Friction and wear behavior of Ni-P coated Si3N4 reinforced Al6061 composites

Al6061 matrix composite reinforced with nickel coated silicon nitride particles were manufactured by liquid metallurgy route. Microstructure and tribological properties of both matrix alloy and developed composites have been evaluated. Dry sliding friction and wear tests were carried out using pin on disk type machine over a load range of 20-100 N and sliding velocities of range 0.31-1.57 m/s. Results revealed that, nickel coated silicon nitride particles are uniformly distributed through out the matrix alloy. Al6061-Ni-P-Si₃N₄ composite exhibited lower coefficient of friction and wear rate compared to matrix alloy. The coefficient of friction of both matrix alloy and developed composite decreased with increase in load up to 80 N. Beyond this, with further increase in the load, the coefficient of friction increased slightly. However, with increase in sliding velocity coefficient of friction of both matrix alloy and developed composite increases continuously. Wear rates of both matrix alloy and developed composites increased with increase in both load and sliding velocity. Worn surfaces and wear debris was examined using scanning electron microscopy (SEM) for possible wear mechanisms. Energy dispersive spectroscope (EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscope (XPS) techniques were used to identify the oxides formed on the worn surfaces and wear debris.     

Friction and wear behaviour of WC-Co-Cr3C2-VC cemented carbides obtained from nanocrystalline mixtures

The effect of adding Cr₃C_2, VC or a mixture of both as a grain growth inhibitors to cemented carbides obtained from WC-12 wt.%Co nanocrystalline mixtures on the behaviour of friction and dry sliding wear have been studied. All the wear tests were performed on a tribometer with ball on disc configuration, using a WC-6 wt.%Co ball as a counterpart with normal contact loads of 40 and 60 N, sliding distance of 2000 m and a sliding speed of 0.1 m/s. A significant reduction in the wear rates was observed by the effect of the aforementioned additives, in particular for the VC, which showed an increase in the wear resistance of the order of 90%. The analysis of wear and surface damage were correlated to the observed behaviour.     

Characterization and mechanical/tribological properties of nano Au-TiO2 composite thin films prepared by a sol-gel process

Nano Au-TiO₂ composite thin films on Si(1 0 0) and glass substrates were successfully prepared with a facile sol-gel process followed by sintering. The morphology and mircostructure of the films were investigated via X-ray diffractometry (XRD), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The Au particles, of diameter 14-22 nm depending on the sintering temperatures used, were found to be well dispersed in the TiO₂ matrix, with a small amount of the particles escaped from the film. The surfaces of the films were uniform, compact and crack-free. Hardness and elastic modulus of the films were measured by using the nanoindentation technique. Friction and wear properties were investigated by using a one-way reciprocating tribometer. It was found that the highest hardness and elastic modulus values were obtained for the films prepared with 500 °C sintering temperature. The films displayed superior antiwear and friction reduction performances in sliding against an AISI 52100 steel ball. With 5.0 mol% Au, the friction coefficient was only 0.09-0.10 and the wear life was more than 2000 sliding cycles. The friction coefficient and wear life decreased with increasing sliding speed and load. The failure mechanism of the Au-TiO₂ films was identified to be light scuffing and abrasion. Those films can be potentially applied as ultra-thin lubricating coatings.     

Tribological properties of spark-plasma-sintered ZrO2(Y2O3)-CaF2-Ag composites at elevated temperatures

Spark-plasma sintering is employed to synthesize self-lubricating ZrO₂(Y₂O₃) matrix composites with different additives of CaF₂ and Ag as solid lubricants by tailoring the composition and by adjusting the sintering temperature. The friction and wear behavior of ZrO₂(Y₂O₃) matrix composites have been investigated in dry sliding against an alumina ball from room temperature to 800 °C. The effective self-lubrication at different temperatures depends mainly on the content of various solid lubricants in the composites. The addition of 35 wt.% Ag and 30 wt.% CaF₂ in the ZrO₂(Y₂O₃) matrix can promote the formation of a well-covered lubricating film, and effectively reduce the friction and wear over the entire temperature range studied. The friction coefficients at low temperatures were at a minimum value for the composite containing 35 wt.% of silver. At this silver concentration, low and intermediate temperature lubricating properties are greatly improved without affecting high-temperature lubrication by the calcium fluoride in ZrO₂(Y₂O₃) matrix composites. The worn surfaces and transfer films formed during wear process have been characterized to identify the synergistic lubrication behavior of CaF₂ and Ag lubricants at different temperatures.     

Tribological characteristics of low-pressure plasma-sprayed A12O3 coating from room temperature to 800 °C

The tribological characteristics of low-pressure plasma-sprayed (LPPS) Al₂O₃ coating sliding against alumina ball have been investigated from room temperature to 800 °C. These friction and wear data have been compared quantitatively with those of bulk sintered alumina to obtain a better understanding of wear mechanisms at elevated temperatures. The friction and wear of Al₂O₃ coating show a strong dependence on temperature, changing from a mild to a severe wear regime with the increase of temperature. The coefficient of friction at room temperature is approximately 0.17 to 0.42, depending on applied load. The tribochemical reaction between the coating surface and water vapor in the environment and the presence of the hydroxide film on the Al₂O₃ coating reduce the friction and wear at room temperature as contrasted to those of bulk sintered alumina. At intermediate temperatures, from 400 to 600 °C, the friction and wear behavior of Al₂O₃ coating depends on the inter-granular fracture and pull-out of Al₂O₃ grains. At above 700 °C, formation and deformation of fine grain layer, and abrasive wear in the form of removal of fine alumina grains further facilitate the friction and wear process of Al₂O₃ coating.     

Friction, wear and N2-lubrication of carbon nitride coatings: a review

Recent results of tribological properties of carbon nitride (CN_x) coatings are reviewed. CN_x coatings of 100 nm thickness were formed on Si-wafer and Si₃N₄ disks by the ion beam mixing method. Friction and wear tests were carried out against Si₃N₄ balls in the environments of vacuum, Ar, N₂, CO₂, O₂ or air by a ball-on-disk tribo-tester in the load range of 80-750 mN and in the velocity range of 4-400 mm/s.It was found that friction coefficient μ is high (μ=0.2-0.4) in air and O₂, and low (μ=0.01-0.1) in N₂, CO₂ and vacuum. The lowest friction coefficient (μ<0.01) was obtained in N₂. It was also found that N₂ gas blown to the sliding surfaces in air effectively reduced the friction coefficient down to μ≈0.017. Wear rate of CN_x coatings varied in the range 10⁻⁹-10⁻⁵ mm³/N m depending on the environment.The wear mechanisms of CN_x in the nanometer scale were studied by abrasive sliding of an AFM diamond pin in air. It was confirmed that the major wear mechanism of CN_x in abrasive friction was low-cycle fatigue which generated thin flaky wear particles of nanometre size.     

Ni3Al matrix high temperature self-lubricating composites

A Ni₃Al matrix high temperature self-lubricating composite Ni₃Al-BaF₂-CaF₂-Ag-Cr was fabricated by the powder metallurgy technique, and tribological behavior at a wide temperature range from room temperature to 800 °C was investigated. The results indicated that the composite exhibited low friction coefficients (0.30-0.36) and wear rates (0.65-2.45×10⁻⁴ mm³ N⁻¹ m⁻¹). It was found that the low friction coefficient was attributed to the synergistic effects of Ag, fluorides and chromates formed in the tribo-chemical reaction at high temperatures. The low wear rate of the composite was due to the high strength and the excellent lubricating properties.     

Tribological properties of Ni3Al-Cr7C3 composite coating under water lubrication

The tribological properties of Ni₃Al-Cr₇C₃ composite coating under water lubrication were examined by using a ball-on-disc reciprocating tribotester. The effects of load and sliding speed on wear rate of the coating were investigated. The worn surface of the coating was analyzed using electron probe microscopy analysis (EPMA) and X-ray photoelectron spectroscopy (XPS). The results show the friction coefficient of the coating is decreased under water lubrication. The wear rate of the coating linearly increases with the load. At high sliding speed, the wear rate of the coating is dramatically increased and a large amount of the counterpart material is transferred to the coating worn surface. The low friction of the coating under water lubrication is due to the oxidizing of the worn surface in the wear. The wear mechanism of the coating is plastic deformation at low normal load and sliding speed. However, the wear mechanism transforms to microfracture and microploughing at high load with low sliding speed, and oxidation wear at high sliding speed. It is concluded that the contribution of the sliding speed to an increase in the coating wear is larger than that of the normal load.     

The friction behavior of Ni-, SiO2- and mica sodium silicate-based solid lubrication composites

The friction behavior of Ni⁻-, SiO⁻₂- and mica sodium silicate-based lubricant composites, which included BN, WS₂ and graphite as lubricants, were examined. A ring-on-disk apparatus, in which a solid lubricant composite disk was held against a rotating stainless ring, was used as the test configuration. The tests were run with a load from 62 to 250 N in temperatures from 20 to 800°C in the laboratory environment. The wear surface was characterized by scanning electron microscope and X-ray photo spectroscopy. The major findings were that both mica sodium silicate- and SiO⁻₂-based composites failed at above 500°C due to severe wear and surface damage; in contrast, Ni⁻-based composite showed a stable friction coefficient and low wear from 20 to 800°C.     

Influence of Cr content on tribological properties of Ni3Al matrix high temperature self-lubricating composites

High temperature self-lubricating composites Ni₃Al-BaF₂-CaF₂-Ag-Cr were fabricated by powder metallurgy technique. In this paper the effect of Cr content on tribological properties at a wide temperature range starting from room temperature to 1000 °C was investigated. It was found that Ni₃Al matrix composite with 20 wt% Cr exhibited low friction coefficient of 0.24-0.37 and a wear rate of 0.52-2.32×10⁻⁴ mm³ N⁻¹ m⁻¹. Especially at 800 °C it showed the lowest friction coefficient of 0.24 and a favorable wear rate of 0.71×10⁻⁴ mm³ N⁻¹ m⁻¹. This implied that 20 wt% Cr was the optimal Cr content and its excellent tribological performance could be attributed to the balance between strength and lubricity.     

Cr2N/CrN multilayer coatings for wood machining tools

The present paper describes results from a recent research project aimed at forming a wear resistant coating based on chromium on tools to wood machining. Cr₂N/CrN multilayer coatings deposited on HS6-5-2 steel substrates using cathodic arc evaporation were tested. These coatings were formed from 7 bilayers being ca. 340 nm thick and equally thick Cr₂N and CrN layers. For comparison, Cr₂N and CrN monolayer coatings were also prepared. Hardness measurements, indentation and scratch tests, friction and wear were performed to characterize the mechanical properties. The wear tracks and Rockwell indentations enable to assess wear mechanisms of the coatings. The results of the Cr₂N/CrN coatings investigated show high hardness: ca. about 22 GPa and a critical force being higher than 95 N and a low wear rate.The industrial tests of planer knives with Cr₂N/CrN multilayer coatings were carried out on a down-spindle milling machine to determine the durability of tools with wear resistant coatings for woodworking. These tools show increase of “life time” two times. Another positive feature of the use of such tools is the increase of the quality of wood surface machined when compared with uncoated tools.     

Tribological performance of MoS2---B2O3 compacts

A recent investigation suggests that selected oxides perform well as additives in molybdenum disulphide (MoS₂) because of their ability to soften at asperity contacts with the result that the solid lubricant can attain and retain a preferred tribological orientation.This research determined the effectiveness of boric oxide (B₂O₃), when used as an additive in MoS₂, for substrate temperatures ranging from 21°C to 316°C. This range was used to allow the asperity contact temperature to vary below and above the softening point of B₂O₃. It was found that a moderate friction coefficient and high wear, which is attributed to the additive acting abrasively, occurred when the asperity contact temperature was well below the softening point of the oxide. When the asperity contact temperature neared the softening point of the oxide, the friction coefficient increased dramatically and wear volume was reduced. It is postulated that B₂O₃ acted adhesively at the interface resulting in a higher coefficient of friction, and wear decreased due to an attainment of a preferred orientation by the MoS₂. For asperity contact temperatures significantly above the softening point of B₂O₃, the friction coefficient returned to about the same value as for temperatures below the softening point. It is speculated that wear continued to increase moderately because of localized melting of the B₂O₃, permitting the MoS₂ to be removed from the interface. These observations support a hypothesis that an additive, such as boric oxide, can soften as the asperity contact temperature approaches the softening point temperature of the additive so that the overall tribological conditions may be improved resulting in reduced interfacial wear. Significant changes in temperature, load or sliding velocity would, of course, dramatically alter the wear characteristics observed at the interface.     

Effect of particle size on tribological behavior of Ni3Al matrix high temperature self-lubricating composites

The Ni₃Al matrix high temperature self-lubricating composites with different particle size were fabricated by the powder metallurgy technique. The effect of particle size on the mechanical and tribological properties of the composites was investigated in this paper. The results showed that the coarse particle composite exhibited the lowest friction coefficient and wear rate compared to the fine particle ones at a wide temperature range from room temperature to 1000 °C. The reason for the low wear rate was that the coarse bulk phase could provide better deformation resistance and higher load bearing capacity than the fine microstructure.     

Friction and wear behaviour of Thordon XL and LgSn80 in sliding against plasma-sprayed Cr2O3 coatings

This paper studies the friction and wear behaviour of two important bearing materials, Thordon XL and LgSn80, in dry and lubricated sliding vs. plasma-sprayed Cr₂O₃ coatings. As a reference, AISI 1043 steel is also studied under the same conditions. SEM, EDS and surface topography were employed to study the wear mechanisms. The results indicate that the Thordon XL/Cr₂O₃ coating pair gives the lowest dry friction coefficient (0.16) under a normal load of 45.3 N (pressure 0.453 MPa) at a velocity of 1 m/s. The dry friction coefficient of Thordon XL/Cr₂O₃ coating increases to 0.38 under a normal load of 88.5 N (pressure 0.885 MPa). The dry friction coefficients of the LgSn80/Cr₂O₃ coating are in the range of 0.31–0.46. Secondly, both dry wear rate under low normal load (45.3 N) and lubricated wear rate under a load of 680 N for Thordon XL are lower than those of LgSn80 in sliding against plasma-sprayed Cr₂O₃ coatings at a speed of 1 m/s. However, under a normal load of 88.5 N the dry wear rate of Thordon XL is much higher than that of LgSn80. Thirdly, a high viscosity lubricant (SAE 140) leads to lower wear for Thordon XL and LgSn80 than a low viscosity lubricant (SAE 30). Finally, the dominating wear mechanism for Thordon XL is shear fracture when against the plasma-sprayed Cr₂O₃ ceramic coating. For LgSn80 against plasma-sprayed Cr₂O₃ ceramic coating, abrasive wear is the governing failure mechanism.     

Microstructure and tribological characteristics of ZrO2–Y2O3 ceramic coatings deposited by laser-assisted plasma hybrid spraying

ZrO₂–Y₂O₃ ceramic coatings were deposited on AISI 304 stainless steel by both a low-pressure plasma spraying (LPPS) and a laser-assisted plasma hybrid spraying (LPHS). Microstructure and tribological characteristics of ZrO₂–Y₂O₃ coatings were studied using an optical microscope, a scanning electron microscope, and an SRV high-temperature friction and wear tester. The LPHS coatings exhibit distinctly reduced porosity, uniform microstructure, high hardness and highly adhesive bonding, although more microcracks and even vertical macrocracks seem to be caused in the LPHS coatings. The ZrO₂ lamellae in the LPHS coatings before and after 800°C wear test consist mainly of the metastable tetragonal (t′) phase of ZrO₂ together with small amount of c phase. The t′ phase is very stable when it is exposed to the wear test at elevated temperatures up to 800°C for 1 h. The friction and wear of the LPHS coatings shows a strong dependence on temperature, changing from a low to a high wear regime with the increase of temperature. At low temperatures, friction and wear of the LPHS coatings is improved by laser irradiation because of the reduced connected pores and high hardness in contrary to the LPPS coating. However, at elevated temperatures, the friction and wear of the LPHS coatings is not reduced by laser irradiation. At room temperature, mild scratching and plastic deformation of the LPHS coatings are the main failure mechanism. However, surface fatigue, microcrack propagation, and localized spallation featured by intersplat fracture, crumbling and pulling-out of ZrO₂ splats become more dominated at elevated temperatures.     

A study on friction and wear characteristics of nanometer Al2O3 /PEEK composites under the dry sliding condition

The friction and wear properties of the polyetheretherketone (PEEK) based composites filled with 5 mass% nanometer or micron Al₂O₃ with or without 10 mass% polytetrafluroethylene (PTFE) against the medium carbon steel (AISI 1045 steel) ring under the dry sliding condition at Amsler wear tester were examined. A constant sliding velocity of 0.42 m s⁻¹ and a load of 196 N were used in all experiments. The average diameter 250 μm PEEK powders, the 15 or 90 nm Al₂O₃ nano-particles or 500 nm Al₂O₃ particles and/or the PTFE fine powders of diameter 50 μm were mechanically mixed in alcohol, and then the block composite specimens were prepared by the heat compression moulding. The homogeneously dispersion of the Al₂O₃ nano-particles in PEEK matrix of the prepared composites was analyzed by the atomic force microscopy (AFM). The wear testing results showed that nanometer and micron Al₂O₃ reduced the wear coefficient of PEEK composites without PTFE effectively, but not reduced the friction coefficient. The filling of 10 mass% PTFE into pure PEEK resulted in a decrease of the friction coefficient and the wear coefficient of the filled composite simultaneously. However, when 10 mass% PTFE was filled into Al₂O₃/ PEEK composites, the friction coefficient was decreased and the wear coefficient increased. The worn scars on the tested composite specimen surfaces and steel ring surfaces were observed by scanning electron microscopy (SEM). A thin, uniform, and tenacious transferred film on the surface of the steel rings against the PEEK composites filled with 5 mass% 15 nm Al₂O₃ particles but without PTFE was formed. The components of the transferred films were detected by energy dispersive spectrometry (EDS). The results indicated that the nanometer Al₂O₃ as the filler, together with PEEK matrix, transferred to the counterpart ring surface during the sliding friction and wear. Therefore, the ability of Al₂O₃ to improve the wear resistant behaviors is closely related to the ability to improve the characteristics of the transfer film.     

Tribological properties of ZrO2 (Y2O3)-Mo-BaF2/CaF2 composites at high temperatures

ZrO₂ (Y₂O₃) with different contents of BaF₂/CaF₂ and Mo were fabricated by hot pressed sintering, and the tribological behavior of the composites against SiC ceramic was investigated from room temperature to 1000 °C. It was found that the ZrO₂ (Y₂O₃)-5BaF₂/CaF₂-10Mo composite possessed excellent self-lubricating and anti-wear properties. The low friction and wear were attributed to enhanced matrix and BaMoO₄ formed on the worn surfaces.     

Sliding friction and wear performance of Ti6Al4V in the presence of surface-capped copper nanoclusters lubricant

The friction and wear properties of Ti₆Al₄V sliding against AISI52100 steel ball under different lubricative media of surface-capped copper nanoclusters lubricant—Cu nanoparticles capped with O,O′-di-n-octyldithiophosphate (Cu-DTP), rapeseed oil and rapeseed oil containing 1 wt% Cu-DTP was evaluated using an Optimol SRV oscillating friction and wear tester. The wear mechanism was examined using scanning electron microscopy (SEM) and X-ray photoelectron spectrosmeter (XPS). Results indicate that Cu-DTP can act as the best lubricant for Ti₆Al₄V as compared with rapeseed oil and rapeseed oil containing 1 wt% Cu-DTP. The applied load and sliding frequency obviously affected the friction and wear behavior of Ti₆Al₄V under Cu-DTP lubricating. The frictional experiment of the Ti₆Al₄V sliding against AISI52100 cannot continue under the lubricating condition of rapeseed oil or rapeseed oil containing 1 wt% Cu-DTP when the applied load are over 100 N. Surprisingly, the frictional experiment of Ti₆Al₄V sliding against AISI52100 steel can continue at the applied load of 450 N under Cu-DTP lubricating. The tribochemical reaction film containing S and P is responsible for the good wear resistance and friction reduction of Ti₆Al₄V under Cu-DTP at the low applied load. However, a conjunct effect of Cu nanoparticle deposited film and tribochemical reaction film containing S and P contributes to the good tribological properties of Ti₆Al₄V under Cu-DTP at the high-applied load.     

Friction and wear of carbon steel near T1-transition under dry sliding

The wear phenomenon of metals under dry sliding is, generally, divided into two modes of severe and mild wear. A discontinuous transition between the wear modes often takes place in a certain load range. The T₁-transition is usually observed at lower levels of load or sliding velocity. There is a great difference in wear rate between severe and mild wear. This indicates that the occurrence of severe wear should be avoided, especially in the field of machine design to prevent energy loss, occurrence of noise and vibration, and life reduction of machines and their components. Therefore, it is important for machine designers to know the relationship between friction and wear and the difference in properties of the wear surfaces in the two wear modes. In this study, wear tests of 0.35% C steel in contact with itself under constant load were conducted in moist air at various contact loads under dry sliding. The friction and wear were measured continuously throughout each test. After the tests, the relationship between friction and wear and the difference in properties of the wear surfaces were investigated in each wear mode. From the results, the upper and lower critical loads (P_acr and P_Acr) appeared between severe and mild wear. The phenomenon of zero wear has been newly found in the early period at very low loads. The zero wear continued for a long sliding distance and then changes to mild wear. The critical load between zero wear and mild wear is defined as P_zerowear. The load was changed once in a step-wise manner from low to high levels in process of test. Since the rubbing history under mild wear condition at the low load in the first stage affected the properties of wear surface, the wear mode at the high load in the second stage changed from ‘mild wear’ to ‘quasi-mild wear’ having a low rate. From the relationship between sliding distance necessary for the appearance of quasi-mild wear and contact load in the first stage, the boundary curve between severe wear and quasi-mild wear in the second stage is hyperbolic. This curve gradually approaches P_zerowear with decreasing contact load. Thus, P_zerowear is one of the important critical loads for elucidating the test results under varying load.     

Dry wear and friction properties of an A356/SiC foam interpenetrating phase composite

The dry sliding wear and friction behaviors of A356 aluminum alloy and a hybrid composite of A356 aluminum alloy and silicon carbide foam in the form of an interpenetrating phase composite were evaluated using a ball-on-disk apparatus at ambient conditions. The stationary 6.35 mm alumina ball produced a wear track (scar) diameter of 7 mm on the rotating specimen surface. Three different loads; 5 N, 10 N and 20 N were applied at a constant sliding speed of 33 mm/s for both materials. Wear tracks were characterized with a scanning electron microscope and measured with an optical surface profilometer. In general, this novel A356/SiC foam composite reduced the friction coefficient and wear rate from that of the base alloy for all loading conditions. In addition, as the load increased, the friction coefficient and wear rate decreased for both materials. The results indicate the composite could be used in light-weight applications where moderate strength and wear properties are needed.