新型相变材料Ti0.5Sb2Te3刻蚀工艺及其机理研究

采用CF4和Ar混合气体研究了新型相变材料Ti0.5Sb2Te3(TST)的刻蚀特性,重点优化和研究了刻蚀气体总流速、CF4/Ar的比例、压力和功率等工艺参数对刻蚀形貌的影响。结果表明,当气体总流量为50 sccm、CF4浓度为26%﹑刻蚀功率为400 W和刻蚀压力为13.3 Pa时,刻蚀速度达到126 nm/min,TST薄膜刻蚀图形侧壁平整而且垂直度好(接近90°)﹑刻蚀表面平整(RMS为0.82 nm)以及刻蚀的片内均匀性等都非常好。     

Dry etching of new phase-change material Al_(1.3)Sb_3Te in CF_4/Ar plasma

正The dry etching characteristic of Al_(1.3)Sb_3Te film was investigated by using a CF_4/Ar gas mixture.The experimental control parameters were gas flow rate into the chamber,CF_4/Ar ratio,the O_2 addition,the chamber background pressure,and the incident RF power applied to the lower electrode.The total flow rate was 50 sccm and the behavior of etch rate of Al_(1.3)Sb_3Te thin films was investigated as a function of the CF_4/Ar ratio,the O_2 addition,the chamber background pressure,and the incident RF power.Then the parameters were optimized.The fast etch rate was up to 70.8 nm/min and a smooth surface was achieved using optimized etching parameters of CF_4 concentration of 4%,power of 300 W and pressure of 80 mTorr.     

用于非易失性相变存储器中Si2Sb2Te5在CF4/Ar等离子体下的反应离子刻蚀

Phase change random access memory（PCRAM） is one of the best candidates for next generation nonvolatile memory,and phase change Si₂Sb₂Te₅ material is expected to be a promising material for PCRAM.In the fabrication of phase change random access memories,the etching process is a critical step.In this paper,the etching characteristics of Si₂Sb₂Te₅ films were studied with a CF₄/Ar gas mixture using a reactive ion etching system.We observed a monotonic decrease in etch rate with decreasing CF4 concentration,meanwhile,Ar concentration went up and smoother etched surfaces were obtained.It proves that CF4 determines the etch rate while Ar plays an important role in defining the smoothness of the etched surface and sidewall edge acuity.Compared with Ge₂Sb₂Te₅, it is found that Si₂Sb₂Te₅ has a greater etch rate.Etching characteristics of Si₂Sb₂Te₅ as a function of power and pressure were also studied.The smoothest surfaces and most vertical sidewalls were achieved using a CF₄/Ar gas mixture ratio of 10/40,a background pressure of 40 mTorr,and power of 200 W.     

新型相变材料Al1.3Sb3Te使用CF4/Ar等离子体干法刻蚀

对使用CF4/Ar 混合气体刻蚀Al1.3Sb3Te的特性进行了研究。实验控制的参数是：气体流入刻蚀腔的速率,CF4/Ar 比例,O2的加入量,腔内压强以及加在底电极上的入射射频功率。总的气体流量是50sccm ,研究刻蚀速率与CF4/Ar的比例,O2加入量,腔内压强和入射射频功率的关系。最后刻蚀参数被优化。 使用优化的刻蚀参数CF4的浓度4%,功率300W,压强800mTorr,刻蚀速率达到70.8nm/min,刻蚀表面平整