等离子堆焊铌元素增强镍基合金堆焊层的组织与性能

利用等离子堆焊技术在304L钢板表面制备了添加Nb粉的Ni40合金堆焊层,并对堆焊层的微观组织、显微硬度和耐磨性进行研究。结果表明,堆焊层组织主要由γ-Ni树枝晶、枝晶间的共晶组织、弥散分布的Nb C颗粒、硼化物和碳化物等相组成。由于增强相Nb C颗粒在堆焊层中均匀分布,使Nb/Ni40复合合金堆焊层与纯Ni40合金堆焊层相比,显微硬度提高约40%(平均达到448 HV0.3),耐磨性也提高约37.5%。     

Mo元素含量对FeAlCuCrNiMox系高熵合金组织结构及性能的影响

为了研究Mo元素对FeAlCuCrNiMo_x系高熵合金的组织结构及性能的影响,将FeAlCuCrNiMo_x系高熵合金粉末制备成药芯焊丝,并用气体保护堆焊到45钢表面制备出FeAlCuCrNiMo_x系高熵合金,而后对堆焊层进行硬度、显微组织、物相组成及耐蚀性能分析. 结果表明,FeCuCrAlNiMo_x系堆焊高熵合金呈现单一的AlFe固溶体,晶格结构为体心立方. 当x = 0.8时,合金堆焊层的晶粒尺寸最为细小,晶界强化明显,硬度最高,平均硬度达到47.8 HRC,磨损量最小,为0.08 g. 加入一定量的Mo元素之后腐蚀电位降低,即耐腐蚀性能下降.     

Ti含量对氩弧熔覆CoCrFeNiCuTix高熵合金涂层组织及性能的影响

采用氩弧熔覆技术在Q235钢基体表面制备了CoCrFeNiCuTi_x(x表示摩尔比值,x=0、0.3、0.5、0.8和1)高熵合金涂层,研究了Ti含量对CoCrFeNiCuTi_x高熵合金微观结构和力学性能的影响。结果表明,不同Ti含量的CoCrFeNiCuTi_x高熵合金均为FCC单相固溶体。CoCrFeNiCu合金的微观组织为柱状晶结构。随着Ti的加入,微观组织中开始出现析出相,且Ti含量越高,析出相越多。同时Ti的加入明显提高了合金的显微硬度,当Ti的摩尔比为1时,涂层的截面显微硬度值达到最高值439.54 HV0.1。Ti对CoCrFeNiCuTi_x高熵合金的耐磨性具有显著影响,CoCrFeNiCuTi合金表现出最好的耐磨性。随着Ti含量的升高,合金的磨损机理由黏着磨损转化成黏着磨损与氧化磨损并存。     

Nb含量对FeAlCuCrNiNbx系高熵合金组织及性能的影响

为了研究Nb对FeAlCuCrNiNb_x系高熵合金的组织及性能的影响,采用药芯焊丝堆焊方法制备FeAlCuCrNiNb_x系高熵合金,对焊缝进行了硬度、显微组织和物相组成的分析。结果表明,对于FeAlCuCrNiNb_x系高熵合金而言,加入Nb对合金硬度的提高有一定的积极作用,当Nb摩尔比为0.8时,合金堆焊层的硬度最高,平均硬度达到49.53HRC,磨损量最小为0.28g。随着Nb的加入,该系高熵合金的晶粒对尺寸先减小后增大,当Nb摩尔比为0.6时,FeAlCuCrNiNb_x系高熵合金晶粒尺寸最小,析出物最少。Nb摩尔比继续增加,合金组织出现大量高硬度析出物。     

FeCrMnAlCux高熵合金的组织与性能

采用真空电弧熔炼炉制备FeCrMnAlCu_x(x=0, 0.5, 1.0, 1.5, 2.0)高熵合金,采用XRD、SEM、TEM、显微硬度仪、电子万能试验机和摩擦磨损实验机检测分析了Cu含量的变化对合金相结构、显微组织、压缩性能、硬度、耐磨性的影响。结果表明：FeCrMnAlCu_x高熵合金为典型的树枝晶组织,由BCC结构的枝晶组织、FCC结构的枝晶间组织及枝晶内析出的具有BCC结构的纳米级析出物构成。随着Cu含量的增加,合金微观组织中的枝晶组织含量减小,枝晶间组织含量增大;BCC结构的枝晶组织中弥散析出的第二相颗粒对合金的强度和硬度有着重要的影响,抗压强度和屈服强度在x=1.0时达到最大(分别为1230.2 MPa和960.5 MPa),合金的压缩变形率在x=2.0时达到最大值20.68%;随着Cu含量的增加,合金的硬度先增加后减少,合金硬度在x=0.5时达到最大值421.4HV,此时合金的摩擦性能最好,其磨损率为2.25×10^-5 mm³/(N·mm)。     

等离子熔覆CrMnFeCoNiMox高熵合金涂层的组织、硬度和腐蚀性能

采用等离子熔覆技术在20钢表面制备了不同成分的CrMnFeCoNiMo_x(x=0、1、1.5)系高熵合金涂层。通过光学显微镜(OM)、扫描电镜(SEM)、能谱仪(EDS)及X射线衍射仪(XRD)等分析了涂层的微观结构；利用显微硬度计和电化学工作站分析了涂层的硬度和耐蚀性。结果表明：在不含Mo的高熵合金(HEA)涂层中存在大量的枝晶和胞状晶，添加Mo元素后主要为等轴晶。3种涂层的基体组织主要为体心立方(BCC)结构，Mo元素的添加使涂层中形成了一定量的第二相。CrMnFeCoNiMo_1.5涂层的第二相含量最多，硬度最大(约720 HV0.3),约为基材的4倍。Mo元素添加后，涂层的耐蚀性显著提升，CrMnFeCoNiMo₁涂层的耐蚀性能最好，腐蚀速率为0.141 mm/year,约为基材的1/20。     

铌元素含量对等离子堆焊镍基合金的影响

采用添加了5种不同比例Nb粉的镍基复合合金粉末,通过等离子堆焊技术在304L上进行堆焊,并对堆焊层的显微组织、元素分布和显微硬度进行对比分析。结果表明,堆焊层组织主要由γ-Ni树枝晶、枝晶间的共晶组织、Cr的硼化物、弥散分布的NbC颗粒等相组成。当Nb粉含量为5wt%时硬度值最高,相比于纯镍基合金堆焊层显微硬度提高了约40%。     

冷喷涂辅助感应重熔合成AlCoxCrFeNiCu高熵合金涂层的显微组织和性能

通过冷喷涂辅助感应重熔技术在45钢基体成功制备AlCo_xCrFeNiCu (x=0、0.5、1.0、1.5、2.0，摩尔分数)高熵合金涂层。研究了Co元素含量对冷喷涂辅助合成高熵合金涂层物相、微观组织的影响。结果表明：通过低压冷喷涂辅助感应重熔技术合成的AlCo_xCrFeNiCu高熵合金涂层由fcc+bcc双相混合结构组成，涂层组织为等轴树枝晶+晶间组织，其中枝晶为bcc结构，晶间组织为fcc结构。Co含量的变化会引起AlCo_xCrFeNiCu高熵合金涂层的晶格畸变状态发生变化，当x=1.0时，AlCo₁CrFeNiCu高熵合金涂层的晶格应变最大。Co元素含量增加会促进AlCo_xCrFeNiCu高熵合金涂层中的枝晶数目增加，同时涂层中的树枝晶尺寸也随着Co元素含量增加而增大。涂层中的树枝晶富集Fe、Cr、Co、Ni元素，枝晶间富集Cu元素，Al均匀地分布在整个涂层中。随着Co含量增加，AlCo_xCrFeNiCu高熵合金涂层的硬度先增加后减小；当x=1.0时...     

Nb元素对高熵合金涂层组织与力学性能的影响

利用激光熔覆技术在Q235基体表面制备CoCrFeNiTi_0.8Nb_y(y=0.25,0.5,0.75,1.0)涂层.采用光学显微镜、X射线衍射仪、扫描电子显微镜、能谱分析仪等方法分析涂层的相结构和微观组织等;用显微维氏硬度计、摩擦磨损试验机测试涂层的硬度与耐磨性能.结果表明,组织中呈现典型的树枝晶结构,加入Nb元素,涂层微观组织的尺寸减小,增加Nb元素含量时,高熵合金涂层的晶体结构由体心立方相(body-centered cubi,BCC)、少量的面心立方相(face-centered cubic,FCC)和Fe₂(Ti,Nb)型的Laves相组成;在细晶强化、固溶强化和第二相强化的共同作用下提高了涂层的显微硬度;中间相的存在一定程度上可以阻碍犁削切削过程的进行,进而提高了涂层的耐磨性能;CoCrFeNiTi_0.8Nb_0.75涂层的硬度和耐磨性最好,硬度为710 HV,约为基体的4倍,涂层的磨损量最小,磨痕较为平整.     

Cr_xCuFe_2Mo_(0.5)Nb_(0.5)Ni_2高熵合金的微观组织与力学性能

采用电弧熔炼工艺制备了CrxCuFe2Mo0.5Nb0.5Ni2(x=0,0.5,1.0,2.0,摩尔比)高熵合金,采用X射线衍射分析(XRD)、扫描电镜(SEM)和显微硬度计对合金的物相结构、微观组织形貌、元素分布和硬度进行了分析。结果表明,合金物相主要由面心立方固溶体相(FCC)、体心立方固溶体相(BCC)和密排六方固溶体相(HCP)组成。Cr含量的增加,有利于BCC相的形成。合金组织主要呈树枝晶和枝晶间结构组成。合金中Nb、Mo和Cu元素分别偏聚于枝晶和枝晶间区域,Fe、Cr和Ni元素的分布相对均匀。合金硬度随Cr含量的增加而逐渐增加,但增幅较小。     

Effect of Ti Addition on the Microstructure and Property of FeAlCuCrNiMo_(0.6) High-Entropy Alloy

FeAlCuCrNiMo_(0.6)Tix(x=0.2,0.6,0.8) high-entropy alloys were fabricated with flux-cored wire and surfaced on low-carbon steel by gas metal arc welding.The effect of Ti addition on the microstructures and properties of FeAlCuCrNiMo_(0.6)Ti_x HEAs surfacing layer was systematically studied.The results show that FeAlCuCrNiMo_(0.6)Ti_x HEAs surfacing layer exhibits a majority of BCC solid solution based on Fe-Cr phase and a small amount of MC phase.Microhardness and wear tests results show that the addition of Ti can significantly improve the microhardness and wear resistance of the surfacing layer.The microhardness of surfacing layer can reach up to 642 HV_(0.5),which is about 2.8 times that of the substrate.Meanwhile,the wear mass loss is minimum.Electrochemical corrosion test results show that the addition of Ti can improve the corrosion resistance of surfacing layer,which is better than 304 stainless steel substrate.With the increase in Ti,the corrosion resistance increases first and then decreases.When the Ti content is 0.6,the self-corrosion current density of polarization curve is the smallest,the capacitive impedance radius of electrochemical impedance spectroscopy is the largest,and the corrosion resistance effect is the best.     

钨表面WTaTiVCr高熵合金层的组织与性能

使用双辉等离子体渗金属技术,通过调整渗金属温度在钨表面制备了WTaTiVCr高熵合金层,使用扫描电镜(SEM)、X射线能谱分析(EDS)、X射线衍射(XRD)、显微硬度计、往复摩擦试验和电化学腐蚀试验等对其组织成分、力学性能、耐磨性和耐蚀性等进行了分析。结果表明:当渗金属温度为1150 ℃、源极与阴极电压差为400 V时,可以得到含有扩散层、沉积层的复合渗金属层,其中扩散层区域各元素的原子分数为W_0.38Ta_0.14Ti_0.2V_0.2Cr_0.08,相结构为单相BCC结构,符合高熵合金层的相结构与元素组成规律。同时其表面硬度由于受到固溶强化、晶格畸变等强化机理,与纯钨相比有很大的提升,达到1300 HV0.2以上。另外,该渗金属层的平均摩擦因数为0.447,磨损率为3.43×10^-8 mm³/(N·mm),腐蚀速率为3.87 mg/(m²·h),具备一定的耐磨性和耐蚀性。综合以上结果,通过双辉技术在钨表面制备的WTaTiVCr高熵合金层可以有效提高W基体的力学性能和耐腐蚀性能。     

激光熔覆AlxNbMn2FeMoTi0.5高熵合金涂层的组织与性能

使用激光熔覆技术在Q235钢基体上制备Al_xNbMn₂FeMoTi_0.5高熵合金涂层,期望借此提高干切削技术适用刀具表层的硬度和耐磨性。经过初步筛选之后,主要研究了Al_xNbMn₂FeMoTi_0.5(x=1、1.5、2)高熵合金涂层体系,并采用XRD和3D激光扫描成像等手段分析了不同Al含量的Al_xNbMn₂FeMoTi_0.5合金涂层的晶相结构、显微组织和具体元素分布。结果显示,对于Al_xNbMn₂FeMoTi_0.5高熵合金涂层,随着Al含量的增加,涂层的相结构由单一的BCC相逐渐转变为双相BCC结构,晶粒逐渐细化。当x=2时,Al_xNbMn₂FeMoTi_0.5高熵合金涂层硬度最高,平均为1089.6 HV0.3,大约为基材的5倍,且其具有最优的耐磨损性能。x=1.5时,Al_xNbMn₂FeMoTi_0.5高熵合金涂层的自腐蚀电位最高,自腐蚀电流密度最小,耐腐蚀性最好。     

304LN不锈钢表面激光熔覆钴基合金组织和性能

为了提高304LN不锈钢的耐磨性,延长控制棒导向筒组件使用寿命,采用激光熔覆技术在304LN不锈钢表面制备了Stellite 6钴基熔覆层.利用光学显微镜(OM)、能谱仪(EDS)、显微硬度计、摩擦磨损试验机、腐蚀试验装置等多种试验测试设备,分析了熔覆层组织形貌、成分、显微硬度、摩擦磨损性能及腐蚀行为,确定了多道多层钴基熔覆层的工艺参数.结果表明,熔覆层与基体之间形成了冶金结合,显微组织主要由平面晶区、胞状和柱状晶区、树枝晶区和等轴晶区组成.熔覆层硬度为500 ~ 550 HV,摩擦磨损系数为0.30 ~ 0.35,熔覆层均匀腐蚀速率和缝隙腐蚀速率分别为0.153 和0.143 mg/(dm2·d). 激光熔覆钴基合金可以有效提高304LN不锈钢表面的硬度、耐磨性能和耐腐蚀性能.     

AlCoCrFeMnZr近共晶高熵合金的组织形貌及耐磨性

采用真空熔炼法制备出了AlCoCrFeMnZr近共晶高熵合金,通过XRD、SEM、显微硬度计和摩擦磨损试验机测试了AlCoCrFeMnZr合金的晶体结构、组织形貌、硬度以及耐磨性能。结果表明,AlCoCrFeMnZr合金的物相结构为BCC和HCP双相结构,组织由初生相和细密的片状共晶组织组成。初生相由富Cr、Fe、Zr的HCP相组成,以树枝晶方式生长,片状共晶组织中枝晶区域(α相)主要分布Co、Cr、Fe,晶间(β相)主要分布Al和Zr,符合高熵合金组织及元素分布规律。磨损方式由粘着磨损和磨粒磨损转变为氧化磨损,摩擦因数出现先增加后减少的趋势,平均摩擦因数为0.5432,显微硬度为768.8 HV0.5,具有优良的硬度和耐磨性。     

感应重熔和激光重熔合成FeCrMnAlCu高熵合金涂层组织与性能

采用冷喷涂辅助感应重熔和冷喷涂辅助激光重熔2种方法分别在45#钢表面制备FeCrMnAlCu高熵合金涂层。对高熵合金涂层的相组成、显微组织、硬度、耐磨性能进行表征与检测,研究2种工艺对涂层耐磨性能的影响。结果表明：2种工艺合成的FeCrMnAlCu高熵合金涂层均由体心立方（bcc）和面心立方（fcc）相组成,涂层组织致密,元素分布均匀。涂层微观组织均为树枝晶+枝晶间组织,枝晶区主要由Mn、Cr和Fe元素构成,枝晶间主要为Cu,Al元素均匀地分布在枝晶和枝晶间。冷喷涂辅助感应重熔合成的FeCrMnAlCu高熵合金涂层中bcc晶格应变大于激光重熔合成的高熵合金涂层的晶格应变。冷喷涂辅助感应重熔合成FeCrMnAlCu高熵合金涂层的显微硬度是冷喷涂辅助激光重熔合成涂层硬度的1.2倍,是45#钢基体硬度的3.5倍。FeCrMnAlCu高熵合金涂层在摩擦过程中主要以磨粒磨损为主,采用冷喷涂辅助感应重熔合成的FeCrMnAlCu高熵合金涂层具有良好的耐磨性能,其磨损率比冷喷涂辅助激光重熔合成涂层的磨损率降低29%。     

等离子堆焊Q235电解打壳锤头的组织和性能

采用等离子堆焊技术在Q235铝电解打壳锤头表面堆焊F40合金粉末熔覆层。利用扫描电镜、能谱仪和显微硬度计等分析等离子堆焊层的微观组织、微区成分和硬度分布。利用磨擦磨损仪对试样进行耐磨性测试,通过恒电位法评估堆焊层和基体的耐蚀性能。结果表明,堆焊层与基体形成了良好的冶金结合,堆焊层为典型的柱状晶组织。等离子堆焊层平均显微硬度为444HV0.1,为基体的2倍;耐磨性为基体的1.6倍;腐蚀速率Rcorr为3.524×10-4 mm/a,为基体的1/(4.2×104)。等离子堆焊后Q235钢材料的耐磨性、硬度和耐腐蚀性均有显著提高,有望提高电解铝打壳锤头的耐磨耐蚀性能。     

B对FeCoCrNiSiBx高熵合金激光熔覆层组织和硬度的影响

采用激光熔覆制备了FeCoCrNiSiB_x高熵合金熔覆层,利用光学显微镜、扫描电镜、X射线衍射仪和显微硬度计研究微量硼元素(摩尔比x=0、0.02、0.04、0.06、0.08)对FeCoCrNiSiB_x高熵合金熔覆层组织和硬度的影响。结果表明:无B高熵合金涂层组织主要为胞状晶。B的添加会促进枝晶的生成,逐渐形成鱼骨状树枝晶,但过量的B会破坏枝晶完整性,形成蠕虫状晶。此外,高熵合金熔覆层组织为FCC和BCC双相结构,B元素的添加会形成大量0.1~2.6 μm的Cr₂B第二相,有助于提高熔覆层硬度,其中x=0.06时激光熔覆层的硬度最高,约为537 HV0.2。     

超细VC对激光熔覆H13合金显微组织和耐磨性的影响

目的 通过添加超细VC颗粒改善Q235合金表面激光熔覆H13涂层的显微组织,并提高其耐磨性.方法 利用激光熔覆技术在Q235表面制备了H13/VC复合涂层,利用光学显微镜、扫描电镜、显微硬度仪以及摩擦磨损试验仪,研究了超细VC颗粒不同添加量对涂层微观结构、显微硬度和摩擦磨损性能的影响.结果 激光熔覆H13/VC复合涂层...