AlGaN/GaN异质结构的欧姆接触

通过改变Ti/Al的结构及退火条件,研究了AlGaN/GaN异质结构上Ti/Al/Ni/Au金属体系所形成的欧姆接触.结果表明,Ti/Al/Ni/Au金属厚度分别为20,120,55和45nm,退火条件为高纯N2气氛中850℃、30s时在AlGaN/GaN异质结构上获得了良好的欧姆接触,其比接触电阻率为3.30×10-6Ω·cm2.SEM分析表明该条件下的欧姆接触具有良好的表面形貌,可以很好地满足高性能AlGaN/GaN高电子迁移率晶体管制造的要求.     

AlGaN/GaN异质结构的欧姆接触

通过改变Ti/Al的结构及退火条件,研究了AlGaN/GaN异质结构上Ti/Al/Ni/Au金属体系所形成的欧姆接触.结果表明,Ti/Al/Ni/Au金属厚度分别为20,120,55和45nm,退火条件为高纯N2气氛中850℃、30s时在AlGaN/GaN异质结构上获得了良好的欧姆接触,其比接触电阻率为3.30×10-6Ω·cm2.SEM分析表明该条件下的欧姆接触具有良好的表面形貌,可以很好地满足高性能AlGaN/GaN高电子迁移率晶体管制造的要求.     

用于紫外探测器的AlGaN/GaN异质结构的Ti/Al/Ni/Au欧姆接触特性

采用Ti/Al/Ni/Au多层金属体系在Al0.27Ga0.73N/GaN异质结构上制备了欧姆接触.分别采用线性传输线方法(LTLM)和圆形传输线方法(CTLM)对其电阻率进行了测试.当Ti(10nm)/Al(100nm)/Ni(40nm)/Au(100nm)金属体系在650℃高纯N2气氛中退火30s时,测量得到的最小比接触电阻率为1.46×10-5Ω·cm2.并制备了Al0.27Ga0.73N/GaN光导型紫外探测器,通过测试发现探测器的暗电流.电压曲线呈线性分布.实验结果表明在Al0.27 Ga0.73N/GaN异质结构上获得了好的欧姆接触,能够满足制备高性能AlGaN/GaN紫外探测器的要求.     

用于紫外探测器的AlGaN/GaN异质结构的Ti/Al/Ni/Au欧姆接触特性

采用Ti/Al/Ni/Au多层金属体系在Al0.27Ga0.73N/GaN异质结构上制备了欧姆接触. 分别采用线性传输线方法(LTLM)和圆形传输线方法(CTLM)对其电阻率进行了测试. 当Ti(10nm)/Al(100nm)/Ni(40nm)/Au(100nm)金属体系在650℃高纯N2气氛中退火30s时,测量得到的最小比接触电阻率为1.46E-5Ω·cm2. 并制备了Al0.27Ga0.73N/GaN光导型紫外探测器,通过测试发现探测器的暗电流-电压曲线呈线性分布. 实验结果表明在Al0.27Ga0.73N/GaN异质结构上获得了好的欧姆接触,能够满足制备高性能AlGaN/GaN紫外探测器的要求.     

n-GaN表面Ti/Al/Ti/Au电极的电学特性

实验研究了淀积在GaN上的Ti/Al/Ti/Au电极的电学和热学特性,绘制了不同退火温度下的I-V曲线,得到了最低的欧姆接触电阻率(ρs=1.2×10-4 Ω·cm2),并通过X射线衍射谱分析了GaN与Ti/Al/Ti/Au电极接触表面在退火过程中的固相反应.实验结果表明,在Ti/Al表面增加Ti/Au保护层能够保证Al层在高温时不发生球化和氧化,电极更稳定可靠能够进一步提高欧姆接触特性.     

n型4H-SiC上Ni/Pt和Ti/Pt欧姆接触(英文)

研究了Ni/Pt和Ti/Pt金属在n型4H-SiC上的欧姆接触。在1 020℃退火后,Ni/Pt与n型4H-SiC欧姆接触的比接触电阻为2.2×10-6Ω·cm2。Ti/Pt与n型4H-SiC欧姆接触的比接触电阻为5.4×10-6Ω·cm2,退火温度为1 050℃。虽然Ni的功函数比Ti的功函数高,但是Ni比Ti更容易与n型4H-SiC形成欧姆接触。使用能谱分析仪(EDX)分析了Ni/Pt和Ti/Pt金属与4HSiC接触面的元素,观察到C原子相对于Pt原子的原子数分数随退火温度的变化而不同。实验验证了在n型4H-SiC中退火导致的碳空位起施主作用是有利于欧姆接触形成的主要原因。     

非故意掺杂GaN上Ti/Al/Ni/Au欧姆接触研究

基于圆形传输线模型,研究了背景载流子浓度为71016cm3的非故意掺杂GaN与Ti/Al/Ni/Au多层金属之间欧姆接触的形成。样品在N2气氛中,分别经过温度450,550,700,800,900℃的1 min快速热退火处理后发现,当退火温度高于700℃欧姆接触开始形成,随着温度升高欧姆接触电阻持续下降,在900℃时获得了最低比接触电阻6.6106O·cm2。研究表明,要获得低的欧姆接触电阻,需要Al与Ti发生充分固相反应,并穿透Ti层到达GaN表面;同时,GaN中N外扩散到金属中,在GaN表面产生N空位起施主作用,可提高界面掺杂浓度,从而有助于电子隧穿界面而形成良好欧姆接触。     

金属/n型AlGaN欧姆接触

用传输线模型对n型AlGaN(n-AlGaN)上Au/Pt/Al/Ti多金属层欧姆接触进行了接触电阻率的测量.在850℃退火5min后,测得欧姆接触电阻率达1.6×10-4Ω·cm2.经X射线衍射分析,Au/Pt/Al/Ti/n-AlGaN界面固相反应得出在500℃以上退火过程中,AlGaN层中N原子向外扩散,在AlGaN表面附近形成n型重掺杂层,导致欧姆接触电阻率下降;随退火温度的升高,N原子外扩散加剧,到800℃以上退火在Au/Pt/Al/Ti/n-AlGaN界面形成Ti2N相,导致欧姆接触电阻率进一步下降.     

金属/n型AlGaN欧姆接触

用传输线模型对n型AlGaN(n-AlGaN)上Au/Pt/Al/Ti多金属层欧姆接触进行了接触电阻率的测量.在850℃退火5min后,测得欧姆接触电阻率达1.6×10-4Ω·cm2.经X射线衍射分析,Au/Pt/Al/Ti/n-AlGaN界面固相反应得出在500℃以上退火过程中,AlGaN层中N原子向外扩散,在AlGaN表面附近形成n型重掺杂层,导致欧姆接触电阻率下降;随退火温度的升高,N原子外扩散加剧,到800℃以上退火在Au/Pt/Al/Ti/n-AlGaN界面形成Ti2N相,导致欧姆接触电阻率进一步下降.     

退火参数对p型GaAs欧姆接触性能的影响

采用磁控溅射的方法在p型GaAs衬底上沉积了Ti/Pt/Au金属薄膜,研究了退火工艺参数(温度和时间)对p-GaAs/Ti/Pt/Au欧姆接触性能的影响。结果表明:p-GaAs上制作的Ti/Pt/Au金属系统能在很短的退火时间(60 s)内形成很好的欧姆接触。过分延长退火时间,并不能改善系统的欧姆接触性能。退火温度在400~450℃时均可得到较好的欧姆接触。当退火温度为420℃,退火时间为120 s时,比接触电阻率达到最低,为1.41×10–6.cm2。     

GaN紫外探测器的Ti/Al接触的电学特性

在非故意掺杂的和掺Si的GaN薄膜上蒸镀Ti(24nm)/Al(nm)薄膜,氮气环境下400～800℃范围内进行退火。实验结果表明,在非故意掺杂的样品上,随退火温度的升高,肖特基势垒高度下降,理想因子升高,表面状况逐渐变差,600℃退火形成较低接触电阻的欧姆接触,比接触电阻率为3.03×10-4Ωcm2,而载流子浓度为5.88×1018cm-3的掺Si的样品未退火就形成欧姆接触,比接触电阻可达到4.03×10-4Ωcm2。     

Ti/Al/Ni/Au在GaN N面上的欧姆接触

以Ti/Al/Ni/Au作为欧姆接触金属体系,通过电感耦合等离子体(ICP)刻蚀的预处理,在氢化物气相外延法生长的单晶氮化镓(GaN)材料的N面实现了良好的欧姆接触,其比接触电阻率为3.7×10-4 Ω·cm2.通过扫描电子显微镜、原子力显微镜、阴极荧光和光致发光谱对GaN N面的表面、光学特性进行了对比表征.结果表明:未刻蚀GaN衬底的N面表面存在一定的损伤层,导致近表面处含有大量缺陷,不利于欧姆接触的形成;而ICP刻蚀处理有效地去除了损伤层.X射线光电子能谱(XPS)分析显示刻蚀后样品的Ga 3d结合能比未刻蚀样品向高能方向移动了约0.3 eV,其肖特基势垒则相应降低,有利于欧姆接触的形成.同时对Fe掺杂半绝缘GaN的N面也进行了刻蚀处理,同样实现了良好的Ti/Al/Ni/Au欧姆接触,其比接触电阻率为0.12 Ω·cm2.     

高Al组分n-AlGaN的Ti/Al/Ti/Au欧姆接触

采用Ti/Al/Ti/Au多层金属电极对高Al组分n-AlxGa1-xN(x=0.6)欧姆接触的制备进行了研究,通过优化Ti接触层厚度以及合金退火条件,获得了较低的比接触电阻率(5.67×10-5Ω.cm2)。研究证实,Ti接触层厚度对欧姆接触特性有着重要影响,同时发现,高低温两步退火方式之所以能够改善欧姆接触特性的本质是与Al3Ti及TiN各自的生成条件直接相关,即低温利于生成Al3Ti,高温利于生成TiN,而这对n型欧姆接触的有效形成至关重要。     

Structural properties of alloyed Ti/Al/Ti/Au and Ti/Al/Mo/Au ohmic contacts to AlGaN/GaN

Two alloyed ohmic contact structures for AlGaN/GaN–Ti/Al/Ti/Au and Ti/Al/Mo/Au were studied. Both structures were optimized for minimum ohmic contact resistance. Structures grown on sapphire and SiC substrates were used to investigate structural properties of ohmic contacts to AlGaN/GaN. Ohmic contacts to AlGaN/GaN on SiC showed higher contact resistance values compared to contacts to AlGaN/GaN on sapphire. Ohmic contact metals were etched on samples after annealing. The alloyed interface was studied with backside illumination under an optical microscope. Alloyed inclusions associated with threading dislocations were observed on the surface. For the AlGaN/GaN on SiC sample the inclusion density was an order of magnitude lower than for the sample on sapphire. Conductive atomic force microscopy with carbon nanotube tip was used to investigate topography and conductivity profile of the surface after ohmic contact metal removal by etching.     

Improved Long-Term Thermal Stability At 350°C Of TiB2–Based Ohmic Contacts On AlGaN/GaN High Electron Mobility Transistors

AlGaN/GaN High Electron Mobility Transistors (HEMTs) were fabricated with Ti/Al/TiB₂/Ti/Au source/drain Ohmic contacts and a variety of gate metal schemes (Pt/Au, Ni/Au, Pt/TiB₂/Au or Ni/TiB₂/Au) and subjected to long-term annealing at 350°C. By comparison with companion devices with conventional Ti/Al/Pt/Au Ohmic contacts and Pt/Au gate contacts, the HEMTs with boride-based Ohmic metal and either Pt/Au, Ni/Au or Ni/TiB₂/Au gate metal showed superior stability of both source-drain current and transconductance after 25 days aging at 350°C.     

基于AlGaN/GaN HEMT的源漏整体刻蚀欧姆接触结构

研究了源漏整体刻蚀欧姆接触结构对AlGaN/GaN高电子迁移率晶体管(HEMT)的欧姆接触电阻和金属电极表面形貌的影响.利用传输线模型(TLM)对样品的电学性能进行测试,使用原子力显微镜(AFM)对样品的表面形貌进行表征,通过透射电子显微镜(TEM)和X射线能谱仪(EDS)对样品的剖面微结构和界面反应进行表征与分析.实验结果显示,采用Ti/Al/Ni/Au(20 nm/120 nm/45 nm/55 nm)金属和源漏整体刻蚀欧姆接触结构,在合金温度870 c℃,升温20 s,退火50 s条件下,欧姆接触电阻最低为0.13 Ω·mm,方块电阻为363.14 Ω/□,比接触电阻率为4.54×10-7Ω·cm2,形成了良好的欧姆接触,降低了器件的导通电阻.     

Formation of Ta/Ti/Al/Mo/Au ohmic contacts to an AlGaN/AlN/GaN heterostructure grown on a silicon substrate

The features of the formation of Ta/Ti/Al/Mo/Au ohmic contacts to a Al_0.26Ga_0.74N/AlN/GaN heterostructure grown on semi-insulating Si(111) substrates are studied. The dependences of the contact resistance on the Al (90, 120, 150, 180 nm) and Ti (15, 30 nm) layer thickness and optimal temperature-time annealing conditions are determined for each studied metallization scheme. It is shown that the minimum achievable contact resistance monotonically increases from 0.43 to 0.58 Ω mm as the Al layer thickness increases from 90 to 180 nm at unchanged Ta, Ti, Mo, Au layer thicknesses. A change in the Ti layer thickness from 15 to 30 nm has no significant effect on the minimum contact resistance. The least contact resistance of 0.4 Ω mm is achieved for Ta/Ti/Al/Mo/Au layers with thicknesses of 10/15/90/40/25 nm, respectively. The optimal annealing temperature for this metallization variant is 825°C at a process duration of 30 s. The grown ohmic contacts have smooth contact-area edges and flat morphology of their surface.     

Alloyed Si/Al-based ohmic contacts to AlGaN/GaN nitride heterostructures

For the first time in Russia, the Si/Al/Ti/Au alloyed contact composition is investigated for the formation of ohmic contacts to AlGaN/GaN heterostructures using thermal annealing. The obtained results are compared with those for conventional Ti/Al/Ni/Au ohmic contacts. Use of the composition under investigation makes it possible to decrease the annealing temperature to 675–700°C, which results in improvement in the morphology of alloyed ohmic contacts in comparison with conventional contacts. The value of the contact resistance using the Si/Al-based composition to the AlGaN/GaN heterostructure is obtained in relation to the temperature and annealing duration. It is shown that no qualitative change in the resistance occurs at an annealing duration of several minutes in the temperature range of 700–750°C. In the temperature range of 675–700°C, there is an asymptotic decrease in the contact resistance with increasing annealing duration. The smallest value of the contact resistance amounts to 0.41 Ω mm.