以低分子蜡作分散剂 ,与陶瓷微粉、聚丙烯树脂一起混合 ,经双螺杆配混挤出机造粒 ,制得性能优良的远红外丙纶母粒。研究了低分子蜡种类、添加量对陶瓷微粉的分散作用 ,以及最佳添加量与陶瓷微粉粒径的关系 ,不同低分子蜡的热稳定性能。优化工艺及配方 ,制得的远红外丙纶母粒 ,可满足细旦高速纺丝及后加工的要求 ,产品质量较好。     

新型改性烟用聚丙烯性能

本研究采用多组分共混方法,制成A、C、D三种改性母粒,用改性母粒与聚丙烯共混,得到改性烟用聚丙烯.通过X衍射、差热分析、结晶速度、流动性和可纺性的检测分析,说明改性烟用聚丙烯具有很好的流动性和可纺性,其结晶性能和热性能比纯聚丙烯均有明显提高,母粒添加量对改性聚丙烯性能有所影响,最佳添加量为5%.     

降温母粒对控制降解聚丙烯结晶性能的影响

研究了共聚聚丙烯和均聚聚丙烯加入降温母粒降解前后结晶性能的变化。发现适量的降温母粒含量(质量分数0.6%)可以改善均聚聚丙烯的结晶性能,但对控制降解共聚聚丙烯的结晶性能影响更为复杂。同时发现相对分子质量分布(MWD)对控制降解聚丙烯结晶形态的变化规律更为显著。     

矿用电器外壳用无卤阻燃抗静电聚丙烯母粒的研制

以超高熔指聚丙烯(PP)为基体材料,通过双转子连续混炼机将聚丙烯、无卤膨胀型阻燃剂FR-1420、抗静电剂及PE蜡和硅酮粉E525进行密炼,经单螺杆挤出、切粒及冷却后,制得无卤阻燃抗静电聚丙烯母粒;再将制备的m(母粒)∶m(PP K7926)=35∶65的比例混合成直接注塑用矿用电器外壳阻燃抗静电聚丙烯材料。本文考察了聚丙烯基料、润滑剂、抗静电剂和加工工艺对母粒制备效果和电器外壳材料性能的影响。研究结果表明:当矿用电器外壳用无卤阻燃抗静电聚丙烯母粒的工艺条件为:熔体温度210℃,主机转速400r/min,切粒转速600r/min,配方质量配比为:m(PP BX3920)∶m(FR-1420)∶m(PE蜡)∶m(E 525)∶m(抗静电剂129)=25.7∶70∶2∶0.3∶2时,母粒制备的效果最佳,且按比例复配后直接注塑的聚丙烯材料力学性能稳定,阻燃和抗静电性能符合MT 113-1995要求。     

费托蜡离聚物的合成及其作为成核剂的应用

费托蜡作为一种应用广泛的新型煤化工原料,由于附加值较低,限制了其进一步应用。费托蜡成盐合成离聚物作为赋予其高值化的改性方法,受到业内广泛关注。成功合成出费托蜡钙型离聚物作为聚丙烯成核剂使用,并使用双螺杆挤出机和注射机制备聚丙烯/费托蜡离聚物复合材料。使用红外光谱、差示扫描量热仪和热重分析仪对产物结构和性能进行了测试,并使用万能拉力机、冲击试验机、热变形温度测试仪对复合材料的性能进行了表征。结果表明:钙离子成功接枝到费托蜡分子链上并形成目标离聚物。费托蜡离聚物的添加可以大幅缩短聚丙烯半结晶时间,使用量在0.5%就可以使聚丙烯的冲击强度、弯曲强度和热变形温度同时得到提高。该研究为费托蜡离聚物作为成核剂应用于聚丙烯改性领域提供了理论基础。     

过氧化物母粒对PP/炭黑导电复合材料的影响

采用含有过氧化物的聚丙烯(PP)母粒,通过熔融共混法制备了不同熔体流动速率(MFR)的PP/炭黑导电复合材料,并研究了复合材料的流变性能、结晶性能、力学性能及导电性能。结果表明:PP过氧化物母粒的加入有效改善了PP/炭黑导电复合材料的流动性。PP过氧化物母粒质量分数为2.2%时,复合材料的结晶度是25.96%,拉伸强度、冲击强度分别达到25.96 MPa、73.70 kJ/m~2。PP过氧化物母粒的加入对复合材料导电性能的影响较小。     

甲基硅树脂微球的制备及其对聚丙烯性能的影响

在碱性条件下利用水解缩聚反应合成了甲基硅树脂微球,用红外光谱仪对其结构进行了表征,采用热重分析仪评价其热稳定性,研究发现制得的甲基硅树脂具有良好的热稳定性。将质量分数分别为5%、10%、15%的甲基硅树脂微球加入聚丙烯中制得改性聚丙烯,检测改性后的聚丙烯的热稳定性、拉伸性能、结晶及熔融行为。结果发现甲基硅树脂微球的加入使聚丙烯的热稳定性有显著的提高,且对其拉伸性能和结晶及熔融行为有一定的影响。     

等规聚丙烯的结晶成核剂

本文介绍了等规聚丙烯α型、β型结晶和成核剂及应用,成核剂与制品透明性、成型收缩、光泽、耐热性能的关系。指出等规聚丙烯的结晶行为对其加工和制品质量及性能关系重大,通过结晶成核剂进行结晶行为改性,可开发高透明、高光泽、耐热、低收缩和后变形小等新品种聚丙烯塑料。     

差示扫描量热仪评价聚丙烯薄膜专用树脂的热性能

用差示扫描量热仪(DSC)对T38F聚丙烯薄膜专用树脂热性能进行了研究,对T38F聚丙烯薄膜专用树脂的熔融结晶行为、非等温结晶特性、热分级及氧化诱导期进行分析,并与目前市场上加工性能较好的T38F聚丙烯薄膜专用树脂进行了对比分析。结果表明:各试样的熔融温度相近,试样3的结晶温度较另2个试样的提高大约3℃。试样3的连续自成核热分级(SSA)熔融曲线较另2个试样有明显的差异。试样1的氧化诱导期比试样2和3的长且测定的重复性明显较好,说明试样2和3的抗氧剂分布不均匀。     

抗菌聚丙烯键盘的研制

研究了抗菌聚丙烯(PP)母粒和抗菌PP键盘的制备方法。将无机复合抗菌剂经过振动分散改性后,与PP基体共混制成抗菌PP母粒,再采用注射成型制得抗菌PP键盘。经测试表明,抗菌聚丙烯键盘的力学性能得到提高,抗菌性能良好,抗菌率达到99％以上,抗菌成分缓释行为好、抗菌持久,可以满足公共场合使用时对抗菌缓释性及长效性的要求。     

纳米复合抗菌丙纶性能研究

将聚丙烯 ,纳米陶瓷粒子 ,沸石混合造粒制得抗菌母粒 ,聚丙烯切片与抗菌母粒共混熔融纺丝 ,得到纳米复合抗菌丙纶。测试了纤维的抗菌性能、热性能、力学性能 ,并对纳米粒子及纤维进行了扫描电镜分析。结果表明 :纳米抗菌剂最佳含量在 0 .8%左右 ,纤维抑菌率达 90 %以上 ,且耐久性好。纤维结晶度下降 ,而熔点提高。纳米抗菌剂在纤维中有少量凝聚 ,纤维断裂强度略有降低 ,但能够满足加工及服用要求     

爽滑抗粘连母料在BOPET薄膜中的应用

采用二氧化硅与高温蜡按质量比2∶1进行复配,经双螺杆挤出机挤出造粒制备了爽滑抗粘连母料,并应用在双向拉伸聚酯(BOPET)薄膜中,分析了爽滑抗粘连母料对BOPET薄膜性能的影响,并与添加进口爽滑抗粘连母料的BOPET薄膜进行对比。结果表明:添加自制爽滑抗粘连母料使BOPET薄膜具有较低的动摩擦系数,且稳定性较好,常温动摩擦系数控制在0.40~0.48,完全能满足包装膜的爽滑性能;BOPET薄膜的光学性能稳定,30 d内薄膜的雾度上升0.1%,光泽度下降0.3%;自制爽滑抗粘连母料对BOPET薄膜的力学性能和热收缩性能没有影响,其总体使用性能已经达到或超过进口同类产品的性能。     

Thermal,viscoelastic and adhesion properties of EVA (ethylene-co-vinyl acetate) hot melts containing polypropylene waxes of different nature

Wax determines the compatibility of tackifier and polymer in hot melt adhesives. Although the influence of the addition of microcrystalline and Fischer-Tropsch waxes on the properties of ethylene-co-vinyl acetate (EVA) hot melts has been studied, the addition of polypropylene wax has not been considered yet. In this study, different polypropylene waxes (polypropylene wax – PP, – maleic anhydride grafted polypropylene wax – PPMA – copolymer of polypropylene and 10.9?wt.% polyethylene wax – PP-E) were added to EVA hot melts and they were characterized by Brookfield viscosity, softening point measurement, differential scanning calorimetry, thermal gravimetric analysis, dynamic mechanical thermal analysis, plate–plate rheology, tack, and single-lap shear adhesion. The viscosities of EVA hot melts containing polypropylene waxes were relatively high, the highest viscosity corresponded to the formulation containing PP-E wax which also showed pseudoplasticity. The change in viscoelastic properties (i.e., from dominantly viscous to dominantly elastic) was produced at lower temperature in EVA hot melt containing PP-E wax, this adhesive exhibited the highest tack. On the other hand, the addition of acrylic PPMA wax increased the adhesion of EVA hot melt but lower tack was obtained. Finally, the PP-E wax was more compatible with EVA copolymer than the other polypropylene waxes.     

The effect of clay type and of clay–masterbatch product in the preparation of polypropylene/clay nanocomposites

Clay containing polypropylene (PP) nanocomposites were prepared by direct melt mixing in a twin screw extruder using different types of organo‐modified montmorillonite (Cloisite 15 and Cloisite 20) and two masterbatch products, one based on pre‐exfoliated clays (Nanofil SE 3000) and another one based on clay–polyolefin resin (Nanomax‐PP). Maleic anhydride‐grafted polypropylene (PP‐g‐MA) was used as a coupling agent to improve the dispersability of organo‐modified clays. The effect of clay type and clay–masterbatch product on the clay exfoliation and nanocomposite properties was investigated. The effect of PP‐g‐MA concentration was also considered. Composite morphologies were characterized by X‐ray diffraction (XRD), field emission gun scanning electron microscopy (FEG‐SEM), and transmission electron microscopy (TEM). The degree of dispersion of organo‐modified clay increased with the PP‐g‐MA content. The thermal and mechanical properties were not affected by organo‐modified clay type, although the masterbatch products did have a significant influence on thermal and mechanical properties of nanocomposites. Intercalation/exfoliation was not achieved in the Nanofil SE 3000 composite. This masterbatch product has intercalants, whose initial decomposition temperature is lower than the processing temperature (T ～ 180°C), indicating that their stability decreased during the process. The Nanomax‐PP composite showed higher thermal and flexural properties than pure PP. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

母料法制备尼龙6/蒙脱土纳米复合材料及其性能

以高流动性聚丙烯接枝马来酸酐(PP-g-MAH)为载体树脂,制备了接枝聚丙烯/有机蒙脱土插层母料,并以此为增强剂制备了PA6/接枝聚丙烯/有机蒙脱土纳米复合材料,研究了有机蒙脱土(OMMT)含量对复合体系力学性能和耐热性能的影响。通过X射线衍射(XRD)、透射电子显微镜(TEM)研究了复合材料的微观结构。结果表明:在所制备的插层母料中,PP-g-MAH大分子能够部分插入OMMT的晶片层间,其层间距有所增大。母料法制备的PA6/接枝聚丙烯/有机蒙脱土纳米复合材料的力学性能得到了较大提高,当OMMT含量为6%时,拉伸强度和弯曲强度分别比PA6/PP-g-MAH共混体系提高了24%和25.1%。     

纳米电气石/聚丙烯驻极熔喷非织造布的研制

研制了一种纳米电气石改性驻极体熔喷聚丙烯非织造布母粒,并采用电晕放电法制备出纳米电气石/聚丙烯驻极熔喷非织造布。探讨了纳米电气石在聚丙烯树脂中的分散状况及改性母粒的流变性能,同时对非织造布力学性能、表面电荷密度和过滤性能进行了测试。结果表明:电气石能较好地分散在聚丙烯树脂中;加入特种电气石之后,纤网的机械性能有所下降;驻极体熔喷非织造布的驻极效果大大改善,其表面电荷密度、过滤性能均有明显提高。     

硅油及钛白粉在聚丙烯膨胀阻燃中的应用研究

选用一种含有聚磷酸铵的高效膨胀型阻燃剂（SR-50A）与聚丙烯（PP）和不同含量的苯基硅油和钛白粉通过挤出造粒法制备了膨胀型阻燃母粒,将其与PP注塑成阻燃复合材料,利用极限氧指数测试仪等对阻燃复合材料的燃烧性能进行测试。结果表明,复合材料中膨胀型阻燃母粒含量为20 %（质量分数,下同）,苯基硅油的添加量为0.17 %时,极限氧指数值提高到35.6 %;钛白粉的添加量为1 %时,极限氧指数值提高到35.1 %,垂直燃烧等级（UL 94）均能达到V-0级;苯基硅油的加入可促进阻燃剂在阻燃初始阶段的分解,降低了复合材料的热分解速率,钛白粉的加入可促进基体成炭。     

聚乙烯蜡的性能及应用

综述了聚乙烯蜡的种类、性能、发展前景及应用,重点介绍了制备色母粒所用聚乙烯蜡的关键指标,并报道了用聚乙烯蜡对蜡制品改性的初步结果     

不同颜料浓度时添加高熔体流动速率PE-LLD的色母粒性能研究

以高熔体流动速率的线形低密度聚乙烯（PE-LLD）与低密度聚乙烯（PE-LD）混合作为载体,不添加任何分散剂制成不同颜料浓度的蓝色母粒。研究了该体系的加工流变性能、母粒的着色性能以及分散性能,并与以低相对分子质量聚乙烯蜡作为分散剂的PE-LD色母粒进行了对比。结果表明,当颜料浓度为30 %（质量分数,下同）时,以PE-LLD/PE-LD作为载体,不用添加任何分散剂,制品的力学性能和色彩性能都可达到使用要求;但当颜料浓度达到40 %及以上时,以PE-LLD/PE-LD为载体和添加聚乙烯蜡2种加工方法都不能得到合格的制品。     

聚丙烯蜡固-固相变材料的制备与工艺优化

针对聚丙烯蜡相变材料难以乳化分散、离子交联定型的问题,利用聚丙烯酸（PAA）羧基的亲水性,易离子化特性,设计了低聚合度聚丙烯酸（PAA）接枝聚丙烯蜡,以自乳化方法制备聚丙烯蜡乳液,通过常温离子交联,在水介质中、短周期内制备了聚丙烯蜡固-固相变材料（PPW SS-PCMs）。首先利用红外光谱仪、核磁共振波谱仪、扫描电子显微镜分析测试,探讨了丙烯酸的浓度及瞬时浓度对聚丙烯蜡（PPW）接枝产物自乳化能力的影响。然后,利用偏光显微镜、X射线衍射仪、差示扫描量热仪、热重分析仪对PPW接枝产物及PPW SS-PCMs的结晶性能、热稳定性做了测试和分析。结果表明：随着丙烯酸（AA）质量占比升高,定型相变材料的相变焓随AA含量的提升而下降。在一定范围内,通过提高AA瞬时浓度能提高改性PPW的自乳化能力,减少定型组分添加量。当AA、PPW、BPO质量比为0.36∶1∶0.05及滴加速率为9mL/min时,所制备的PPW SS-PCMs的结晶温度为52.46℃,结晶焓为-53.61J/g,储能效率为81.26%,具有较好的热稳定性。