Pr_(0.15)Tb_(0.85)Fe_(1.9)B_x内禀磁致伸缩的测量与分析

利用电弧熔炼法制备了Pr_(0.15)Tb_(0.85)Fe_(1.9)B_x系列样品,通过X射线衍射法对粉末样品的(440)衍射峰进行精细步进扫描并拟合数据,分析获得样品的内禀磁致伸缩λ_(111),通过电阻应变片法测得块状样品在外加磁场下的磁致伸缩值变化趋势,外推得到宏观饱和磁致伸缩值λ_s,并从Laves相晶体结构特性出发对两者进行详细比较对照和进一步深化分析.结果表明,常温下Pr在Laves相化合物中对磁致伸缩具有较大的贡献,适量B的掺入可以增加Pr在Laves相化合物中的含量且不降低材料的磁致伸缩性能.     

磁场热处理和预压力对Tb0.3Dy0.7Fe1.95合金磁致伸缩"跳跃"效应的影响

研究了磁场热处理对<110>取向Tb0.3Dy0.7Fe1.95多晶合金磁致伸缩"跳跃"效应的影响.在真空超导体强磁场装置中,将经定向凝固的<110>取向Tb0.3Dy0.7Fe1.95多晶合金棒,沿垂直轴向施加强度为1 T的磁场,加热到623 和723 K下,保温5 min后随炉冷却.研究结果表明,磁场热处理增强预压力下的"跳跃"效应,提高不同预压力下的饱和磁致伸缩系数λs,其中623 K磁场热处理样品在8.1 MPa下的λs达到1950×10-6.磁场热处理提高预压力(8.1 MPa)下的动态磁致伸缩系数最大值dmax33,但同时增大dmax33对应的磁场.     

热处理工艺对〈110〉轴向取向Tb-Dy-Fe合金性能与显微组织的影响

研究了热处理工艺对<110>轴向取向Tb0.3Dy0.7(Fe1-xMx)1.95(M=Mn,Al,Ti,B,x=0.03)合金磁致伸缩性能与显微组织的影响。实验结果表明,热处理后合金的磁致伸缩应变λ和dλ/dH都显著提高,显微组织由片状晶向多边形晶粒转化,而且富稀土相在样品表面和晶界析出,晶粒内部的富稀土相有球化趋势。合理控制热处理温度和时间可以显著提高该合金的磁致伸缩性能。     

粉末冶金法制备稀土超磁致伸缩材料的研究

介绍了一种粉末冶金制备稀土磁致伸缩材料的方法,该方法包括铸造Tb0.30Dy0.70Fe1.80合金锭、制粉、磁场取向、压制成型和烧结工序。实验结果表明:粒度小于0.147 mm的Tb0.30Dy0.70Fe1.80合金粉末,经磁场取向后压制成型,在1200℃烧结2 h,并在950℃热处理24 h,当磁场强度为240 kA.m-1,预应力为8 MPa时,材料的磁致伸缩系数达到1.613×10-3。     

Pr2Fe14B/α-Fe型纳米稀土永磁材料的高温磁性能研究

通过熔体快淬的方法制备出Pr9-xDyxFe86B5和Pr9-xDyxFe84.4-yCoyGa1Mn0.6B5(x=0～2.0;y=0～15)薄带样品,利用X射线衍射和振动样品磁强计进行了相成分分析和磁性能研究.对不同成分的样品磁性能进行分析比较,发现用Co替代Fe、用Dy替代Pr可以明显改善Pr2Fe14B/α-Fe型纳米复合稀土永磁材料的室温和高温磁性能.适当的Co和Dy联合添加时,材料表现出很好的高温永磁性能,其中Pr8Dy1Fe76.4Co8Ga1Mn0.6B5样品在550 K时仍具有5.0 MGOe的最大磁能积,显示出很好的高温应用前景.     

稀土超磁致伸缩材料表面离子渗氮研究

采用辉光放电离子渗氮方法研究了表面氮化对（Tb,Dy）Fe2稀土超磁致伸缩材料的耐腐性能、表面机械性能及磁致伸缩性能的影响。结果发现：通过表面离子渗氮处理,可显著改善材料耐腐性能,材料表面硬度由587 HV提高到622 HV,耐磨性能也大幅提高,并且材料磁致伸缩性能几乎未受影响。研究表明,表面离子渗氮是一种适用于稀土超磁致伸缩材料表面改性的方法。     

粘结超磁致伸缩Tb-Dy-Fe合金磁致伸缩性能的研究

采用粘结方法制备了Tb1-xDyxFe2棒状合金样品，经筛选确定了粘结材料的制备工艺，测试了粘结棒状合金样品的静态、动态磁致伸缩系数和磁机械耦合系数k33。结果表明，所制备的粘结棒状样品具有较高的磁致伸缩性能，且动态磁致伸缩参数k33和磁机械耦合系数k33高于国外所报道的结果。     

稀土电解质Ce0.9M0.1O2-δ(M=Pr,Nd,Sm,Gd,Dy)的制备与性能

用溶胶-凝胶法制备中温电解质材料Ce0．9M0.1O2-δ,(M=Pr，Nd，Sm，Gd，Dy)系列样品。X射线衍射分析表明，样品为单相立方萤石结构，晶胞体积随着M原子序数的增加而减小。高温阻抗测量表明样品Ce0．9M0.1O2-δ电导率最高。Ce0．9M0.1O2-δ系列样品随着M原子序数的增加热膨胀系数减小。     

镧系元素的双(十七钨二砷)杂多酸钾的合成和鉴定

本文报道了镧系元素的杂多钨砷酸钾K17[Ln(As2W17O61)2].xH2O(Ln=La, Ce,Pr, Nd, Sm, En, Gd, Tb, Dy, Tm, Yb)的合成方法和X射线粉末衍射, 紫外, 红外, 差热, X光电子能谱, 有效磁矩及极谱的研究结果.     

有生物活性的稀土-腺苷三磷酸系列物的合成及其量子化学理论计算的研究

本文首次报道合成了稀土-腺苷三磷酸固态配合物RE(Ⅲ)-ATP(RE=Y、La、Ce、Pr、Nd、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu)。运用红外、激光Raman、热分析、紫外、顺磁、X射线衍射、元素分析、配位滴定等技术测定了上述配合物的化学组成和分子结构,其分子式用通式表为[RE(Ⅲ)(HATP)(H_2O)_4]。采用量子化学INDO方法计算了系列物的电子结构,依据计算结果讨论了生物化学中高能磷酸键的本质。     

Dichroism of absorption and polarization of phosphorescence of molecules of the closed form of nitrobenzospirothiopyran

The spectral-polarization characteristics of absorption and phosphorescence of molecules of the initial form of nitro-substituted indolinospirobenzothiopyran were studied in oriented polyethylene films and in solutions with different polarity. An oscillator model of the electron transitions responsible for the formation of absorption and luminescence spectra was suggested. It was established that the principal differences in the spectral and photophysical properties of the compound studied and its oxygen-containing analog are associated with the fact that the electronegativity of the S atom is lower than that of the O atom. Translated fromIzvestiya Akademii Nauk. Seriya Khimicheskaya, No. 6, pp. 1143–1146, June, 1997.     

恶臭嗅辨实验室建设探讨

针对恶臭测试的环境影响问题,提出了解决的实例方案,并对方案的要点及优缺点进行讨论,此方案在实际操作中具有较好的效果。     

Determination of heats of detonation and influence of components of composite explosives on heats of detonation of high explosives

The heats of detonation of 20 simple high explosives and explosive mixtures were determined by means of an adiabatic detonation calorimeter designed by the authors. The results indicated that the performance of the instrument was reliable and the experimental data were very accurate. For explosive mixtures, there was a linear accumulative relationship between the heats of detonation of the explosive mixture and its components. Accordingly, the heats of detonation of explosive mixtures could be calculated directly from the heats of detonation of simple explosives and the characteristic heats of other components. The experiments showed that the gold or brass shell of the cylindrical charge could be substituted by a thick-walled porcelain shell, which had the advantage of cheapness.

     

非那雄胺合成工艺改进

非那雄胺能抑制5α-还原酶的活性,明显降低二氢睾酮水平,是一种治疗良性前列腺增生的有效药品。该合成工艺以甾烯酮酸为原料,将其与氯化亚砜反应,无须分离即与叔丁胺反应得17β-酰胺化合物,再氧化开环,环合,氢化,脱氢合成了非那雄胺。经元素分析、IR、1HNMR、13CNMR、MS分析表征了其结构。该法无须使用昂贵的2,2-二吡啶二硫化物和剧毒药品苯亚硒酸酐,且以乙酸铵代替氨气,降低了对设备的要求和腐蚀,更适用于工业生产。     

Synthesis of phenolic components of Grains of Paradise

Two vanilloids, (5E)-8-(4-hydroxy-3-methoxyphenyl)oct-5-en-4-one (1) and 4-[3-hydroxydecyl]-2-methoxyphenol (2), isolated from the dried seeds of Grains of Paradise (Aframomum melegueta), were synthesized; the latter compound was made as the S-enantiomer and the material derived from the seeds was found to be a 1:1.7 mixture of the R and S isomers. The synthetic route used should allow the preparation of analogs having extended alkyl chains and consequently different lipophilicity, and 3, a homolog of 2, was also prepared.     

解决能源问题的新途径——光解水制氢的研究

面对日益枯竭的能源危机,氢能是一种洁净、最有前景的替代能源。目前在各种制氢的方法中光催化分解水制氢的研究最多,光解水过程中催化剂最关键,本文对利用太阳能光解水的途径、提高光催化反应效率以及光催化剂的开发研究进行了综述。     

黄酮化合物的合成研究进展

黄酮化合物是一类具有多种生物活性的天然产物,其经典的合成方法主要为查耳酮路线和β-丙二酮路线.近年来出现了许多新技术、新方法.本文介绍了2'-羟基查尔酮的氧化关环法、黄烷酮氧化法、改进的Baker-Venkataraman法及其他合成黄酮化合物的方法.     

Summary of development of the theory of stability of colloids and thin films

In this review, the research of the author in the field of colloidal systems is summarized. The factors influencing colloidal stability are systematized and analyzed. Examples are presented to illustrate the practical utilization of the theory of stability of colloids and thin films.This review was prepared on the basis of the works of the author, which were awarded the State Premium for 1991 in the field of science and technology, chemistry section.Institute of Physical Chemistry, Russian Academy of Sciences, 117915 Moscow. Translated from Izvestiya Akademii Nauk, Seriya Khimicheskaya, No. 8, pp. 1708–1717, August, 1992.     

NiY分子筛表面酸性影响其选择性吸附脱硫性能的机理研究

采用原位红外光谱技术,以噻吩、环己烯和苯为模型探针分子,分别考察单一烃分子在NiY分子筛上的吸附与反应行为以及噻吩与烯烃、芳烃间的竞争吸附和催化反应行为。单一探针分子吸附研究发现,NiY分子筛中与Ni物种相关的Lewis(L)酸位是噻吩的选择性吸附活性位;噻吩和环己烯在NiY分子筛中Brnsted(B)酸位上发生的质子化和低聚反应明显弱于HY分子筛。双探针分子竞争吸附研究发现,环己烯二聚体在NiY中强B酸位上的强化学吸附与噻吩存在显著的竞争吸附行为。另外,苯和噻吩在NiY上的竞争吸附现象在373K时明显减弱。由此,在选择性吸附脱硫过程中,减少吸附剂表面B酸中心可降低烯烃对噻吩的竞争吸附,另外适当提高吸附体系的温度可以有效避免芳烃对噻吩的竞争吸附。     

化学单元教学设计的探索

论述了单元教学是落实化学新课程三维目标的基本教学过程,同时对教学单元的含义、教学单元的选择与建构、化学单元教学设计及其意义进行了阐述。