核-壳结构P(AM-co-MAA)-W-Ag复合微球的制备

以丙烯酰胺(acrylamide, AM)和甲基丙烯酸(methacrylic acid, MAA)的共聚微凝胶(P(AM-co-MAA))为模板, 通过离心沉积法将钨粉沉积于高分子微凝胶表面, 得到具有核-壳结构的P(AM-co-MAA)-W复合微球; 再以经聚乙烯基吡咯烷酮(PVP)修饰的P(AM-co-MAA)-W复合微球为模板, 在硝酸银溶液中充分溶胀后, 通过向反相悬浮体系中缓慢通入氨气, 制备得到了具有核-壳结构的P(AM-co-MAA)-W-Ag双金属复合微球材料. 实验发现, 通过改变制备过程中AgNO3的初始浓度和PVP的用量等条件, 可以改变复合微球表面银的沉积量; 并结合实验结果初步提出了银的形成机理, 即PVP的存在, 不仅可以作为稳定剂固定Ag+离子, 同时可以作为还原剂促进Ag+还原为Ag的反应.     

多层核-壳结构P(AM-co-MAA)/W/UF复合微球制备研究

以反相悬浮聚合技术合成的丙烯酰胺(acrylamide,AM)和甲基丙烯酸(methacrylic acid,MAA)共聚高分子微凝胶P(AM-co-MAA)为模板,通过离心沉积法将微米级钨粉沉积于高分子微凝胶表面,得到具有核-壳结构的P(AM-co-MAA)/W复合微球材料;再以P(AM-co-MAA)/W复合微球为模板,通过控制甲醛和尿素的缩聚反应在模板与油/水相界面进行,制备得到了具有多层核-壳结构的高分子/钨/脲醛树脂[P(AM-co-MAA)/W/Urea-formaldehyde resin]复合微球材料.利用扫描电子显微镜(SEM)、红外(FT-IR)、X射线衍射(XRD)和热分析(TGA)等手段对复合微球进行了表征.实验结果表明,外壳层脲醛树脂的包覆量、复合微球的表面形貌可通过改变甲醛和尿素溶液的浓度、甲醛和尿素的物质的量之比等因素进行控制.复合微球的导电性测试结果表明,P(AM-co-MAA)/W复合微球表面壳层脲醛树脂包覆前后,其电导率由1.9×10-3降低为0.9×10-8S·m-1.该研究获得的三层核-壳复合微球材料其外层脲醛树脂的包覆较为完整、致密,其导电性接近于绝缘材料,为含钨复合微球作为电子元件的抗辐射涂层材料打下了基础.     

聚苯乙烯/银核/壳复合微球的制备及其表征

通过分散聚合法制备了单分散性好,粒径均一的聚苯乙烯(PS)微球.以PS微球为核,用浓硫酸进行表面改性,使其表面带有负电.加入一定量的[Ag(NH3)2]+溶液,由于静电吸引,使其吸附在PS微球表面,通过化学还原的方法制备了PS/Ag核/壳结构复合微球.采用透射电镜(TEM)、扫描电镜(SEM)、红外光谱(IR)、X射线衍射(XRD)以及紫外-可见光谱对PS/Ag复合微球进行表征.结果表明:通过PS微球的表面改性,在其表面引入了磺酸基团,提高了微球表面的电负性和亲水性,对包覆过程起到了很好的促进作用;通过稳定剂(PVP)和不同还原剂(一缩二乙二醇DEG和乙二醇EG)的使用,形成的PS/Ag核/壳复合微球形貌不一样,同时研究表明制备出的PS/Ag复合微球可以用于催化剂催化还原有机染料溶液,表现出很好的催化活性.     

Ag_3PO_4/BiVO_4复合光催化剂的制备及可见光催化降解染料(英文)

结合回流法和原位沉淀法成功制备磷酸银/矾酸铋(Ag3PO4/BiVO4)复合光催化剂.通过X射线衍射(XRD)、场发射扫描电子显微镜(FESEM)、能量色散X射线光谱(EDS)、紫外-可见漫反射光谱(UV-Vis DRS)及光致发光(PL)光谱对制备样品进行表征.XRD和FESEM结果表明成功制备Ag3PO4/BiVO4复合光催化剂.采用节能发光二极管灯(LED)作为可见光光源,在低消耗光催化系统中评价制备样品可见光催化降解染料的活性.当Ag3PO4和BiVO4的组成摩尔比为1:3时,复合Ag3PO4/BiVO4光催化剂呈现出高于纯相Ag3PO4的催化活性,可减少Ag3PO4的使用量.Ag3PO4/BiVO4复合光催化剂在中性溶液中表现出高活性,同时证实其对阳离子染料的光催化降解效果强于阴离子染料.在Ag3PO4/BiVO4系统中,超氧自由基和空穴是主要的活性物种.经过三次循环利用,Ag3PO4/BiVO4复合催化剂的可见光催化活性表现出不同程度的降低,归因于降解过程中产生金属银.     

细乳液法制备聚硅氧烷-Ag纳米复合微球及其抗菌性

首先以苯乙烯(St)及3-甲基丙烯酰氧基三甲氧基硅烷(MPS)为反应单体,通过细乳液聚合制备表面功能化聚硅氧烷微球,然后利用该微球表面的硅羟基及硅氧烷基团对Ag+的吸附及还原作用原位制备聚硅氧烷-Ag纳米复合微球。采用透射电镜(TEM)、紫外(UV-Vis)、热重分析(TG)及X射线衍射(XRD)等对聚硅氧烷-Ag纳米复合微球的形貌和组成进行了表征。研究表明:改变MPS和硝酸银的用量可调控聚硅氧烷-Ag纳米复合微球的形貌及表面银含量;抗菌实验结果表明,聚硅氧烷-Ag纳米复合微球具有较好的抑菌性。     

苯乙烯和N-乙烯基吡咯烷酮共聚物/Ag复合微球的制备及性能研究

首先用无皂乳液聚合法制备了单分散聚苯乙烯(PSt)乳液,以此为种子乳液,使用N,N-亚甲基双丙烯酰胺(MBA)为交联剂,过硫酸钾(KPS)为引发剂,进行苯乙烯和N-乙烯基吡咯烷酮(NVP)共聚合制备了以PSt为核、St和NVP共聚物为壳的具有核-壳结构的聚合物微球(P(St-NVP)).以此微球为模板通过化学沉积法得到了粒径分布均匀、单分散的P(St-NVP)/Ag复合微球.傅里叶红外光谱、X-射线衍射、扫描电镜、透射电镜、激光粒度仪和紫外-可见光谱对复合微球的结构、形貌、物相及催化性能进行了表征.结果表明,P(St-NVP)/Ag复合微球具有规则的球形结构,粒径在400～700 nm之间,随交联剂浓度或种子乳液浓度的增加,复合微球粒径减小.粒径在十几个纳米左右的银粒子均匀分布在微球表面和内部.载银复合微球在NaBH4还原4-硝基苯酚为4-氨基苯酚的模型反应中表现出较高的催化活性.     

制备方法对模板法制备SiO_2中空微球形貌的影响

模板法是制备无机中空微球的重要方法之一.首先通过苯乙烯和甲基丙烯酸的无皂乳液聚合法制得表面含羧基、粒径为360nm的单分散聚苯乙烯(PSt)乳胶粒,并以此为模板,分别采用表面改性-前驱体水解法(PHC)和SiO2纳米颗粒层层自组装法(LBL),制备出了不同壳层厚度的PSt/SiO2核壳结构复合微球,然后经500℃煅烧4h,得到SiO2中空微球.利用透射电镜和扫描电镜对微球结构形态进行了表征.研究表明,首先利用γ-氨丙基三乙氧基硅烷(KH-550)对PSt模板微球进行表面改性、然后再在乙醇-水混合介质中进行原硅酸乙酯(TEOS)水解与缩合反应的PHC法,是制备PSt/SiO2核壳结构复合微球的简便方法,复合微球经煅烧可制得表面均匀、结构致密、壳层厚度和形貌可控的SiO2中空微球;而LBL法制备PSt/SiO2核壳结构复合微球的工艺复杂,煅烧后所得SiO2中空微球结构疏松,易于破碎.     

聚苯乙烯/银纳米粒子复合微球的合成及催化性能

首先通过乳液聚合和浓硫酸酸化制备表面富含磺酸根的磺化聚苯乙烯(PS)微球(直径532 nm),再用其静电吸附[Ag(NH_3)_2]~+离子,最后采用聚乙烯吡咯烷酮还原表面吸附的[Ag(NH_3)_2]~+离子,得到了负载银纳米粒子的PS/AgNPs复合微球.采用扫描电子显微镜、透射电子显微镜、紫外-可见光谱、红外光谱和X射线衍射表征了PS/AgNPs复合微球,并考察了其对甲基蓝(MB)的催化性能.结果表明,Ag纳米粒子高度分散在磺化PS微球表面;该PS/AgNPs复合微球对催化转化MB有较高的催化活性,并可多次重复利用.本研究在催化降解有机污染物方面有一定的实用价值.     

水热法制备Ag3PO4/HAP复合光催化剂及其光催化性能（英文）

以牡蛎壳为原料,利用水热法合成高纯度的羟基磷灰石(HAP)载体,经磷酸银负载后,制备出纳米棒状Ag3PO4/HAP复合光催化剂。利用扫描电镜(SEM)、高分辨透射电镜(HRTEM)、X射线衍射(XRD)、X射线光电子能谱仪(XPS)对样品进行表征,并考察不同的制备因素对催化剂降解亚甲基蓝溶液性能的影响。结果表明,当质量比为1∶2时制备的1∶2-Ag3PO4/HAP催化剂的表现最为突出,在10 min时即可达到50%的降解率,在40 min时基本降解完全,是一种高效的复合光催化剂。     

Ag/Ag_3PO_4/g-C_3N_4复合光催化剂的合成与再生及其可见光下的光催化性能(英文)

研究了用离子交换沉淀法制备的Ag/Ag3PO4/g-C3N4的可见光光催化性能及再生方法.通过X射线衍射(XRD)、场发射扫描电子显微镜(FESEM)、紫外-可见(UV-Vis)吸收光谱及X射线光电子能谱(XPS)对其进行了结构特性分析.XRD结果显示再生后催化剂的结构未发生改变.FESEM及UV-Vis分析结果说明催化剂由Ag3PO4与g-C3N4复合而成.XPS分析结果表明催化剂表面出现少量的银单质.利用可见光(λ420nm)照射下的苯酚降解实验评价了样品的光催化活性,并通过活性物种及能带结构的分析对催化剂的光催化机理进行了推测.研究表明,Ag/Ag3PO4/g-C3N4的光催化活性明显高于纯Ag3PO4及纯g-C3N4,主要原因归结为单质银、Ag3PO4及g-C3N4的协同效应.经过氧化氢和磷酸氢铵钠(NaNH4HPO4)的再生可完全恢复催化剂的活性,这表明该绿色环保的再生方法可实现Ag/Ag3PO4/g-C3N4催化剂在环境中的实际应用.     

Ag-polymer composite microspheres with patterned surface structures

Novel silver-poly(acrylamide-co-methacrylic acid) [Ag-P(AM-co-MAA)] composite microspheres, in tens of micrometer size range, with patterned surface and core/shell structures were prepared by chemical reduction of Ag₂CrO₄-P(AM-co-MAA) composite microspheres in ethanol. Characterization with various techniques revealed that the chemical composition of the “shell” is dominated by Ag, but the “core” is dominated by the template, P(AM-co-MAA). It was also demonstrated that the surface morphology of the Ag-polymer composite microspheres is similar to that of their precursors and can be controlled to a certain extent by varying the composition of template copolymer, approaches, and amount of Ag₂CrO₄ deposited. This morphology transfer technique is also applicable for other silver salts-polymer composite microspheres. The same silver-polymer composite microspheres with very different morphology have also been prepared by utilizing this technique, but the different precursor microspheres, Ag₃PO₄-P(AM-co-MAA), were used. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.     

表面图案化磁性复合微球的原位制备与表征

采用反相悬浮聚合法合成了丙烯酸(AA)含量不同的N-异丙基丙烯酰胺-丙烯酸共聚物P(NIPAM-co-AA)微凝胶, 并以其作为微反应器, 通过原位外源沉积法制备了一系列微米级、表面具有图案化结构的SiO₂-Fe₃O₄-P(NIPAM-co-AA)磁性复合微球. 实验结果表明, 复合微球的表面结构与微凝胶的组成、Fe₃O₄和SiO₂的沉积量有关. 在微球表面进行修饰, 可得到表面带有氨基等官能基团的磁性复合材料. 将这种功能化磁性微球用于识别生物大分子并进一步用于生物医学领域具有重要的意义.     

Design of Cadmium Hydroxyapatite Hierarchical Structures with Adjustable Morphology by a Template-free Hydrothermal Route

Cadmium hydroxyapatite(Cd-Hap) hierarchical structures with novel morphologies were successfully synthesized via a simple template-free and mild hydrothermal method. By properly monitoring the initial p H value of the reaction solutions, the morphology of the Cd-Hap crystals could be tuned to be bunch-like(consist of nanosized cuboids), quasi peanut-like(consist of nanoparticles) and flower-like(consist of assembled bundles units). On the basis of a series of contrast experiments over time, the probable growth mechanism and fabrication process of the products were proposed. The optical and photocatalytic properties of the obtained Cd-Hap hierarchical structures were firstly investigated. The results showed that pure Cd-Hap could only absorb UV light with wavelength shorter than ~350 nm while hydroxyapatite supported Ag_3PO_4 composites showed a pronounced photocatalytic activity upon decomposition of methyl orange dye in aqueous solution under visible light irradiation. The support of hydroxyapatite can also greatly reduce the cost of expensive Ag_3PO_4 photocatalysts in practical applications.     

Controllable synthesis of CuS-P(AM-co-MAA) composite microspheres with patterned surface structures

Copper sulfide-poly(acrylamide-co-methacrylic acid) (CuS-P(AM-co-MAA)) composite microspheres with patterned surface structures have been synthesized in a controllable manner by means of the polymer microgel template method. The formation of CuS particles can be regulated by controlling the decomposition of thioacetamide (TAA) in acidic solution. Compared with the microgel template, the surface morphologies of the composite microspheres are characterized by compact and creased textures. The surface morphology of the composite microspheres has been found to be mainly influenced by the amount of copper sulfide precipitated and hence by the rate of H(2)S gas generation. This study might provide a potential route for controlling the synthesis of various metal sulfide-polymer composites with patterned surface structures.     

硫化物-高分子复合微球表面形貌与模板组成关系的研究

以N-异丙基丙烯酰胺(NIPAM)和甲基丙烯酸(MAA)为单体, 通过反相悬浮聚合法制备了多种MAA含量不同的阴离子型P(NIPAM-co-MAA)共聚微凝胶. 以这些共聚微凝胶为模板, 在不同表面活性剂存在下, 合成了一系列CuS(CdS、ZnS)-P(NIPAM-co-MAA)无机-有机复合微球材料, 研究了表面活性剂种类, 模板组成等因素对上述硫化物-高分子复合微球表面形貌的影响. 结果表明, 实验条件下所得复合微球表面均具有图案化结构, 该结构明显依赖于表面活性剂的种类和模板微凝胶的组成. 就模型体系而言, 随表面活性剂Span-20、Span-80和Span-85的HLB(亲水亲油平衡)值降低, 微球表面形貌趋于粗糙, 但仍然十分规整; 就模板组成而言, 模板中MAA含量增加使得复合微球的表面形貌变得更加精细. 据此, 认为通过选用合适的表面活性剂和微凝胶模板可以在一定范围内调控这些无机-有机复合微球的表面形貌, 从而为后续应用研究奠定基础.     

Preparation and characterization of hollow carambola-shaped silver sulfide microspheres using a microwave-assisted template-free method

A simple and convenient method, free of template, has been proposed to synthesize hollow carambolashaped Ag_2 S microspheres with Ag NO3, thiourea(TU), Na Cl and diethanolamine as reagents using a microwave-assisted method, at low temperatures of below 100 8C. Powder X-ray diffraction(XRD),scanning electron microscopy(FESEM) and high resolution transmission electron microscopy(HRTEM)were employed to characterize the morphology and composition of those microspheres. The results indicated that the hollow carambola-shaped silver sulfide microspheres(with high purity and homogeneous morphology) were prepared by an Ostwald ripening process. A possible formation mechanism of hollow carambola-shaped Ag2 S microspheres was proposed.     

Graphene-wrapped Ag_3PO_4/LaCO_3OH heterostructures for water purification under visible light

We demonstrated a unique synthesis approach of graphene(GR)-wrapped Ag_3PO_4/LaCO_3OH(APO/LCO)heterostructures by an in-situ wet chemical method. FESEM analysis reveals the formation of rhombic dodecahedrons of APO decorated with LCO and later wrapped with GR flakes. Optical studies shows two absorption edges corresponding to the band gap energies of APO(2.41 eV) and LCO(4.1 eV). Considering the absorption edge of the heterostructures in the visible region, the photocatalytic activities of photocatalysts containing different APO/LCO mass ratios were evaluated by the degradation of MB. GR-decorated composite with 20% LCO(APO/LCO20/GR) exhibited the highest photocatalytic activity for MB degradation, with a rate constant, k of 0.541 min~(-1). The photocatalytic activity of APO/LCO20/GR more greatly enhanced than those of the individual constituents(APO, LCO, APO/LCO20). The enhanced photocatalytic activity of the heterostructure can be attributed to the co-catalytic effect of LCO as well as intriguing physicochemical properties of GR. To understand the enhanced photocatalytic activity of the heterostructures the photocatalytic reaction mechanism is proposed in detail. The recyclability of the APO/LCO/GR composite photocatalyst is further evaluated by reusing the catalyst in replicate photocatalytic experiments which shows consistent photocatalytic activity thereby confirms the stability and reusability of heterostructure photocatalyst.     

具有核壳结构磁性复合微球的制备与表征

采用两步法制备了具有核壳结构的Fe3O4/P(MMA/DVB)(core)-P(St/GMA/DVB)(shell)磁性复合微球.首先,用改进的细乳液聚合制备了Fe3O4/P(MMA/DVB)微球;然后,加入总量不同的苯乙烯(St)、甲基丙烯酸缩水甘油酯(GMA)和二乙烯基苯(DVB),通过种子乳液聚合,制备了不同磁含量的核壳结构的磁性复合微球.分别用X-射线衍射(XRD)、高倍透射电镜(HR-TEM)、热重分析(TGA)、振动样品磁力计(VSM)等手段对磁性微球的性能进行了表征.实验结果表明,Fe3O4/P(MMA/DVB)微球的磁含量为84 wt%;通过改变加入壳层单体的量,核壳复合微球的磁含量可控在20 wt%~76 wt%之间.该微球具有超顺磁性,相应的饱和磁化强度为12~50Am2/kg.