Study on purification and application of novel precipitant for ceria-based polishing powder

Novel precipitant prepared through carbonation with MgCl2 wastewater generated from rare earth extraction separation process and low-price dolomite as raw materials was studied in this paper. The purification methods of novel precipitant by adding appropriate oxidizing agent were studied. It was found that optimal purification result could be achieved with sodium hypochlorite as iron removal reagent and the iron removal rate could reach up to 90% when the adding amount was 0.1 vol.%. During the preparation, the particle size and distribution of ceria-based polishing powder were affected obviously by the parameters such as concentration, reaction temperature and feeding rate. The results showed that ceria-based polishing powder with D50 =2.5-3.5 μm and the particle size distribution of 0.65-0.75 μm could be prepared when the concentration of CeCl3 was 0.6 mol/L, the reaction temperature was maintained at 50 °C and the feeding speed was controlled at 25 ml/min. Compared with commercial powder, the self-made polishing powder had roughly the same cutting amount, but the surface finish of polished glass was better than that of commercial polishing powder.     

Effect of MgF2-H3BO3 flux on the properties of (Ce,Tb)MgAl11O19 phosphor

The green-emitting(Ce,Tb)MgAl11O19(CTMA) phosphor was prepared by the conventional high temperature solid-state reaction method.The effect of fluxes on the crystal structure,particle morphology,size distribution and photoluminescence properties of CTMA phosphor was investigated by means of the X-ray powder diffraction,scanning electron microscopy and photoluminescence spectrum.The results showed that the addition of appropriate amount of MgF2-H3BO3 flux improved the phase purity of CTMA phosphor,and influen...     

生态化利用油页岩制备白炭黑和氧化铝

利用油页岩为原料,首先采用碱溶-沉淀法制备了白炭黑,降低了油页岩中的SiO₂的含量,具体工艺条件为：NaOH/SiO₂（物质的量）＝4,水/油页岩（质量）＝1,100℃,6 h,粒径≥0.15 mm。然后采用酸浸法,制备了γ-Al₂O₃,降低了油页岩中的Al₂O₃和Fe₂O₃的含量,具体条件为：酸浸液中用NaOH溶液调整到pH＝12.0,过滤分离,再用HCl调整溶液pH＝6.0,使Al₂O₃和Fe₂O₃完全分离。最后得到了含量为71.6％的干酪根,并经FT-IR验证。     

以油页岩渣为原料制备微晶泡沫玻璃

以油页岩渣为主要原料,加入其他辅助原料制备了微晶泡沫玻璃,并分析了各种因素对微晶泡沫玻璃性能的影响.结果表明,发泡剂碳酸钙和稳泡剂磷酸钠的最佳掺量为4%和6%;最佳的工艺条件为:发泡温度1080℃,发泡时间15 min,升温速率14℃/min.试样经过预热、烧结、发泡、稳泡和退火等热处理工艺,完成了发泡和析晶过程.其中发泡工艺需要较高温度,并在短时间内保温.XRD,SEM及FT-IR分析表明,试样已经完全转化为微晶泡沫玻璃,主晶相为普通辉石,次晶相为钙长石,晶体呈纤维状结构且相互交织.与相关材料比较,微晶泡沫玻璃具有机械强度高和质轻保温隔热的优点.     

油页岩制备白炭黑与分散剂应用的研究

以油页岩为原料,采用碱溶-沉淀法制备了白炭黑。具体工艺条件为:NaOH/SiO2(摩尔比)=4,水/油页岩(质量)=1,100℃,6 h,粒径≥0.15 mm。分别研究了NH4Cl、正丁醇、PEG三种分散剂对制备白炭黑的影响。FT-IR和XRD分析表明,三种分散剂对白炭黑的化学结构和无定型状态没有改变;TEM分析表明,三种分散剂对白炭黑的粒度和分散效果都有明显的作用,其中PEG对白炭黑的粒度和分散性能具有很好的效果。     

利用油页岩渣制备氧化铝和白炭黑

以油页岩渣为原料, 分别用酸浸法和碱溶法制备了氧化铝和白炭黑。讨论了焙烧活化作用、酸浸温度、盐酸用量以及酸浸时间等对氧化铝提取率的影响。实验结果表明, 油页岩渣不需活化可以直接采用酸浸法制备氧化铝,最佳工艺条件为: 酸浸温度100 ℃、酸浸时间2.0 h、盐酸/油页岩＝40.0 mL/15.0 g; 氧化铝提取率为90.6%, 纯度为91.7%。探讨了反应温度、反应时间以及碱浓度等对白炭黑提取率的影响,最佳工艺条件为: 反应温度100 ℃、反应时间6.0 h、NaOH浓度为6 mol/L; 白炭黑提取率为80.5%, 纯度为95.9%。灰渣剩余量不到原来的5%, 达到了油页岩渣生态化利用的目的。     

油页岩渣微晶玻璃的晶化过程

以油页岩渣为主要原料制备微晶玻璃,利用DTA、XRD、SEM及FT-IR等技术对微晶玻璃的晶化过程和微观结构进行研究。结果表明：在一定的热处理条件下可以以基础玻璃制备出主晶相为钙铁透辉石,次晶相为钙长石的纤维状结构的微晶玻璃：最佳的热处理工艺为：850℃核化100min,980℃晶化80min;随着热处理温度的升高,红外吸收带发生明显的分裂：玻璃结构中的[A1O4]向[AlO6]转化;网络结构中的钛离子逐渐转变为六配位,形成微晶相——钛酸镁和钛铁晶石,为晶体的生长提供非均匀形核位置。     

用油页岩渣制备白炭黑的工艺

以油页岩渣为原料,经950℃煅烧4 h, 加入3.30 mol/L NaOH溶液于100℃处理4 h,用HCl酸化至pH 8~9时,SiO2的浸出率为75.8%. 经X射线荧光分析,白炭黑产品中的SiO2纯度为91.8%;经FT-IR检测白炭黑的化学结构为水合二氧化硅;经XRD分析,白碳黑为无定型结构;TEM图像显示白炭黑的形貌近似为球状粒子,平均粒径在50 nm以下. 白炭黑的比表面积(BET)为114 m2/g, pH值为5.5~6.0,加热减量为5.82%, 1000℃灼烧减量为6.16%,产品符合中国行业标准HG/T 3061-1999的要求.     

硼泥基烧结砖工艺实验研究

目的为了解决辽宁省硼工业废弃硼泥污染环境、浪费资源问题，研制新型建材使硼泥得到有效利用．方法以硼泥、粉煤灰、铁尾矿为原料，利用工业马弗炉采用正交实验的方法研究硼泥基烧结砖的烧结工艺参数．结果得到原料的最佳质量配比为4：2：4：最佳工艺为塑性成型压力20MPa、最高烧成温度1100℃．对烧结砖试样的测试结果表明本工艺烧结砖的强度高于MU15的普通黏土砖；保温性能优于普通黏土砖．结论烧结工艺使硼泥掺入量提高到了40％，为硼泥的大量利用、解决环境问题开辟了一条新的途径．     

改性油页岩灰吸附Cu^2＋的研究

油页岩灰经HNO3和不同浓度NaOH溶液改性处理制备了改性油页岩灰吸附剂，比较了各种改性油页岩灰吸附剂对Cu^2＋的吸附性能，分别讨论了吸附时间、Cu^2＋浓度和溶液pH值对吸附性能的影响．结果表明，分别经50％HNO3、20％NaOH溶液处理制备的改性油页岩灰吸附剂对Cu^2＋具有较好的吸附性能，且以化学吸附作用方式为主．该改性油页岩灰吸附剂对Cu^2＋的吸附符合Freundlich等温吸附方程．