1.
通过溶胶-凝胶法制备了La2／3Sr1／3MnO3＋xWO3（x=0～25％）系列多晶陶瓷样品．结果表明。随着WO3掺杂量的增加，样品的电阻率增大，金属-绝缘体相变温度（Tp）值下降．在1．4T磁场下，当0≤x≤12．5％时，样品的室温磁电阻值从5％增大到15％，提高了200％．当12．5％〈x≤25％时，室温磁电阻值从15％降低到0．这对磁电阻材料在室温下的应用提供实验依据． 相似文献
2.
Effect of Fe3O4 segregation at grain boundaries on the electrical transport and magnetic properties of La0.67Ca0.33MnO3 is investigated. The experimental results show that the Fe3O4 segregation not only shifts the paramagnetic-ferromagnetic transition temperature of La0.6TCa0.33MnO3 to a lower temperature region but also induces a new transition in a lower temperature region. Meanwhile, the transition processes observed in both the resistivity and magnetization curves are obviously widened. Compared to pure La0.67Ca0.33MnO3, we assume that the Fe3O4 segregation level at the grain boundaries can modify the electrical transport and magnetic properties of La0.67Ca0.33MnO3. 相似文献
3.
通过固相反应法制备了(1-x)La2/3Ba1/3MnO3 xTiO2(x=0％～5％)多晶陶瓷样品，实验发现，随着TiO2掺杂量的增加，电阻率明显增大，金属绝缘相转变温度Tp值下降．通过室温(300K)和低温(78K)下不同磁场的磁电阻计算表明，适量的TiO2掺杂会明显提高材料的磁电阻性能；在1T磁场下，TiO2掺杂量为1％的样品室温磁电阻达到12％，这是未掺杂La2/3Ba1/3MnO3相同条件下的3倍，为磁电阻传感器研究提供了实验依据。 相似文献
4.
WO3掺杂的La2/3Ba1/3MnO3电输运与磁电阻特性 总被引：1，自引：0，他引：1
在溶胶-凝胶法制备的La2/3Ba1/3MnO3（LBMO）微粉中掺入WO3，制备了La2/3Ba1/3MnO3＋xWO3（x=0～0．20）多晶陶瓷样品．实验发现，随x增加，样品的电阻率增加，金属-绝缘相变温度（Tp）由340K下降到26lK，在1T的磁场下，当0〈x≤0．05时，样品的室温磁电阻迅速上升，从4％增加到10．5％，当0．05〈x≤0．10时，样品的室温磁电阻从10．5％增加到11．5％，上升速度明显放缓，当0．10〈x≤0．20时，样品的室温磁电阻从11．5％降低到2％，这为磁电阻器件研究提供了实验依据． 相似文献
1