Synthesis and Eu luminescence in new oxysilicates, ALa3Bi(SiO4)3O and ALa2Bi2(SiO4)3O [ACa, Sr and Ba] with apatite-related structure

New oxysilicates with the general formula ALa₃Bi(SiO₄)₃O and ALa₂Bi₂(SiO₄)₃O [ACa, Sr and Ba] are synthesized and characterized. Powder X-ray diffraction of these silicates show that they are isostructural with BiCa₄(VO₄)₃O which has an apatite-related structure. Eu³⁺ luminescence in the newly synthesized oxysilicates show broad emission lines due to disorder of cations. The relatively high intense magnetic dipole transition ⁵D₀→⁷F₁ points to a more symmetric environment. The photoluminescence results confirm that the compounds have apatite-related crystal structure.     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

Preparation, crystal structure, and photoluminescence of Ca2SnO4:Eu, Y

Eu³⁺-doped Ca₂SnO₄ (solid solutions of Ca_2−xEu_2xSn_1−xO₄, 0?x?0.3) and Eu³⁺ and Y³⁺-codoped Ca₂SnO₄ (Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄) were prepared by solid-state reaction at 1400 °C in air. Rietveld analysis of the X-ray powder diffraction patterns revealed that Eu³⁺ replaced Ca²⁺ and Sn⁴⁺ in Eu³⁺-doped Ca₂SnO₄, and that Eu³⁺ replaced Ca²⁺ and Y³⁺ replaced Sn⁴⁺ in Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄. Red luminescence at 616 nm due to the electric dipole transition ⁵D_o→⁷F₂ was observed in the photoluminescence (PL) spectra of Ca_2−xEu_2xSn_1−xO₄ and Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ at room temperature. The maximum PL intensity in the solid solutions of Ca_2−xEu_2xSn_1−xO₄ was obtained for x=0.1. The PL intensity of Ca_1.8Y_0.2Eu_0.2Sn_0.8O₄ was 1.26 times greater than that of Ca_2−xEu_2xSn_1−xO₄ with x=0.1.     

Eu luminescence in La5Si2BO13 with apatite related structure and magnetic studies in Ln5Si2BO13 (Ln=Gd, Dy)

Eu³⁺ photoluminescence is studied in La₅Si₂BO₁₃ with apatite related structure. La_5−xEu_xSi₂BO₁₃ [x=0.05, 0.1, 0.3, 0.5, 0.7, 1.0, 2.0] compositions are synthesized. The emission results shows that Eu³⁺ ions occupy two different cationic sites viz., La(1) and La(2). The increase in the intensity of ⁵D₀-⁷F₀ line with increasing Eu³⁺ content shows the preferential occupancy of Eu³⁺ in La(2) site due to the existence of short La(2)-O(4) (free oxide ion) bond. The observation of antiferromagnetic interactions in Gd and Dy analogues supports the structural features elucidates from photoluminescence studies.     

A novel red emitting phosphor Ca2SnO4: Eu

A novel red emitting phosphor, Eu³⁺-doped Ca₂SnO₄, was prepared by the solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the formation of Ca₂SnO₄: Eu³⁺. Field-emission scanning electron-microscopy (FE-SEM) observation indicated a narrow size-distribution of about 500 nm for the particles with spherical shape. Photoluminescence measurements indicated that the phosphor exhibits bright red emission at about 615 nm under UV excitation. The excellent luminescence properties make it possible as a good candidate for plasma display panels (PDP) application. Splitting of the ⁵D₀-⁷F_J transitions of Ca₂SnO₄: Eu³⁺ suggests that the Eu³⁺ ions occupied two nonequivalent sites in the crystallite. The luminescence lifetime measurement showed a bi-exponential decay, providing other evidence for the existence of two different environments for Eu³⁺ ions.     

Synthesis of Gd3PO7:Eu nanospheres via a facile combustion method and optical properties

Eu³⁺-doped Gd₃PO₇ nanospheres with an average diameter of ∼300 nm and a narrow size distribution have been prepared by a facile combustion method and structurally characterized by X-ray diffraction and field emission scanning electron microscopy. The luminescent properties were systemically studied by the measurement of excitation/emission spectra, and emission spectra under different temperatures, as well as by photostability. The strong red-emission intensity peaking at 614 nm originates the ⁵D₀→⁷F₂ transition and is observed under 254-nm irradiation, indicating that Eu³⁺ ions in Gd₃PO₇ mainly occupied non-centrosymmetry sites. The CIE1931 XY chromaticity coordinates of Gd₃PO₇:Eu³⁺ nanospheres are (x=0.654, y=0.345) in the red area, which is near the National Television Standard Committee standard chromaticity coordinates for red. Thus, Gd₃PO₇:Eu³⁺ nanospheres may be potential red-emitting phosphors for PDP and Xe-based mercury-free lamps.     

La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)/Tb~(3+)荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为5D0→7F2特征能级跃迁,Eu~(3+)的最优掺杂浓度为0.08,对应的CIE坐标为(0.610 2,0.382 3);La_7O_6(BO_3)(PO_4)_2∶Tb~(3+)材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb~(3+)的5D4→7F5能级跃迁,Tb~(3+)离子的最优掺杂浓度为0.15,对应的CIE坐标为(0.317 7,0.535 2)。此外,对2种材料的变温光谱分析发现Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2荧光材料均具有良好的热稳定性。     

Preparation and photoluminescence property of a loose powder, Ca3Al2O6:Eu by calcination of a layered double hydroxide precursor

A novel red light-emitting material, Ca₃Al₂O₆:Eu³⁺, which is the first example found in the Ca₃Al₂O₆ host, was prepared by calcination of a layered double hydroxide precursor at 1350 °C. The precursor, [Ca_2.9−xAl₂Eu_x(OH)_9.8](NO₃)_2+x·2.5H₂O, was prepared by coprecipitation of metal nitrates with sodium hydroxide. The material is a loose powder composed of irregular particles formed from aggregation of particles of a few nanometers, as shown in scanning electron microscope (SEM) images. It was found that the photoluminescence intensity reached the maximum when the calcination temperature was 1350 °C and the concentration of Eu³⁺ was 1.0%. The material emits bright red emission at 614 nm under a radiation of λ=250 nm.     

Synthesis and structural study of a new NASICON-type solid solution: Li1−xLax/3Zr2(PO4)3

A new complete solid solution of NASICON-type compounds between LiZr₂(PO₄)₃ and La_1/3Zr₂(PO₄)₃ was evidenced with the general formula Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1). These phases were synthesized by a complex polymerizable method and structurally characterized from Rietveld treatment of their X-ray and neutron powder diffraction data. This solid solution results from the substitution mechanism Li⁺→1/3La³⁺+2/3□ leading to an increase of the vacancies number correlated to an increase of the La content. According to this substitution mechanism, the general formula can then be written Li_1−xLa_x/3□_2x/3Zr₂(PO₄)₃ (0?x?1) in order to underline the correlation between the La content and the vacancies rate. For all the compounds, the structure is clearly related to that of the NASICON family with three crystallographic domains evidenced. For 0?x?0.5, all the members adopt at high temperature the typical NASICON-type structure (s.g. R3¯c), while at lower temperature, their structure distorts to a triclinic form (s.g. C 1¯), as observed for LiZr₂(PO₄)₃ prepared above 1100 °C. Moreover, in this domain, the reversible transition is clearly soft and the transition temperature strongly depends of the x value. For 0.6?x?0.9, the compounds crystallize in a rhombohedral cell (s.g. R3¯), while for x=1, the phase La_1/3Zr₂(PO₄)₃ is obtained (s.g. P3¯, Z=6, a=8.7378(2) Å, c=23.2156(7) Å).This paper is devoted to the structure analysis of the series Li_1−xLa_x/3Zr₂(PO₄)₃ (0?x?1), from X-ray and neutron powder thermo diffraction and transmission electron microscopy (TEM) studies.     

M5(PO4)3F (M=Ca, Sr, Ba)中Sm3+的电荷迁移态及Sm3+和Eu3+的电荷迁移能量关系

采用高温固相反应合成了M_5-2xSm_xNa_x(PO₄)₃F(M=Ca,Sr,Ba)荧光体,研究了其在真空紫外-可见光范围的发光特性。发现在Ca₅(PO₄)₃F中Sm³⁺的电荷迁移带约在191 nm,在Sr₅(PO₄)₃F中约在199 nm,而在Ba₅(PO₄)₃F中约在204 nm,随着被取代碱土离子半径的增大电荷迁移能量逐渐减小。比较了M₅(PO₄)₃F (M=Ca,Sr,Ba)中Sm³⁺和Eu³⁺电荷迁移能量的关系。     

Luminescence of Tb-doped Ca3Y2(Si3O9)2 oxide upon UV and VUV synchrotron radiation excitation

Powders of calcium yttrium silicate, Ca₃Y₂(Si₃O₉)₂, containing 0.1-3% Tb³⁺ were prepared using a sol-gel method and characterized with XRD, IR, UV-vis and UV-VUV spectroscopies at room temperature and 10 K. Structural analysis revealed pure monoclinic phase of Ca₃Y₂(Si₃O₉)₂ after heat-treatment at 1000 °C. Infrared spectroscopy showed that between 800 and 900 °C a short-range structural organization of the components proceeded, yet without crystallization. A strong emission of Tb³⁺ had been observed both in the green part of the spectrum due to the ⁵D₄→⁷F_J transitions and in the blue-violet region owing to the ⁵D₃→⁷F_J radiative relaxation. The color of the light could be tuned from yellowish-green to bluish-white both by means of the dopant content and the temperature of synthesis. Efficient luminescence of Tb³⁺-doped Ca₃Y₂(Si₃O₉)₂ phosphors could also be obtained upon stimulation with vacuum ultraviolet synchrotron radiation demonstrating that an energy transfer from the host to the Tb³⁺ ions takes place.     

Sonochemical synthesis and luminescence properties of single-crystalline BaF2:Eu nanospheres

BaF₂ nanocrystals doped with 5.0 mol% Eu³⁺ has been successfully synthesized via a facile, quick and efficient ultrasonic solution route employing the reactions between Ba(NO₃)₂, Eu(NO₃)₃ and KBF₄ under ambient conditions. The product was characterized via X-ray powder diffraction (XRD), scanning electron micrographs (SEM), transmission electron microscopy (TEM), high-resolution transmission electron micrographs (HRTEM), selected area electron diffraction (SAED) and photoluminescence (PL) spectra. The ultrasonic irradiation has a strong effect on the morphology of the BaF₂:Eu³⁺ particles. The caddice-sphere-like particles with an average diameter of 250 nm could be obtained with ultrasonic irradiation, whereas only olive-like particles were produced without ultrasonic irradiation. The results of XRD indicate that the obtained BaF₂:Eu³⁺ nanospheres crystallized well with a cubic structure. The PL spectrum shows that the BaF₂:Eu³⁺ nanospheres has the characteristic emission of Eu^{3+ 5}D₀-⁷F_J (J=1-4) transitions, with the magnetic dipole ⁵D₀-⁷F₁ allowed transition (590 nm) being the most prominent emission line.     

Synthesis and spectral characteristics of Sr2Y8(SiO4)6O2: Eu polycrystals

Spectral-luminescent characteristics of Sr₂Y₈(SiO₄)₆O₂: Eu powder crystal phosphor with the apatite structure and high-intensity luminescence of Eu³⁺ ions have been studied. The charge state of europium in the samples has been characterized by means of X-ray L₃-adsorption spectroscopy. It was established that Eu³⁺ forms two types of optical centers. Besides, luminescence of Eu²⁺ions was found. Reduction Eu³⁺→Eu²⁺ was considered, which may be due to vacancy formation in the 4f crystal lattice position and to negative charge transfer by this vacancy to two ions. Thus, in the silicate lattice there exist inhomogeneously distributed oxygen-deficient centers, which are responsible for nonradiative transfer of excitation energy to Eu³⁺ and Eu²⁺ ions. To study electron-vibrational interactions in the crystal phosphor samples, their IR and Raman spectra were examined. In the luminescence spectrum of Eu²⁺, a series of low-intensity bands caused by interaction of the 4f⁶5d state of Eu²⁺ with silicate lattice vibrations was observed.     

A new type of charge compensating mechanism in Ca5(PO4)3F:Eu phosphor

The X-ray powder diffraction, reflectance, photoluminescence, photoluminescence excitation and ESR spectra of Ca₅(PO₄)₃F:Eu³⁺ phosphor have been studied. Three distinct variants of calcium substitutional Eu³⁺-sites have been observed in this host and the charge compensating species related to each of these sites has been identified. It is noted that the host related trace impurities those have prospects of acting as charge compensator, and the reaction environment that exists during the preparation of the material, greatly influence the preferential substitution of different Ca²⁺-sites by the Eu³⁺ ions. It is also noted that the charge compensating species in a suitable case, takes part in the photophysical process of luminescence of the Eu³⁺.     

Structural and P NMR investigation of Bi(MM′)2PO6 statistic solid solutions: Deconvolution of lattice constraints and cationic influences

Two solid solutions BiM_xMg_(2−x)PO₆ (with M²⁺=Zn or Cd) have been studied through ³¹P MAS NMR. The analysis has been performed on the basis of refined crystal structures through X-ray diffraction and neutron diffraction. The BiZn_xMg_(2−x)PO₆ does not provide direct evidence for sensitive changes in the phosphorus local symmetry. This result is in good agreement with structural data which show nearly unchanged lattices and atomic separations through the Zn²⁺ for Mg²⁺ substitution. On the other hand, the Cd²⁺ for Mg²⁺ substitution behaves differently. Indeed, up to five resonances are observed, each corresponding to one of the five first-cationic neighbour distributions, i.e. 4Mg/0Cd, 3Mg/1Cd, 2Mg/2Cd, 1Mg/3Cd and 0Mg/4Cd. Their intensities match rather well the expected weight for each configuration of the statistical Cd²⁺/Mg²⁺ mixed occupancy. The match is further improved when one takes into account the influence of the 2nd cationic sphere that is available from high-field NMR data (18.8 T). Finally, the fine examination of the chemical shift for each resonance versus x allows to de-convolute the mean Z/a² effective field into two sub-effects: a lattice constraint-only term and a chemical-only term whose effects are directly quantifiable.     

Photoluminescence properties of a novel phosphor, Na3La9O3(BO3)8:RE(RE=Eu,Tb)

The new oxyborate phosphors, Na₃La₉O₃(BO₃)₈:Eu³⁺ (NLBO:Eu) and Na₃La₉O₃(BO₃)₈:Tb³⁺ (NLBO:Tb) were prepared by solid-state reactions. The photoluminescence characteristics under UV excitation were investigated. The dominated emission of Eu³⁺ corresponding to the electric dipole transition ⁵D₀→⁷F₂ is located at 613 nm and bright green luminescence of NLBO:Tb attributed to the transition ⁵D₄→⁷F₅ is centered at 544 nm. The concentration dependence of the emission intensity showed that the optimum doping concentration of Eu and Tb is 30% and 10%, respectively.     

Photoluminescence of new red phosphor SrZnO2:Eu

SrZnO₂:Eu³⁺ has been synthesized by solid-state reaction and its photoluminescence in ultraviolet (UV)-vacuum ultraviolet (VUV) range was investigated. The broad bands around 254 nm are assigned to CT band of Eu³⁺-O²⁻. With the increasing of Eu³⁺ concentration, Eu³⁺ could occupy different sites, which leads to the broadening of CT band. A sharp band is observed in the region of 110-130 nm, which is related to the host absorption. The phosphors emit red luminescence centered at about 616 nm due to Eu³⁺⁵D₀→⁷F₂ both under 254 and 147 nm, but none of Eu²⁺ blue emission can be observed.     

IR and Raman spectra of two layered aluminium phosphates Co(en)3Al3P4O16 · 3H2O and [NH4]3[Co(NH3)6]3[Al2(PO4)4]2 · 2H2O

The FT IR and FT Raman spectra of Co(en)₃Al₃P₄O₁₆ · 3H₂O (compound I) and [NH₄]₃[Co(NH₃)₆]₃[Al₂(PO₄)₄]₂ · 2H₂O (compound II) are recorded and analysed based on the vibrations of Co(en)₃³⁺, Co(NH₃)₆³⁺, NH₄⁺, Al---O---P, PO₃, PO₂ and H₂O. The observed splitting of bands indicate that the site symmetry and correlation field effects are appreciable in both the compounds. In compound I, the overtone of CH₂ deformation Fermi resonates with its symmetric stretching vibration. The NH₄ ion in compound II is not free to rotate in the crystalline lattice. Hydrogen bonding of different groups is also discussed.     

Structural, spectroscopic and photoluminescence studies of LiEu(WO4)2−x(MoO4)x as a near-UV convertible phosphor

A series of lithium europium double tungsto-molybdate phosphors LiEu(WO₄)_2−x(MoO₄)_x (x=0, 0.4, 0.8, 1.2, 1.6, 2.0) have been synthesized by solid-state reactions and their crystal structure, optical and luminescent properties were studied. As the molybdate content increases, the intensity of the ⁵D₀→⁷F₂ emission of Eu³⁺ activated at wavelength of 396 nm was found to increase and reach a maximum when the relative ratio of Mo/W is 2:0. These changes were found to be accompanied with the changes in the spectral feature, which can be attributed to the crystal field splitting of the ⁵D₀→⁷F₂ transition. As the molybdate content increases the emission intensity of the 615 nm peak also increases. The intense red-emission of the tungstomolybdate phosphors under near-UV excitation suggests them to be potential candidate for white light generation by using near-UV LEDs. In this study the effect of chemical compositions and crystal structure on the photoluminescent properties of LiEu(WO₄)_2−x(MoO₄)_x is investigated and discussed.     

钙钛矿结构荧光材料MZrO3:Eu3+,A (M=Ca2+, Ba2+; A=Li+, Na+, K+)的制备及其发光性质

Calcium and barium zirconate powders based upon CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) were prepared by combustion synthesis method and heating to ~1000℃ to improve crystallinity.The structure and morphology of materials were examined by X-ray diffraction (XRD) and scanningelectron microscopy (SEM). XRD results showed that CaZrO₃:Eu³⁺,A and BaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) perovskites possessed orthorhombic and cubic structures, respectively. The morphologies of all powderswere very similar consisting of small, coagulated, cubical particles with narrow size distributions andsmooth and regular surfaces. The characteristic luminescences of Eu³⁺ ions in CaZrO₃:Eu³⁺,A (A=Li⁺, Na⁺, K⁺) lattices were present with strong emissions at 614 and 625 nm for ⁵D₀→⁷F₂ transitions with other weakeremissions observed at 575, 592, 655, and 701 nm corresponding to ⁵D₀→⁷F_n transitions (where n=0, 1, 3, 4 respectively). In BaZrO₃:Eu³⁺ both the ⁵D₀→⁷F₁ and ⁵D₀→⁷F₂ transitions at 595 and 613 nm were strong.Photoluminescence intensities of CaZrO₃:Eu³⁺ samples were higher than those of BaZrO₃:Eu³⁺ lattices. Thisremarkable increase of photoluminescence intensity (corresponding to ⁵D₀→⁷F_n transitions) was observedin CaZrO₃:Eu³⁺ and BaZrO₃:Eu³⁺ if co-doped with Li⁺ ions. An additional broad band composed of manypeaks between 440 to 575 nm was observed in BaZrO₃:Eu³⁺,,A samples. The intensity of this band wasgreatest in Li⁺ co-doped samples and lowest for K⁺ doped samples.