Process Intensification of Living Cationic Polymerization of Isobutylene by a Flow Reaction System

Increasing the reaction temperature of the living cationic polymerization of isobutylene is crucial for industrial production due to the cost of refrigeration. The reaction temperature increase was achieved with an accelerated reaction rate using a flow reaction system. The polymerization conditions, including the flow reactor design, were based on the results of kinetic studies. Utilizing a milli‐scale flow reactor, polyisobutylene, which has a narrow molecular weight distribution, was obtained within a considerably short residence time at a high temperature. Furthermore, it was confirmed that the value of M_w/M_n correlates with the product of the Reynolds number and the angle of collision.     

Combustion synthesis of AlN doped with carbon and oxygen

Carbon-and-oxygen-doped AlN specimens were prepared by combustion synthesis using Al, graphite, and AlN. Graphite addition changed the product color from white to blue. By XRD, the lattice constant increased slightly with increasing carbon content. Blue AlN powder was synthesized with a molar ratio of the diluent AlN of 0.2-0.5 with a fixed graphite content of 0.05. At an AlN molar ratio exceeding 0.6, carbon was not successfully incorporated due to the lower reaction temperature. Calcination at 800°C in air removed residual graphite without changing the crystal structure or product color. Oxygen, nitrogen, and carbon analyses revealed that blue AlN powders contained 0.45-0.54 mass% carbon and 1.4-1.6 mass% oxygen, while the undoped AlN contained 0.021 mass% carbon and 0.94 mass% oxygen. The origin of the white-to-blue color change was investigated via reflection measurements. Blue AlN exhibits an absorption peak at 634 nm (1.96 eV). From first-principles electronic structure calculations, the C-doped AlN and carbon-and-oxygen-doped AlN with a 1:1 ratio could be classified as p-type, whereas the O-doped AlN and 1:3 carbon-and-oxygen-doped AlN were n-type. One reason for the absorption peak at 634 nm may be a transition from the conduction band to an upper unoccupied state. These results suggest the possible control of optical and electronic properties of AlN via carbon-and-oxygen doping.     

Synthesis and Initial Characterization of a Selective,Pseudo-irreversible Inhibitor of Human Butyrylcholinesterase as PET Tracer

The enzyme butyrylcholinesterase (BChE) represents a promising target for imaging probes to potentially enable early diagnosis of neurodegenerative diseases like Alzheimer's disease (AD) and to monitor disease progression in some forms of cancer. In this study, we present the design, facile synthesis, in vitro and preliminary ex vivo and in vivo evaluation of a morpholine-based, selective inhibitor of human BChE as a positron emission tomography (PET) tracer with a pseudo-irreversible binding mode. We demonstrate a novel protecting group strategy for ¹⁸F radiolabeling of carbamate precursors and show that the inhibitory potency as well as kinetic properties of our unlabeled reference compound were retained in comparison to the parent compound. In particular, the prolonged duration of enzyme inhibition of such a morpholinocarbamate motivated us to design a PET tracer, possibly enabling a precise mapping of BChE distribution.     

Fine-tuned,molecular-composite,organosilica membranes for highly efficient propylene/propane separation via suitable pore size

Fine-tuned, molecular-composite, organosilica membranes were fabricated via the co-condensation of organosilica precursors bis(triethoxysilyl)acetylene (BTESA) and bis(triethoxysilyl)benzene (BTESB). Fourier transform infrared and UV–vis spectra confirmed the co-condensation behaviors of BTESA and BTESB. The evolution of the network structure indicated that the incorporated BTESB decreased the membrane pore size, which was determined by a modified gas translation model according to the steric effect of the phenyl groups. The incorporation of BTESB to BTESA finely tuned the membrane structure and endowed the resultant composite membrane with improved separation properties. The BTESAB 9:1 membrane (molar ratio of BTESA/BTESB was 9:1) exhibited high C₃H₆ permeance at 4.5 × 10⁻⁸ mol m⁻² s⁻¹ Pa⁻¹ and a C₃H₆/C₃H₈ permeance ratio of 33 at 50°C. One of the most important developments of this study involved clearly defining the relationship between membrane pore size and C₃H₆/C₃H₈ separation performance for organosilica membranes in single and binary separation systems.     

Synthesis and characterization of dextrin derivatives by heterogeneous esterification

A series of fully-acylated dextrin esters (DS = 3) with varying side-chain lengths (C2–12) were synthesized by heterogeneous esterification using trifluoroacetic anhydride/carboxylic acid. The influence of side-chain lengths on structure and properties of dextrin esters were investigated by structural, thermal, mechanical and hydrophobic analysis. The thermal stability of dextrin was enhanced by esterification, presenting ca. 40–60 °C higher decomposition temperatures than that of neat-dextrin. The transition temperatures of melting and crystallization were not observed for all dextrin esters because they were amorphous polymers. The glass transition temperature (T_g) was not observed in dextrin but was observed in dextrin esters. As increasing side-chain length, T_gs of dextrin esters decreased ranged from 162.2 °C (C2) to 49.2 °C (C12). Colorless and transparent dextrin ester films were prepared to measure the film properties. Tensile strength of dextrin ester films tended to decrease with increasing side-chain lengths, whereas the elongation at break increased. And, dextrin ester films showed significantly increased hydrophobicity with a contact angle of up to 102° (C12).     

Influence of LiBO2 addition on the microstructure and lithium-ion conductivity of Li1+xAlxTi2−x(PO4)3(x = 0.3) ceramic electrolyte

Concerning the safety problems of conventional Li-ion batteries with liquid electrolytes, it is crucial to develop reliable solid-state electrolytes with high ionic conductivity. Li_1+xAl_xTi_2?x(PO₄)₃ (LATP, x = 0.3) is regarded as one of the most promising solid electrolytes due to its high ionic conductivity and excellent chemical stability to humidity.Herein, a new strategy is proposed for improving the sintering behavior and enhancing the ionic conductivity of LATP by using LiBO₂ as the sintering aid via liquid phase sintering. The as-prepared sample LATP with homogeneous microstructure and high relative density of 97.1% was successfully synthesized, yielding high total ionic conductivity of 3.5 × 10^?4 S cm^?1 and low activation energy of 0.39 eV at room temperature. It was found that the addition of LiBO₂ could effectively enhance the densification and increase the ionic conductivity of LATP electrolyte, proving an effective way to synthesis LATP ceramics by a simple and reliable route.     

Decomposing regional income inequality in China and Indonesia using two-stage nested Theil decomposition method

The objective of this paper is to present an inequality decomposition method, the two-stage nested Theil decomposition method, which is an extension of the ordinary one-stage Theil decomposition method. The method is analogous to a two-stage nested design in the analysis of variance (ANOVA). It considers the three-level hierarchical structure of a country: region-province-district, and decomposes overall regional inequality, as measured by Theil indices based on district-level mean incomes, into three components: the between-region, between-province, and within-province inequality components. The within-province component is a weighted-average of within-province income inequalities for each province, while the between-province component is a weighted-average of between-province income inequalities within each region. The method uses a district as the underlying regional unit to measure regional income inequality, rather than a province, and thus can analyze the contribution of within-province inequalities as well as between-province and between-region inequalities to the overall regional income inequality in a coherent framework. This paper applies the two-stage nested Theil decomposition method to district-level income and population data in China and Indonesia and explores factors determining regional income inequality in China and Indonesia. Received: October 2000/Accepted: June 2002 The author is grateful to the Foundation of International Education (Kokusai Kyoiku Zaidan) and Japan Society for the Promotion of Science (Grant-in-Aid for Scientific Research No. 12630073) for their financial support, and to anonymous referees for helpful comments.     

Phragmites australis: a novel biosorbent for the removal of heavy metals from aqueous solution

Reed (Phragmites australis), a commonly used macrophyte in the wetlands constructed for water purification, was investigated as a new biosorbent for the removal of Cu(2+), Cd(2+), Ni(2+), Pb(2+) and Zn(2+) from aqueous solution. The metal adsorption capacity of reed biomass was improved significantly by water-wash, base- and acid-treatment. The maximum sorption of NaOH-pretreated reed biomass was observed near neutral pH for Cu(2+), Cd(2+), Ni(2+) and Zn(2+), while that for Pb(2+) was from an acidic range of pH 4.0 or higher. The maximum metal adsorption capacity on a molar basis assumed by Langmuir model was in the order of Cu(2+)>Ni(2+)>Cd(2+)>Zn(2+)>Pb(2+). Reed biosorbent showed a very high adsorption affinity value, which helps predict its high ability to adsorb heavy metals at low concentration. Desorption of heavy metals and regeneration of the biosorbent was attained simultaneously by acid elution. Even after three cycles of adsorption-elution, the adsorption capacity was regained completely and the desorption efficiency of metal was maintained at around 90%.     

Improving the photovoltaic performance of co‐evaporated Cu2ZnSnS4 thin‐film solar cells by incorporation of sodium from NaF layers

We have investigated the influence of sodium (Na) on the properties of co‐evaporated Cu₂ZnSnS₄ (CZTS) layer microstructures and solar cells. The photovoltaic performance and diode properties were improved by incorporating Na from NaF layers into the CZTS layers, while Na had a negligible effect on the microstructural properties of the layer. The best cell fabricated by using an optimal CZTS layer (Cu/(Zn + Sn) = 0.70, Zn/Sn = 1.8) yielded an active area efficiency of 5.23%. The analysis of device properties suggests that charge‐carrier recombination at CZTS/CdS interface is suppressed by intentional Na incorporation from NaF layers. Copyright © 2016 John Wiley & Sons, Ltd.