Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

Grain size effect on microwave dielectric properties of Na2WO4 ceramics prepared by cold sintering process

In this work, cold sintering was adopted to prepare Na₂WO₄ ceramics with different grain sizes ranging from 0.632 μm to 17.825 μm. Their microstructures, complex impedance, and microwave dielectric properties were studied in-depth. It was found that samples with relative densities higher than 92% can be successfully synthesized by cold sintering process at a low temperature of 240 °C. However, their electrical properties have strong dependence on the grain size. Specifically, the resistance of grain boundaries decreases dramatically with the increase of grain sizes, while the quality factor has a positive correlation with the grain sizes of Na₂WO₄ ceramics. Excellent microwave dielectric properties, including permittivity = 5.80, Q × f = 22,000 GHz, and TCF = −70 ppm/°C, are obtained for Na₂WO₄ ceramics with a grain size of 4.477 μm prepared by cold sintering process.     

寒冷地区某既有办公建筑围护结构优化改造研究

既有公共建筑能耗中,围护结构节能潜力巨大。以兰州某既有办公建筑为例,采用DeST-C软件模拟围护结构不同材料厚度、窗型,得出系列负荷,通过对数据分析、比较,得出如下结论:外墙外保温适宜材料为50mm的挤塑板,最大热负荷节能率为45.66%;屋面适宜保温材料为65mm的挤塑板,最大热负荷节能率为4.25%;外窗各个朝向全部更换玻璃,推荐选用内张膜中空玻璃(双膜),最大热负荷节能率为7.36%;单独更换南向外窗材料,推荐选用真空镀膜复合中空玻璃,最大热负荷节能率为1.78%。     

浅谈压延铜箔光面色差的成因

针对压延铜箔在表面处理过程中光面易出现色差的问题,从设备、工艺、人员操作等方面进行成因探讨,并给出了应对措施。     

优化作业方式提高始极片质量

针对某厂铜电解种板工序存在的始极片质量波动较大的问题,从种板系统体积控制和添加剂匹配的角度出发,分析各种因素对始极片质量的影响,做出了相应的改进措施,使种板系统运行更加稳定,始极片质量得到进一步提升。     

Cell Sheet Comprised of Mesenchymal Stromal Cells Overexpressing Stem Cell Factor Promotes Epicardium Activation and Heart Function Improvement in a Rat Model of Myocardium Infarction

Cell therapy of the post-infarcted myocardium is still far from clinical use. Poor survival of transplanted cells, insufficient regeneration, and replacement of the damaged tissue limit the potential of currently available cell-based techniques. In this study, we generated a multilayered construct from adipose-derived mesenchymal stromal cells (MSCs) modified to secrete stem cell factor, SCF. In a rat model of myocardium infarction, we show that transplantation of SCF producing cell sheet induced activation of the epicardium and promoted the accumulation of c-kit positive cells in ischemic muscle. Morphometry showed the reduction of infarct size (16%) and a left ventricle expansion index (0.12) in the treatment group compared to controls (24–28%; 0.17–0.32). The ratio of viable myocardium was more than 1.5-fold higher, reaching 49% compared to the control (28%) or unmodified cell sheet group (30%). Finally, by day 30 after myocardium infarction, SCF-producing cell sheet transplantation increased left ventricle ejection fraction from 37% in the control sham-operated group to 53%. Our results suggest that, combining the genetic modification of MSCs and their assembly into a multilayered construct, we can provide prolonged pleiotropic effects to the damaged heart, induce endogenous regenerative processes, and improve cardiac function.     

Automated and Continuous Production of Microstructured Metallic Plates via Cold Embossing

Many critical issues need to be addressed when microstructured reactors are manufactured in large unit volumes. The most crucial of these are cost, ease of production, and reliability. The lack of breakthrough manufacturing technology to provide high‐efficiency, low‐cost, high‐precision plates is a hindrance to the early market implementation of systems requiring metallic microstructured plates. This contribution focuses on the development and optimization of a combined embossing and bending tool for the quick and continuous manufacture of easily machined plates.     

Bulging in incremental sheet forming of cold bonded multi-layered Cu clad sheet: Influence of forming conditions and bending

Bulge is a defect that causes geometrical inaccuracy and premature failure in the innovative incremental sheet forming (ISF) process. This study has two-fold objectives: (1) knowing the bulging behavior of a Cu clad tri-layered steel sheet as a function of forming conditions, and (2) analyzing the bending effect on bulging in an attempt to identify the associated mechanism. A series of ISF tests and bending analysis are performed to realize these objectives. From the cause-effect analysis, it is found that bulge formation in the layered sheet is sensitive to forming conditions in a way that bulging can be minimized utilizing annealed material and performing ISF with larger tool diameter and step size. The bending under tension analysis reveals that the formation of bulge is an outgrowth of bending moment that the forming tool applies on the sheet during ISF. Furthermore, the magnitude of bending moment depending upon the forming conditions varies from 0.046 to 10.24 N·m/m and causes a corresponding change in the mean bulge height from 0.07 to 0.91 mm. The bending moment governs bulging in layered sheet through a linear law. These findings lead to a conclusion that the bulge defect can be overcome by controlling the bending moment and the formula proposed can be helpful in this regards.     

轧制始极片

本文介绍了轧制法生产始极片的工艺，比较了轧制法和传统的钛种板生产始极片的优缺点，讨论了采用轧制始极片的经济效益和应用前景。