立方氮化硼（c－BN）膜的制备、性能及应用

本文综合分析了立方氮化硼（ｃ－ＢＮ）膜的制备方法，介绍了ｃ－ＢＮ膜的结构及其机械、电学、光学和热学性能。最后总结了ｃ－ＢＮ膜在机械和电子领域的应用概况。     

ICP-AES法测定封严涂层中BN含量

利用IC－AES法测定了封严涂层的BN，并对样品的溶解方法，仪器工作参数，光谱干扰等进行了研究。方法的相对标准偏差＜2％（n=10)，加标回收率在95％以上，方法简便，可靠，结果令人满意。     

TiB2与BN复相陶瓷的渗流模型

试验结果证实,TiB₂与BN复相陶瓷的导电性能符合渗流理论,原料粉粒度配比下,其渗流阀值为V_c%=22.9%;原料粉粒度比的改变将改变渗流阀值,从而改变各配比下的电阻率值;TiB₂与BN在SPS系统中快速烧结,晶粒的尺度比与原料粉的粒度比基本保持一致。     

ArF准分子激光立方氮化硼薄膜的制备

采用ＡｒＦ准分子脉冲激光沉积方法（ＰＬＤ），以六方氮化硼（ｈ－ＢＮ）作靶在Ｓｉ（１００）衬底上制备氮化硼薄膜。ＸＲＤ及ＦＴＩＲ透射谱测量表明生成的氮化硼薄膜是含有少量六方氮化硼结构的立方氮化硼（Ｃ－ＢＮ）．ＡＥＳ测量表明不同条件下生成的薄膜中Ｎ与Ｂ的相对含量是不同的，最大比例近乎为１：１，薄膜的维氏显微硬度ＨＶ最大值为１５８０ｋｇ／ｍｍ２。     

Recent Advances in Boron Nitride Based Hybrid Polymer Nanocomposites

Boron nitride (BN) is an eminent inorganic compound having many interesting characteristics such as improved oxidation resistance, mechanical strength, good thermal conductivity (TC), higher bandgap, high chemical stability, thermal stability, high hydrophobicity, and electrical insulation. The use of BN as a filler in polymers is a well-established strategy to tailor the properties of polymer composites. Recent studies depict an interesting urge to reap the synergistic effect of various nanofillers with BN in the form of hybrids. Hence the consolidation of the works on BN based hybrid fillers would definitely attract researchers so that these new filler systems could be transformed into useful polymer nanocomposites in future. This review article focuses on the synthesis and characterization of various boron nitride based hybrids in detail. Moreover, the review also throws light on different BN hybrid reinforced polymer nanocomposites (PNCs) and their thermal, electrical, electronic as well as biomedical applications in a detailed manner. Thus the review anticipates serving as a tool toward understanding the recent trends in the field of boron nitride hybrid based ternary polymer composites.     

10B21含硼冷镦钢轧后结疤成因分析及工艺改进

通过实验及热力学分析得出,轧制10B21钢结疤形成主要原因为钢中平均N含量为127×10^-6,导致铸坯角部冷却过程中在奥氏体晶界析出细小的BN和AlN夹杂,增加了铸坯的裂纹敏感性,形成铸坯裂纹。通过提高铁水比≥920 kg/t、转炉终点C-T-P(碳-温度-磷)命中率≥85%、出钢口圆流出钢以及LF加热次数≤3次,时间≤25 min等措施可将钢中的氮含量稳定控制在≤50×10^-6,有效避免10B21钢轧后盘条结疤,提高成材率,降低成本。     

AlN-BN复合陶瓷制备工艺研究进展

本文详细介绍了AlN-BN复合陶瓷材料制备工艺的研究状况,包括AlN、BN粉末的合成制备和AlN-BN复合材料的制备工艺,评述了各种方法和工艺的优缺点。最后指出了粉末制备工艺中的自蔓延高温合成法、电弧等离子体法和烧结工艺中的反应烧结、放电等离子烧结是很有价值的研究方向。     

AlN-BN复合陶瓷制备工艺研究进展

本文详细介绍了AlN-BN复合陶瓷材料制备工艺的研究状况,包括AlN、BN粉末的合成制备和AlN-BN复合材料的制备工艺,评述了各种方法和工艺的优缺点。最后指出了粉末制备工艺中的自蔓延高温合成法、电弧等离子体法和烧结工艺中的反应烧结、放电等离子烧结是很有价值的研究方向。