Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

National-scale implementation of mandatory freshwater farm plans: a mechanism to deliver water quality improvement in productive catchments in New Zealand?

Nutrient Cycling in Agroecosystems - Reducing agriculturally derived diffuse contaminant losses (via non-point sources) from land to water has proven difficult for decades. Owing to the diversity...     

A Modified Imperialist Competitive Algorithm for Spoofing Attack Detection in Single-Frequency GPS Receivers

Wireless Personal Communications - A GPS spoofing attack broadcasts counterfeit signals to resemble standard GPS satellite signals to take control of the correlation peaks of GPS signals to force...     

Analysis of ZTE MRI application to sandstone and carbonate

Microtomography (μCT) and nuclear magnetic resonance (NMR) have been used to characterize porous media for decades. Magnetic resonance imaging (MRI) enables direct visualization of pore architecture and many pulse sequences exist. In this work, we tested the MRI pulse sequence Zero Echo Time (ZTE) to study sandstone and carbonate for its ability to address short relaxation times. We aimed at resolving two fluid conduit scales, that is, pores and fractures. In this research, we study tighter porous systems than those previously reported using ZTE. Additionally, pore cluster analysis (PCA), combined with ZTE, can be used to analyze pore-fracture connectivity of relatively large core plugs. We show that ZTE can resolve two-scale pore systems simultaneously, that is, fractures and pores. By combining time-domain NMR pore-size analysis and PCA, we show that careful selection of resolution is necessary to understand transport in porous media.     

Thermal depolarization and electromechanical hardening in Zn2+-doped Na1/2Bi1/2TiO3-BaTiO3

Na_1/2Bi_1/2TiO₃-based materials have been earmarked for one of the first large-volume applications of lead-free piezoceramics in high-power ultrasonics. Zn²⁺-doping is demonstrated as a viable route to enhance the thermal depolarization temperature and electromechanically harden (1-y)Na_1/2Bi_1/2TiO₃-yBaTiO₃ (NBT100yBT) with a maximum achievable operating temperature of 150 °C and mechanical quality factor of 627 for 1 mole % Zn²⁺-doped NBT6BT. Although quenching from sintering temperatures has been recently touted to enhance T_F-R, with quenching the doped compositions featuring an additional increase in T_F-R by 17 °C, it exhibits negligible effect on the electromechanical properties. The effect is rationalized considering the missing influence on conductivity and therefore, negligible changes in the defect chemistry upon quenching. High-resolution diffraction indicates that Zn²⁺-doped samples favor the tetragonal phase with enhanced lattice distortion, further corroborated by ²³Na Nuclear Magnetic Resonance investigations.     

Microstructure and electromagnetic properties of LiFe5O8 ferrite ceramics prepared from wet- and dry-milled powders

The effect of dry and wet ball milling of LiFe₅O₈ ferrite powder on the microstructure and electromagnetic properties of ferrite ceramics was studied using XRD analysis, scanning electron microscopy, dilatometry, thermogravimetry, calorimetry, and measurement of specific magnetization and electrical resistance. The sintering temperature was 1050 °C; the sintering time was 2 h. It was found that ferrite fabricated from dry-milled powder exhibits an ordered α-LiFe₅O₈ phase with bulk density of 91%. Its saturation magnetization and Curie temperature are 55 emu/g and 628°С, respectively. Specific electrical resistance is 4?10⁶ Ω cm. Wet milling in isopropyl alcohol causes formation of a disordered β-LiFe₅O₈ phase. Ceramics produced by this method shows higher bulk density (97%) and low porosity, and an order of magnitude lower resistivity. Its saturation magnetization and Curie temperature are 51 emu/g and 607°С, respectively.     

Batch Tests for Optimisation of Solvent Composition and Process Flexibility of the CHALMEX FS-13 Process

ABSTRACT

Studies have been performed with the purpose of determining the optimal solvent composition of a Chalmers grouped actinide extraction (CHALMEX) solvent for the selective co-extraction of transuranic elements in a novel Grouped ActiNide EXtraction (GANEX) process. The solvent is composed of 6,6’-bis(5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-benzo-[1,2,4]-triazin-3-yl)-[2,2’]-bipyridine (CyMe₄-BTBP) and tri-n-butyl phosphate (TBP) in phenyl trifluoromethyl sulfone (FS-13). The performance of the system has been shown to significantly depend on the ratios of the two extracting agents and the diluent to one another. Furthermore, the performance of the determined optimal solvent (10 mM CyMe₄-BTBP in 30% v/v TBP and 70% v/v FS-13) on various simulated PUREX raffinate solutions was tested. It was found that the solvent extracts all transuranic elements with high efficiency and good selectivity with regard to most other elements (fission products/activation products) present in the simulated PUREX raffinate solutions. Moreover, the solvent was found to extract a significant amount of acid. Palladium, silver, and cadmium were co-extracted along with the TRU-radionuclides, which has also been observed in other similar CHALMEX systems. The extraction of plutonium and uranium was preserved for all tested simulated PUREX raffinate solutions compared to experiments using trace amounts.     

Photocatalytic degradation of methylene blue and sulfisoxazole from water using biosynthesized zinc ferrite nanoparticles

The extensive occurrence of textile and pharmaceutical contaminants and their metabolites in water systems has posed significant concerns regarding their possible threat to human health and the environmental system. As a result, herein ZnFe₂O₄ nanoparticles were synthesized through the use of Monsonia burkeana plant extract. The synthesized nanoparticles were characterized using XRD, FTIR, UV–vis, SEM, EDS, TGA, BET, PL, EPR and VSM. XRD showed that the crystalline structure of ZnFe₂O₄ nanoparticles with a calculated crystal size of 25.03 nm was formed. FT-IR confirmed the characteristic functional groups contained within the M. burkeana plant were deposited on the formed ferrite nanoparticles. BET analysis confirmed the mesoporous nature of ZnFe₂O₄ with an average pore diameter of 31.6 nm. Morphological studies demonstrated that the formed nanoparticles had spherical as well as rod-like shapes. ZnFe₂O₄ photocatalyst illustrated that it may be effortlessly detached by an external magnetic field. The optimum conditions for the 99.8% removal of Methylene Blue was obtained at pH12, within 45min and at the optimum dosage of 25 mg of the catalyst. The as-prepared ZnFe₂O₄ nanoparticles proved to be easily separated and recycled, and remained efficient even after 5 reuses, proving that the material is highly stable. The ROS studies also demonstrated that electrons are the main factors contributing to the degradation of MB. Upon testing the photocatalytic performance of the sulfonamide antibiotic, sulfisoxazole in water showed a degradation of 67%. This study has shown that these materials can be used in targeting textile and pharmaceutically polluted water.     

A novel ceramic matrix composite based on YNbO4–TiO2 for microwave applications

This work presents the dielectric properties of YNbO₄ (YNO)–TiO₂ composites in the microwave range. X-ray diffraction analysis demonstrates that the addition of TiO₂ to YNO results in the formation of a Y(Nb_0.5Ti_0.5)₂O₆ phase. In the microwave range, the values of permittivity and dielectric loss did not present major changes with the increment of TiO₂. Moreover, the addition of TiO₂ results in an improvement in the thermal stability of YNO, with YNO63 demonstrating a resonant frequency of ?8.96 ppm.°C^?1. We utilised numerical simulations to evaluate the behaviour of these materials as dielectric resonator antennae and it is found that they exhibit a reflection coefficient below ?10 dB at the resonant frequency, with a realised gain of 4.94 – 5.76 dBi, a bandwidth of 665–1050 MHz and a radiation efficiency above 84%. Our results indicate that YNO–TiO₂ composites are interesting candidates for microwave operating devices.