Designing amorphous formulations of polyphenols with naringin by spray-drying for enhanced solubility and permeability

Naringin (NAR), a major flavanone (FVA) glycoside, is a component of food mainly obtained from grapefruit. We used NAR as a food additive to improve the solubility and permeability of hydrophobic polyphenols used as supplements in the food industry. The spray-dried particles (SDPs) of NAR alone show an amorphous state with a glass transition temperature (T_g) at 93.2 °C. SDPs of hydrophobic polyphenols, such as flavone (FVO), quercetin (QCT), naringenin (NRG), and resveratrol (RVT) were prepared by adding varying amounts of NAR. All SDPs of hydrophobic polyphenols with added NAR were in an amorphous state with a single T_g, but SDPs of hydrophobic polyphenols without added NAR showed diffraction peaks derived from each crystal. The SDPs with NAR could keep an amorphous state after storage at a high humidity condition for one month, except for SDPs of RVT/NAR. SDPs with NAR enhanced the solubility of hydrophobic polyphenols, especially NRG solubility, which was enhanced more than 9 times compared to NRG crystal. The enhanced solubility resulted in the increased membrane permeability of NRG. The antioxidant effect of the hydrophobic NRG was also enhanced by the synergetic effect of NAR. The findings demonstrated that NAR could be used as a food additive to enhance the solubility and membrane permeability of hydrophobic polyphenols.     

The influence of FeNi nanoparticles on the microstructures and soft magnetic properties of FeSi soft magnetic composites

In this work, a new type of FeSi/FeNi soft magnetic powder core (SMPC) was successfully fabricated by coating FeNi nanoparticles on the surface of FeSi micrometer powder. The effects of different contents of FeNi nanoparticles on the micromorphology, internal structures, and soft magnetic properties of SMPCs were studied. The results show that FeNi nanoparticles adhere to the surface of FeSi powder, which can effectively fill the air gap between FeSi powder and is beneficial to the compaction of the powder cores during the pressing process. Thus, the density of the SMPCs is increased. Compared to FeSi SMPCs, the comprehensive soft magnetic properties of FeSi/FeNi SMPCs have been greatly improved. When adding 15 wt% FeNi nanoparticles, the SMPCs exhibit excellent magnetic properties with high effective permeability (increased by 43.8 %) and low core loss (decreased by 22.1 %). The high performance FeSi/FeNi SMPCs prepared in this work are expected to be widely used in power choke coils, uninterruptible power supplies, and boosts and inverter inductors.     

柿竹园多金属矿选矿废水处理试验研究

针对柿竹园多金属矿选矿废水量大、难沉降、pH值高、COD高等特点,研究了石灰沉降+ZJYH03氧化法、石灰沉降+漂白粉氧化法、石灰沉降+NaClO氧化法、聚合硫酸铁沉降+ZJYH03氧化法和石灰沉降+生物氧化法等废水处理工艺,并对比分析了各工艺的处理效果和药剂成本,结果表明: 聚合硫酸铁沉降+ZJYH03氧化法取得了较好的处理效果,该方法具有工艺简单、水质无色透明、药剂成本低等特点。     

脱硫胶粉在乳化改性沥青中的应用

考察了不同规格胶粉及不同脱硫程度的脱硫胶粉对橡胶改性乳化沥青性能的影响,结果表明,采用100目胶粉即可制备出橡胶改性乳化沥青,但乳化沥青的性能较差;采用活化度为50%左右的100目脱硫胶粉制备乳化沥青时,脱硫胶粉的用量相比于胶粉可大幅提高;在通过外掺100目50%左右活化度的脱硫胶粉(质量分数15%,以沥青计,下同)和质量分数2%的苯乙烯-丁二烯-苯乙烯嵌段共聚物改性的乳化沥青中添加质量分数1%的丁苯胶乳,所制备橡胶改性乳化沥青无筛上剩余物,5 d储存稳定性为2.9%,蒸发残留物的25℃针入度、软化点和5℃延度分别为55 (0.1 mm)、64.5℃和22.5 cm,能够满足乳化改性沥青的技术指标要求。     

Effect of hydrometallurgical process parameters on the Mn2O3 nano catalysts derived from spent batteries used in the plasma catalytic oxidation of BTX

Manganese oxide catalysts have been synthesized from the used batteries via hydrometallurgical method and effect of hydrometallurgical parameters such as the effect of acid type (H₂SO₄, HNO₃, HCl), acid concentration (0.5, 1, 1.5, 2 %v/v) and powder to acid ratio (1/50, 1/60, 1/70, 1/80) were in detail investigated. The physico-chemical properties of as-prepared catalysts were characterized by FT-IR, XRD, FESEM, EDX, BET, TEM, and TPR-H₂ analysis. The activity of as-prepared catalysts were investigated towards the oxidation of benzene, toluene, and xylene (BTX) in a plasma-catalytic process. The results show that benzene and toluene conversion were almost constant in the range of 97–98% in case of various acid types, acid concentrations and solid to liquid ratios. However, the xylene conversion were varied in case of different hydrometallurgical factors. The highest xylene conversion was obtained in the presence of MnS0.5–60, which was prepared using H₂SO₄ with concentration of 0.5%v/v and solid to liquid ratio of 1/60. The effect of the input voltage and BTX flow rate on the BTX conversion was also investigated using MnS0.5–60 catalyst in detail.     

两种3D打印用雾化Ti-6Al-4V粉末的对比研究

本研究分别利用水冷铜坩埚真空感应熔炼气雾化(VIGA-CC)和等离子旋转电极(PREP)两种技术制备出球形Ti-6Al-4V合金粉末,作者利用SEM、同步辐射CT扫描-三维重建和氩气含量测试等分析手段对不同粒径的Ti-6Al-4V合金粉末的孔洞缺陷和氩气含量、硬度值进行了表征。实验结果表明, VIGA-CC粉末粒度分布宽,细粉收得率较多,粉末粒度分布在40~180 μm之间, PREP粉末的粒度分布较窄,主要集中在110~180 μm之间；金属粉末内部的孔隙率、气体含量和孔尺寸随着粉末粒度的增大而增大,且同一粒径范围内VIGA-CC粉末的气孔概率多于PREP粉末；随着粉末粒径减小,粉末截面组织逐渐细化,其硬度值逐渐升高,整体上VIGA-CC粉末硬度值高于PREP粉末。     

Low-temperature hot-press sintering of AlN ceramics with MgO–CaO–Al2O3–SiO2 glass additives for ceramic heater applications

Aluminum nitride (AlN) is used a ceramic heater material for the semiconductor industry. Because extremely high temperatures are required to achieve dense AlN components, sintering aids such as Y₂O₃ are typically added to reduce the sintering temperature and time. To further reduce the sintering temperature, in this study, a low-melting-temperature glass (MgO–CaO–Al₂O₃–SiO₂; MCAS) was used as a sintering additive for AlN. With MCAS addition, fully dense AlN was obtained by hot-press sintering at 1500 °C for 3 h at 30 MPa. The mechanical properties, thermal conductivity, and volume resistance of the sintered AlN–MCAS sample were evaluated and compared with those of a reference sample (AlN prepared with 5 wt% Y2O3 sintering aid sintered at 1750 °C for 8 h at 10 MPa). The thermal conductivity of AlN prepared with 0.5 wt% MCAS was 91.2 W/m?K, which was 84.8 W/m?K lower than that of the reference sample at 25 °C; however, the difference in thermal conductivity between the samples was only 14.2 W/m?K at the ceramic-heater operating temperature of 500 °C. The flexural strength of AlN–MCAS was 550 MPa, which was higher than that of the reference sample (425 MPa); this was attributed to the smaller grain size achieved by low-temperature sintering. The volume resistance of AlN–MCAS was lower than that of the reference sample in the range of 200–400 °C. However, the resistivity of the proposed AlN–MCAS sample was higher than that of the reference sample (500 °C) owing to grain-boundary scattering of phonons. In summary, the proposed sintering strategy produces AlN materials for heater applications with low production cost, while achieving the properties required by the semiconductor industry.     

Additive manufacturing of bipolar plates for hydrogen production in proton exchange membrane water electrolysis cells

Water electrolysis is a process that can produce hydrogen in a clean way when renewable energy sources are used. This allows managing large renewable surpluses and transferring this energy to other sectors, such as industry or transport. Among the electrolytic technologies to produce hydrogen, proton exchange membrane (PEM) electrolysis is a promising alternative. One of the main components of PEM electrolysis cells are the bipolar plates, which are machined with a series of flow distribution channels, largely responsible for their performance and durability. In this work, AISI 316L stainless steel bipolar plates have been built by additive manufacturing (AM), using laser powder bed fusion (PBF-L) technology. These bipolar plates were subjected to ex-situ corrosion tests and assembled in an electrolysis cell to evaluate the polarization curve. Furthermore, the obtained results were compared with bipolar plates manufactured by conventional machining processes (MEC). The obtained experimental results are very similar for both manufacturing methods. This demonstrates the viability of the PBF-L technology to produce metal bipolar plates for PEM electrolyzers and opens the possibilities to design new and more complex flow distribution channels and to test these designs in initial phases before scaling them to larger surfaces.