Al2O3/Yttria‐Stabilized Zirconia Hollow‐Fiber Membrane Incorporated with Iron Oxide for Pb(II) Removal

Removal by absorptive ceramic membranes can simultaneously absorb and separate metal ions from water. Alumina/yttria‐stabilized zirconia (Al₂O₃/YSZ) hollow‐fiber membranes, fabricated using phase inversion and sintering process, were deposited with iron oxide by an in‐situ hydrothermal process. The results showed that α‐Fe₂O₃ was produced and incorporated across the membranes. A reduction in flux was recorded with the deposition of α‐Fe₂O_3. However, it improved the adsorption capacity for heavy metal adsorption. The adsorption‐separation test demonstrated that the optimized membrane is able to completely remove Pb(II) ions after two hours.     

Influence of the silicon surface treatment by plasma etching and scratching on the nucleation of diamond grown in HFCVD - a comparative study

A comparative study for the nucleation of diamond was carried out using surface treatment like (i) surface scratching with 1 μm diamond paste and (ii) surface etching using chlorine plasma at different RF powers (50, 100 and 150 W). Atomic force microscopic study shows variation in roughness from 31 nm to 110 nm. Scratching results in random scratches, whereas plasma etches a surface uniformly. Scanning electron microscopic observations show well faceted crystallites with a predominance of angular shaped grains corresponding to 〈100〉 and 〈110〉 crystallite surfaces for the scratched as well as plasma etched substrate. Surface etching at 150 W plasma power results in a better growth in comparison with 50 and 100 W plasma powers. Chlorine-radical is found responsible for the changes in the growth morphology. Raman spectroscopy shows a sharp peak at 1,332 cm⁻¹ and a peak at ∼1,580 cm⁻¹ for both samples.     

A review on fault detection and diagnosis techniques: basics and beyond

Safety and reliability are absolutely important for modern sophisticated systems and technologies. Therefore, malfunction monitoring capabilities are instilled in the system for detection of the incipient faults and anticipation of their impact on the future behavior of the system using fault diagnosis techniques. In particular, state-of-the-art applications rely on the quick and efficient treatment of malfunctions within the equipment/system, resulting in increased production and reduced downtimes. This paper presents developments within Fault Detection and Diagnosis (FDD) methods and reviews of research work in this area. The review presents both traditional model-based and relatively new signal processing-based FDD approaches, with a special consideration paid to artificial intelligence-based FDD methods. Typical steps involved in the design and development of automatic FDD system, including system knowledge representation, data-acquisition and signal processing, fault classification, and maintenance related decision actions, are systematically presented to outline the present status of FDD. Future research trends, challenges and prospective solutions are also highlighted.

     

Synthesis,characterization, and cell viability of bifunctional medical-grade polyurethane nanofiber: Functionalization by bone inducing and bacteria ablating materials

There is an extensive possibility of improving characteristics of fibers used in hard tissue engineering, being hydrophobic and less osteoconductive, resulting in the dynamic growth of new tissues. The current work focuses on the fabrication of nanofibers incorporated with titanium dioxide (TiO₂) ''as osteoconductive'' and silver (Ag) ''as self-healing'' nanoparticles (NPs). The incorporation of AgNO₃ by in situ method not only helped to impart the antibacterial activity but also changed the contact angle from 81 ± 03° in the case of pristine nanofibers to 74 ± 03°, 61 ± 03°, 50 ± 08°, and 39 ± 1.1°, in the composite scaffolds containing 0.01, 0.03, 0.05, and 0.07 M of Ag salts. The incubation in simulated body fluid at 37°C to induce mineralization on nanofiber scaffolds indicated Ca and P crystals' formation. The antibacterial activity showed significantly more toxicity toward E. coli (8.3 ± 0.9 mm) than S. aureus (1.2 ± 0.1 mm). Biocompatibility studies using MTT assay on the pre-osteoblasts showed that both TiO₂ and Ag NPs present in the nanofibers are non-toxic to the bone-like cells. However, results show that a higher concentration of Ag NPs (i.e., 0.07 M) is toxic to cells growing. Finally, all the results suggest that the nanofiber scaffolds have considerable scope for future bone tissue engineering materials.     

Biosynthesis and characterisation of nano‐silica as potential system for carrying streptomycin at nano‐scale drug delivery

A growing trend within nanomedicine has been the fabrication of self‐delivering supramolecular nanomedicines containing a high and fixed drug content ensuring eco‐friendly conditions. This study reports on green synthesis of silica nanoparticles (Si‐NPs) using Azadirachta indica leaves extract as an effective chelating agent. X‐ray diffraction analysis and Fourier transform‐infra‐red spectroscopic examination were studied. Scanning electron microscopy analysis revealed that the average size of particles formed via plant extract as reducing agent without any surfactant is in the range of 100–170 nm while addition of cetyltrimethyl ammonium bromide were more uniform with 200 nm in size. Streptomycin as model drug was successfully loaded to green synthesised Si‐NPs, sustain release of the drug from this conjugate unit were examined. Prolong release pattern of the adsorbed drug ensure that Si‐NPs have great potential in nano‐drug delivery keeping the environment preferably biocompatible, future cytotoxic studies in this connection is helpful in achieving safe mode for nano‐drug delivery.Inspec keywords: silicon compounds, nanofabrication, nanomedicine, drug delivery systems, nanoparticles, X‐ray diffraction, Fourier transform infrared spectra, scanning electron microscopyOther keywords: nanosilica, streptomycin, nanoscale drug delivery, nanomedicine, silica nanoparticles, Azadirachta indica leaves extract, X‐ray diffraction analysis, Fourier transform‐infrared spectroscopy, scanning electron microscopy, cetyltrimethyl ammonium bromide, SiO₂      

Effectiveness of pressurised carbon dioxide for inactivation of Escherichia coli isolated from sewage sludge

This research explored the possible application of pressurised carbon dioxide (P CO(2)), a promising non-thermal sterilisation technique, for the treatment of sewage sludge (SS) before anaerobic digestion to inactivate pathogenic microorganisms. Escherichia coli was selected as the test organism and was isolated from SS and maintained in pure culture. The growth curve of the isolated strain was determined by measuring the optical density (OD) in liquid culture medium and relating this information to the spread plate count so that a culture of known cell density could be grown for optimisation experiments. Inactivation of E. coli was enhanced by increase in pressure (1,500, 2,000 and 2,800 kPa) and treatment time (from 0.75 to 24 h). A short exposure time at high pressure was sufficient to provide a degree of inactivation which could also be achieved by longer exposure at lower pressure. Complete inactivation (8 log(10) reduction) was possible at all three pressures. scanning (SEM) and transmission (TEM) electron microscopy studies of E. coli treated with P CO(2) revealed that the cell walls were ruptured, and the cytoplasm was unevenly distributed and had lost its density, indicating the possible leakage of intracellular substances.     

Pollen morphological investigations of family Cactaceae and its taxonomic implication by light microscopy and scanning electron microscopy

The family Cactaceae is the diversified group of angiosperm plants whose pollen statistics has been used for taxonomic identification. In this article, we present the pollen morphology of eight species belong to seven taxonomically complex genera of Cactaceae including Astrophytum, Cylindropuntia, Echinocereus, Echinopsis, Mammillaria, Opuntia, and Thelocactus using light and scanning electron microscopy. The pollen grains were acetolyzed, measured, described, and electron photomicrographs were taken. Cactaceae can be characterized by presenting different palynomorphological features including pollen type, sculpturing, polar and equatorial diameter, aperture orientation, exine thickness, P/E ratio, and echini features. Four types of pollen shapes, that is, prolate spheroidal (three species), subprolate (two species), prolate (two species), and oblate spheroidal in Echinocereus reichenbachii were observed. The polar and equatorial diameter observed maximum in O. ficus indica 116.95 and 112.27 μm while minimum in M. compressa 38.42 and 21.05 μm. Pollen of two types, tricolpate in members of subfamily Cactioideae and pantoporate in the Opuntioideae were examined. The fertility percentage has been observed maximum in Opuntia macrocentra (83.84%) and minimum in Opuntia ficus‐indica (57.89%). Exine sculpturing showing great variations such as granulate, reticulate, granulate perforate and micro‐echinate foveolate ornamentation was examined only in Echinopsis eyriesii. A key to species, based on pollen micromorphological attributes, has been constructed for correct identification of complex cactus species.