胶粉料成分对玻化微珠保温砂浆性能的影响

通过设计不同配比的胶粉料,研究了胶粉料中粉煤灰、聚丙烯纤维和引气剂对保温砂浆的干密度、抗压强度和导热系数的影响。结果表明,通过在保温砂浆中掺加粉煤灰,可一定程度上降低砂浆的干密度和导热系数,但抗压强度也随之降低;在保温砂浆中掺入聚丙烯纤维可有效提高砂浆的抗压强度,但对保温砂浆的干密度和抗压强度无明显影响;引气剂的掺入可明显降低保温砂浆的干密度和导热系数,使保温砂浆性能达到GB/T 20473-2006《建筑保温砂浆》中Ⅰ型的技术要求。     

以钢渣和粉煤灰为掺合料的水泥基泡沫混凝土的研制

研究了钢渣和粉煤灰为掺合料对水泥基泡沫混凝土性能的影响。结果表明：用优质粉煤灰等质量取代水泥。不仅可降低泡沫混凝土的干体积密度和导热系数,而且在同条件下可提高低泡沫混凝土的强度;钢渣粉对泡沫混凝土的干体积密度影响不大。但会降低泡沫混凝土的强度．而钢渣粉与粉煤灰复合取代水泥时可以得到良好的效果：泡沫用量是影响泡沫混凝土的干体积密度、抗压强度和导热系数的主要因素,泡沫量增加会导致泡沫混凝土的密度降低,强度也减小,导热系数减小;泡沫混凝土的导热系数与干体积密度近似呈指数函数关系。     

陶瓷微珠在轻质高强保温砂浆中的应用研究

陶瓷微珠具有质轻、导热系数低的特点,目前主要应用于建筑反射隔热涂料中,采用热线法导热系数仪测试其导热系数为0.0350W/(m·K),比玻化微珠和膨胀珍珠岩导热系数低20%~30%,干密度为78kg/m~3,有利于制备轻质高强、保温性能好的保温砂浆。为降低保温砂浆的导热系数,通过复掺少量陶瓷微珠和聚苯颗粒,制备的保温砂浆的干密度为228kg/m~3,28d抗压强度为0.4MPa,导热系数为0.060W/(m·K),除干密度稍偏高外,其它主要性能指标满足GB/T 10303—2001《膨胀珍珠岩绝热制品》中200号优等品标准要求。     

物理发泡法制备结构-保温一体化碱激发多孔材料

为探索以物理发泡法制备兼具承重能力和保温功能的碱激发多孔材料,研究了泡沫掺量对碱激发多孔材料工作性能以及干密度、抗压强度和导热系数等关键性能的影响。结果表明:通过控制泡沫掺量制备的多孔碱激发材料干密度为628~1409 kg/m~3,抗压强度为2.18~22.01 MPa,导热系数为0.138~0.342 W/(m·K)。和物理发泡法制备的传统多孔混凝土相比,该材料强度和保温性能远优于相同干密度传统多孔混凝土,且工作性能优异,可用于自流平保温地面及其它传统泡沫混凝土应用的领域。     

磷酸镁水泥制备加气混凝土砌块抹面砂浆的试验研究

针对加气混凝土砌块的多孔和吸水慢的性能特点,采用磷酸镁水泥配制备出适用于加气混凝土的抹面砂浆。研究了粉煤灰掺量和漂珠体积掺量对抹面砂浆保水率、抗压强度、黏结强度、导热系数和干缩率的影响。结果表明,掺入漂珠可大幅度降低砂浆的导热系数,但在一定程度降低其力学性能和保水性,当漂珠完全取代石英砂时,所制备的砂浆导热系数为0.28 W/(m·K),14 d黏结强度为0.60 MPa,干缩率仅为0.050 mm/m,用于加气混凝土砌块抹面可解决抹面砂浆存在的开裂、空鼓问题。     

建筑垃圾制备泡沫混凝土的研究

以建筑垃圾、普通水泥、废泡沫塑料(EPS)和发泡剂为原料制备泡沫混凝土,研究了建筑垃圾用量对泡沫混凝土抗压强度、干表观密度和导热系数等物理性能的影响.结果表明,采用激发剂的情况下,建筑垃圾用量达到70%(质量百分数),可以制得干表观密度为860 kg/m3、28 d抗压强度大于3 MPa、导热系数小于0.20 W/(m·K)的泡沫混凝土,可作为非承重围护结构的保温材料使用.     

全矿渣碱激发制备内养护泡沫混凝土的研究

研究了碱激发环境下矿渣替代水泥制备泡沫混凝土的方案。结果表明,激发剂水玻璃模数选择n=1.2,提高矿渣替代水泥的比例能有效提高泡沫混凝土的抗压强度,取代比例可以达到为100%,制品密度为600 kgm3,28 d抗压强度为6.5 MPa,导热系数为0.178 W(m·K),收缩为0.87 mm/m。同时,试验还研究了掺入超轻陶粒或者聚丙烯酸钠盐SAP作为内养护材料对泡沫混凝土性能的影响,发现二者都能有效降低导热系数和收缩,掺入陶粒时能提高制品的强度,而掺入SAP会降低制品的强度。最终复掺陶粒和SAP对泡沫混凝土进行改性,制品性能:密度为600 kgm3,28 d抗压强度为5.5 MPa,导热系数为0.142 W(m·K),收缩为0.45 mmm,总体性能良好。     

复合改性剂对页岩陶砂保温砂浆物理力学性能的影响

为了改善页岩陶砂保温砂浆的物理力学性能和可施工性能,通过复掺纤维素醚和可再分散乳胶粉等方法,系统地研究了复合改性剂对砂浆稠度、分层度、干表观密度、导热系数、抗压强度和黏结拉伸强度的影响。结果表明:纤维素醚能够有效改善砂浆的物理力学性能和可施工性能,并在掺量为0.3%时各项测试指标为综合最优。     

短切玄武岩纤维对保温砂浆性能影响的研究

为了研究短切玄武岩纤维对保温砂浆性能的影响,以水泥、石膏、粉煤灰作为三元胶凝材料,膨胀珍珠岩和聚苯颗粒作为骨料,同时掺入短切玄武岩纤维,通过对保温砂浆稠度、抗折强度、干密度、抗压强度、软化系数、导热系数的检测,得出以下结论:玄武岩纤维能够降低保温砂浆的稠度,增强保温砂浆的耐水性,软化系数,提高保温砂浆的抗折抗压强度,对导热系数无明显影响。当掺入量为1. 5%时,短切玄武岩纤维对保温砂浆性能的改善效果最好;18㎜长的玄武岩纤维比8㎜长的改善效果更明显。     

基于氯氧镁水泥制备的EPS保温砂浆研究

以氯氧镁水泥为胶凝材料,掺入聚苯颗粒制备出复合保温砂浆。分别研究了聚苯颗粒掺量对复合保温砂浆的力学强度、密度、导热系数的影响,以及粉煤灰对复合保温砂浆容重和导热系数的影响。研究表明,聚苯颗粒能降低砂浆的抗压强度、抗折强度、密度和导热系数。聚苯颗粒掺量为0.486%时,复合保温砂浆密度和导热系数分别是805kg/m~3、0.2191W/(m·K);小掺量粉煤灰能增加砂浆容重,粉煤灰掺量为10.974%时,砂浆的密度和导热系数均显著降低。     

轻质GRC配方及应用性能的研究

通过低碱度硫铝酸盐水泥和耐碱玻璃纤维，配合轻质材料（膨胀珍珠岩、聚苯乙烯、膨胀蛭石）研制成轻质GRC材料，对GRC材料的密度、力学性能（抗拉强度、抗弯强度）以及导热性能进行测试分析，发现在合适的抗碱纤维配比，水配比，水灰比，轻质材料配比的情况下，其性能最好，达到密度为0．85g/cm^3，抗弯强度21．5MPa，抗拉强度7．47MPa，导热系数0．358W／m．K。该材料具有轻质、阻燃、隔热、保温、耐用等优越性能。     

无机玻化微珠保温砂浆的质量控制

测试了是否掺0.1%的引气剂时无机保温砂浆的性能,并通过线性回归拟合,研究了无机保温砂浆干密度、抗压强度、导热系数与堆积密度的关系。研究表明:由相同原材料配制的无机保温砂浆,干密度、抗压强度、导热系数与堆积密度存在较好的正相关性;在已知堆积密度的条件下,可利用拟合公式推算出干密度、抗压强度与导热系数;可通过控制无机保温砂浆的堆积密度控制其质量。     

Investigation of properties of low-strength lightweight concrete for thermal insulation

In this study, block elements with diatomite, which have different aggregate granulometries and cement contents, were produced and the effect of these parameters on physical and mechanical properties of block elements were investigated. Diatomite samples were taken from the region of Afyon. In the mixes, water/cement ratio was kept at 0.15. Analyses include compressive strength, thermal conductivity, ultrasonic velocity tests, bulk density and specific porosity. According to experimental results, while dry unit weight is varied between 900 and 1190 kg/m³, compressive strength of 7–56 days specimens ranged from 2.5 to 8 MPa. Materials with a ratio of 30% fine, 40% medium and 30% coarse size have the best compressive strength and thermal insulation in all series. Due to low thermal conductivity, lightweight aggregate concrete with diatomite can be used to prove high isolation in the structure.     

粉煤灰纤维架构弹性保温隔热材料的研究

选用了粉煤灰纤维、超细粉煤灰纤维作为空间架构材料,采用阴离子表面活性剂发泡,以纯熟料水泥凝胶硬化定型,辅以真空抽吸破泡,通过充分干燥及表面防水处理工艺制得了粉煤灰纤维架构弹性保温隔热材料。结果表明:当超细粉煤灰纤维掺量为5%~15%、粉煤灰纤维与纯熟料水泥质量比为0.25、纯熟料水泥掺量为5%~20%时,材料的导热系数普遍在0.04~0.06 W/(m·K)之间,表观密度集中在80~150 kg/m^3,抗压强度普遍低于0.20 MPa,所制得的保温隔热材料具有一定的弹性,永久变形量在0.050~0.090 mm之间。     

玻化微珠保温砂浆性能影响因素研究

研究了玻化微珠、聚苯颗粒、矿渣、聚丙烯纤维和硬脂酸钙5个组分的掺量及水灰比对玻化微珠保温砂浆性能的影响。试验结果表明:增大水灰比及增加玻化微珠、聚苯颗粒的掺量都会降低保温砂浆的干表观密度及导热系数;水灰比和玻化微珠掺量的增大均会降低保温砂浆的28 d抗压强度;随聚苯颗粒掺量的增加,保温砂浆的28 d抗压强度逐渐提高;增加矿渣和不同长度聚丙烯纤维的掺量,仅在一定范围内提高砂浆的28 d抗压强度;硬脂酸钙能显著降低保温砂浆的吸水率。最佳水灰比为2.1~2.2,玻化微珠、聚苯颗粒、矿渣、聚丙烯纤维(短纤维)和硬脂酸钙的最佳掺量分别为42%~46%、2%、10%、0.1%、2%~4%。     

水泥基不燃性轻质保温材料制备的研究

以水泥为主要原料制成的密度小于300 kg/m3的泡沫混凝土,是一种新型外墙外保温材料。采用硅酸盐水泥为主要原料在实验室研究了这种材料的制备方法,并系统地研究了几种混凝土外加剂对该材料制备过程及其性能的影响。结果表明,以硅酸盐水泥为主要原料,并适量添加适宜的混凝土外加剂,可以制得性能优良的低密度泡沫混凝土;其中,几种外加剂的适宜掺量分别为:早强剂1.8%,促凝剂0.8%;聚丙烯纤维0.8%～1.0%;憎水剂0.1%～0.2%,苯丙乳液0.3%～0.4%。在此最佳条件下制得泡沫混凝土的干密度为290 kg/m3,28 d抗压强度可达1.1 MPa,吸水率为6.11%,导热系数为0.07 W(/m.K)。     

高流态超早强聚合物修补砂浆的性能研究

采用可再分散乳胶粉改性硫铝酸盐水泥制备修补砂浆,研究了乳胶粉掺量对修补砂浆力学性能和粘结性能的影响。结果表明:乳胶粉掺量从0增加到2%时,修补砂浆的抗压强度逐渐降低,而抗折强度和粘结强度却逐渐提高。当乳胶粉掺量为1.5%时,修补砂浆2 h、1 d和28 d抗压强度分别为27.3、42.3、57.0 MPa,拉伸粘结强度为1.8 MPa,界面弯拉强度为7.8 MPa,抗拉强度恢复率为73.4%。在乳胶粉和聚氧化乙烯(PEO)复掺条件下,砂浆的拉伸粘结强度进一步提高,当乳胶粉和PEO掺量分别为1.5%和0.5%时,拉伸粘结强度可达2.31 MPa。     

玻化微珠对无机轻集料保温砂浆性能的影响

测试了2种不同玻化微珠配制的无机轻集料保温砂浆的性能,并通过线性回归拟合,研究了不同玻化微珠对保温砂浆干密度与导热系数、抗压强度之间相关性的影响情况。结果表明,堆积密度、筒压强度、导热系数相对较大、颗粒粒径相对较小的玻化微珠配制的保温砂浆具有更好的物理力学性能及保温隔热性能;同一种玻化微珠配制的保温砂浆,干密度与抗压强度、导热系数间有较好的相关性;在已知干密度的条件下,2种保温砂浆利用同一个拟合公式,推算出来的导热系数值具有一定的参考价值。     

聚合物增强煤矸石泡沫混凝土性能研究

以800kg/m3为设计干密度,采取物理发泡的方式,将泡沫与煤矸石水泥净浆混合均匀,分别加入不同用量的PVA或EVA乳液制成聚合物-煤矸石泡沫混凝土,测量干密度、导热系数、28 d抗压强度,并利用Nano Measurer软件测量平均孔径.PVA的加入量选取水泥质量的1％、2％、3％,EVA乳液的加入量选取水泥质量的3...     

多元胶凝体系泡沫混凝土性能研究

采用正交试验研究了粉煤灰、矿粉、硅灰及减水剂对泡沫混凝土力学性能的影响,设计了泡沫混凝土配合比,研究了在不同干密度下泡沫混凝土的抗压强度、孔隙率和导热性能。初步探究了利用珊瑚砂制备泡沫混凝土的可行性。结果表明:复掺矿粉和硅灰能有效提高泡沫混凝土的强度;泡沫混凝土的抗压强度、导热系数与干密度存在非线性关系,孔隙率与泡沫混凝土干密度呈线性负相关。珊瑚砂的掺入对泡沫混凝土性能存在不利影响。