Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

稀土钬及铒钇丙氨酸配合物的量热与热分析研究

合成了两种固态稀土丙氨酸配合物[Ho2(Ala)4(H2O)8]Cl6和[ErY(Ala)4(H2O)8](ClO4)6 (Ala为丙氨酸),用量热和热分析方法研究了这两种配合物的热力学性质.用全自动高精密绝热量热计测定了在78～377 K温区内的低温热容.对于[Ho2(Ala)4(H2O)8]Cl6,在214～255 K温区内发现一固-固相变,其相变温度为235.09 K.对于[ErY(Ala)4(H2O)8](ClO4)6,在99～121 K温区内也发现一固-固相变,其相变温度为115.78 K. [Ho2(Ala)4(H2O)8]Cl6固-固相变焓为3.02 kJ• mol－1,相变熵为12.83 J•K－1•mol－1； [ErY(Ala)4(H2O)8](ClO4)6 固-固相变焓为1.96 kJ•mol－1,相变熵为16.90 J•K－1•mol－1.同时,用TG技术在40～800 ℃温区研究了两配合物的热稳定性.由TG/DTG曲线分析可知, [Ho2(Ala)4(H2O)8]Cl6从80 ℃到479 ℃热分解分两步完成, [ErY(Ala)4(H2O)8](ClO4)6从120 ℃到430 ℃热分解分三步完成.     

M5(PO4)3F (M=Ca, Sr, Ba)中Sm3+的电荷迁移态及Sm3+和Eu3+的电荷迁移能量关系

采用高温固相反应合成了M_5-2xSm_xNa_x(PO₄)₃F(M=Ca,Sr,Ba)荧光体,研究了其在真空紫外-可见光范围的发光特性。发现在Ca₅(PO₄)₃F中Sm³⁺的电荷迁移带约在191 nm,在Sr₅(PO₄)₃F中约在199 nm,而在Ba₅(PO₄)₃F中约在204 nm,随着被取代碱土离子半径的增大电荷迁移能量逐渐减小。比较了M₅(PO₄)₃F (M=Ca,Sr,Ba)中Sm³⁺和Eu³⁺电荷迁移能量的关系。     

镥晶体的绝热量热法测试和热力学函数

文章合成了Lu(NO₃)₃(C₂H₅O₂N)_4.H₂O,用红外和元素分析对其进行了表征。用高精度全自动绝热量热仪,测定了该配合物80-382 K温区的热容, 利用实验热容数据, 根据热容与焓、熵的热力学关系, 求出了配合物85-350 K温区内每隔5 K相对于298.15K的标准热力学函数(HT - H298.15)m和(ST - S298.15)m.在80-350 K温度区间内,配合物的热容随温度升高而增大,没有相转移点和热力学吸收峰的出现,该配合物在此温度区间内是稳定存在的。     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

g-C3N4/CaTi2O5复合材料制备及其光催化性能

利用类石墨氮化碳（g-C₃N₄）和亚稳相钙钛氧化物（CaTi₂O₅）固相法制备C₃N₄/CaTi₂O₅复合材料。利用X射线衍射（XRD）、金相显微镜、扫描电子显微镜（SEM）及附带能谱分析仪（EDS）和N₂吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计（UV-Vis）测试了样品的光吸收性能,研究C₃N₄与CaTi₂O₅物质的量之比（n_C3N4/nCaTi₂O₅）对C₃N₄/CaTi₂O₅复合样品的物相结构和微观形貌的影响,同时考察C₃N₄/CaTi₂O₅复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明：相比纯C₃N₄和CaTi₂O₅样品,C₃N₄/CaTi₂O₅复合样品在可见光下具有较高的光催化性能,随着n_C3N4/nCaTi₂O₅增加,样品的光催化降解率随之增加而后降低,当n_C3N4/nCaTi₂O₅=1：1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃‐Bi₂O₃‐ZnO‐Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1364,介电损耗低至1.2%。     

钛酸铋系化合物的光催化性能研究

采用化学溶液分解法制备了钛酸铋化合物: Bi₁₂TiO₂₀, Bi₄Ti₃O₁₂和Bi₂Ti₂O₇, 并采用XRD表征了其结构. 用TEM观察发现其平均粒径＞100 nm, UV-Vis漫反射谱测定显示它们在可见光区均呈现极强的吸收特征. 紫外光照射下甲基橙的光催化降解脱色实验表明, 三种钛酸铋化合物均具有较强的光催化活性, 其中, Bi₁₂TiO₂₀的光催化活性最强, 几乎与P-25相同. 钛酸铋化合物光催化性能的不同在于它们具有不同的晶相结构和电子结构.     

La2(CO3)3纳米线的微乳液法制备与表征

La₂(CO₃)₃ nanowires were prepared in the nonionic surfactant microemulsion(Triton X-100/cyclohexane/water)system. Transmission electron microscopy (TEM) and selected area electronic diffraction (SAED) were used to characterize the shape and size of the products. The results showed that the pH value and concentration of mother solution, temperature and aging time all could affect the morphology and size of the La₂(CO₃)₃ nanowires. The lengths of the nanowires were more than 10 μm and the diameters were in the range of 30～200 nm.     

(ZrO2)0.92(Gd2O3)0.08纳米晶的水热合成及其烧结体的电性能

用新制备的(Gd，Zr)(OH)_x·yH₂O共沉淀作前驱体，在强碱性介质中用水热法合成了(ZrO₂)_0.92(Gd₂O₃)_0.08纳米立方晶，考察了反应温度、pH值等水热反应条件对纳米晶粒大小的影响。将(ZrO₂)_0.92(Gd₂O₃)_0.08     

不同晶化度γ-FeOOH的合成及其液相转化研究

进行了空气氧化Fe(OH)2悬浮液, EDTA作用下可见光诱导, 不同温度(14～20 ℃)制备不同晶化度γ-FeOOH的研究, 进行了其沸腾回流液相转化历程的探讨. 结果表明: 随温度的升高, γ-FeOOH的晶化程度变差; 而γ-FeOOH的晶化程度越差, 在液相沸腾回流时就越易转化成α-Fe2O3, 反之则易转化为α-FeOOH. 在pH近中性, 微量Fe(II)存在条件下低晶态的γ-FeOOH可以快速转化为均匀球形的α-Fe2O3.     

Fe物种改性海胆状Nb2O5光催化降解类吩噻嗪染料

我们在合成海胆状Nb2O5纳米球光催化剂的基础上,向体系中直接引入Fe3+离子,制备了Fe物种修饰的Nb2O5纳米球。对产物进行了X射线粉末衍射(XRD)、傅里叶变换红外光谱(FT-IR)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、N2吸附-脱附测试、紫外可见吸收谱(UV-Vis)和光致发光谱(PL)表征。结果表明,引入Fe3+后,Nb2O5纳米球的微观形貌和晶型结构没有发生显著变化,但其比表面积有所增加,原位复合的Fe物种以低结晶度的Fe2O3和Fe(Ⅱ)NbxOy物种分布在Nb2O5纳米球表面。相比于单一海胆状Nb2O5,Fe物种修饰的Nb2O5催化剂表现出了良好的光催化活性,能高效且选择性地降解类吩噻嗪染料亚甲基蓝(MB)和甲苯胺蓝(TB),原因为:(1) Fe物种可以对类吩噻嗪染料分子中的N和S形成配位吸附;(2) Fe物种与Nb2O5导带匹配,可以有效分离其光生电子,提高空穴的氧化能力;(3) Fenton反应在快速消耗光生电子的同时产生大量·OH用于染料的氧化。     

Environmental Mobility of Pu(IV) in the Presence of Ethylenediaminetetraacetic Acid: Myth or Reality?

Ethylenediaminetetracetic acid (EDTA), which was co-disposed with Pu at several US Department of Energy sites, has been reported to enhance the solubility and transport of Pu. It is generally assumed that this enhanced transport of Pu in geologic environments is a result of complexation of Pu(IV) with EDTA. However, the fundamental basis for this assumption has never been fully explored. Whether EDTA can mobilize Pu(IV) in geologic environments is dependent on many factors, chief among them are not only the complexation constants of Pu with EDTA and dominant oxidation state and the nature of Pu solids, but also (1) the complexation constants of environmentally important metal ions (e.g., Fe, Al, Ca, Mg) that compete with Pu for EDTA and (2) EDTA interactions with the geomedia (e.g., adsorption, biodegradation) that reduce effective EDTA concentrations available for complexation. Extensive studies over a large range of pH values (1 to 14) and EDTA concentrations (0.0001 to 0.01 mol⋅L⁻¹) as a function of time were conducted on the solubility of 2-line ferrihydrite (Fe(OH)₃(s)), PuO₂(am) in the presence of different concentrations of Ca ions, and mixtures of PuO₂(am) and Fe(OH)₃(s). The solubility data were interpreted using Pitzer’s ion-interaction approach to determine/validate the solubility product of Fe(OH)₃(s), the complexation constants of Pu(IV)-EDTA and Fe(III)-EDTA, and to determine the effect of EDTA in solubilizing Pu(IV) from PuO₂(am) in the presence of Fe(III) compounds and aqueous Ca concentrations. Predictions based on these extensive fundamental data show that environmental mobility of Pu as a result of Pu(IV)-EDTA complexation as reported/implied in the literature is a myth rather than the reality. The data also show that in geologic environments where Pu(III) and Pu(V) are stable, the EDTA complexes of these oxidation states may play an important role in Pu mobility.     

Effects of doping on the thermal stability of spindle-shaped γ-Fe2O3 particles

Spindle-shaped α-FeOOH particles were synthesized using the chemical coprecipitation method in Fe(CO₃)_x(OH)_2(?x) suspensions system by adding metallic ions. The spindle-shaped γ-Fe₂O₃ particles were obtained by dehydration of α-FeOOH, and subsequent reduction and oxidation. Its thermal stability was investigated by differential thermal analysis (DTA). It was found that the transition temperature of γ-Fe₂O₃→α-Fe₂O₃ of samples doped with metallic ions is higher than that of the pure γ-Fe₂O₃ and increasing with increase of the size of the metallic ions, and γ-Fe₂O₃ by doping with two or more different metallic ions together has even higher thermal stability. The origin of the improved thermal stability was discussed. Additionally, the magnetic properties of γ-Fe₂O₃ were measured.     

Nano size crystals of goethite, α-FeOOH: Synthesis and thermal transformation

An aqueous suspension of amorphous iron(III) hydroxide was kept at room temperature (298 K) for 23 years. During this period of time the pH of the liquid phase changed from 4.3 to 2.85, and nano size crystals of goethite, α-FeOOH crystallised from the amorphous iron(III) hydroxide. Transmission electron microscopy (TEM) investigations, Mössbauer spectra, and powder X-ray diffraction using Co Kα radiation showed that the only iron containing crystalline phase present in the recovered product was α-FeOOH. The size of these nano particles range from 10 to 100 nm measured by TEM. The thermal decomposition of α-FeOOH was investigated by time-resolved in situ synchrotron radiation powder X-ray diffraction and the data showed that the sample of α-FeOOH transformed to α-Fe₂O₃ in the temperature range 444-584 K. A quantitative phase analysis shows the increase in scattered X-ray intensity from α-Fe₂O₃ to follow the decrease of intensity from α-FeOOH in agreement with the topotactic phase transition.     

Hydrothermal synthesis, characterization and thermochemistry of Ca2[B2O4(OH)2]·0.5H2O

A pure calcium borate Ca₂[B₂O₄(OH)₂]·0.5H₂O has been synthesized under hydrothermal condition and characterized by XRD, FT-IR and TG as well as by chemical analysis. The molar enthalpy of solution of Ca₂[B₂O₄(OH)₂]·0.5H₂O in HC1·54.582H₂O was determined. From a combination of this result with measured enthalpies of solution of H₃BO₃ in HC1·54.561H₂O and of CaO in (HCl + H₃BO₃) solution, together with the standard molar enthalpies of formation of CaO(s), H₃BO₃(s) and H₂O(l), the standard molar enthalpy of formation of −(3172.5 ± 2.5) kJ mol⁻¹ of Ca₂[B₂O₄(OH)₂]·0.5H₂O was obtained.     

Synergetic effect of FeVO4 and α-Fe2O3 in Fe-V-O catalysts for liquid phase oxidation of toluene to benzaldehyde

Synergistic effect of FeVO₄ withα-Fe₂O₃ was found in Fe-V-O catalyst,which was responsible for the high apparent formation rate（A.F.R.） of benzaldehyde in liquid phase oxidation of toluene by hydrogen peroxide.The synergistic effect might create VO_πspecies as active sites;moreover,it improved the reducibility and the reactivity of Fe-V-O catalyst.In order to gain the high A.F.R. of benzaldehyde,the catalyst should have the moderate reducibihty.     

葡聚糖分子对氢氧化铁矿化结晶的调制作用

通过对比五种不同葡聚糖浓度的Fe3＋/葡聚糖矿化作用体系中Fe(OH)3凝胶在早期矿化阶段的成核和相变过程来研究葡聚糖对铁矿物的结晶与转化的调控作用. 运用ICP-AES(等离子发射光谱仪)观察各个矿化体系中上清液的[Fe3＋]浓度及相应pH的变化, 矿化产物运用FTIR、XRD进行表征. 结果发现, 上清液中[Fe3＋]经历了两次下降过程, 在陈化的第三天突然回增. 与不含葡聚糖的矿化作用体系很快形成结晶良好的α-FeOOH不同, 在含有葡聚糖的矿化作用体系中最初形成的物相主要为β-FeOOH. 葡聚糖分子通过与Fe3＋配位吸附在铁氧化物颗粒的表面促进了β-FeOOH转化为α-Fe2O3. 相变是经过溶解-再结晶机制进行的. [Fe3＋]第二次下降正是由于β-FeOOH转化为α-Fe2O3引起的. 葡聚糖浓度适当增大, β-FeOOH溶解加快, 有利于相变的进行. 因此葡聚糖的存在能显著影响在氢氧化铁凝胶中形成晶核的结构类型及其相变历程.     

The formation and physicochemical characterization of Al2O3-doped manganese ferrites

Mn/Fe mixed oxide solids doped with Al₂O₃ (0.32-1.27 wt.%) were prepared by impregnation of manganese nitrate with finely powdered ferric oxide, then treated with different amounts of aluminum nitrate. The obtained samples were calcined in air at 700-1000 °C for 6 h. The specific surface area (S_BET) and the catalytic activity of pure and doped precalcined at 700-1000 °C have been measured by using N₂ adsorption isotherms and CO oxidation by O₂. The structure and the phase changes were characterized by DTA and XRD techniques. The obtained results revealed that Mn₂O₃ interacted readily with Fe₂O₃ to produce well-crystallized manganese ferrite (MnFe₂O₄) at temperatures of 800 °C and above. The degree of propagation of this reaction increased by Al₂O₃-doping and also by increasing the heating temperature. The treatment with 1.27 wt.% Al₂O₃ followed by heating at 1000 °C resulted in complete conversion of Mn/Fe oxides into the corresponding ferrite phase. The catalytic activity and S_BET of pure and doped solids were found to decrease, by increasing both the calcination temperature and the amount of Al₂O₃ added, due to the enhanced formation of MnFe₂O₄ phase which is less reactive than the free oxides (Mn₂O₃ and Fe₂O₃). The activation energy of formation (ΔE) of MnFe₂O₄ was determined for pure and doped solids. The promotion effect of aluminum in formation of MnFe₂O₄ was attributed to an effective increase in the mobility of reacting cations.     

Studies on synthesis, characterization and thermochemistry of Mg2[B2O4(OH)2]·H2O

A new magnesium borate Mg₂[B₂O₄(OH)₂]·H₂O has been synthesized by the method of phase transformation of double salt at hydrothermal condition and characterized by XRD, IR, TG and DSC. The enthalpy of solution of Mg₂[B₂O₄(OH)₂]·H₂O in 0.9764 mol L^–1 HCl was determined. With the incorporation of the enthalpies of solution of H₃BO₃ in HCl (aq), of MgO in (HCl+H₃BO₃) (aq), and the standard molar enthalpies of formation of MgO(s), H₃BO₃(s), and H₂O(l), the standard molar enthalpy of formation of –(3185.78±1.91) kJ mol^–1 of Mg₂[B₂O₄(OH)₂]·H₂O was obtained.This revised version was published online in November 2005 with corrections to the Cover Date.