Mg0.9-xTi0.1PdxNi(x=O.04～0.1)贮氢合金电极腐蚀行为研究

研究了Pd部分替代Mg对Mg0.9-xTi0.1PdxNi(x=0.04～0.1)贮氢合金腐蚀性能的影响.利用机械合金化方法制备了Mg0.9-xTi0.1PdxNi(x=0.04～0.1)贮氢合金.XRD和TEM分析表明经120 h球磨后该合金完全非晶化.循环充放电测试结果表明,Pd的替代有效地延长了Mg0.9-xTi0.1PdxNi(x=0.04～0.1)合金的循环寿命.采用开路电位测量,阳极极化,电化学阻抗和X射线光电子能谱研究了该合金的腐蚀行为.结果表明,随着Pd含量增加,合金腐蚀电位正移,初始腐蚀电流下降,腐蚀电流增加的速度变缓.采用本文提出的等效电路模型较好地拟合了合金的电化学阻抗谱.分析表明,随着Pd含量的增加,合金表面钝化膜厚度和电阻逐渐增大.X射线光电子能谱分析表明,Pd的加入减弱了合金在充放电过程中的氧化程度.当Pd含量达到0.1时,Mg0.9-xTi0.1PdxNi(x=0.04～0.1)合金的耐腐蚀性能最好,其放电容量保持率最高.     

Electrochemical Characteristics of Mg0.9Ti0.1-xZrxNi （x=0.02, 0.04, 0.06） Alloys

Mg-based hydrogen storage alloys Mg0.9Ti0.1-xZrxNi (x=0.02, 0.04, 0.06) were successfully prepared by means of mechanical alloying (MA). The effects of Zr addition on the discharge capacity and the cycle performance of the Mg-based electrodes were also studied. It was found that the discharge capacities were improved with addition of a small amount of Zr and the cycle performances of the alloy were stabilized with the addition of Ti. The effects of surface modification or coating on the properties of Mg0.9Ti0.06Zr0.04Ni were also studied. The results indicated that coating with graphite improved both the discharge capacity and cycle life of the amorphous Mg0.9Ti0.06Zr0.04Ni electrode.     

四元Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金的制备及性能研究

用机械合金化法合成了Mg0.9Ti0.1Ni0.9X0.1(X=Mn, Zn, Co, Fe)系列合金. X射线衍射(XRD)结构分析表明, 用X部分替代Ni后, 促进了Mg0.9Ti0.1Ni合金的非晶化过程. 用Co和Fe部分替代Ni提高了合金的放电容量, 但却降低了合金的循环稳定性. 用Zn和Mn部分替代Ni提高了合金电极的循环寿命, 尤其是Mg0.9Ti0.1Ni0.9Zn0.1合金电极经10个充放电循环后, 其放电容量仍可达到313.8 mA·h/g. 对添加Co后的合金进行p-c-T测试发现, Mg0.9Ti0.1Ni0.9Co0.1合金的吸放氢容量明显比Mg0.9Ti0.1Ni合金高, 这与电化学所测到的结果一致.     

我国金属氢化物化学研究

综述了我国金属氢化物化学的发展。我国是从５０年代中期开始研究离子型金属氢化物的合成、性能和应用的,发展了一些合成方法,获得了多项中国专利。储氢合金的化学研究是７０年代中期开始的。在储氢合金的化学合成、吸放氢热力学与动力学、储氢合金氢化催化和电化学方面都有较深入的研究,特别是储氢电极合金电化学及其在Ｎｉ／ＭＨ可逆电池中的应用研究,在国家８６３计划强有力的支持下,某些方面进入了国际先进行列。     

LiV3O8的合成及其电化学性能研究

The layered trivanadate, LiV₃O₈, was prepared by sol-gel method with LiOH, V₂O₅ and H₂O₂ as initial reagents. The materials at different heat treatment conditions were characterized by XRD and TG-DTA. Their electrochemical behaviors were studied by galvanostatic charge-discharge and cyclic voltammetry. The results show that LiV₃O₈ prepared by sintering at 300 ℃ for 16 h has higher capacity, and its initial discharge capacity is 333.1 mAh·g^-1, and maintains a discharge capacity of 302.8 mAh·g^-1 after 10 cycles at 0.2 C and the voltage range of 1.8～4.0 V.     

可再充镁离子电池正极材料MgV_2O_6的制备及其电化学性能研究

以MgO和V2O5为原料,应用固相合成法制备具有单斜结构的MgV2O6.在非质子性电解液(如Mg(AlBu2Cl2)2/THF溶液)中,Mg2+在这一正极材料中表现出较好的充/放电循环性能.     

新型镁基储氢合金的合成及电化学性能的研究

用扩散法成功地合成了Mg_1.5Al_0.5-xNiV_x(x=0,0.1,0.2,0.3,0.4)系列合金。XRD结构分析表明,合金中出现一个新的物相,其化学式为Mg₃AlNi₂,属立方晶系,Fd3m空间群,新相具有很好的电化学性能。钒的添加使合金的容量进一步提高。未经任何预处理的Mg_1.5Al_0.3V_0.2Ni合金的最大放电容量达到333mA·h·g^-1(50mA·g^-1,-0.5Vvs.Hg/HgO).Al对六方晶系Mg₂Ni合金结构中Mg的部分取代对于延长合金的循环寿命有重要作用。     

无定形硅的制备及其性能研究

随着非晶硅半导体材料研究的发展,人们发现非晶硅能够吸收18-50原子％的氢。这一结果引起了储氢材料研究者的极大兴趣.1978年,德国的Winstel首次用非晶硅来储存氢,并申请了用非晶硅作为储氢材料的专利.随后,日本、美国、德国的许多研究者相继开展了这方面的工作。     

镁基复合储氢材料

镁基储氢材料以其低成本，高能量密度，引起人们的广泛关注，本文简要介绍了镁基复合储氢材料的最新进展。     

Ti和Zr的取代对MgNi型储氢合金电极电化学性能的影响

使用机械合金化法成功地合成了镁基储氢合金MgNi, Mg_0.9Ti_0.1Ni,和Mg_0.9Ti_0.06Zr_0.04Ni，并对其结构和电化学性能进行了研究。X射线衍射（XRD）表明，这一系列合金的主相为非晶态，透射电镜（TEM）表明，Ti和Zr取代的合金的颗粒直径约为2~4 μm。Ti和Zr的取代提高了合金电极的循环寿命。50周充放电循环后， Mg_0.9Ti_0.06Zr_0.04Ni合金电极的放电容量高于MgNi合金电极91.74%，高于Mg_0.9Ti_0.1Ni合金电极37.96%。电极容量衰减的主要原因是在合金电极表面形成Mg的腐蚀产物Mg(OH)₂。动电位扫描结果显示，Ti和Zr的添加提高了合金电极在碱液中的抗腐蚀性能。交流阻抗(EIS)测试表明，适量Ti和Zr的添加可以明显提高合金电极的电催化活性。