1.
对AZ31镁合金板材进行不同累积应变的连续弯曲变形及退火处理,随后对显微组织与力学性能的变化进行了研究。结果表明:经不同累积应变的连续弯曲变形后,镁合金板材的显微组织中没有发现孪晶,退火后,板材表层的晶粒异常长大,粗晶层的厚度随着累积应变的增加而增加,并且镁合金板材的织构朝RD方向偏转,偏转角度随累积应变的增加而增大;与原始板材相比,连续弯曲变形及退火处理使镁合金板材呈现出较好的室温成形性能(杯突值由2.3 mm提高到4.9 mm,提高了~113%),这主要归因于基面织构的改善使镁合金板材的r值减小与n值增大。 相似文献
2.
3.
The deformation behavior of AZ31B magnesium alloy as extruded under hot compression conditions was characterized in the temperature range of 200 - 400 ℃ and strain rate range of 0. 001 - 1 s^-1. The processing maps were obtained at different strains. The results show that the map exhibits flow instabilities as two domains. The domain at beyond 300 ℃ and strain rate of 1 s^-1 appears with a peak efficiency of power dissipation about 56% occurring. This domain is expected to happen in a hot process, such as hot rolling, hot extrusion and hot forging. There is high efficiency of power dissipation at temperature beyond 350 ℃ and strain rate 0. 001 s^-1. Such domains suggest the occurrence of superplastic deformation. 相似文献
4.
镁合金板材轧制工艺及组织性能分析 总被引:12,自引:0,他引:12
在研究镁合金板材熔铸及加工工艺的基础上,以AZ31B镁合金为材料,以优化组织性能为目标,通过控制轧制温度、压下制度、控温轧制和退火制度,轧制出σb≥280MPa,σo.2≥160MPa,d≥16%的镁合金板材,所轧制出的板材成功地得到实际应用,并对工艺制度的合理性从理论上进行了分析。 相似文献
5.
Flow stress and softening behavior of wrought magnesium alloy AZ31B at elevated temperature 总被引:3,自引:0,他引:3
1 INTRODUCTIONThewroughtmagnesiumalloyshaveexcellentspecificstrengthandstiffness ,machinability ,dampcapacity ,dimensionalstability ,lowmeltingcostsandare ,hence ,veryattractiveinsuchapplicationsasau tomobile ,aviation ,electronicandcommunicationin dustry[16 ] .Investigationsontheflowstressandsofteningbehaviorofmagnesiumalloysathigherformingtem peratureandstrainratehavebeenanimportantsub jectinwroughtmagnesiumalloysforming[710 ] .InthispapertheflowstressandsofteningbehaviorofAZ31Bdeform… 相似文献
6.
7.
8.
当光射入染料敏化太阳能电池(DSCs)时,有部分光不能被染料、电解液、导电玻璃等吸收,这部分光将透过电池而未被利用,本研究利用普通镀铝玻璃镜做为背底,将这部分透射光通过背反射重新射入电池来提高DSCs的光电转换效率.研究结果表明,背反射能大幅度提高DSCs的短路电流,短路电流的增加率随着测试遮光罩开孔尺寸的增加而增加,并且随纳米TiO2薄膜厚度的增加而降低. 相似文献
9.
10.