排序方式: 共有8条查询结果,搜索用时 15 毫秒
1
1.
Pd(OH)2/C催化剂是制备六硝基六氮杂异伍兹烷(HNIW,C L-20)的关键材料。选择三种市售的活性炭为载体,采用浸渍沉积法制备了几种六苄基六氮杂异伍兹烷(HBIW)氢解脱苄Pd(OH)2/C催化剂。考察了载体活性炭的表面性质、孔径分布、催化剂制备温度、碱的种类及钯负载量对Pd(OH)2/C催化剂的催化活性的影响。催化活性和N2吸附、程序升温脱附(TPD)、粉末X射线衍射(XRD)和透射电镜(TEM)的特性表明,活性炭的表面性质、孔径分布、反应温度和钯负载量显著影响Pd(OH)2/C催化剂的催化活性,而活性炭的比表面积和催化剂制备过程中所用碱的种类不是影响Pd(OH)2/C催化剂性能的关键因素。用30%硝酸预处理AC RO S O rganics公司产的颗粒状活性炭为载体,碳酸钠为碱源,在反应温度5℃下,制得的9%Pd(O H)2/C催化剂有最佳的催化活性。催化剂中钯用量为底物HBIW的0.3%(质量分数)时,氢解脱苄乙酰化产物收率达93%。 相似文献
2.
3.
4.
A facile procedure was carried out to prepare macroporous perovskite-type complex oxide catalysts of La1-xKxCo1-yFeyO3(x=0,0.1,y=0,0.1) by using the combined method of organic ligation and solution combustion.This method could ensure the formation of the desired macroporous structures and the desired crystal phases of the prepared catalysts.It was found that the macroporous catalysts showed higher catalytic activities for soot combustion than that of the corresponding nanometric samples,and the macroporous ... 相似文献
5.
从Au纳米粒子出发,利用竖直浸渍提拉法(dip-coating)成功将Au纳米粒子负载于基底(云母片/单晶硅片),并以3-氨丙基三甲氧基硅烷(APTMS)对单晶硅片进行改性,得到具有密度分布不同的Au纳米粒子two dimensional(2D)组装结构,制备方法简单易行。利用原子力显微镜(AFM)表征了不同制备条件下Au纳米粒子在基底表面的分布状态,结果表明,Au纳米粒子溶胶和偶联剂APTMS的浓度以及浸渍时间对Au纳米粒子在单晶硅片表面的密度分布起到决定性作用。 相似文献
6.
7.
大孔钙钛矿型氧化物催化剂制备及其对碳烟燃烧的催化性能 总被引:1,自引:1,他引:0
采用有机络合和溶液燃烧相结合的方法制备了La1-xKxFe1-yCoyO3 (x=0, 0.1;y=0, 0.5)催化剂,通过X射线衍射(XRD)、傅立叶红外吸收光谱(FT-IR)和扫描电镜等分析手段对La1-xKxFe1-yCoyO3 催化剂进行了表征。结果表明,制备的催化剂为钙钛矿型复合氧化物,具有蜂窝状大孔结构,平均孔径大于50 nm。采用超声辅助的方法让碳烟颗粒扩散到催化剂孔道内,利用程序升温反应技术评价了La1-xKxFe1-yCoyO3 催化剂对柴油车尾气中碳烟颗粒物的催化燃烧活性,结果表明,大孔钙钛矿催化剂具有较高的碳烟催化燃烧活性,与纯碳烟的燃烧峰值温度(Tm)相比,下降了(165~239) ℃。通过A位和B位离子的部分取代,可以使钙钛矿型氧化物催化剂的催化氧化性能进一步提高,m降低超过70 ℃。 相似文献
8.