Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

Effect of Cation Substitution and Non-Stoichiometry on the Microwave Dielectric Properties of Sr(B'0.5Ta0.5)O3 [B'=Lanthanides] Perovskites

The Sr(B'_0.5Ta_0.5)O₃ ceramics where B'=La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, and Yb have been prepared by the conventional solid-state ceramic route and their microwave dielectric properties have been investigated. The structure and microstructure of the ceramics have been characterized by X-ray diffraction and scanning electron microscope techniques. The relative permittiviy (ɛ_r) varies linearly with B'-site ionic radii, except for La, and the temperature coefficient of resonant frequency (τ_f) varies linearly with the tolerance factor. The Sr(B'_0.5Ta_0.5)O₃ ceramics have ɛ_r in the range 25.9–32, Q _u× f =4500–54 300 GHz, and τ_f=−79 to −42 ppm/°C. A slight deviation from stoichiometry affects the dielectric properties of these double perovskites. Partial substitution of Ba for Sr could tune the dielectric properties. Addition of rutile (TiO₂) lowered the sintering temperature and improved the dielectric properties of Sr(B'_0.5Ta_0.5)O₃ ceramics.     

Preparation and Dielectric Properties of Low-Temperature-Sinterable (Zr0.8Sn0.2)TiO4 Powder

Low-temperature-sinterable (Zr_0.8Sn_0.2)TiO₄ powders were prepared using 3 mol% Zn(NO₃)₂ additive and then compared with powders prepared using 3 mol% ZnO additive and no additives. Sintering at 1200°C for 2 h produced a dielectric ceramic with ρ= 98.6% of theoretical density (TD), ɛ_r= 38.4, Q × f (GHz) = 42000, and τ _f =−1 ppm/°C. Sintering at 1250°C resulted in an excellent dielectric with ρ= 99% of TD, epsilon_r= 40.9, Q × f (GHz) = 49000, and τ _f =−2 ppm/°C. Scanning electron microscopy showed a microstructure with grains measuring 0.5 to 1 μm, and transmission electron microscopy revealed secondary phase in the grain boundaries.     

Glass-Free Zn2Te3O8 Microwave Ceramic for LTCC Applications

A Zn₂Te₃O₈ ceramic was investigated as a promising dielectric material for low-temperature co-fired ceramics (LTCC) applications. The Zn₂Te₃O₈ ceramic was synthesized using the solid-state reaction method by sintering in the temperature range 540°–600°C. The structure and microstructure of the compounds were investigated using X-ray diffraction (XRD) and scanning electron microscopy methods. The dielectric properties of the ceramics were studied in the frequency range 4–6 GHz. The Zn₂Te₃O₈ ceramic has a dielectric constant (ɛ_r) of 16.2, a quality factor ( Q _u× f ) of 66 000 at 4.97 GHz, and a temperature coefficient of resonant frequency (τ_f) of −60 ppm/°C, respectively. Addition of 4 wt% TiO₂ improved the τ_f to −8.7 ppm/°C with an ɛ_r of 19.3 and a Q _u× f of 27 000 at 5.14 GHz when sintered at 650°C. The chemical reactivity of the Zn₂Te₃O₈ ceramic with Ag and Al metal electrodes was also investigated.     

A Novel Temperature-Compensated Microwave Dielectric (1−x)(Mg0.95Ni0.05)TiO3−xCa0.6La0.8/3TiO3 Ceramics System

The microstructure and microwave dielectric properties of a (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics system have been investigated. The system was prepared using a conventional solid-state ceramic route. In order to produce a temperature-stable material, Ca_0.6La_0.8/3TiO₃ was added for a near-zero temperature coefficient (τ_f). With partial replacement of Mg²⁺ by Ni²⁺, the dielectric properties of the (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics can be promoted. The microwave dielectric properties are strongly correlated with the sintering temperature and the composition. An excellent Q × f value of 118,000 GHz can be obtained for the system with x =0.9 at 1325°C. For practical application, a dielectric constant (ɛ_r) of 24.61, a Q × f value of 102,000 GHz, and a temperature coefficient of resonant frequency (τ_f) of −3.6 ppm/°C for 0.85(Mg_0.95Ni_0.05)TiO₃−0.15Ca_0.6La_0.8/3TiO₃ at 1325°C are proposed. A parallel-coupled line band-pass filter is designed and simulated using the proposed dielectric to study its performance.     

Effects of Calcium Substitution on the Structural and Microwave Dielectric Characteristics of [(Pb1−xCax)1/2La1/2](Mg1/2Nb1/2)O3 Ceramics

The effects of calcium substitution on the structural and microwave dielectric characteristics of [(Pb_{1− x} Ca _x )_1/2La_1/2](Mg_1/2Nb_1/2)O₃ ceramics (with x = 0.01–0.5) were investigated. All the materials were observed to have an ordered A(B_1/2^'B_1/2^")O₃-type perovskite structure; however, the space group of the structure changed from Fm 3 m to Pa 3 as the calcium content increased to x = 0.1, and then from Pa 3 to R 3¯ at the x = 0.5 composition. During the structural evolution, the lattice parameter of the perovskite cell decreased linearly, and the dielectric constant ( k ) also decreased, from k = 80 to k = 38. However, the product of the quality factor and the resonant frequency ( Q × f ) increased from 50 000 GHz to 90 000 GHz as the calcium content increased. Also, the temperature coefficient of resonant frequency (τ_ƒ) gradually changed from 120 ppm/°C to −40 ppm/°C as the calcium content increased. At the x = 0.3 composition, a combination of properties— k ∼ 50, Q × f ∼ 86 000 GHz, and τ_ƒ∼ 0 ppm/°C—can be obtained.     

Effect of V2O5 Doping on the Sintering and Dielectric Properties of M-Phase Li1+x−yNb1−x−3yTix+4yO3 Ceramics

The effect of the addition of V₂O₅ on the structure, sintering and dielectric properties of M -phase (Li_{1+ x − y} Nb_{1− x −3 y} Ti _x +4 _y )O₃ ceramics has been investigated. Homogeneous substitution of V⁵⁺ for Nb⁵⁺ was obtained in LiNb_{0.6(1− x )}V_{0.6 x} Ti_0.5O₃ for x ≤ 0.02. The addition of V₂O₅ led to a large reduction in the sintering temperature and samples with x = 0.02 could be fully densified at 900°C. The substitution of vanadia had a relatively minor adverse effect on the microwave dielectric properties of the M -phase system and the x = 0.02 ceramics had [alt epsilon]_r= 66, Q × f = 3800 at 5.6 GHz, and τ_f= 11 ppm/°C. Preliminary investigations suggest that silver metallization does not diffuse into the V₂O₅-doped M -phase ceramics at 900°C, making these materials potential candidates for low-temperature cofired ceramic (LTCC) applications.     

Synthesis of BaCu(B2O5) Ceramics and their Effect on the Sintering Temperature and Microwave Dielectric Properties of Ba(Zn1/3Nb2/3)O3 Ceramics

BaCu(B₂O₅) ceramics were synthesized and their microwave dielectric properties were investigated. BaCu(B₂O₅) phase was formed at 700°C and melted above 850°C. The BaCu(B₂O₅) ceramic sintered at 810°C had a dielectric constant (ɛ_r) of 7.4, a quality factor ( Q × f ) of 50 000 GHz and a temperature coefficient of resonance frequency (τ_f) of −32 ppm/°C. As the BaCu(B₂O₅) ceramic had a low melting temperature and good microwave dielectric properties, it can be used as a low-temperature sintering aid for microwave dielectric materials for low temperature co-fired ceramic application. When BaCu(B₂O₅) was added to the Ba(Zn_1/3Nb_2/3)O₃ (BZN) ceramic, BZN ceramics were well sintered even at 850°C. BaCu(B₂O₅) existed as a liquid phase during the sintering and assisted the densification of the BZN ceramic. Good microwave dielectric properties of Q × f =16 000 GHz, ɛ_r=35, and τ_f=22.1 ppm/°C were obtained for the BZN+6.0 mol% BaCu(B₂O₅) ceramic sintered at 875°C for 2 h.     

Microwave Dielectric Properties and Low-Temperature Cofiring of BaTe4O9 with Aluminum Metal Electrode

Polycrystalline BaTe₄O₉ ceramic compound was investigated as a promising microwave dielectric compound for low-temperature cofired ceramics (LTCC) applications. The binary phase BaTe₄O₉ was synthesized and subsequently densified over the temperature range of only 500°–550°C, which allows for low-temperature cofiring with aluminum metal. The dielectric properties of BaTe₄O₉ ceramics sintered at 550°C for 2 h were determined in the microwave region of 12–14 GHz. The dielectric constant and Q × f product obtained were 17.5 and 54 700 GHz at 12 GHz, respectively. The temperature coefficient of resonance frequency showed a negative value of −90 ppm/°C. In terms of its evaluation for LTCC, the BaTe₄O₉ composition was found to be chemically compatible and successfully cofired with highly conductive aluminum electrode, while maintaining good electrical performance.     

Dielectric Behavior of Na0.5Bi0.5TiO3-Based Composites Incorporating Silver Particles

The dielectric properties of Na_0.5Bi_0.5TiO₃ (NBT) -based composites incorporating silver particles prepared by sintering at a low temperature of ∼900°C are reported. The dielectric constant increases with the amount of metal silver particles in the measured frequency range (150 Hz to 1 MHz), and could be enhanced up to ∼20 times higher than that of pure NBT ceramics, which was ascribed to the effective electric fields developed between the dispersed particles in the matrix and the percolation effect. Further investigation revealed that the dielectric constant of the composites has weak frequency and temperature dependence (−50°C to +50°C).     

Phase Transitional Behavior and Piezoelectric Properties of Lead-Free (Na0.5K0.5)NbO3–(Bi0.5K0.5)TiO3 Ceramics

(1− x )(Na_0.5K_0.5)NbO₃–(Bi_0.5K_0.5)TiO₃ solid solution ceramics were successfully fabricated, exhibiting a continuous phase transition with changing x at room temperature from orthorhombic, to tetragonal, to cubic, and finally to tetragonal symmetries. A morphotropic phase boundary (MPB) between orthorhombic and tetragonal ferroelectric phases was found at 2–3 mol% (Bi_0.5K_0.5)TiO₃ (BKT), which brings about enhanced piezoelectric and electromechanical properties of piezoelectric constant d ₃₃=192 pC/N and planar electromechanical coupling coefficient k _p=45%. The MPB composition has a Curie temperature of 370°–380°C, comparable with that of the widely used PZT materials. These results demonstrate that this system is a promising lead-free piezoelectric candidate material.     

Dielectric Properties of (1−x)CaTiO3–xCa(Zn1/3Nb2/3)O3 Ceramic System at Microwave Frequency

The microwave dielectric properties of the (1− x )CaTiO₃– x Ca(Zn_1/3Nb_2/3)O₃ ceramic system have been investigated. The ceramic samples sintered at 1300°–1450°C for 4 h in air exhibit orthorhombic pervoskite and form a complete solid solution for different x value. When the x value increased from 0.2 to 0.8, the permittivity ɛ_r decreased from 115 to 42, the unloaded quality factor Q × f increased from 5030 to 13 030 GHz, and the temperature coefficient τ_f decreased from 336 to −28 ppm/°C. When x =0.7, the best combination of dielectric properties, a near zero temperature coefficient of resonant frequency of τ_f∼−6 ppm/°C, Q × f ∼10 860 GHz and ɛ_r∼51 is obtained.     

Characteristics of High-Q Microwave Dielectric Ceramics Nd(Co1/2Ti1/2)O3 With CuO Addition

We report the microwave dielectric properties and the microstructures of Nd(Co_1/2Ti_1/2)O₃ ceramics prepared by the conventional solid-state route. The prepared Nd(Co_1/2Ti_1/2)O₃ exhibits a mixture of Co and Ti showing a 1:1 order in the B site. Lowering the sintering temperature (as low as 1260°C) and promoting the densification of Nd(Co_1/2Ti_1/2)O₃ ceramics could be effectively achieved by adding CuO (up to 0.75 wt%). At 1350°C, Nd(Co_1/2Ti_1/2)O₃ ceramics with 0.5 wt% CuO addition possess a dielectric constant (ɛ_r) of 27.6, a Q × f value of 165 000 GHz (at 9 GHz), and a temperature coefficient of resonant frequency (τ_f) of −20 ppm/°C. By comparing with pure Nd(Co_1/2Ti_1/2)O₃ ceramics, incorporating additional CuO helps to render a dielectric material with a higher dielectric constant, a smaller τ_f value, and a 20% dielectric loss reduction, which makes it a very promising candidate for applications requiring low microwave dielectric loss.     

High-Q Microwave Dielectrics in the (Mg1−xCox)2TiO4 Ceramics

The microwave dielectric properties and the microstructures of (Mg_{1− x} Co _x )₂TiO₄ ceramics prepared by the conventional solid-state route were investigated. Lattice parameters were also measured for specimens with different x . The formation of solid solution (Mg_{1− x} Co _x )₂TiO₄ ( x =0.02–0.1) was confirmed by the X-ray diffraction patterns, energy dispersive X-ray analysis, and the lattice parameters measured. By increasing x from 0 to 0.05, the Q × f of the specimen can be tremendously boosted from 150 000 GHz to a maximum of 286 000 GHz. A fine combination of microwave dielectric properties (ɛ_r∼15.7, Q × f ∼286 000 GHz at 10.4 GHz, τ_f∼−52.5 ppm/°C) was achieved for (Mg_0.95Co_0.05)₂TiO₄ ceramics sintered at 1390°C for 4 h. Ilmenite-structured (Mg_0.95Co_0.05)TiO₃ was detected as a second phase. The presence of the second phase would cause no significant variation in the dielectric properties of the specimen because it possesses compatible properties compared with that of the main phase. In addition, only a small deviation in the dielectric properties was monitored for specimens with x =0.04–0.05 at 1360°–1420°C. It not only provides a wide process window but also ensures an extremely reliable material proposed as a very promising dielectric for low-loss microwave and millimeter wave applications.     

Structure and Microwave Dielectric Properties of Hexagonal Ba[Ti1−x(Ni1/2W1/2)x]O3 Ceramics

Microwave dielectric ceramics with the composition of Ba[Ti_{1− x} (Ni_1/2W_1/2) _x ]O₃ ( x =0.4–0.6) were prepared by a solid-state reaction method. The evolution of the crystalline phases was investigated by X-ray powder diffraction analysis. A cubic-to-hexagonal phase transition occurred between 1000° and 1300°C. The phase transition is irreversible; thus, the hexagonal phase remains stable at room temperature. The X-ray powder diffraction data for x =0.5 were refined using the Rietveld method. It was identified as a h -BaTiO₃-type hexagonal perovksite with the space group of P 6₃/ mmc . It also reveals that random occupancy of Ti⁴⁺ and W⁶⁺ ions occurs in the B-site substructures, whereas Ni²⁺ ions exclusively occupy the octahedral site in the corner-sharing octahedron. The dielectric properties of dense-sintered ceramics were characterized at microwave frequencies. With an increase in x from 0.4 to 0.6, the Q × f value increased from 26 700 to 42 000 GHz, whereas ɛ_r decreased from 29.8 to 20.0, and τ_f from +6.5 to −9.9 ppm/°C.     

High Q Microwave Dielectric Ceramics in (Ni1−x Znx)Nb2O6 System

(Ni_{1− x} Zn _x )Nb₂O₆, 0≤ x ≤1.0, ceramics with >97% density were prepared by a conventional solid-state reaction, followed by sintering at 1200°–1300°C (depending on the value of x ). The XRD patterns of the sintered samples (0≤ x ≤1.0) revealed single-phase formation with a columbite ( Pbcn ) structure. The unit cell volume slightly increased with increasing Zn content ( x ). All the compositions showed high electrical resistivity (ρ_dc=1.6±0.3 × 10¹¹Ω·cm). The microwave (4–5 GHz) dielectric properties of (Ni_{1− x} Zn _x )Nb₂O₆ ceramics exhibited a significant dependence on the Zn content and to some extent on the morphology of the grains. As x was increased from 0 to 1, the average grain size monotonically increased from 7.6 to 21.2 μm and the microwave dielectric constant (ɛ'_r) increased from 23.6 to 26.1, while the quality factors ( Q _u× f ) increased from 18 900 to 103 730 GHz and the temperature coefficient of resonant frequency (τ_f) increased from −62 to −73 ppm/°C. In the present work, we report the highest observed values of Q _u× f =103 730 GHz, and ɛ'_r=26.1 for the ZnNb₂O₆-sintered ceramics.     

Microwave Dielectrics in the (La1/2Na1/2)TiO3–Ca(Fe1/2Nb1/2)O3 System

Dielectric properties of the system (1 − x)(La_1/2Na_1/2)TiO₃– _x Ca(Fe_1/2Nb_1/2)O₃, where 0.4 # x # 0.6, have been investigated at microwave frequencies. The temperature coefficient of resonant frequency (τ_f), nearly 0 ppm/°C, was realized at x = 0.58. These ceramics had perovskite structure and showed relatively low dielectric losses. A new dielectric material applicable to microwave devices having Q · f of 12000–14000 GHz and a dielectric constant (ε_r) of 59–60 has been obtained at 1300–1350°C for 5–15 h sintering.     

Microwave Dielectric Properties of a New A5B4O15-Type Cation-Deficient Perovskite Ba2La3Ti3TaO15

High dielectric constant and low loss ceramics with composition Ba₂La₃Ti₃TaO₁₅ have been prepared by a conventional solid-state ceramic route. This compound adopts A₅B₄O₁₅ cation-deficient hexagonal perovskite structure. The dielectric properties of dense ceramics sintered in air at 1520°C have been characterized at microwave frequencies. It shows a relative dielectric constant of ∼45, quality factor Q _u× f of ∼26 828 GHz and temperature variation of resonant frequency of −0.97 ppm/°C.     

Low-Dielectric Loss Characteristics of Nd(Co1/2Ti1/2)O3 Ceramics at Microwave Frequencies

The microwave dielectric properties and the microstructures of Nd(Co_1/2Ti_1/2)O₃ (NCT) ceramics using starting powders of Nd₂O₃, CoO, and TiO₂ prepared by the conventional solid-state route have been researched. The dielectric constant values (ɛ_r) saturated at 24.8–27. Quality factor ( Q × f ) values of 37 900–140 000 (at 9 GHz) and the measured τ_f values ranging from −45 to −48 ppm/°C can be obtained when the sintering temperatures are in the range of 1410°–1500°C. The ɛ_r value of 27, the Q × f value of 140 000 (at 9 GHz) and the τ_f value of −46 ppm/°C were obtained for NCT ceramics sintered at 1440°C for 4 h. For applications of high selective microwave ceramic resonator, filter, and antenna, NCT is proposed as a suitable material candidate.     

Low-Temperature Sintering of K0.5Na0.5NbO3 Ceramics

The objective of this work was to lower the sintering temperature of K_0.5Na_0.5NbO₃ (KNN) without reducing its piezoelectric properties. The KNN was sintered using 0.5, 1, 2, and 4 mass% of (K, Na)-germanate. The influence of the novel sintering aid, based on alkaline germanate with a melting point near 700°C, on the sintering, density, and piezoelectric properties of KNN is presented. The alkaline-germanate-modified KNN ceramics reach up to 96% of theoretical density at sintering temperatures as low as 1000°C, which is approximately 100°C less than the sintering temperature of pure KNN. The relative dielectric permittivity (ɛ/ɛ₀) and losses (tanδ), measured at 10 kHz, the piezo d ₃₃ coefficient, the electromechanical coupling and mechanical quality factors ( k _p, k _t, Q _m) of KNN modified with 1 mass% of alkaline germanate are 397, 0.02, 120 pC/N, 0.40, 0.44, and 77, respectively. These values are comparable to the best values obtained for KNN ceramics sintered above 1100°C.