Effect of copper pretreatment on the zincate process and subsequent electroplating of a protective copper/nickel deposit on the AZ91D magnesium alloy

To obtain a durable Ni coating with excellent adhesion strength on an AZ91D Mg alloy, a pretreatment was performed with a small amount of Cu²⁺ ions added to the activation bath used in the pretreatment prior to the plating process. In the pretreatment activation process, a high density Cu layer was deposited on both the α-phase and β-phase areas of the substrate accompanied with Mg dissolution. The Cu deposit acted as nucleation seeds for the Zn deposition in the following zincate process which provided a uniform and dense Zn layer almost completely covering the substrate. Then a thin Cu layer was electroplated on this zincated substrate as an undercoating for the succeeding electroplating with Ni. Cross-sectional scanning electron microscopy observations showed that the Cu deposited by the pretreatment enabled the deposition of a protective Ni layer with few defects. This structure also contributed to the improvement of adhesion strength and corrosion resistance as compared with the non-Cu added sample.     

Observation of corrosion behavior of stainless steels in a salt manufacturing plant environment using the multichannel electrode method

Crevice corrosion of four kinds of stainless steel, SUS316L, NAS64, NAS185N and NAS254N, in saturated NaCl solution at temperatures up to 100 °C was investigated using the multichannel electrode method. In this method, a pile of five individual working electrodes (WEs) of stainless steel sheet were embedded in epoxy resin and a small hole penetrating through the five WEs was treated as an artificial crevice. Time transition and distribution of the coupling current between the five WEs were measured as a function of crevice depth, kind of stainless steel, temperature and concentration of dissolved oxygen (DO). Anodic or cathodic coupling current on the five WEs of SUS316L changed depending on their corroding state. On the other hand, NAS64, NAS185N and NAS254N showed that the WE outside the crevice contributed as a cathode and that WEs inside the crevice contributed as an anode. The coupling current on SUS316L was strongly affected by concentration of DO, while the coupling current on NAS64, NAS185N and NAS254N was not affected by DO, probably due to the establishment of a passive state inside the crevice.     

Display Method for Online Bookstore Emulating Real Bookstore by WebGL

Thanks to the spread of the Internet, opportunities to use online bookstores have been increasing in recent years. However, it is difficult for the typical customer to intuitively grasp which book sells well or which book is recommended by the shop. We have therefore developed a display system for virtual bookstores in which an image of books arranged in a bookshelf or stacked on a table is reproduced by using WebGL. Since the amount of book stock that is managed by the server side needs to be changed as orders come in from clients, we introduce a server side technology using a hypertext preprocessor(PHP).     

資源環境の保全をめざした二次副産材を導入するコンクリ一ト材料の発展的利用に関する研究

日本では,21世紀半ばに人工の固体物質の代表である解体コンクリート塊の排出量がピークを迎えると同時に,最終処分が困難になる状況が想定されていることから,コンクリート材料の完全資源型の利活用要求はより一層高まるといえる.本研究は,副産微粉,再生骨材などの二次副産材を積極的に混和し,同一産地*種類型の調合条件のもとで,コンクリートの物性改善,資源有効利活用を目的としたコンクリートを製造し,その基礎的物性の評価と環境影響評価を行い,環境保全に資するコンクリート材料の発展的利用のあり方を検討した.