Fabrication of robust Bi3.25La0.75Ti3O12 thin film resistant to hydrogen damage

Ferroelectric bismuth lanthanum titanate (Bi_3.25La_0.75Ti₃O₁₂; BLT) thin films were deposited on Pt/TiO₂/SiO₂/Si substrate by chemical solution deposition method. The films were crystallized in the temperature range of 600–700 °C. The spontaneous polarization (P_s) and the switching polarization (2P_r) of BLT film annealed at 700 °C for 30 min were 22.6 μC/cm² and 29.1 μC/cm², respectively. Moreover, the BLT capacitor did not show any significant reduction of hysteresis for 90 min at 300 °C in the forming gas atmosphere.     

Structural, dielectric and optical properties of Ba(Ti, Zr)O3 thin films prepared by chemical solution deposition

Ba(Ti_0.95Zr_0.05)O₃ (BTZ) thin films grown on Pt/Ti/SiO₂/Si(100) substrates were prepared by chemical solution deposition. The structure and surface morphology of BTZ thin films has been studied by X-ray diffraction (XRD) and scanning electron microscope (SEM). At 100 kHz, the dielectric constant and dissipation factor of the BTZ film are 121 and 0.016, respectively. The ellipsometric spectrum of the BTZ thin film annealed at 730 °C was measured in the range of wavelength from 355 to 1700 nm. Assuming a five-layer model (air/surface roughness layer/BTZ/interface layer/Pt) for the BTZ thin films on platinized silicon substrates, the optical constant spectra (refractive index n and the extinction coefficient k) of the BTZ thin films were obtained.     

Alkoxide route to La0.5Sr0.5CoO3 epitaxial thin films on SrTiO3

An all alkoxide based sol–gel route was investigated for preparation of epitaxial La_0.5Sr_0.5CoO₃ (LSCO) films on 100 SrTiO₃ (STO) substrates. Films with 20–30 to 80–100 nm thickness were prepared by spin-coating 0.2–0.6 M (metal) solutions on the STO substrates and heat treatment to 800 °C at 2 °C min^− 1, 30 min, in air. The films were epitaxial with a cube-on-cube alignment and the LSCO cell was strained to match the STO substrate of 3.905 Å closely; a and b = 3.894 Å and 3.897 Å for the 20–30 and 80–100 nm films, respectively. The c-axis was compressed to 3.789 Å and 3.782 Å for the 20–30 and 80–100 nm films, respectively, which resulted in an almost unchanged cell volume as compared to polycrystalline film and nano-phase powders prepared in the same way. The SEM study showed mainly very smooth, featureless surfaces, but also some defects. A film prepared in the same way on an -Al₂O₃ substrate was dense and polycrystalline with crystallite sizes in the range 10–50 nm and gave cubic cell dimensions of a_c = 3.825 Å. The conductivity of the ca 30–40 nm thick polycrystalline film was 1.7 mΩcm, while the epitaxial 80–100 nm film had a conductivity of around 1.9 mΩcm.     

Synthesis, structure refinement and characterization of tetrahydrated acid gadolinium diphosphate HGdP2O7·4H2O

Synthesis and single crystal structure are reported for a new gadolinium acid diphosphate tetrahydrate HGdP₂O₇·4H₂O. This salt crystallizes in the monoclinic system, space group P2₁/n, with the following unit-cell parameters: a = 6.6137(2) Å, b = 11.4954(4) Å, c = 11.377(4) Å, β = 87.53(2)° and Z = 4. Its crystal structure was refined to R = 0.0333 using 1783 reflections. The corresponding atomic arrangement can be described as an alternation of corrugated layers of monohydrogendiphosphate groups and GdO₈ polyhedra parallel to the () plane. The cohesion between the different diphosphoric groups is provided by strong hydrogen bonding involving the W4 water molecule.

IR and Raman spectra of HGdP₂O₇·4H₂O confirm the existence of the characteristic bands of diphosphate group in 980–700 cm⁻¹ area. The IR spectrum reveals also the characteristic bands of water molecules vibration (3600–3230 cm⁻¹) and acidic hydrogen ones (2340 cm⁻¹). TG and DTA investigations show that the dehydration of this salt occurs between 79 and 900 °C. It decomposes after dehydration into an amorphous phase. Gadolinium diphosphate Gd₄(P₂O₇)₃ was obtained by heating HGdP₂O₇·4H₂O in a static air furnace at 850 °C for 48 h.     

New transparent conducting MgIn2O4---Zn2In2O5 thin films prepared by magnetron sputtering

New materials for a transparent conducting oxide film are demonstrated. Highly transparent Zn₂In₂O₅ films with a resistivity of 3.9 × 10⁻⁴ Ω cm were prepared on substrates at room temperature using a pseudobinary compound powder target composed of ZnO (50 mol.%) and In₂O₃ (50 mol.%) by r.f. magnetron sputtering. MgIn₂O₄---Zn₂In₂O₅ films were prepared using MgIn₂O₄ targets with a ZnO content of 0–100 wt.%. The resistivity of the deposited films gradually decreased from 2 × 10⁻³ to 3.9 × 10⁻⁴ Ω cm as the Zn/(Mg + Zn) atomic ratio introduced into the films was increased. The greatest transparency was obtained in a MgIn₂O₄ film. The optical absorption edge of the films decreased as the Zn/(Mg + Zn) atomic ratio was increased, corresponding to the bandgap energy of their materials. It was found that the resistance of the undoped Zn₂In₂O₅ films was more stable than either the undoped MgIn₂O₄, ZnO or In₂O₃ films in oxidizing environments at high temperatures.     

Preparation and optical properties of sol–gel derived Er-doped Al2O3–Ta2O5 films

Thin films of the system xAl₂O₃–(100 − x)Ta₂O₅–1Er₂O₃ were prepared by a sol–gel method and a dip-coating technique. The influences of the composition and the crystallization of the films on Er³⁺ optical properties were investigated. Results of X-ray diffraction indicated that the crystallization temperature of Ta₂O₅ increased from 800 to 1000 °C with increased values of x. In crystallized films, the intensities of the visible fluorescence and upconversion fluorescence tend to decrease with an increase in x values, due to the high phonon energy of Al₂O₃; the strongest fluorescence is observed in a crystallized film for x = 4 heat treated at 1000 °C. In amorphous films obtained by heat treatment at relatively low temperatures the Er³⁺ fluorescence could not be observed because strong fluorescence from organic residues remaining in the films thoroughly covered the Er³⁺ fluorescence. On the other hand, the Er³⁺ upconversion fluorescence in the amorphous films was observed to be stronger than that in the crystallized films. The strongest upconversion fluorescence is observed in an amorphous film for x = 75 heat treated at 800 °C.     

Investigation on the cross sensitivity of NO2 sensors based on In2O3 thin films prepared by sol-gel and vacuum thermal evaporation

In₂O₃ thin films have been prepared from commercially available pure In₂O₃ powders by high vacuum thermal evaporation (HVTE) and from indium iso-propoxide solutions by sol-gel techniques (SG). The films have been deposited on sapphire substrates provided with platinum interdigital sputtered electrodes. The as-deposited HVTE and SG films have been annealed at 500°C for 24 and 1 h, respectively. The film morphology, crystalline phase and chemical composition have been characterised by SEM, glancing angle XRD and XPS techniques. After annealing at 500°C the films’ microstructure turns from amorphous to crystalline with the development of highly crystalline cubic In₂O_3−x (JCPDS card 6-0416). XPS characterisation has revealed the formation of stoichiometric In₂O₃ (HVTE) and nearly stoichiometric In₂O_3−x (SG) after annealing. SEM characterisation has highlighted substantial morphological differences between the SG (highly porous microstructure) and HVTE (denser) films. All the films show the highest sensitivity to NO₂ gas (0.7–7 ppm concentration range), at 250°C working temperature. At this temperature and 0.7 ppm NO₂ the calculated sensitivities (S=R_g/R_a) yield S=10 and S=7 for SG and HVTE, respectively. No cross sensitivity have been found by exposing the In₂O₃ films to CO and CH₄. Negligible H₂O cross has resulted in the 40–80% relative humidity range, as well as to 1 ppm Cl₂ and 10 ppm NO. Only 1000 ppm C₂H₅OH has resulted to have a significant cross to the NO₂ response.     

Deposition and dielectric properties of CaCu3Ti4O12 thin films on Pt/Ti/SiO2/Si substrates using pulsed-laser deposition

CaCu₃Ti₄O₁₂ (CCTO) thin films were successfully deposited on Pt/Ti/SiO₂/Si(1 0 0) substrates using pulsed-laser deposition technique. The crystalline structure and the surface morphology of the CCTO thin films were greatly affected by the substrate temperature and oxygen pressure. Thin films with a (2 2 0) preferential orientation were obtained at the substrate temperature above 700 °C and oxygen pressure above 13.3 Pa. The 480-nm thin films deposited under 720 °C and 26.6 Pa have a fairly high dielectric constant of near 2000 at 10 kHz and room temperature. The values of the dielectric constant and loss and their temperature-dependence under different frequency are comparable with those obtained in the epitaxial CCTO films grown on oxide substrates.     

Preparation of highly c-axis-oriented Bi4Ti3O12 thin films and their crystallographic, dielectric and optical properties

Bismuth titanate (Bi₄Ti₃O₁₂) thin films with a high c-axis orientation up to 99% were prepared on (100)-oriented silicon wafers by r.f. planar magnetron sputtering using a Bi₂TiO₅ ceramic target at a substrate temperature of 600 °C. From the Auger electron spectroscopy depth profile of the film, there is no evidence of interdiffusion of a specific element between the film and the substrate. Relative dielectric constant of these films depends on film thickness. The behavior was explained assuming a low-dielectric-constant interface layer. Using this assumption, the relative dielectric constant of Bi₄Ti₃O₁₂ film was estimated to be approximately 140. This value is close to that along the c axis in a bulk form. The remanent polarization and the coercive field were 0.8 μC cm⁻² and 20 kV cm⁻¹, respectively.     

Optical properties of a-(Se70Te30)100−x(Se98 Bi2)x thin films

Measurements of optical constants (absorption coefficient, refractive index, extinction coefficient, real and imaginary part of the dielectric constant) have been made on a-(Se₇₀Te₃₀)_100−x (Se₉₈Bi₂)_x thin films (where x=0, 5, 10, 15 and 20) of thickness 2000 Å in the wavelength range 450–1000 nm. It is found that the optical bandgap decreases with the increase of Se₉₈Bi₂ concentration in the a-(Se₇₀Te₃₀)_100−x(Se₉₈Bi₂)_x system. The value of refractive index (n) decreases, while the extinction coefficient (k) increases with increasing photon energy. The results are interpreted in terms of concentration of localized states varying effective Fermi level.     

Fabrication of a depletion mode GaAs MOSFET using Al2O3 as a gate insulator through the selective wet oxidation of AlAs

A 1 μm thick undoped GaAs buffer layer, a 1500 Å thick n-type GaAs layer, an undoped 500 Å thick AlAs layer and a 50 Å thick GaAs cap layer were consecutively grown by molecular beam epitaxy (MBE) on a [100] oriented semi-insulating GaAs substrate. The AlAs layer was oxidized in a N₂ bubbled H₂O vapor ambient at 400°C for 3 h and fully converted to Al₂O₃ for use as a gate insulator. The I–V characteristics, having a maximum drain current of 10.6 mA, a current cut-off voltage of −4.5 V and a maximum transconductance value of 11.25 mS/mm, indicate that the selective wet thermal oxidation of AlAs/GaAs was successful in producing a depletion mode GaAs MOSFET.     

Fabrication and characterization of (1−x)SrBi2Ta2O9–xBi3TaTiO9 layered structure solid solution thin films for ferroelectric random access memory (FRAM) applications

We report on the properties of (1−x)SrBi₂Ta₂O₉–xBi₃TaTiO₉ solid solution thin films for ferroelectric non-volatile memory applications. The solid solution thin films fabricated by modified metalorganic solution deposition technique showed much improved properties compared to SrBi₂Ta₂O₉. A pyrochlore free crystalline phase was obtained at a low annealing temperature of 600°C and grain size was found to be considerably increased for the solid solution compositions. The film properties were found to be strongly dependent on the composition and annealing temperatures. The measured dielectric constant of the solid solution thin films was in the range 180–225 for films with 10–50% of Bi₃TaTiO₉ content in the solid solution. Ferroelectric properties of (1−x)SrBi₂Ta₂O₉–xBi₃TaTiO₉ thin films were significantly improved compared to SrBi₂Ta₂O₉. For example, the observed remanent polarization (2P_r) and coercive field (E_c) values for films with 0.7SrBi₂Ta₂O₉–0.3Bi₃TaTiO₉ composition, annealed at 650°C, were 12.4 μC/cm² and 80 kV/cm, respectively. The solid solution thin films showed less than 5% decay of the polarization charge after 10¹⁰ switching cycles and good memory retention characteristics after about 10⁶ s of memory retention. The improved microstructural and ferroelectric properties of (1−x)SrBi₂Ta₂O₉–xBi₃TaTiO₉ thin films compared to SrBi₂Ta₂O₉, especially at lower annealing temperatures, suggest their suitability for high density FRAM applications.     

Deposition of Sm2O3 doped CeO2 thin films from Ce(DPM)4 and Sm(DPM)3 (DPM=2,2,6,6-tetramethyl-3,5-heptanedionato) by aerosol-assisted metal–organic chemical vapor deposition

Samarium-doped ceria (SDC) thin films were prepared from Sm(DPM)₃ (DPM = 2,2,6,6-tetramethyl-3,5-heptanedionato) and Ce(DPM)₄ using the aerosol-assisted metal–organic chemical vapor deposition method. -Al₂O₃ and NiO-YSZ (YSZ = Y₂O₃-stabilized ZrO₂) disks were chosen as substrates in order to investigate the difference in the growth process on the two substrates. Single cubic structure could be obtained on either -Al₂O₃ or NiO-YSZ substrates at deposition temperatures above 450 °C; the similar structure between YSZ and SDC results in matching growth compared with the deposition on -Al₂O₃ substrate. A typical columnar structure could be obtained at 650 °C on -Al₂O₃ substrate and a more uniform surface was produced on NiO-YSZ substrate at 500 °C. The composition of SDC film deposited at 450 °C is close to that of precursor solution (Sm : Ce = 1 : 4), higher or lower deposition temperature will both lead to sharp deviation from this elemental ratio. The different thermal properties of Sm(DPM)₃ and Ce(DPM)₄ may be the key reason for the variation in composition with the increase of deposition temperature.     

Preparation of Pt-PtOx thin films as electrode for memory capacitors

Pt-PtO_x thin films were prepared on Si(100) substrates at temperatures from 30 to 700°C by reactive r.f. magnetron sputtering with platinum target. Deposition atmosphere was varied with O₂/Ar flow ratio. The deposited films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy and scanning electron microscopy. Resistively of the deposited films was measured by d.c. four probe method. The films mainly consisted of amorphous PtO and Pt₃O₄ (or Pt₂O₃) below 400°C, and amorphous Pt was increased in the film as a deposition temperature increased to 600°C. When deposition temperature was thoroughly increased, (111) oriented pure Pt films were formed at 700°C. Compounds included in the films strongly depended on substrate temperature rather than O₂/Ar flow ratio. Electrical resistivity of Pt-PtO_x films was measured to be from the order of 10⁻¹ Ω cm to 10⁻⁵ Ω cm, which was related to the amount of Pt phase included in the deposited films.     

Characterization of indium zinc oxide thin films prepared by pulsed laser deposition using a Zn3In2O6 target

Using a Zn₃In₂O₆ target, indium-zinc oxide films were prepared by pulsed laser deposition. The influence of the substrate deposition temperature and the oxygen pressure on the structure, optical and electrical properties were studied. Crystalline films are obtained for substrate temperatures above 200°C. At the optimum substrate deposition temperature of 500°C and the optimum oxygen pressure of 10⁻³ mbar, both conditions that indeed lead to the highest conductivity, Zn₃In₂O₆ films exhibit a transparency of 85% in the visible region and a conductivity of 1000 S/cm. Depositions carried out in oxygen and reducing gas, 93% Ar/7% H₂, result in large discrepancies between the target stoichiometry and the film composition. The Zn/In (at.%) ratio of 1.5 is only preserved for oxygen pressures of 10⁻²–10⁻³ mbar and a 93% Ar/7% H₂ pressure of 10⁻² mbar. The optical properties are basically not affected by the type of atmosphere used during the film deposition, unlike the conductivity which significantly increases from 80 to 1400 S/cm for a film deposited in 10⁻² mbar of O₂ and in 93% Ar/7% H₂, respectively.     

Structural, chemical, and electrical characterisation of reactively sputtered WSx thin films

WS_x films were sputter-deposited on Si, SiO₂/Si, and glass substrates from a WS₂ target in an Ar/H₂S atmosphere. Their structure, morphology, chemical composition, and electrical properties were investigated as a function of deposition parameters such as working pressure and H₂S fraction. Films could be grown in the composition range WS_0.3−WS_3.5. Crystallisation was achieved at substrate temperatures T_s > 70 °C and compositions 0.7 ≤ x ≤ 1.95. While the first 5–50 nm near the interface exhibited a basal orientation (c), further growth resulted in the formation of edge-oriented platelets (c) giving rise to a porous, lamellar microstructure. The crystalline structure was mainly turbostratic, while some degree of ordered stacking was present in samples grown at high substrate temperature (600 °C). Resistivity measurements showed a semiconductor-type temperature dependence characterised by activation energies up to 95 meV. Sheet resistance was found to be nearly independent of film thickness, suggesting that the main carrier transport takes place in an interfacial layer of about 20 nm in thickness.     

Controllable formation of Er–Yb codoped Al2O3 films by the non-aqueous sol–gel method

1 mol%Er³⁺–10 mol%Yb³⁺ codoped Al₂O₃ thin films have been prepared on thermally oxidized SiO₂/Si(110) substrates by a dip-coating process in the non-aqueous sol–gel method from the hydrolysis of aluminum isopropoxide [Al(OC₃H₇)₃] under isopropanol environment. Addition of N,N-dimethylformamide (DMF) as a drying control chemical additive (DCCA) into the sol suppresses formation of the cracks in the Er³⁺–Yb³⁺ codoped Al₂O₃ thin films when the rare-earth ion is doped with a high doping concentration. Homogeneous, smooth and crack-free Er³⁺–Yb³⁺ codoped Al₂O₃ thin films form at the conditions by a molar ratio of 1:1 for DMF:Al(OC₃H₇)₃. A strong photoluminescence spectrum with a broadband extending from 1.400 to 1.700 µm centered at 1.533 µm is obtained for the Er³⁺–Yb³⁺ codoped Al₂O₃ thin films, which is unrelated to the addition of DMF. Controllable formation of the Er³⁺–Yb³⁺ codoped Al₂O₃ thin films may be explained by the fact that the DMF assisted the deprotonation process of Al–OH at the surfaces of gel particles, resulting in enhancement of the degree of polymerization of sols and improvement of the mechanical properties of gel thin films.     

Molecular beam epitaxial growth of SmBa2Cu3O7−δ thin films and effect of substrate temperature on the surface roughness

Stoichiometrically optimized, epitaxial SmBa₂Cu₃O_7-δ thin films with high T_{c, R = 0} and high critical current densities j_c have been prepared for the first time in a tightly controlled molecular beam epitaxy process in non-reactive molecular oxygen, followed by an in situ loading process with molecular oxygen. The surface roughness (on a submicrometre scale) of single-crystal films with their c axes perpendicular to the surface depends markedly on the surface temperature of the substrate during the deposition of the epitaxial films, within a range of only a few degrees centigrade. The calibrated optimal temperature for the preparation of epitaxial films 200 nm thick of this single orientation is found to be 680 ± 5 °C. In scanning tunnelling microscopy investigations, they show a surface roughness of less than 6 nm (five SmBa₂Cu₃O_7−δ unit cells) on a 2 μm × 2 μm scale. At deposition temperatures below this optimal deposition temperature, the well-known a-axis growth increases rapidly, whereas higher temperatures give a significantly higher surface roughness, which can be observed by scanning electron microscopy.     

Structure and electrical properties of boron-added (Ba,Sr)TiO3 thin films fabricated by the sol-gel method

Thin films of Ba_xSr_1−xTiO₃ (BST, with x=0.5) were fabricated on a RuO₂/Ru/SiO₂/Si substrate by the spin coating of the multicomponent sol prepared using metal alkoxides. Boron alkoxide was intentionally introduced to establish a better microstructure and to reduce the leakage current. AFM indicated that a crack-free uniform microstructure having a smooth surface was gradually developed with increasing boron content. The relative dielectric permittivity of the 250-nm thick BST thin films fired at 700°C decreased with increasing content of boron, from 420 for the undoped film to 190 for the 10 mol% boron-added film at 1 MHz. This observation was interpreted in terms of a serial capacitance composed of the perovskite BST grain and the interfacial B₂O₃ glassy phase having a low dielectric permittivity. The leakage current density (J) also decreased with the amount of boron added. The leakage current for the applied voltage greater than 1 V showed a linear variation of logJ with E^1/2 at room temperature, suggesting that the interface-controlled Schottky emission was the dominant conduction process for the BST thin films fabricated on the RuO₂ electrode.     

Structural and optical properties of (100 − x)(Li2B4O7) − x(SrO–Bi2O3–0.7Nb2O5–0.3V2O5) glasses and glass nanocrystal composites

Glasses of various compositions in the system (100 − x)(Li₂B₄O₇) − x(SrO–Bi₂O₃–0.7Nb₂O₅–0.3V₂O₅) (10  x  60, in molar ratio) were prepared by splat quenching technique. The glassy nature of the as-quenched samples was established by differential thermal analyses (DTA). The amorphous nature of the as-quenched glasses and crystallinity of glass nanocrystal composites were confirmed by X-ray powder diffraction studies. Glass composites comprising strontium bismuth niobate doped with vanadium (SrBi₂(Nb_0.7V_0.3)₂O_9−δ (SBVN)) nanocrystallites were obtained by controlled heat-treatment of the as-quenched glasses at 783 K for 6 h. High resolution transmission electron microscopy (HRTEM) of the glass nanocrystal composites (heat-treated at 783 K/6 h) confirm the presence of rod shaped crystallites of SBVN embedded in Li₂B₄O₇ glass matrix. The optical transmission spectra of these glasses and glass nanocrystal composites of various compositions were recorded in the wavelength range 190–900 nm. Various optical parameters such as optical band gap (E_opt), Urbach energy (ΔE), refractive index (n), optical dielectric constant and ratio of carrier concentration to the effective mass (N/m^*) were determined. The effects of composition of the glasses and glass nanocrystal composites on these parameters were studied.