Design and fabrication of RESURF MOSFETs on 4H-SiC(0001), (112~0), and 6H-SiC(0001)

Design and fabrication of lateral SiC reduced surface field (RESURF) MOSFETs have been investigated. The doping concentration (dose) of the RESURF and lightly doped drain regions has been optimized to reduce the electric field crowding at the drain edge or in the gate oxide by using device simulation. The optimum oxidation condition depends on the polytype: N/sub 2/O oxidation at 1300/spl deg/C seems to be suitable for 4H-SiC, and dry O/sub 2/ oxidation at 1250/spl deg/C for 6H-SiC. The average inversion-channel mobility is 22, 78, and 68 cm/sup 2//Vs for 4H-SiC(0001), (112~0), and 6H-SiC(0001) MOSFETs, respectively. RESURF MOSFETs have been fabricated on 10-/spl mu/m-thick p-type 4H-SiC(0001), (112~0), and 6H-SiC(0001) epilayers with an acceptor concentration of 1/spl times/10/sup 16/ cm/sup -3/. A 6H-SiC(0001) RESURF MOSFET with a 3-/spl mu/m channel length exhibits a high breakdown voltage of 1620 V and an on-resistance of 234 m/spl Omega//spl middot/cm/sup 2/. A 4H-SiC(112~0) RESURF MOSFET shows the characteristics of 1230 V-138 m/spl Omega//spl middot/cm/sup 2/.     

Body effects on SAR distributions for microwave exposures in a realistic model of the human head.

The finite-difference time-domain (FDTD) simulations of specific absorption rate (SAR) in a human head exposed to microwaves have, to date, been carried out on models of the head only. This was because it was believed that the body effects on the average SAR of the head could be ignored at high frequencies of around 1 GHz. That opinion, however, was based on inappropriate calculation conditions and is therefore unreliable. In this paper, we have re-examined the body effects on the SAR distributions in a realistic homogeneous model of the adult head exposed to microwaves. We found that the SAR on the eye surface of the head-only model exposed to E-polarized waves was 31% smaller than that of the whole-body model at 900 MHz, and 43% larger at 1.5 GHz. For a size that can practically be considered whole-body, it is necessary to have the top of the head to the belly for 900 MHz and to the chest area for 1.5 GHz. The previously unclear body effects of H-polarized waves were assumed to be less than those of E-polarized waves, suggesting that the chest area would be sufficient for both frequencies.     

Analytical studies of four-inch pipe whip tests under BWR LOCA conditions

The purpose of pipe rupture studies in JAERI is to perform model tests on pipe whip, restraint behavior, jet impingement and jet thrust force, and to establish a computational method for analyzing these phenomena. This report presents the analytical results of 4-inch pipe whip tests under BWR LOCA conditions.Dynamic response analyses were performed using the general-purpose finite element program ADINA. The test pipe was modelled by straight beam elements and the four restraints were modelled by a single truss element. The analytical results were compared with the experimental results. Impact time and maximum total restraint force showed good agreement with experimental results. On the other hand, pipe strain and pipe deflection could not be predicted so well. The reason for this is that the sliding of the restraint during the pipe whip movement cannot be considered in the analyses.     

Requirement for transglutaminase in progesterone-induced decidualization of human endometrial stromal cells

Differentiation of endometrial stromal cells (decidualization) is essential for embryo implantation and maintenance of pregnancy. By sequential complementary DNA subtractive hybridization, one of the messenger RNAs (mRNA) induced by progesterone in human endometrial stromal cells decidualized in vitro was identified as that of a tissue transglutaminase type II (TGase). TGase mRNA was induced within 6 h after the addition of progesterone to the culture, and the effect was dose dependent. Both the TGase inhibitor monodansylcadaverine and oligodeoxynucleotide complementary to the TGase mRNA inhibited the decidualization, as assessed by PRL production and morphological transformation. Expression of TGase mRNA in human decidua and endometria exposed to high levels of progesterone in vivo was demonstrated by Northern blotting and in situ hybridization. These data suggest that TGase is necessary for the decidualization of human endometrial stromal cells and that clarification of the mechanism of action of TGase will facilitate further insight into the diagnosis and treatment of infertility.     

High-Strength and High-Fracture-Toughness Ceramics in the Al2O3/LaAl11O18 Systems

Control of microstructure in the Al₂O₃/LaAl₁₁O₁₈ system was performed. Elongated alumina grains were formed by doping with small addition of silica, and 20 vol% lanthana- luminate was formed in situ by the reaction of LaAlO₃- A1₂O₃ in an alumina matrix. Strengths of over 600 MPa and a high fracture toughness (6 MPa.m^1/2) were achieved in the material with both elongated A1₂O₃ grains and LaAl₁₁O₁₈ platelets. Generally antagonistic properties such as strength and fracture toughness have been made compatible in the same ceramic system.     

Fracture Energies of Tape-Cast Silicon Nitride with β-Si3N4 Seed Addition

The fracture energies of the tape-cast silicon nitride with and without 3 wt% rod-like β-Si₃N₄ seed addition were investigated by a chevron-notched-beam technique. The material was doped with Lu₂O₃–SiO₂ as sintering additives for giving rigid grain boundaries and good heat resistance. The seeded and tape-cast silicon nitride has anisotropic microstructure, where the fibrous grains grown from seeds were preferentially aligned parallel to the casting direction. When a stress was applied parallel to the fibrous grain alignment direction, the strength measured at 1500°C was 738 MPa, which was almost the same as room temperature strength 739 MPa. The fracture energy of the tape-cast Si₃N₄ without seed addition was 109 and 454 J/m² at room temperature and 1500°C, respectively. On the contrary, the fracture energy of the seeded and tape-cast Si₃N₄ was 301 and 781 J/m² at room temperature and 1500°C, respectively, when a stress was applied parallel to the fibrous gain alignment. The large fracture energies were attributable primarily to the unidirectional alignment fibrous Si₃N₄ grains.     

Densification and Thermal Conductivity of AIN Doped with Y2O3, CaO, and Li2O

Small amounts of Li₂O result in sintering in the AIN-Y₂O₃-CaO and AIN-CaO systems at firing temperatures <1600°C. The effect is ascribed to reduction of the liquidus temperature. Furthermore, Li₂O is removed by volatization at temperatures from 1300° to 1600°C, and its content decreases several ppm from the initial 0.3 wt%. Li₂O-doped AIN specimens containing Y₂O₃ and CaO additives are well densified by firing at 1600°C for 6 h, and their thermal conductivity is 135 W^.m^−1.K⁻¹.The effect of Li₂O addition on sintering and thermal conductivity also is discussed through thermo-dynamic considerations.     

Synthesis of Monodispersed Spherical β-Silicon Carbide Powder by a Sol-Gel Process

Monodispersed spherical β-SiC powder was synthesized by heating spherical gel powder derived from the hydrolysis of a mixture of phenyltriethoxysilane and tetraethyl orthosilicate. The solution was prepared in a beaker and hydrolyzed by NH₄OH without stirring. The monodispersed spherical gel powder of submicrometer size was obtained when the added amount of NH₄OH was greater than 16 moles per mole of silane plus alkoxide, and it became monodispersed spherical β-SiC powder by heat-treating at 1500°C for 4 h in an Ar atmosphere. The SiC content of the powder was 92.6 wt%.     

High Thermal Conductivity in Silicon Nitride with Anisotropie Microstructure

Silicon nitride was fabricated by tape casting of α-Si₃N₄ powder with 5 wt% Y₂O₃ and 5 vol% rodlike β-Si₃N₄ seed particles, followed by tape stacking, hot pressing under 40 MPa, and annealing at 1850°C for 2-66 h under a nitrogen pressure of 0.9 MPa. Silicon nitrides fabricated by this procedure exhibited a highly anisotropic microstructure with large elongated grains (developed from seed particles) uniaxially oriented parallel to the casting direction. Thermal conductivities parallel to the grain alignment were much higher than those measured in other directions and exhibited high values of up to 120 W/(m.K). The anisotropic thermal conductivity of the specimen could be explained by the rule of mixture, considering that large elongated grains developed from seeds have higher thermal conductivity than a small-grained matrix.