Microwave absorption properties of composite powders with low density

The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

Synthesis of MgAl2O4 Spinel Nanometer Powder via Biology Polysaccharide Assisted Sol-Gel Process

A novel and cost-effective sol-gel process for preparation of MgAl₂O₄ spinel nanometer powders has been developed in this study. A solution of magnesium and aluminum nitrates in stoichiometric proportion was successfully embraced in the biology polysaccharide gel network, formed by the synergistic interaction between xanthan gum (XG) and locust bean gum (LBG) utilizing their broad-spectrum stability of salt tolerance and character of transformation from sol to gel on the condition of proper temperature and relative proportion of polymeric components. Dry gel could be obtained by vacuum dehydration of aqueous gel at low temperatures. Monolithic MgAl₂O₄ spinel nanometer powders were produced by calcining the dry gel above 800°C, with average crystallite size of 20 nanometers.     

复合型铁氧体全极化器

应用耦合波理论 ,对有两组NS/N′S′四磁极磁化铁氧体中极化传输进行了分析 .在X、S波段对多种椭圆极化进行了测试 ,还完成了 0°～ 180°范围内多种线极化波测试 .最后对全极化器应用作了简单介绍 .     

Mössbauer study of nanodimensional nickel ferrite – mechanochemical synthesis and catalytic properties

Iron–nickel spinel oxide NiFe₂O₄ nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol decomposition to CO and methane is tested. An influence of the preparation method on the reduction and catalytic properties of iron–nickel samples is established.     

Effects of pH and citric acid contents on characteristics of ester-derived BaFe12O19 powder

The single domain size of BaFe₁₂O₁₉ powder with crystallite sizes less than 200 nm was produced using a citric acid precursor method. Fe³⁺ and Ba²⁺, in a molar ratio of 12, were chelated by COOH⁻ in an aqueous solution. After ethylene glycol additions, esterification, dehydration, and calcination led to the formation of ester-derived BaFe₁₂O₁₉ powder. High pH and/or high citric acid contents in the starting solution are required to complete chelate metallic ions in the solution and to form pure barium ferrite powder at 1073 K. Pure single magnetic domain BaFe₁₂O₁₉ particles of M(30 kOe)≈54 emu/g, M_r≈28 emu/g, and H_c≈3.7 kOe were produced using [citric acid]/[metallic ions]=1.5 and pH7.     

Effects of microstructure on the temperature dependence of relative initial permeability of NiCuZn ferrites

In the present work, ferrites with compositions of (Ni_0.27Zn_0.64Cu_x)Fe_1.98O₄ (x=0.1, 0.2) were prepared by conventional ceramic methods. The relationship between the microstructure and the temperature dependence of relative initial permeability was investigated. It was found that intergranular pores in the ferrites generate large demagnetizing fields, reducing the temperature dependence of the effective anisotropy field H_eff, and decreasing the temperature dependence of the relative initial permeability accordingly. However, intragranular pores pin the movement of domain walls. Compared with the permeability induced by domain wall motion, the permeability that resulted from the spin rotation is more sensitive to temperature. As a result, the relative initial permeability of ferrites becomes more sensitive to temperature with increasing micropores within grains.     

Al掺杂对尖晶石型LiMn2O4结构及循环性能的影响

用柠檬酸作为螯和物的载体,采用溶胶-凝胶法合成了A l3 掺杂的锂离子电池正极材料L iA lxMn2-xO4。XRD,SEM研究表明,于800℃煅烧可获得单一尖晶石结构的物相;随着A l3 掺入量的增加,L iA lxMn2-xO4的晶格常数变小,晶格更趋于完整,有利于抑制因锂的反复脱嵌而造成的结构破坏。x=0.05时,首次放电容量为103.8 mAh.g-1,25次循环后放电容量还有100.6 mAh.g-1,容量衰减仅为3.08%。     

棒状钡铁氧体的反相微乳法制备

A rodlike barium ferrite precursor with an average size of 0.72～19.6 μm and aspect ratio of 2.6～8.3 has been successfully prepared in an inverse microemulsion consisting of isooctane, cetanyl trimethyl ammonium bromide (CTAB), n-C₄H₉OH and water with ammonia and ammonium oxalate as precipitants. On sintering at 780(C, the rodlike precursor particles could be transformed into rodlike particles of barium ferrite(BaFe₁₂O₁₉) with the average size and aspect ratio of 0.69～18.2 μm and 2.3～5.8, respectively. The effect of volume ratio of aqueous phase to oleic phase, the starting concentrations of metal ions and the starting concentration ratios of metal ions to precipitants were investigated.     

尖晶石锂锰氧化物锂离子嵌脱过程的交流阻抗谱研究

用粉末微电极研究了尖晶石锂锰氧化物在不同嵌锂状态下嵌脱锂过程的交流阻 抗图谱，提出了新的等效电路模型。描述锂离子在固体中扩散的Warburg阻抗与累 积或消耗的嵌入电容在Lix MnO4中的x≤0．5时串联，0．5＜x≤1时并联。用提出 的等效电路模型分阶段拟合了实验所得的交流阻抗谱，拟合值与实验值相当吻合， 由拟合结果得到不同电位下锂离子在表面膜中的迁移电阻和电容，界面电荷传递电 阻，双层电容，锂离子在固体中扩散系数和累积或消耗的嵌入电容。