Fabrication and electromagnetic wave absorption properties of amorphous Ni-P nanotubes

Amorphous Ni-P nanotubes are fabricated through electroless chemical deposition inside an anodic aluminum oxide template. The hysteresis loops of Ni-P nanotube arrays are each found to exhibit an unusual isotropic behaviour, which is believed to be due to the competition results between the shape anisotropy and the magnetostatic interaction among nanotubes. The dynamic dependence of permittivity on the frequency spectrum is fitted to the Lorentzian-type dispersion law. The permeability dispersion behaviours have been fitted based on the Kittel equation. Electromagnetic wave absorption properties of Ni-P nanotubes/paraffin composites with different values of thickness (t) are clearly shown by a three-dimensional graph. Furthermore, the bandwidths of composites with different "t" values can be well presented by a two-dimensional contour graph, which is a novel presentation form. The results show that the composites each have a good microwave absorption performance with t larger than 5.5 mm and with the frequency around 8 gigahertz.     

具有横向磁晶各向异性的钴纳米线的微波吸收性能

使用电化学脉冲沉积法制备了磁晶各向异性易磁化方向(c轴)垂直纳米线长轴方向的钴纳米线.受到磁晶各向异性、静磁相互作用等因素与形状各向异性相互竞争的结果,纳米线阵列的磁滞回线显示出较弱的磁各向异性.此外,在2—18 GHz频率范围内,纳米线/石蜡复合材料的介电色散谱的虚部在5 GHz处有一个主峰,在10 GHz附近有一个较弱的峰;德拜弛豫特性和材料的电导率对这两个峰的形成均有贡献.同时,其磁导率色散谱的虚部在频率为6.1 GHz处有一个主峰,在10 GHz以上有两个较微弱的峰. 前一个峰源于自 关键词： 钴纳米线 介电色散谱 磁导率色散谱 微波吸收剂     

Annealing effects on the microwave permittivity and permeability properties of Fe79Si16B5 microwires and their micowave absorption performances

This paper reports that amorphous magnetic microwires(Fe79Si16B5) have been fabricated by a melt-extraction technique and have been annealed at 600°C and 750°C respectively.Differential scanning calorimeter measurements show that nanocrystalline magnetic phase(α-Fe) has been formed in the amorphous matrix when it was annealed at 600°C.Hard magnetic phase(Fe2B) was formed in the microwires annealed at 750°C,which increases the magnetic coercivity.Microwave permittivity and permeability are found to be dependent on the microstructures.The permittivity fitting results show that multi Lorentzian dispersion processes exist.For microwires annealed at 750°C,their resonance peaks due to the domain wall movements and natural resonance are found higher than those of microwires annealed at 600°C.The microwave absorption performance of microwires annealed at 600°C is found better than microwires annealed at 750°C.     

超材料微波磁导率色散行为的电可调控性研究

研究在开口金属谐振环(SRR)结构嵌入一个电容二极管后,通过电压调控二极管的电容使得SRR结构的等效电容值发生改变,能实现对SRR的谐振频率和等效磁导率的调控,从而提出了一种智能的微波磁性超材料结构.采用时域差分有限元法(Finite-Difference Time-Domain)和恢复算法模拟了变容二极管的工作电压变化下,SRR结构谐振频率和磁导率的变化规律.研究结果表明工作电压增大使变容二极管的电容值减小时,将导致SRR结构的谐振频率向低频段移动,其磁导率的共振频率也将向低频移动.最后指出了SRR结构与常规磁性材料(如铁氧体)磁导率色散行为的不同之处. 关键词： 超材料 微波磁导率     

Mssbauer studies on the shape effect of Fe_(84.94)Si_(9.68)Al_(5.38) particles on their microwave permeability

Ball milling for long time (such as 10, 20, and 30 h) can transform Fe 84.94 Si 9.68 Al 5.38 alloy powders with irregular shapes into flakes. X-ray diffraction (XRD) and Mssbauer measurements have proven that the unmilled particles and the flakes obtained by milling for 10 h have the same D0 3 -type superlattice structure. The flakes obtained by milling for 20 h and 30 h have the same disorder α-Fe(Si, Al) structure. There are more than 6 absorption peaks in the transmission Mssbauer spectra (TMSs) for the particles with D0 3 -type superlattice structure, which can be fitted with 5 sextets representing 5 different Fe-site environments. However, only 6 TMS absorption peaks have been found for particles with a disorder α-Fe(Si, Al) structure, which can be fitted with the distributions of Mssbauer parameters (Bhf, isomer shift). The TMS results show that the flaky particles have a stronger tendency to possess the planar magnetic anisotropy. As the result, the flakes have larger microwave permeability values than particles with irregular shapes. The conversion electron Mssbauer spectra (CEMSs) also show the significantly different Fe-sites environments between the alloy surface and the inside.     

Fabrication of CoFe_2O_4 ferrite nanowire arrays in porous silicon template and their local magnetic properties

CoFe_2O_4 ferrite nanowire arrays are fabricated in porous silicon templates. The porous silicon templates are prepared via metal-assisted chemical etching with gold(Au) nanoparticles as the catalyst. Subsequently, CoFe_2O_4 ferrite nanowires are successfully synthesized into porous silicon templates by the sol–gel method. The magnetic hysteresis loop of nanowire array shows an isotropic feature of magnetic properties. The coercivity and squareness ratio(M_r/M_s) of ensemble nanowires are found to be 630 Oe(1 Oe = 79.5775 A·m~(-1) and 0.4 respectively. However, the first-order reversal curve(FORC) is adopted to reveal the probability density function of local magnetostatic properties(i.e., interwire interaction field and coercivity). The FORC diagram shows an obvious distribution feature for interaction field and coercivity. The local coercivity with a value of about 1000 Oe is found to have the highest probability.     

Electromagnetic wave absorbing properties and hyperfine interactions of Fe–Cu–Nb–Si–B nanocomposites

The Fe–Cu–Nb–Si–B alloy nanocomposite containing two ferromagnetic phases(amorphous phase and nanophase phase) is obtained by properly annealing the as-prepared alloys. High resolution transmission electron microscopy(HRTEM) images show the coexistence of these two phases. It is found that Fe–Si nanograins are surrounded by the retained amorphous ferromagnetic phase. M¨ossbauer spectroscopy measurements show that the nanophase is the D03-type Fe–Si phase, which is employed to find the atomic fractions of resonant57 Fe atoms in these two phases. The microwave permittivity and permeability spectra of Fe–Cu–Nb–Si–B nanocomposite are measured in the frequency range of 0.5 GHz–10 GHz. Large relative microwave permeability values are obtained. The results show that the absorber containing the nanocomposite flakes with a volume fraction of 28.59% exhibits good microwave absorption properties. The reflection loss of the absorber is less than-10 dB in a frequency band of 1.93 GHz–3.20 GHz.     

磁性多孔纳米片微波磁导率的微磁学研究

本文基于微磁学理论模拟了多孔α-Fe纳米片的微波磁性能. 与无纳米孔洞的纳米片对比, 发现由于纳米孔洞的引入导致退磁能发生改变, 破坏了纳米片原有的磁畴分布, 使纳米片内部存在数目更多、体积更小、局域有效场强不同的磁畴, 从而增加了高频磁损耗峰的数目. 由于部分损耗峰的相互交叠, 为在10–30 GHz范围拓宽电磁波吸收的带宽提供了潜在可能性. 模拟结果表明多孔纳米片的磁损耗峰数目、强度、峰宽和频率分布受孔洞排布方式和孔洞数目的影响. 由于纳米孔洞的存在可以降低材料的密度, 模拟结果表明多孔α-Fe纳米片可用于开发吸收频段宽、重量轻的电磁波吸收材料.     

Co纳米线磁矩反转动态过程的有限元微磁学模拟

采用有限元微磁学模拟方法研究了Co纳米线在不同外加恒磁场下磁矩的翻转过程.研究结果表明在直径为10 nm的Co纳米线内,经过一定的形核时间将在其一端形成一个反向磁畴.磁畴壁的类型为横向畴壁,该畴壁将在一外加恒定磁场的驱动下匀速地从一端运动到另一端.畴壁的运动速度与外加磁场大小呈线性关系.在H为1000 kA/m时,发现在纳米线的两端均会形成一个“头对头”的反向磁畴.计算结果表明,畴壁内磁矩的方向旋转一个周期所导致的畴壁运动的距离相同,与外加磁场强度无关. 关键词： 磁性纳米线 微磁学模拟 磁畴 横向畴壁     

Effect of annealing treatments on the microwave electromagnetic properties of amorphous FeCuNbSiB microwires

The amorphous FeCuNbSiB microwires are fabricated by using the melt extraction method and annealed separately at temperatures T = 573, 673, 723 and 773K for 1h. The effect of annealing treatment on the microwave electromagnetic properties of FeCuNbSiB wires/wax composites has been investigated for the first time. It is found that in a frequency range of 0.5--4.0GHz, the complex permittivity, permeability, magnetic and electric loss tangents of FeCuNbSiB wires/wax composites are strongly dependent on the annealing temperature and frequency. For T = 573, 723 and 773K, two resonance peaks are found at frequency f = 1.2 and 3.3GHz. However, for T = 673K, only one resonance peak occurs at f = 3.3GHz. The resonance peak at f = 1.2GHz is believed to be due to the stress-induced anisotropy, while the resonance peak at f = 3.3GHz is attributed to the random anisotropy.