辐照接枝改性涤纶织物的亲水性能

利用电子束辐照接枝的方法将丙烯酸(Acrylic acid,AA)单体接枝到涤纶织物上来改善其亲水性。通过改变吸收剂量、接枝单体浓度、阻聚剂浓度、预辐照的吸收剂量以及前处理氢氧化钠浓度等影响因素来获得具有不同接枝率的改性涤纶织物。优化的反应条件:吸收剂量为195 k Gy、AA浓度为50%、阻聚剂(Fe SO4?7H2O)浓度为0.8%、预辐照的吸收剂量为43 k Gy、前处理Na OH浓度为15 g/L。傅里叶红外光谱证明AA已接枝成功;扫描电子显微镜分析表明改性涤纶织物的表面具有覆盖物,且随着接枝率的增大,其覆盖物明显增多;回潮率测试结果表明,改性涤纶的回潮率随接枝率的增加而逐渐增大,当接枝率达到最大值27.84%时,改性涤纶的回潮率可达3.51%。涤纶织物经30次洗涤后减重率仅1%左右,说明接枝牢度优异。     

γ共辐射接枝丙烯酸改善聚醚砜粉体亲水性的研究

利用γ射线共照射技术在聚醚砜（Polyethersulfone,PES）粉体上按枝了丙烯酸。研究了丙烯酸单体体积分数、接枝溶液pH值、吸收剂量、阻聚剂（Cu^2＋）浓度等对接枝率的影响规律。通过与称重法相结合,得到了利用红外光谱对接枝率进行定量分析的工作曲线。研究结果表明,当吸收剂量为25kGy、单体体积分数为30％、阻聚剂用量为0．004mol／L时,可以获得最高的接枝率。接枝溶液中盐酸的添加有利于提高接枝率。提高接枝率有助于改善PES的亲水性。     

电子束辐射接枝丙烯酸改性聚四氟乙烯

采用电子束辐射接枝工艺,在保持本体强度的前提下实现了对聚四氟乙烯(PTFE)板材的表面丙烯酸接枝改性。傅里叶变换红外扫描测试表明丙烯酸成功接枝到PTFE板材表面。通过单因素分析法研究了辐射接枝工艺参数对接枝量的影响,并择优选出最佳的辐射接枝工艺条件:吸收剂量为18 kGy,丙烯酸浓度为60%,反应温度为70℃。表面接触角测试表明,接枝改性后PTFE板材表面浸润性较改性前大幅提高,水接触角由120°下降到60°。黏接性能测试结果表明,辐射接枝改性可显著提高PTFE的黏接强度,达到23 N/cm~2。     

γ射线共辐照接枝聚偏氟乙烯超滤膜表面亲水性研究

采用γ射线液相共辐照法对聚偏氟乙烯(Poly(vinylidene fluoride),PVDF)超滤膜进行接枝改性,研究了单体浓度、辐照剂量、链转移剂异丙醇(Isopropanol,IPA)、盐酸(Hydrochloric acid,HCl)、阻聚剂CuSO4浓度对接枝率及膜表面亲水性的影响.结果表明,在所涉实验条件下,接枝率随辐照剂量和接枝体系中单体浓度的增大,随CuSO4及IPA含量的增大而减小,改性膜表面接触角表现出相反的趋势;接枝体系中HCl的添加可以显著提高接枝率,有效降低改性膜表面接触角;改性后PVDF超滤膜表面亲水性显著提高,表面接触角由改性前的83.3°可降低至改性后的39.2°.     

电子束预辐照聚丙烯接枝丙烯酸和丙烯腈的研究

研究了以电子束辐照预处理聚丙烯(PP)无纺布接枝丙烯酸(AA)和丙烯腈(AN)，AA与AN的共接枝的最佳反应条件是：辐照剂量为200kGy，反应温度为75℃，反应4h，添加剂用硫酸约0．05moL／L，摩尔盐为0．08％，且单体比例为40／60、浓度为50％，同时也探讨了阻聚剂[（NI-h)2Fe(SO4)2]对反应接枝率的影响。FT-IR结果反映了单体浓度变化时总接枝率的变化情况，单体比例对总接枝率的影响与其单体自身的稳定性有关，但总接枝率在所给定的单体浓度范围内一直增大。     

LDPE片材的共辐射接枝改性及其表面粘接性

研究了甲醇作链调节剂、Ｍｏｈｒ＇ｓ盐作阻聚剂、水作溶剂，在低密度聚乙烯（ＬＤＰＥ）片材上γ射线辐射接枝丙烯酸（ＡＡＣ），以改善其表面粘接性。研究表明ＬＤＰＥ片材的接枝率依赖于辐照剂量、剂量率、单体浓度、甲醇浓度。如果接枝液中有一定数量的甲醇，能明显地抑制均聚反应，并且接枝液可再次使用。ＬＤＰＥ表面经改性后，粘接性有了很大的提高，采用改性环氧胶，其粘接强度很容易达到高于材料本身的强度。     

尼龙-66滤膜电子束预辐照接枝丙烯酸的研究

采用电子束预辐照接枝法,以水为溶剂,硫酸铜为阻聚剂,将丙烯酸接枝到尼龙-66滤膜上面。探讨电子束吸收剂量、丙烯酸单体浓度、接枝时间和反应温度对滤膜接枝率的影响。对不同接枝率的滤膜进行吸水性测试,并利用扫描电子显微镜和傅里叶红外光谱仪对接枝前后的滤膜进行表征。结果表明:丙烯酸成功接枝到尼龙-66滤膜表面,接枝后样品表面孔洞减少,表面粗糙度增加;接枝率随着吸收剂量、丙烯酸单体浓度、接枝时间和反应温度的增加而增大,而后渐渐趋于平缓;接枝后的滤膜吸水率有很大的提高。     

预辐照聚偏氟乙烯粉体接枝甲基丙烯酸缩水甘油酯

用<'60>Co γ射线预辐照接枝法,在聚偏氟乙烯(PVDF)粉体上接枝甲基丙烯酸缩水甘油酯(GMA),制备了含有高活环氧基团的PVDF-g-PGMA粉体.结果表明,接枝率随反应时间增大,5 h后基本不变;接枝率随辐照剂量增大;单体浓度较低时接枝率随单体浓度增大,单体浓度>15%后接枝率减小;温度较低时并无接枝反应发生,温度高于30℃,接枝率随着温度增加,50℃时达最大值,温度继续升高接枝率又有所降低.傅里叶红外光谱测试表明接枝物为PVDF-g-PGMA共聚物;差热扫描量热仪分析表明,接枝粉体的熔融温度Tm以及熔融焓△Hf均随接枝率的增大而降低.对接枝粉体进行化学改性得到了多胺基吸附材料.实验证明,改性粉体材料对Cu2+有较好的吸附作用.     

用预辐射接枝技术制备复合型离子交换纤维

以皮芯复合纤维为原料,采用有氧预辐射接枝法制备了弱酸性复合型离子交换纤维。对吸收剂量、反应温度、阻聚剂质量分数以及光敏剂含量等影响因素进行了研究。结果表明,在一定的吸收剂量范围内,接枝率随吸收剂量的增加而提高,最高可达1600％以上;接枝率随反应温度和阻聚剂质量分数的提高,都呈现先增加后降低的趋势,其中最佳反应温度在70℃左右,最佳阻聚剂质量分数在0．25％左右;在加入一定量光敏剂后,在相同条件下,所需的吸收剂量显著降低,且随光敏剂加入量的增大,效果更加明显。     

HDPE辐照接枝AA与SSS体系阻聚剂用量对接枝率的影响

考察了预、共辐照两种接枝方法中阻聚剂硫酸铜和摩尔盐对接枝率的影响规律。发现不同接枝方法的阻聚剂硫酸铜和摩尔盐对接枝率有着不同的影响规律。共辐照接枝体系中加入相同量的阻聚剂时,摩尔盐的阻聚效果明显弱于硫酸铜。空气气氛预辐照接枝时,较高反应温度下接枝率随摩尔盐用量的增加呈下降趋势,而反应温度较低时,随着摩尔盐用量的增加接枝率先升高,出现峰值后又降低。这是因为在摩尔盐的催化下,过氧化物可以在较低的温度下分解产生烷基自由基,从而引发接枝反应。     

IPN’s of acrylic acid and N-isopropylacrylamide by gamma and electron beam irradiation

Interpenetrating networks (IPN) of temperature sensitive N-isopropylacrylamide (NIPAAm) and pH sensitive acrylic acid (AAc) monomer were prepared in two consecutive steps. Hydrogels of AAc were synthesized by gamma radiation from a ⁶⁰Co gamma source and an electron beam from a Van de Graaff accelerator. A second hydrogel of NIPAAm was synthesized within the first AAc hydrogel by polymerization and cross-linking with a redox initiator and cross-linking agent. The thermal and pH sensitivity of the hydrogels were determined by measuring the swelling, and the morphology and composition by SEM.     

Metal sorption and swelling characters of acrylic acid and sodium alginate based hydrogels synthesized by gamma irradiation

Hydrophilic hydrogels based on poly(acrylic acid) as synthetic polymer and sodium alginates as natural polymer (AG) were prepared by gamma irradiation. The AAc/AG hydrogels were characterized by X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The effect of temperature and pH on the degree of swelling in water was studied. In addition, the metal sorption affinity of the prepared hydrogels for Cu⁺², Co⁺² and Ni⁺² was investigated. The XRD spectroscopic analysis indicates the formation of interpenetrating polymer networks. The TGA study showed that the hydrogels based on AAc/AG hydrogels at different ratios displayed lower thermal stability than PAAc hydrogel. The kinetic study of swelling in water showed that PAAc and AAc/AG hydrogels reached the equilibrium swelling state after five hours. However, AAc/AG hydrogels showed degree of swelling in water greater than PAAc hydrogel. The degree of swelling of AAc/AG hydrogels was affected by temperature, it increases within the temperature range 25-40 °C and displayed pH sensitivity within the range 5.5-9 depending on composition. The metal sorption study showed that PAAc hydrogel possessed higher affinity for Cu⁺² ions than AAc/AG hydrogels, whereas AAc/AG hydrogels showed higher affinity for Co⁺² and Ni⁺² ions than PAAc hydrogel.     

丙烯酸在PET膜表面的紫外光共辐射接枝

讨论了水性体系中，经紫外光（ＵＶ）辐射引发在ＰＥＴ膜表面的丙烯酸接枝聚合反应的实验影响因素，考察了光敏剂、单体浓度以及接枝反应温度对接枝率的影响，以及不同接枝率下接枝膜对水接触角的变化。     

Determining the degree of grafting for poly（vinylidene fluoride） graft-copolymers using fluorine elemental analysis

Acrylic acid (AAc) and styrene (St) were grafted onto poly(vinylidene fluoride) (PVDF) powder or membrane samples by pre-irradiation graft copolymerization.The grafted chains were proved by FT-IR spectroscopy analysis.The degree of grafting (DG) of the grafted PVDF was determined by fluorine elemental analysis (FEA) method,and was compared with the DGs determined by weighing method,acid-base back titration method and quantitative FT-IR method.The results show that the FEA method is accurate,convenient and universal,especially for the grafted polymer powders.     

Radiation-induced grafting of N-isopropylacrylamide and acrylic acid onto polypropylene films by two step method

Binary graft copolymerization of pH sensitive acrylic acid (AAc) and thermosensitive N-isopropylacrylamide (NIPAAm) monomers onto pre-irradiated polypropylene films (PP) was carried out by two individual steps using a Co⁶⁰ gamma radiation source. The influence of preparation conditions, such as pre-irradiation dose and reaction time on grafting yield was studied. The swelling behavior and FTIR-ATR study for PP films grafted films were investigated.     

NIPAAm-AAc二元线型共聚物对Er3+、UO2+2、Cr(Ⅵ)的浓集研究

利用γ辐射聚合法（总剂量３ｋＧｙ,剂量率３８．４Ｇｙ／ｍｉｎ）以ＮＩＰＡＡｍ和ＡＡｃ为单体在ＴＨＦ溶液中制备了二元线型共聚物,红外光谱证实了线型共聚物中羧基的存在;性质测定表明此共聚物具有温度敏感性,其相转变温度（ＬＣＳＴ）值随体系ｐＨ值而升高;利用这种共聚物对水溶液中微量Ｅｒ３＋、ＵＯ２＋２、Ｃｒ（Ⅵ）离子进行浓集分离研究,表明具有较好的浓集与分离效果,并对浓集机理进行了探讨     

接枝丙烯酸聚乙烯表面诱导生成硫化镉及其形貌研究

分别以体积比为1∶1的异丙醇/水、甲醇/水混合溶剂作为接枝溶剂,通过调节丙烯酸单体浓度得到不同接枝率和不同表面接枝链分布的接枝膜,用接枝膜诱导形成了不同形貌特征的硫化镉.研究表明,接枝率越大,硫化镉在聚乙烯接枝膜表面的分布越密集;与甲醇/水为混合接枝溶剂相比,在异丙醇/水为混合接枝溶剂的接枝膜上的硫化镉颗粒分布比较均匀.     

HDPE预辐射接枝NIPA/AAc的性能研究

高密度聚乙烯膜(HDPE)在N2保护下预辐射接枝N-异丙基丙烯酰胺(NIPA)和丙烯酸(AAc),制备了既具有温度敏感又兼具pH敏感的水凝胶,应用傅立叶变换红外光谱(FTIR)、差示扫描量热仪(DSC)、扫描电镜(SEM),研究了该水凝胶的接枝物组成、物理性质以及表面形态。结果表明接枝复合物在不同pH值的介质环境中表现出不同的温敏特性：在酸性条件下随温度升高,体积溶胀增加,表现为“热胀温敏水凝胶”;在中性或碱性条件下随温度升高,溶胀体积在相变温度附近急剧收缩,表现为“热缩温敏水凝胶”。     

甲异羟肟酸-硝酸辐解产生的H2和CO

甲异羟肟酸(FHA)是有望用于乏燃料后处理的新型无盐络合剂.用5(A)分子筛填充柱与热导池检测器(TCD)联用的气相色谱法研究了HNO_3-0.2 mol/L FHA辐解产生的H_2和CO.H_2的分析是以Ar作载气,柱温为85 ℃,TCD温度为120 ℃; CO的分析是以H_2作载气,柱温为50 ℃, TCD温度为80 ℃.研究结果表明,H_2的体积分数随剂量的增加而增大,随HNO_3浓度的增大而减小;CO只有在剂量很高时才产生,且其体积分数远比H_2低,CO的体积分数随剂量的增加而增加.当c(HNO_3)≤0.5 mol/L时,CO体积分数低于0.2 mol/L FHA水溶液辐解产生的CO,但当c(HNO_3)≥1.0 mol/L时,CO的体积分数大于0.2 mol/L FHA水溶液辐解产生的CO, 且CO体积分数随c(HNO_3)的增大而增大.     

不饱和聚合物的辐射效应Ⅱ.EGDMA对无规1,2-聚丁二烯辐射效应的影响

本文研究了双甲基丙烯酸乙二醇酯(EGDMA)对无规1,2-聚丁二烯(1,2-PB)辐射效应的影响。通过辐照1,2-PB和不同EGDMA/1,2-PB比率体系的溶胶分数测定,红外光谱分析及~1H-NMR测试结果,讨论了EGDMA对1,2-PB辐射化学反应(分子间交联及分子内环化)的作用及机理。结果证明,1,2-PB辐射引起的链式交联反应不因EGDMA的存在而改变(无规链反应),但EGDMA的存在将增加1,2-PB的交联引发G(I)值和交联G(c.1)同时导致G(-V)和G(cy)值的减小,抑制或减少,内环化过程。