Cr doped ZnAl2O4 spinel samples were prepared by the traditional solid state reaction and co-precipitation synthetic route, and the results suggest that the co-precipitation method has some superiority in contrast to the solid state reaction method. XRD, FT-IR, and XPS spectra confirmed that the well-crystallized spinel cubic phase of ZnAl2O4: Cr3+ samples were successfully formed. The morphology of the samples was investigated by FE-SEM and FE-TEM, and the results show that the samples by the co-precipitation route can generate a smaller size of particles compared to the solid state reaction. Photoluminescence excitation spectra monitored at 686 nm are comprised of two broad excitation bands near 530 nm and 395 nm, and the emission spectra show emissions ranging from 640 to 780 nm, due to the 2E?→?4A2 spin-forbidden transition of Cr3+ ions in spinel lattices. The optimized concentration monitored at 686 nm is 1%, while at 693 nm is 3.5%. Compared with the samples by solid state reaction method, the samples by co-precipitation method show preferable luminescent properties, such as the higher photoluminescence intensity and higher quantum efficiency. Several phosphor-converted LEDs were to investigate the applicability of the prepared samples. The results confirm that the phosphor has potential applications in plant growth and supplementing the red region in white-LEDs and the phosphors prepared by co-precipitation are more suitable to be used in phosphor-converted LED devices due to their preferable luminescent properties.
In this paper, the stabilization for Schrödinger equation subject to internal damping and boundary disturbance at the control end is investigated. Due to its immeasurability, the nonlinear observer system is designed to obtain the state information, and the existence of weak solution and its convergence for the nonlinear observer system are proved. The feedback control is realized by the backstepping transformation. In addition, the adaptive disturbance rejection control is applied to estimate the disturbance. According to the observer and disturbance estimation, the feedback control is finally designed to stabilize the system asymptotically.
Here we report a transparent dual-phase ZnO·2.7Al2O3 ceramic. The composite is pore-free and consists of thin nanosheets with a spinel phase and a hexagonal phase, while the two phases match closely in both lattice and refractive index. Such features result in excellent optical transmittance (maximum value >80% in the visible spectrum) at comparable phase volume. This work may provide a new thought for the rational structural design of optical nanocomposites. 相似文献
In this work, the composition-dependent point defect types and formation energies of RE2Hf2O7 (RE = La, Ce, Pr, Nd, Pm, Sm, Eu and Gd) as well as the oxygen diffusion behavior are systematically investigated by first-principles calculations. The possible defect reactions and dominant defect complexes under stoichiometric and non-stoichiometric conditions are revealed. It is found that O Frenkel pairs are the predominant defect in stoichiometric pyrochlore hafnates. Hf-RE cation anti-site defects, accompanied by RE vacancies and/or oxygen interstitials, are stable in the non-stoichiometric case of HfO2 excess. On the other hand, RE-Hf anti-site defects together with oxygen vacancies and/or RE interstitials are preferable in the case of RE2O3 excess. The energy barriers for the migration along the VO48f - VO48f pathway of pyrochlore hafnates were calculated to be between 0.81 eV and 0.89 eV. Based on these results, a defect engineering strategy is proposed and the pyrochlore hafnates investigated here are predicted to exhibit potential oxygen ionic conductivity. 相似文献
The waterline corrosion behaviors of carbon steel partially immersed in a 3.5 wt% NaCl solution were investigated using the wire beam electrode technique, and the effects of corrosion products on the processes of waterline corrosion were analyzed. The results demonstrated that the initial stage and development stage of waterline corrosion were mainly controlled by the concentration and diffusion of dissolved oxygen, respectively, and the deceleration stage of waterline corrosion was mainly affected by corrosion products. The main component of the yellow corrosion products was γ-FeOOH, and γ-FeOOH that exhibited a high reduction reactivity could be involved in the cathodic reaction. The black corrosion products were mainly composed of Fe3O4 with strong thermodynamic stability and the processes of dissolved oxygen diffusion and ion transports were obviously affected due to the continuous accumulation of Fe3O4 on the surface of the electrodes. Polarity reversals were observed on the single electrodes below the waterline, but the reasons for the phenomena were different from each other. 相似文献
The electrode materials with high pseudocapacitance can enhance the rate capability and cycling stabil-ity of lithium-ion storage devices.Herein,we fabricated MoS2 nanoflowers with ultra-large interlayer spacing on N-doped hollow multi-nanochannel carbon nanofibers(F2-MoS2/NHMCFs)as freestanding binder-free anodes for lithium-ion batteries(LIBs).The ultra-large interlayer spacing(0.78~1.11 nm)of MoS2 nanoflowers can not only reduce the internal resistance,but also increase accessible active sur-face area,which ensures the fast Li+intercalation and deintercalation.The NHMCFs with hollow and multi-nanochannel structure can accommodate the large internal strain and volume change during lithi-ation/delithiation process,it is beneficial to improving the cycling stability of LIBs.Benefiting from the above combined structure merits,the F2-MoS2/NHMCFs electrodes deliver a high rate capability 832 mA h g-1 at 10 A g-1 and ultralong cycling stability with 99.29 and 91.60%capacity retention at 10 A g-1 after 1000 and 2000 cycles,respectively.It is one of the largest capacities and best cycling stability at 10 A g-1 ever reported to date,indicating the freestanding F2-MoS2/NHMCFs electrodes have potential applications in high power density LIBs. 相似文献
Pathogens pose a serious challenge to environmental sanitation and a threat to public health.The frequent use of chemicals for sterilization in recent years has not only caused secondary damage to the environment but also increased pathogen resistance to drugs,which further threatens public health.To address this issue,the use of non-chemical antibacterial means has become a new trend for environmental disinfection.In this study,we developed red phosphorus nanoparticles(RPNPs),a safe and degradable photosensitive material with good photocatalytic and photothermal properties.The red phosphorus nanoparticles were prepared using a template method and ultrasonication.Under the irradiation of simulated sunlight for 20 min,the RPNPs exhibited an efficiency of 99.98%in killing Staphylococcus aureus due to their excellent photocatalytic and photothermal abilities.Transmission electron microscopy and ultraviolet–visible spectroscopy revealed that the RPNPs exhibited degradability within eight weeks.Both the RPNPs and their degradation products were nontoxic to fibroblast cells.Therefore,such RPNPs are expected to be used as a new type of low-cost,efficient,degradable,biocompatible,and eco-friendly photosensitive material for environmental disinfection. 相似文献