高强度铸造铝合金凝固过程中的元素偏析 总被引:3,自引:0,他引:3
通过液淬的方法,研究Al-4.5Cu合金及添加Si,Mn,Ni,Zr元素后合金的凝固过程及溶质分布。结果表明,将Si,Mn,Ni,Zr元素的加入,都能使Al-Cu合金的结晶温度间隔不同程度地减少,其中Al4.5Cu3Si的结晶温度间隔最小,Cu的分布,特点是:晶界高于晶内,一次晶界高于二次晶界”,并随着温度的降低Cu向晶界偏析的趋势加剧,Ni的分布,晶界高于晶内,Mn的分布,晶界高于晶内,但差别不大,Zr在晶界与枝晶间的偏析处的含量较高。 相似文献
3.
4.
梁艳峰 《武汉理工大学学报(材料科学英文版)》2008,23(3):342-345
The thermodynamic analysis of the formation of in-situ reinforced phases in (TiB2+Al3Ti)/Al-4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by differential thermal analysis(DTA).The results show that although TiB2 possesses the strongest formation ability in Al-Ti-B ternary system, [Ti] is relatively excessive in the in-situ reaction and it combines with Al to form AlaTi phase. The reinforced phases are TiB2 and AlaTi in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ℃ and 1 032 ℃. 相似文献
5.
6.
采用熔体接触反应法制备了TiC/Al-4.5Cu复合材料,通过光学显微镜、透射电镜等,对TiC颗粒增强Al-4.5Cu原位复合材料的相结构进行分析。结果表明,5%TiC/Al-4.5Cu原位复合材料的主要增强相为TiC;TiC弥散分布在α-Al基体中,与基体结合良好且界面光滑。在5%TiC/Al-4.5Cu原位复合材料中TiC呈球形或近球形,颗粒细小,其尺寸约为0.1~0.5μm;而在5%TiC/Al-4.5Cu-ХMg原位复合材料中TiC呈规则六边形,颗粒较大,其尺寸约为0.5~0.8μm。 相似文献
7.
采用接触反应法制备原位颗粒增强铸造Al-12Si-4Cu复合材料,研究超声处理工艺对原位TiC和TiAl_3颗粒形貌的影响。结果表明:在铸造Al-12Si-4Cu复合材料中可以原位生成团聚态TiC颗粒、长杆状或块状TiAl_3颗粒;未经超声处理时,TiC颗粒团聚等效直径约70μm,经1500 W超声处理后,其减小到45μm;当超声处理功率增大到3000 W,TiC的团聚现象消失,颗粒均匀分散在基体中,并且长杆状TiAl_3颗粒长度减小到50~150μm,块状TiAl_3颗粒转变为相互独立的小尺寸块状。 相似文献