以不同温度处理的SiO2载体制备的Cu/SiO2催化剂在NO+CO反应中的活性

以不同温度处理SiO2为载体，用交换法制备Cu／SiO2催化剂．催化剂的表面结构用UV-VIR，TPR等方法进行表征．结果表明，不同温度焙烧的SiO2表面的-OH有差异．在NO＋CO的反应中，以500℃焙烧处理的SiO2为载体制备的催化剂显示了更高的催化活性，说明催化剂表面的结构对催化剂的制备有一定的影响．     

Co修饰碳纳米管作为低碳醇合成CoMoK催化剂的高效促进剂

利用化学还原沉积法,制备一类Co修饰的多壁碳纳米管基复合材料(记为y%Co/MWCNT,y%为质量分数),进而用其作为促进剂,制备共沉淀型y%Co/MWCNT促进的Co-Mo-K氧化物基催化剂,CoiMojKk-x%(y%Co/MWC-NT)(x%为质量分数).实验发现,Co对MWCNT的预修饰明显地提高了单纯MWCNT促进的Co-Mo-K催化剂对CO加氢制低碳醇的催化活性.在所制备的Co1Mo1K0.05-12%(4.2%Co/MWCNT)催化剂上,在经优化的两种反应条件(5.0MPa,563 K,V(H2)/V(CO)/V(N2)=60/30/10,GHSV=8000 mL/(h.g)和5.0 MPa,593 K,V(H2)/V(CO)/V(CO2)/V(N2)=60/30/5/5,GHSV=10 000 mL/(h.g))下,C2~9-醇的时空产率分别达294和628 mg/(h.g),分别是单纯MWCNT促进的对应物在其最佳操作条件下这个值(269 mg/(h.g))的1.09和2.33倍;在所制得两种低碳混合醇产物中,C2~9-醇的含量分别达89%和96%(质量分数),并分别以C7-醇和C5-醇为主要醇产物.本文结果表明,Co对MWCNT的预修饰并辅以原料合成气中添加适量CO2对于CO加氢转化率和C2~9-醇时空产率的显著提高起重要作用.     

荆芥挥发油的超临界CO2萃取分离及GC-MS分析

通过正交试验研究了超临界CO2萃取荆芥挥发油的最佳工艺条件,利用GC-MS联用技术对荆芥挥发油化学成分及相对含量进行测定.结果表明,萃取荆芥挥发油最佳工艺条件为萃取压力25 MPa、萃取温度45℃、萃取时间100 min、CO2流量为30 kg/h.在最佳工艺条件时,荆芥挥发油得率为1.316 3%.荆芥挥发油的主要成分为胡薄荷酮和薄荷酮.此外,还发现了荆芥挥发油中含有二氢茉莉酮、土曲霉酮等成分.为了提纯荆芥挥发油,首次采用了二级分离法.与一级分离法相比,二级分离法能够有效降低荆芥挥发油中不饱和脂肪酸及其酯的含量,显著提高胡薄荷酮和薄荷酮的含量.     

膨润土再生砂对 CO_2 水玻璃再生砂性能的影响

将膨润土湿型砂和ＣＯ２水玻璃砂分别进行机械法再生,再按不同比例混合,用ＣＯ２水玻璃工艺研究了再生砂的主要工艺性能．研究结果表明,膨润土再生砂对ＣＯ２水玻璃再生砂的影响不大,随着膨润土再生砂比例的增加,混合再生砂的终强度缓慢降低,而８００℃的残留强度急剧下降．     

B121型无铬高变催化剂低汽气比性能的研究

通过ＸＰＳ、ＦＴ－ＩＲ及催化剂性能测定,Ｂ１２１型无铬高变催化剂加入的Ｂ助剂有２／３以氢氧化物形态存在,增加了催化剂表面ＯＨ－１浓度,提高变换反应速率．使催化剂在低汽气比下仍具有高活性,０３汽气比下活性优于Ｂ１１２、ＩＣＩ７１－４,并未发现Ｆ－Ｔ副产物生成．工业使用表明,Ｂ１２１型催化剂最佳使用汽气比为０４６,与一般高变催化剂相比,汽气比低约０１５,节能效果显著．     

Comparative study of the net exchange of CO<Subscript>2</Subscript> in 3 types of vegetation ecosystems on the Qinghai-Tibetan Plateau

Using the eddy covariance method, from 1 July 2003 to 30 June 2004, we conducted the observation and analysis of ecosystem CO2 flux in 3 types of alpine meadow vegetation （Kobresia humilis, Potentilla fruticosa shrub and Kobresia tibetica swamp meadows） on the Qinghai-Tibetan Plateau. The results show that the Kobresia humilis meadow, the shrub meadow and the swamp meadow＇s highest CO2 uptake rates are 16.78, 10.42 and 16.57 μmol·m^-2·-s^-1 respectively, while their highest CO2 release rates are 8.22, 7.73 and 18.67μmol·m^-2·-s^-1 respectively. The Kobresia humilis meadow and shrub meadow＇s annual atmospheric uptakes are 282 g CO2/m^2 and 53 g CO2/m^2, respectively, while swamp meadow＇s annual atmospheric release is 478 g CO2/m^2. This proves that the Kobresia humilis meadow and the shrub meadow on the Qinghai-Tibetan Plateau have relatively low potential for CO2 uptake and release compared to C4 grasslands, a number of lowland grasslands, and forests. Moreover, swamp meadow has relatively high release potential. This, in turn, reveals clear differences in carbon source/sink between different types of vegetation in the Qinghai-Tibetan Plateau alpine meadow ecosystem. These differences are mainly brought by differences in the vegetations＇ photosynthetic capacity and soil respiration.     

Ag修饰La0.6Sr0.4MnO3基催化剂氧物种的谱学表征

采用柠檬酸溶胶-凝胶法制备钙钛矿型La0.6Sr0.4MnO3 氧化物, 并用Ag 对其进行修饰,制得Ag/La0.6Sr0.4MnO3 催化剂.活性评价结果显示, Ag 的修饰能显著提高原基质催化剂La0.6Sr0.4MnO3 对低浓度CH3OH和CO完全氧化的催化活性, 相应于95% CH3OH和CO转化所需反应温度T95分别可低至421 和370 K. 催化剂的XPS和LRS谱学表征结果揭示, 在6% Ag/La0.6Sr0.4MnO3上, 具高度反应活性的表面氧物种O22- (a)和O-(a)在总表面氧中所占克分子百分数(m ol% )几近未经Ag 修饰的基质体系La0.6Sr0.4MnO3 的两倍. O2-TPD测试结果证实,Ag 对La0.6Sr0.4MnO3基质的修饰、掺杂和部分取代使其对O2 的低温吸附能力大为提高,诱生出一类数量可观具有低温吸-脱附性能的吸附氧物种. 本文结果表明, Ag/La0.6Sr0.4MnO3 催化剂对CH3OH和CO完全氧化高的催化活性与Ag 的修饰提高了催化剂对氧的低温吸附活化能力, 并使催化剂上对CHX, CH3OH, HCHO和CO具高度反应活性的表面氧物种O22- (a)和O-(a)的相对含量明显增加密切相关.     

β-胡萝卜素原料筛选及其超临界二氧化碳萃取

建立了柱层析／分光光度计法测定β－胡萝卜素的分析方法。筛选出富含β－胡萝卜素的螺旋藻做为原料。分别以石油醚和超临界二氧化碳萃取螺旋藻中β－胡萝卜素。结果表明,超临界二氧化碳萃取藻粉中β－胡萝卜素与石油醚萃取相比具有萃取效率高、速度快、工艺简单、萃取物色味纯正、藻粉可以进一步利用和再出售的优点。     

激光家族中的一氧化碳激光器(英)

描述了作为激光光谱分析仪中光源的纵向直流激励自持放电小功率宽频带可调谐一氧化碳激光器,并给出了有关高功率一氧化碳激光器的发展概况．在所描述的一氧化碳激光器中,有相当一部分是由作者在近20年中研制成功的．最后给出了5μm波段一氧化碳激光器和10．6μm波段二氧化碳激光器在金属切割方面的比较实例,并指出了在一氧化碳激光器研究领域尚需解决的问题．     

A_2BO_4型催化活性材料结构与性能的研究──ⅡLa_2Li_xCu_（1－x

Ａ２ＢＯ４型复合氧化物具有非完整结构，Ａ，Ｂ及Ｏ位均有空位，本文以硝酸盐为原料，用柠檬酸络合法使Ｂ位中掺入了Ｌｉ离子，制得的活性组分Ｌａ２ＬｉｘＣｕ１－ｘＯ４（ｘ≤０．１）在６５０℃活化２小时，对于ＣＯ氧化反应和ＮＯｘ还原反应同时有较高的他化活性，ＣＯ和ＮＯｘ的转化率分别高于９０％和８０％．