Removal of Ammonia from Drinking Water by Clinoptilolite

0INTRODUCTION~ntjcIncreasingawarenessoftLhepublicofthetovicityofammoniainaqUeoussolution,drinkingwaterinpal-ticular,forinstance,thetoXicityofnoxioushalogenatedcomPOundsoftrichloridesandchlordrinesresultingfromreactionwithchlorinehashelpedfoeestablishmentofstringentwaterqUalitystandards.Inaddition,ammoniaisnotoriousforitstovicityinwatertofish,cormsionofmelalsandconcrete,andeutrophicationofreceivingwaterhaly.Theprincipalmethodsofammoniaremovalfromaqueoussolutionincludeair.trippi.g['~3],ni…     

掺铁二氧化钛为催化剂光催化氧化汽油气研究

采用溶胶－凝胶法制备了掺铁TiO2催化剂薄膜，并用其光催化处理汽油废气，考察了不同掺铁比的TiO2薄膜光催化降解汽油气的效果，确定TiO2最佳掺铁比为wFe为0．166，探讨了光催化氧化过程中相对温度对汽油降解的影响，结果表明，湿度对光催化降解汽油气影响大反应体系中最佳相对湿度为30％，对光催化氧化降解汽油气动力学进行了探讨，并对汽油气降解的组分进行了鉴定。     

γ-(甲基丙烯酰氧)丙基倍半硅氧烷膜性能研究

为了研究γ-(甲基丙烯酰氧)丙基倍半硅氧烷膜(m-M-S)的性能,采用溶胶-凝胶法制备了TEOS改性的倍半硅氧烷膜材料(m-MST),利用扫描探针电镜、扫描电镜、差示扫描量热法、热重分析等技术对m-MST成膜材料的性能进行了表征.研究结果表明,此膜为有机-无机杂化纳米结构薄膜材料,波长345～2500nm范围内膜层的透光率为98%～99%;TEOS含量在20%时,薄膜体系的机械性能和耐腐蚀性性能最佳.     

好氧生物流化床处理抗生素废水的试验研究

采用以新型高分子材料为生物载体的生物流化床工艺处理高浓度的抗生素废水。试验结果表明,该载体挂膜容易,启动快,一个月后载体附着的生物量可达4136mg/L,在载体表观体积为反应器总体积的50%、进水COD容积负荷低于2.5kg/(m3·d)的情况下,COD去除率可达85%以上。该生物流化床对BOD5的去除率平均高达89.21%,与COD的去除率具有同步性。并研究了反应器中悬浮污泥浓度SS和总生物量MLSS在整个实验期间的动态变化,表明稳定运行时SS和总MLSS基本上稳定不变,当系统受到高负荷冲击时,SS降低,总MLSS升高,而且生物活性也大幅度提高,生物膜处在适应期,反应器抗冲击负荷能力增强。     

水力旋流器流场分析与测试

利用CFD方法,采用Fluent软件对水力旋流器的流场进行了研究和分析,主要分析了水力旋流器内部速度场和流体迹线的分布特点以及随分流比的变化情况,并采用激光多普勒测速仪(LDA)对部分模拟分析结果进行了验证。     

VMS有机-无机杂化膜的制备及其防腐性能研究

以乙烯基三甲氧基硅烷（VMS）为前驱体,采用浸涂法在LY12铝合金表面制备了有机一无机杂化防腐保护膜．分别考察了涂膜次数、固化剂用量和溶剂用量对膜层防腐性能的影响,成膜的最佳工艺条件为：固化剂过氧化苯甲酰（BPO）的加入量为凝胶量的2％（质量分数）;凝胶质量与溶剂质量的比为0．17;涂膜四次．利用动电位极化曲线、盐雾实验和盐水浸泡实验评价了膜层的耐腐蚀性能．结果表明,乙烯基三甲氧基硅烷（VMS）膜层可使腐蚀电流减小到原来的1／300左右,同时也使得试片耐长久腐蚀的能力显著增强．     

超临界水处理对碳纳米管结构的影响研究

为了提高多壁碳纳米管(MWNTs)的吸附性能,采用超临界水(SCW)技术改性MWNTs,研究了在超临界水中不同处理温度和处理时间对MWNTs结构和形貌的影响.分别利用傅里叶变换红外光谱(FT-IR)、X-射线光电子能谱(XPS)、拉曼光谱(Raman)和扫描电子显微镜(SEM)等测试手段分析了改性前后MWNTs结构和形貌的变化.结果表明:超临界水对MWNTs有较弱的氧化能力和较强的物理刻蚀作用,处理时间对MWNTs的影响高于温度的影响.     

化学氧化及高级氧化工艺处理废碱液的研究

采用均相化学催化氧化及高级氧化两步工艺对石油化工乙烯裂解废碱液中的硫化物、有机物进行了处理研究,结果表明：在反应温度40℃、化学催化氧化反应时间90min、Mn^2 15mg／L、气水比(曝气量)75：1以及高级氧化反应时间120min、H2O2的加入量(H2O2／COD)为0．8等条件下,硫化物的转化率可达96％以上,COD去除率可达78％．BOD5／CODcr的比值可由处理前的0．21升至0．54．     

ZnAl类水滑石制备温度对吸附剩余污泥脱水液中磷酸根的影响

A group of Zn-Al layered double hydroxides (LDHs) were synthesized at different temperatures from 25–90 °C in order to investigate the influence of synthesis temperature on characteristics of the LDHs and their phosphate adsorption behaviour. The results reveal that an increase in the synthesis temperature generally improves the specific surface area of the sample and the phos-phate adsorption capacity. The significantly enhanced crystallinity of the Zn-Al-30, synthesized at 30 °C, leads to a remarkable de-crease in the specific surface area and consequently a poor phosphate adsorption capacity. It is suggested that the surface adsorption plays an important role in the phosphate uptake by the Zn-Al LDHs. Zn-Al-70 presents a relatively higher crystallinity and a lower specific surface area, compared with Zn-Al-60 and Zn-Al-80, but the highest phosphate adsorption capacity, indicating that surface adsorption is only one of the pathways for phosphate removal. The phosphate adsorption by the Zn-Al follows a pseudo-second-order kinetic equation. The adsorption isotherms fit Langmuir models, and the maximum adsorption capacities of the Zn-Al-25, Zn-Al-50 and Zn-Al-70 are estimated to be 17.82, 21.01 and 27.10 mg•g1 adsorbent, respectively.     

不同炭材料对Zn-PANi二次电池性能的影响

在聚苯胺合成过程中加入石墨、活性炭和酚醛炭,得到的PANi/C复合材料用于组装Zn-PANi二次电池.研究发现:具有苯环结构的石墨和酚醛炭,能够大幅度提高材料的导电性:减小电池内阻;而活性炭和酚醛炭具有大的比表面积和羟基官能团,有利于PANi在其表面的物理和化学吸附,提高PANi分散性,电池容量大幅度提高.尤其是酚醛炭...