的定量关系。     

钒微合金化非调质钢48MnVS的奥氏体动态再结晶行为

实验用非调质钢48MnVS（/%:0.48C,0.60Si,1.50Mn,0.35Cr,0.14V,0.05S,0.020Al,0.0150N）由100t EAF冶炼,连铸成280 mm×360 mm坯,轧成Φ100 mm棒材。通过Gleeble-3800热模拟实验机研究了变形温度950~1150℃,变形速率0.1~10 s^-1,变形量60%的单道次压缩钒微合金非调质钢48MnVS的奥氏体再结晶过程得出真应力-应变曲线,计算得出实验钢的动态再结晶晶粒尺寸模型和动态再结晶状态图。结果表明,钒微合金化非调质钢48MnVS变形温度越高,变形速率越低,则发生动态再结晶的形变储能越小,越容易发生动态再结晶。实验钢48MnVS的动态再结晶激活能为Q_d=343.202 kJ/mol。     

高强度钢的动态再结晶行为研究

采用Gleeble1500热模拟实验机研究了高强度钢在不同条件下热变形时的动态再结晶行为以及晶粒尺寸的变化规律,确定了该钢的动态再结晶激活能为294096J/mol,建立了动态再结晶行为的数学模型,分析了变形工艺参数对再结晶行为以及晶粒尺寸的影响。变形温度和变形速率是影响动态再结晶的主要因素,一般在高的变形温度和小的变形速率下,动态再结晶才能发生。     

变形条件对GH625合金高温变形动态再结晶的影响

采用Gleeble高温压缩实验研究了变形条件对GH625合金高温变形动态再结晶的影响,结果表明:当变形程度较小时,原始晶粒内部出现大量孪晶,晶界呈现锯齿状凸出;随变形程度的增加,在晶界弓出部位开始形核,形成大量再结晶晶粒,随变形程度进一步增加,GH625合金动态再结晶体积分数增大,但是再结晶晶粒尺寸无明显变化;GH625合金动态再结晶是一个受变形温度和应变速率控制的过程,变形温度越高,动态再结晶越容易形核,应变速率越小,动态再结晶过程进行得越充分。在低应变速率条件下,GH625合金获得完全动态再结晶组织的温度随变形速率的升高而升高,而在高应变速率条件下必须考虑变形热效应对合金变形组织的影响。     

���ºϽ�800H�Ķ�̬�ٽᾧ����ģ�͵Ľ���

The effect of deformation parameters on hot deformation of superalloy 800H was studied by means of single-pass compression test. It was found that smaller initial grain size, higher deformation temperature and lower strain rate are more easily to cause dynamic recrystallization. And when dynamic recrystallization can take place during deformation, the fraction of dynamic recrystallization increases with increasing of strain. The models of dynamic recrystallization activation energy, critical strain, dynamic recrystallization kinetics, dynamic recrystallization kinematics and grain size of dynamic recrystallization for 800H were obtained through the analysis of data obtained by single-pass compression. The variation tendency for grain size simulated by Deform-2D is consistent with metallographic statistics, and the average error is 4. 5??m. Very small average error shows that the model is consistent with practical situation and can be used to predict recrystallized grain size for 800H during thermal deformation.     

Study on dynamic recrystallization behavior of hot rolled TRIP steel produced by CSP process

The dynamic recrystallization behavior of hot rolled TRIP steel produced by CSP process was studied by means of Gleeble-3500 thermal simulation testing machine in the temperature range of 950-1150℃ with the strain rate of 0.1-10s-1 and the strain of 65%. And the effect of initial austenite grain size on the dynamic recrystallization behavior of TRIP steel was explored. The results show that the finer initial austenite grain size, the higher deformation temperature and the lower strain rate, the more positive austenite dynamic recrystallization of TRIP steel. Moreover, it is found that when the coarse grained samples (initial austenite grain size is 767.54μm) deform in the range of 1050℃ to 1150℃, the austenite dynamic recrystallization will take place, and the dynamic recrystallization activation energy of TRIP steel is deduced as 361539.17J/mol. The Zener-Hollomon parameter equation as a function of strain rate and temperature is determined. And the model of critical strain for dynamic recrystallization, the flow stress model of austenite at high temperature and the grain size model for dynamic recrystallization are also established. The calculation results are coincided well with the experimental results.     

Ti 465Al 25V 10Cr 03Ni合金高温变形动态再结晶行为

 采用热模拟实验研究了变形参数(应变量、变形温度、应变速率)对Ti 465Al 25V 10Cr 03Ni合金微观变形组织的影响。研究结果表明,在应变量逐渐增加的热压缩变形过程中,一定变形量后开始出现层片弯曲、折曲或破碎,随着应变量的增加,动态再结晶形成的等轴晶粒增多,残余层片团减少。变形温度对钛铝合金的变形组织有着显著影响,提高热变形温度,有利于合金中的动态再结晶以及变形组织的均匀化,降低残余层片团的体积分数。较低的应变速率能促进变形时的动态再结晶,有利于提高变形组织的均匀性。还对γ TiAl合金动态再结晶新晶粒形成过程进行了讨论。     

高强钢300M静态再结晶动力学研究

为研究高强钢300 M静态再结晶行为,采用Gleeble-3800型热模拟试验机对300M钢进行单/双道次热压缩试验.通过双道次热压缩试验分析了变形温度、应变速率、变形量和初始晶粒尺寸对静态再结晶体积分数的影响.变形温度越高,应变速率越大,变形量越大,初始晶粒尺寸越小,则静态再结晶体积分数越大.其中变形温度、变形量和应变速率对静态再结晶体积分数影响较大,初始晶粒尺寸的影响相比较小.基于双道次热压缩试验结果建立了300 M钢的静态再结晶体积分数模型,基于单道次热压缩试验结果建立了300 M钢完全静态再结晶晶粒尺寸模型,并验证了静态再结晶体积分数模型的正确性.      

FGH4102粉末高温合金等温热模拟压缩试验及动态再结晶组织研究

本文研究了新型第四代粉末高温合金FGH4102在等温热模拟压缩过程中的组织演变,对γ′相在动态再结晶过程中的作用进行了探讨。结果表明,热等静压态合金在1060~1120℃温度范围变形时,热加工性能较好。1140℃变形后试样容易发生开裂,合金热加工性能较差。合金在γ+γ′两相区变形时均发生了不同程度的动态再结晶,再结晶晶粒尺寸远小于热等静压态的晶粒尺寸。变形过程中,尺寸较大的γ′相起到促进动态再结晶的作用。变形参数对动态再结晶的影响非常显著。低温高应变速率变形时,γ′相促进动态再结晶形核占主导地位,再结晶晶粒比较细小;高温低应变速率变形时,晶粒长大逐渐占据主导地位,再结晶晶粒尺寸较大。     

核电用奥氏体不锈钢的动态再结晶行为

利用Gleeble-1500D热模拟试验机对316LN奥氏体不锈钢进行单道次热压缩试验,分别设置变形温度为900~1200℃、应变速率为0.001~10 s-1、真应变为0.1~0.9及试样的初始晶粒度为122~297μm之间,以研究热变形条件及初始晶粒度对316LN钢动态再结晶行为的影响.对试验数据进行处理,得到临界应变与峰值应变以及临界应力与峰值应力的比值分别为0.38和0.89,建立了动态再结晶动力学方程和晶粒尺寸演变方程.对建立的动态再结晶模型进行修正,将修正后的模型嵌入DEFORM-3D有限元模拟软件中进行计算,发现修正模型的模拟值和试验值符合较好,证明修正模型的准确性.      

26MnB5钢的动态再结晶行为

利用Gleeble-1500热模拟压缩试验获得了26MnB5钢在880～1000℃、0.01～10s-1、最大变形55％条件下的真应力-真应变曲线,研究了26MnB5钢在试验条件下的动态再结晶行为.结果表明:26MnB5的真应力-真应变曲线在高温、低应变速率条件下出现明显峰值点特征,意味着样品发生了动态再结晶;26MnB5再结晶程度和奥氏体晶粒均匀度随温度的增加或应变速率的降低而提高,而晶粒平均尺寸则表现出先减小后增大的趋势;利用Johnson-Mehl-Avrami(JMA)方程可以建立26MnB5钢动态再结晶动力学模型,模型预测值与实测值基本吻合.