Rapid anti-solvent vapor-assisted synthesis of CsPbBr3/Cs4PbBr6 microcrystals with high brightness and stability of green light emission

Journal of Materials Science - The CsPbBr3/Cs4PbBr6 perovskite composite material has received wide attention due to its good stability and photoelectric properties, and it is promising to appear...     

橡胶在相变材料封装中的应用研究进展

相变材料主要用于建筑、热防护、纺织和储能等领域,节能环保。三元乙丙橡胶和硅橡胶用于石蜡和硬脂酸等有机相变材料的封装具有很好的效果,泄漏率较低,且随着相变材料含量的增大,复合相变材料的相变焓增大,相变温度变化不大,橡胶作为相变材料封装材料,具有十分广泛的应用前景。对导热性要求高的相变材料,可以在橡胶中添加导热填料进行改性,常用的导热填料有三氧化二铝、膨胀石墨、氮化物等,目前橡胶的导热改性技术已较为成熟。     

SDN中基于KMOBPSO的高可靠性控制器部署算法

针对SDN中控制器系统的单节点故障问题,兼顾系统成本和系统时延,应用N+1冗余备份模型来提高SDN控制器部署的可靠性,并将其抽象为多目标优化问题.同时,提出了一种融合K-means聚类算法和遗传算子的多目标二进制粒子群算法——KMOBPSO算法,以求解SDN控制器高可靠性部署问题的解.仿真结果表明,所提算法具有求解精度高、分布均匀、沿Pareto前沿面覆盖广的特点,能够显著提高SDN中控制器部署的可靠性.     

Synthesis of non-agglomerating submicron/nano-Yb2Si2O7 powders by a carbon-coated coprecipitation method

We herein report a novel carbon-coated coprecipitation method to synthesize non-agglomerating submicron/nano-β-Yb₂Si₂O₇ powders. Yb(C₂H₃O₂)₃·4H₂O and silica sol (alkaline) were chosen as the ytterbium source and silicon source, respectively. A carbon surface layer is processed using sucrose as carbon source to hinder the contact and sintering of β-Yb₂Si₂O₇ particles during heat treatment under a protective atmosphere, and then the carbon layer could be completely removed by inletting air at 900°C during cooling process. The as-synthesized Yb₂Si₂O₇ powders demonstrate an average size of 271 nm with a narrow distribution of 142–531 nm. The results show that the carbon layer could successfully solve the severe agglomeration or sintering of nanometer β-Yb₂Si₂O₇ particles during the calcination process. The as-developed carbon-coated coprecipitation technique is an effective method to fabricate high purity submicron/nano-Yb₂Si₂O₇ powders.     

双恶唑啉及环氧类扩链剂对PA6的改性效果比较

通过熔融挤出的方法分别用环氧类扩链剂和双恶唑啉类扩链剂对尼龙(PA)6进行扩链增黏,并对扩链产物的特性黏度,力学性能和加工性能等进行了测试,对比了两类扩链剂对PA6的改性效果。结果表明,当这两类扩链剂的质量分数均为0.9%时,PA6的各项性能最佳;双恶唑啉类扩链剂对PA6的改性效果比环氧类扩链剂要好。相对于纯PA6,添加质量分数为0.9%的双恶唑啉类扩链剂,可使扩链PA6的特性黏度由0.86 d L/g增加到1.57 d L/g,熔体流动速率由14.3 g/10 min降到5 g/10 min,缺口冲击强度由5.5 k J/m2增加到7.3 k J/m2,拉伸强度由54 MPa增加到65.85 MPa,断裂伸长率由130%增加到450.9%,弯曲强度由53.16 MPa增加到72.66 MPa,平衡扭矩由2.1 N·m升高到5.3 N·m。     