改进型单晶炉提拉系统偏心平衡研究

随着光伏行业的快速发展, 对硅单晶的品质和长晶装备的稳定性的要求也不断提高。直拉法是生产硅单晶的主要方法,通过提高单晶炉副室的高度以扩大单晶硅的生产规模。由于副室高度的大幅增加,且单晶炉提拉头质心相对于旋转轴心有一定距离,对单晶炉整体稳定性有较大影响,从而降低了单晶硅的生产质量。针对此问题,对单晶炉建立可靠的力学分析模型,采用数值仿真方法,对单晶炉整体进行动力学响应分析,计算得到副室高度增加后的单晶炉工作时中钨丝绳下端晶棒的运动规律以及最大摆动幅度,为改进设计提供依据。数值仿真分析表明提高单晶炉副室高度后,提拉头较大的质心偏心是单晶炉提拉系统发生摆动的主要原因。在此基础上提出在提拉头上添加质心调节装置,通过控制系统调节可保证提拉头质心位置在旋转轴线上以降低提拉系统的摆动。     

真空热解析分析系统的研制

系统主要针对金属材料中氢同位素和氦的热解析研究而研制，系统原理图如图l所示。系统支路中设计消气剂床，用以避免金属氚化物解析时氚的排放问题；温度、压力和解析组分等由采集系统采集与分析。     

环境微量元素与大骨节病

通过对两个自然村的大骨节病的流行病学调查结果表明，患病率在１７．２％，从Ｘ线检查病变部位都在干骺端，说明致病因素的持续作用仍在发展中，所采水样中微量元素低于国家饮水标准，在今后疾病的防治中，应根据营养条件，生态环境，元素比例，农作物的病害，制作相关的防治措施。     

Nanostructure Pt Electrode Obtained via Self-assembly of Nanoparticles on Conductive Oxide-coated Glass Substrate

Self-assembly of platinum nanoparticles were applied to fabrication of counter electrode for dye-sensitized solar cells on conductive oxide-coated glass substrate. The present Pt electrode exhibits high exchange current density of 220 mA/cm^2, which is comparable to those prepared by electrodeposition, magnetron sputtering or thermal decomposition of platinum chloride. After analysis by transmission electron microscopy (TEM), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS), it was found that the catalyst was structurally characterized as nanosized platinum metal clusters and was continuously arranged on electrode surface. The present nanostructure electrode had high electrocatalytic activity for the reduction of iodine in organic solution.     

环氧交联网Tg转变的tanδ-T曲线解析

 本文系统地研完了预聚物分子量、固化剂配比和固化条件对环氧交联网T_g松弛内耗峰松弛时间分布的影响。本实验和理论研究结果首次证明了环氧交联网T_g松弛过程具有单一松弛时间描述的线性标准固体的特征,与预聚体分子量、固化剂配比和固化条件无关。此结果可用环氧交联网的两相结构特征加以解释。     

热历史对聚醚醚酮及其碳纤维复合材料——Ⅱ.熔融行为的影响

 本文利用差示扫描量热仪(DSC)研究了聚醚醚酮(PEEK)和以PEEK为基体的碳纤维复合材料(APC-2)的热历史对它们熔融行为的影响。在200—315℃结晶并退火热处理后,试样的DSC曲线上出现了两个吸热峰。低温吸热峰(峰温T′_m)较小,并与结晶和退火温度(T_c与在不同T_c下生成的不完整晶体的熔融和重结晶过程有关,而T_m的出现则与完整晶体的熔融过程有关。实验结果表明,T′_m与T_c之间呈线性关系。按文献报道的方法,将T′_m与T_c的直线外推至与T′_m=T_c直线相交,其交点温度即为平衡熔点.结果表明,PEEK和APC-2试样的“平衡熔点”受不同热历史条件下生成晶体的完整程度的影响。当结晶并退火时间越长,求出的“平衡熔点”值越低,并与理论值接近。实验结果还表明,碳纤维表面具有促进PEEK树脂基体晶体完整化的作用,因而导致APC-2试样中PEEK树脂基体的熔点高于纯PEEK树脂。     

方酸染料在远红光区／近红外区对纳米晶二氧化钛电极的高效敏化作用

Four para-dialkylaminophenyl （PDAAP1-PDAAP4） bearing carboxyl groups were studied for application to the dye-sensitized solar cells （DSC）. It was found the short spacer CH2 between carboxyl and dialkylaminophenyl chromophore in PDAAP3 and PDAAP4 led to highly efficient monochromatic incident photon-to-current conversion efficiencies （IPCE）, however the long alkyl group C4H9 attached on aniline moieties in PDAAP2 and PDAAP4 favored improvement of open-circuit photovoltage. Thus, the solar cell sensitized by PDAAP4, having both short carboxyl groups CH2COOH and long alkyl groups C4H9, exhibited the IPCE maximum of 73% at 670 nm and overall energy conversion efficiency η of 3.06%, representing the highest IPCE and η values so far in dialkylaminophenyl-based organic dye-sensitized semiconductor solar cells. Taking advantage of the highly efficient sensitizing ability of PDAAP4 in far-red region, the data of IPCE above 630 nm of the solar cells were improved greatly by cosensitization with both N3 and PDAAP4. The influences of the TiO2 film thickness and the concentration of 4-tert-butylpyridine （TBP） in electrolyte were also investigated.     

含氧膦结构的可溶性感光聚酰亚胺合成与表征

聚酰亚胺(PI)是一类综合性能优异的功能性材料,广泛应用于航天、航空及电子工业等领域[1].感光聚酰亚胺可以采用光刻工艺,大大简化了其应用加工程序[2,3],因而备受人们所青睐.含查尔酮结构的聚合物对UV辐射敏感度高和化学稳定性好,最近被广泛的研究和应用[4～7].主链含查尔酮结     

热解-还原法制备单分散Fe3O4亚微空心球

在用模板法水解FeCl3制备单分散聚(苯乙烯-共-丙烯酸)/Fe2O3[P(St-co-AA)/Fe2O3]核壳粒子的基础上, 于N2环境下热解内核直接得到了单分散的磁性Fe3O4亚微空心球. 用透射电镜(TEM)、场发射扫描电镜(FESEM)、X射线衍射(XRD)、振动样品磁强计(VSM)表征并测试了空心微球的结构形貌、成分以及静磁性能. 结果表明, P(St-co-AA)/Fe2O3核壳粒子在热处理过程中, 由于内核热解生成的有机小分子将Fe2O3 壳层同时还原为Fe3O4, 从而生成了粒径和壁厚均匀的单分散Fe3O4亚微空心球. 该空心微球在室温下的饱和磁化强度、剩余磁化强度和矫顽力分别为50.91 A·m2·kg-1、3.97 A·m2·kg-1和2.33 kA·m-1.     

热历史对聚醚醚酮及其碳纤维复合材料——Ⅱ.熔融行为的影响

本文利用差示扫描量热仪(DSC)研究了聚醚醚酮(PEEK)和以PEEK为基体的碳纤维复合材料(APC-2)的热历史对它们熔融行为的影响。在200—315℃结晶并退火热处理后,试样的DSC曲线上出现了两个吸热峰。低温吸热峰(峰温T′_m)较小,并与结晶和退火温度(T_c)有关;高温吸热峰(峰温T_m)较大,几乎不受T_n的影响。T′_m的出现与在不同T_c下生成的不完整晶体的熔融和重结晶过程有关,而T_m的出现则与完整晶体的熔融过程有关。实验结果表明,T′_m与T_c之间呈线性关系。按文献报道的方法,将T′_m与T_c的直线外推至与T′_m=T_c直线相交,其交点温度即为平衡熔点.结果表明,PEEK和APC-2试样的“平衡熔点”受不同热历史条件下生成晶体的完整程度的影响。当结晶并退火时间越长,求出的“平衡熔点”值越低,并与理论值接近。实验结果还表明,碳纤维表面具有促进PEEK树脂基体晶体完整化的作用,因而导致APC-2试样中PEEK树脂基体的熔点高于纯PEEK树脂。