Cystoseira hakodatensis is an unutilised brown algae belonging to family Sargassaceae. A crude methanol extract from the algae showed inhibitory effects on the growths of Bacillus cereus and Bacillus licheniformis. To isolate the major antimicrobial agent, a sequential active‐guided isolation procedure was applied: liquid–liquid extraction, column chromatography and bio‐autography. A marked antimicrobial agent (active α) was isolated in hydrophobic fraction and was determined to phenolics without carbohydrates and proteins by phytochemical test. Regarding the antimicrobial potential, the isolated active α showed better inhibitory effects against B. cereus and B. licheniformis at 2 and 4 times of lower concentrations (62.5 and 31.3 μg mL^?1) in comparison with epigallocatechin gallate. These results showed that C. hakodatensis is a potential source of antimicrobial agent capable of preventing the growth of the two bacteria.     

Distribution of carbon contamination in MgAl2O4 spinel occurring during spark-plasma-sintering (SPS) processing: I – Effect of heating rate and post-annealing

Carbon contamination from the carbon paper/dies during spark-plasma-sintering (SPS) processing was examined in the MgAl₂O₄ spinel. The carbon contamination sensitively changes with the heating rate during the SPS processing. At the high heating rate of 100 °C/min, the carbon contamination having organized structures occurred over almost the entire area from the surface to deep inside the SPSed spinel disk. In contrast, at the slow heating rate of 10 °C/min, the carbon contamination having disordered structures occurred only around the surface area. The carbon phases transform into high pressure CO/CO₂ gases by post-annealing in air and lead to pore formation along the grain junctions. The pore formation significantly occurs at the high heating rate due to the large amount of the contaminant carbon phases. This suggests that if once the carbon contamination was formed in the materials, it is very difficult to remove the carbon phases from the materials.     

Hydrogen production through dry reforming of biogas using a porous electrochemical cell: Effects of a cobalt catalyst in the electrode and mixing of air with biogas

This paper reports the performance of porous Gd-doped ceria (GDC) electrochemical cells with Co metal in both electrodes (cell No. 1) and with Ni metal in the cathode and Co metal in the anode (cell No. 2) for CO₂ decomposition, CH₄ decomposition, and the dry reforming reaction of a biogas with CO₂ gas (CH₄ + CO₂ → 2H₂ + 2CO) or with O₂ gas in air (3CH₄ +?1.875CO₂ +?1.314O₂ → 6H₂ +?4.875CO +?0.7515O₂). GDC cell No. 1 produced H₂ gas at formation rates of 0.055 and 0.33?mL-H₂/(min?m²-electrode) per 1?mL-supplied gas/(min?m²-electrode) at 600?°C and 800?°C, respectively, by the reforming of the biogas with CO₂ gas. Similarly, cell No. 2 produced H₂ gas at formation rates of 0.40?mL-H₂/(min?m²) per 1?mL-supplied gas/(min?m²) at 800?°C from a mixture of biogas and CO₂ gas. The dry reforming of a real biogas with CO₂ or O₂ gas at 800?°C proceeded thermodynamically over the Co or Ni metal catalyst in the cathode of the porous GDC cell. Faraday's law controlled the dry reforming rate of the biogas at 600?°C in cell No. 2. This paper also clarifies the influence of carbon deposition, which originates from CH₄ pyrolysis (CH₄ → C + 2H₂) and disproportionation of CO gas (2CO → C + CO₂), on the cell performance during dry reforming. The dry reforming of a biogas with O₂ molecules from air exhibits high durability because of the oxidation of the deposited carbon by supplied air.     

Iodine-123-BMIPP myocardial washout and cardiac work during exercise in normal and ischemic hearts

Due to the changes in the frequency of penicillin-resistant strains of S. pneumoniae, it is necessary to perform surveillance studies of bacterial resistance. Isolates from the upper respiratory tract of asymptomatic children have been useful. There is no information about the difference between isolates from children with and without upper respiratory tract infection (URTI). The objective of the authors in this paper is to establish the prevalence of carrier-state, serotype and antimicrobial resistance of S. pneumoniae isolates from children with and without acute upper respiratory tract infection (URTI) in a rural area in Mexico. A cross-sectional comparative study was performed in Tlaxcala, Mexico. Children from one month 5 years of age were included. Nasopharyngeal swabs were obtained. Identification was done by international microbiology standards. Serotyping was done by the capsular Quellung test. The susceptibility testing was performed by the agar dilution method. Four-hundred and fifty patients were included. S. pneumoniae was isolated in 134 children (29.7%). Frequency of carriers was greater in patients with URTI (107/323) than without URTI (27/127) (33.1% vs. 21.1% p = 0.012, OR 1.84, IC 95% 1.1-3.08). The six most frequent serotypes were: 6B (16.4%); 19F (11.9%); 19A (6.7%); 14, 23F, and 35 (5.2% each), with no difference among the groups. Only 3% of the strains had high level resistance to penicillin, and 12.6% had intermediate resistance, and for ampicillin 4%, amoxicillin 4%, amoxicillin-clavulanate 4%, ceftriaxone 3%, cefotaxime 1.5%, erythromycin 6%, miocamycin 3%, chloramphenicol 4%, and vancomycin 0%. Trimethoprim-sulfamethoxazole resistance was very high (42%). In conclusion, colonization is higher in children with URTI. Five of the most frequent serotypes identified in this study were the same as those identified in patients with S. pneumoniae invasive diseases in Mexico City. In Tlaxcala, Mexico, beta-lactams could be the drug of choice for the treatment of S. pneumoniae lower respiratory tract infections. It is necessary to perform clinical assays to evaluate the efficacy of trimethoprim-sulfamethoxazole due to the high resistance in vitro.     

Low-loss athermal silica-based lattice-form interleave filter with silicone-filled grooves

We describe a low-loss athermal silica-based interleave filter with a lattice-form structure. We athermalize the filter by using a silicone-filled groove formed in each delay line and we employ a low-loss design to reduce the accumulated groove excess loss in the multiple delay lines. By using these designs, we obtained a very low groove excess loss of 0.4 dB and achieved satisfactory temperature insensitivity and optical characteristics with this filter.     

Fracture toughness evaluation of adjacent flow weld line in polystyrene by the SENB method

Fracture toughness of adjacent flow weld lines, defined as weld lines that occur when two flow fronts meet and continue to flow together in the same direction (meld line or hot weld line), was evaluated by the single‐edge notched‐bend (SENB) method using three differently‐shaped obstructive pins. Although the fracture toughness varied depending upon the shapes of the pin, the values could be standardized as the distance from the meeting point of the two flow fronts flowing around the pin. The fracture toughness decreased drastically from the meeting point along the weld line and then slightly increased. These characteristic features could be explained by flow‐induced molecular orientation at the weld line interface. The molecules around the meeting point that were initially oriented parallel to the weld line due to fountain flow were able to relax, and then entanglement across the weld line interface developed because the flow stopped in the middle of the filling process, resulting in high fracture toughness. In contrast, the material at the downstream side of the weld line continued flowing during the filling process, being stretched along the flow direction. So, the molecular orientation at this area could not relax. In addition, the V‐notch shape, i.e., the depth and length at the surface of the weld line, which also varied depending on the shape of the obstacles, was considered to be identical when the meeting point was allowed to be a datum point. Thus, the meeting point was found to be a significant factor when the properties of weld lines are investigated. POLYM. ENG. SCI., 45:1059–1066, 2005. © 2005 Society of Plastics Engineers     

Extremely low-loss 1.5%-/spl Delta/ 32-channel athermal arrayed-waveguide grating multi/demultiplexer

A silica-based 1.5%-/spl Delta/ 100 GHz-spacing 32-channel athermal arrayed-waveguide grating (AWG) with compact size and extremely low insertion loss is described. By reducing the fibre coupling loss and the excess loss in a silicone-filled groove, an insertion loss of 1.3 dB was achieved with this athermal AWG.