掺钪AlN材料特性及HBAR器件性能研究

该文基于掺钪AlN薄膜制备了高次谐波体声波谐振器(HBAR),研究了钪(Sc)掺杂浓度对AlN压电薄膜材料特性及器件性能的影响。研究表明,当掺入Sc的摩尔分数从0增加到25%时,压电应力系数e₃₃增加、刚度 下降,导致Al₁-_xSc_xN压电薄膜的机电耦合系数 从5.6%提升至15.8%,从而使HBAR器件的有效机电耦合系数 提升了3倍。同时,当Sc掺杂摩尔分数达25%时,Al₁-_xSc_xN(x为Sc掺杂摩尔分数)压电薄膜的声速下降13%,声学损耗提高,导致HBAR器件的谐振频率和品质因数降低。     

Effects of (Li0.5Sm0.5)/W co-substitution and sintering temperature on the structure and electrical properties of ultrahigh Curie temperature piezoceramics,Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9

With co-substitution of (Li_0.5Sm_0.5) at A site and W at B site, the electrical properties of modified Ca_0.92(Li_0.5Sm_0.5)_0.08Bi₂Nb_2-xW_xO₉ [(CLS)BN-xW, x = 0, 0.015 and 0.03] piezoceramics with ultrahigh Curie temperature (T_C) of > 930 °C were enhanced dramatically. The increased resistivity induced by the co-substitution ensure them to be polarized under an enough high field. Combined with the increase of spontaneous ferroelectric polarization (P_S), the significant enhancements in the piezoelectric, dielectric and ferroelectric properties can be obtained in the composition x = 0.015. Furthermore, the piezoelectric activity (d₃₃) and bulk resistivity (ρ_b) of (CLS)BN-0.015 W can be further enhanced at an appropriate sintering temperature. This optimum composition sintered at 1170 °C shows ultrahigh T_C of ～948 °C, d₃₃ of ～17.3 pC/N and ρ_b of ～6.9 MΩ cm at 600 °C, which are comparable to those of the reported high-temperature Aurivillius piezoceramics with T_C > 850 °C.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Marine Phospholipids from Fishery By-Products Attenuate Atherosclerosis

In this study, the anti-atherosclerotic properties of three marine phospholipids (MPLs) extracts from fishery by-products including codfish roe, squid gonad, and shrimp head are verified. Their effects on key factors involved in atherosclerosis are examined and compared to explore whether the differences in their constitutions lead to the differences in the function. All three MPLs dampen oxidation of low- density lipoproteins (LDL) in vitro. Treating RAW264.7 macrophages and HUVECs endothelial cells with each MPLs ranging 10–100 µg mL⁻¹ does not decrease cell viability, yet ox-LDL caused cytotoxicity of both cells are alleviated by 50 or 100 µg mL⁻¹ MPLs treatment. In addition, the three MPLs reduce ox-LDL induced macrophage foam-like transition, mainly through inhibition of lipid uptake. Of the three MPLs, the one from squid gonad exhibits the best effect. On the other hand, all three MPLs modulate inflammatory responses, equally, by inhibiting the adhesion of monocytes to endothelial cells, and decreasing secretion of pro-inflammatory cytokines IL-6 and MCP-1. Using a high-cholesterol diet induced zebrafish model, it is found that all three MPLs, especially the one from squid gonad, alleviates cholesterol accumulation in early plaques, and decreases total cholesterol as well as lipid peroxide in vivo. Practical Applications: As a way of making the best of the increasingly scarce marine resources, valuable lipid components can be recovered from by-products and wastes from the fishery industry. Here, we tested the anti-atherosclerotic effects and the mechanisms of three MPLs extracted from codfish roe, squid gonad, and shrimp head. Our study provides further evidence that marine phospholipids extracted from fishery by-products could protect against atherosclerosis, and helps to elucidate the structure-function relationship of MPLs.     

肠靶向海藻酸钙基微胶囊的制备及控释性能研究

利用毛细管共挤出技术结合静电吸附和仿生硅化的方法，制备了海藻酸钙-壳聚糖/精蛋白/二氧化硅(ACPSi)复合微胶囊。ACPSi复合微胶囊的平均粒径约3.18 mm，单分散性好，囊壁最外层的二氧化硅层可抑制其在肠液pH环境中的溶胀，增强囊的机械稳定性。将羟丙甲基纤维素邻苯二甲酸酯(HPMCP)肠溶微球作为释药“微阀门”，嵌入囊壁可以更好地控制微胶囊的释药行为。以吲哚美辛为模型药物，当药物浓度为22.5 mg/ml时，ACPSi载药微胶囊在pH 2.5模拟胃液中3 h时累计释药率仅为0.33%，而转移至pH 6.8模拟肠液中19 h时累计释药率为77.78%；囊壁嵌入HPMCP微球后，22 h时累计释药率可提高约4%。因此，该复合微胶囊具有良好的肠靶向作用和控释特性，作为口服肠靶向缓控释制剂具有良好的应用前景。     

基于神经网络和遗传算法的锭子弹性管性能优化

为得到减振弹性管对下锭胆的支承弹性和锭子高速运动下的稳定性等性能的最优匹配效率,依据减振弹性管的等效抗弯刚度及底部等效刚度系数公式,利用MatLab数值分析软件构建弹性管抗弯刚度和底部挠度数学模型。首先,结合Isight优化软件基于径向基神经网络构建其近似模型,且使精度达到可接受水平,并以模型的关键结构参数弹性模量、螺距、槽宽、壁厚为设计变量,结合遗传算法对弹性管抗弯刚度和底部挠度进行多目标优化设计,得到Pareto最优解集和Pareto前沿图,确定出减振弹性管结构工艺参数的优化方案。通过对优化数据进行分析发现,该方案在保证减振弹性管弹性的同时,其底部振幅明显减弱。     

基于模糊多模型的堆芯功率控制

传统的堆芯功率PID控制器是基于单一功率水平处的堆芯局部模型设计的，难以准确描述整个堆芯功率水平范围的控制。因此，本文基于5个不同功率水平下的传递函数模型，通过三角隶属度函数加权，建立堆芯模糊多模型，并依据该模型设计堆芯功率模糊PID控制。以TMI型压水堆堆芯为对象，开展不同初始功率水平下的堆芯功率跟踪、堆芯进口温度扰动的控制仿真。结果表明，基于模糊多模型设计的堆芯功率模糊PID控制器可实现对堆芯功率的良好控制。     

蓝藻基生物降解共混膜的力学性能

以聚乙烯醇(PVA)和水华蓝藻为主要原料,通过溶液铺膜法制备了蓝藻/PVA共混膜,采用万能试验机,研究了不同助剂对蓝藻/PVA共混膜力学性能的影响。结果表明,蓝藻的添加显著降低了共混膜的力学性能。当添加比例为PVA的1/2时,膜的拉伸强度和断裂伸长率分别比无藻处理下降了65.89%和79.57%。甘油、尿素显著提升了蓝藻/PVA共混膜的断裂伸长率,当添加比例为蓝藻的1/2时,分别能使共混膜的断裂伸长率提高73.20倍和62.02倍。虽然柠檬酸、硅烷偶联剂能够提升蓝藻/PVA共混膜的拉伸强度,但只能在低剂量时促进断裂伸长率的小幅提高,当柠檬酸添加比例为蓝藻的1/40时,膜的断裂伸长率能提高4.41倍,而当硅烷偶联剂添加比例为蓝藻的1/20时,膜的断裂伸长率能提高1.49倍。尿素与甘油复合增塑,更有利于提升共混膜的断裂伸长率。硅烷偶联剂与甘油复合增塑,更有利于提升共混膜的拉伸强度。     

Photopolymerization synthesis of polyacrylic acid dispersant with methoxysilicon end groups and its application in a nano‐SiO2 aqueous system

In order to improve the dispersity and stability of the nano‐SiO₂ aqueous system with high solid content, a kind of polyacrylic acid dispersant with methoxysilicon end groups (KH590‐PAA) was synthesized by photopolymerization of acrylic acid (AA) initiated with (3‐mercaptopropyl)trimethoxysilane (KH590). After adding KH590‐PAA into the nano‐SiO₂ aqueous dispersion system (20 wt% solid content), the viscosity and the curing time of the system were measured with a rotational viscometer and the inverted bottle method. Moreover, the dispersion mechanism of KH590‐PAA for the nano‐SiO₂ aqueous system was researched by measuring the adsorption capacity, the particle size and the zeta potential of the nanoparticles with a conductivity meter, dynamic light scattering, SEM and TEM, respectively. The results showed that the methoxysilicon groups in KH590‐PAA could react with hydroxyl groups on the surface of nano‐SiO₂ in the process of stirring, which enhanced the adsorption capacity of the dispersant and then increased the surface charge of the particles. Therefore, electrostatic repulsion and steric hindrance effects between the SiO₂ nanoparticles could be further enhanced by adding the KH590‐PAA dispersant, and then the nano‐SiO₂ aqueous system exhibited better dispersity and stability. Besides, the dispersion properties of SiO₂ nanoparticles in water were closely related to the addition amount and the molecular weight of the KH590‐PAA dispersant. © 2018 Society of Chemical Industry