褐铁矿致密化烧结技术试验研究

分析了褐铁矿的烧结特性及成矿机理,根据性能优势互补配矿理论,通过试验将褐铁矿与镜铁矿合理搭配进行烧结.试验结果表明：褐铁矿烧结性能得到强化,烧结矿指标明显改善,主要是镜铁矿液相生成温度高、流动性差,褐铁矿颗粒被镜铁矿包裹,使得褐铁矿颗粒在与液相接触之前得到致密,避免了脆化结构的形成.褐铁矿致密化烧结使得烧结矿的矿物结构发生变化,多孔薄壁结构减少,有利于改善烧结矿高温性能.     

细磨海砂矿烧结特性及其对烧结矿质量影响机理

通过细磨海砂矿研究其粒级分布、微观结构和烧结高温特性的变化,结合烧结杯试验、扫描电镜能谱分析等研究方法考察海砂矿粒级分布对烧结矿质量的作用机理.经细磨后海砂矿颗粒不规则程度增大,制粒性能得到改善.随着海砂矿粒度变细,其烧结高温特性呈现出与普通铁矿粉相反规律,其中海砂矿3(细磨25 min的海砂矿)与海砂矿1(未经细磨的海砂矿)相比,同化温度升高21℃,1280℃时液相流动性指数减小0.35,细磨后海砂矿与Ca O反应生成钙钛矿增多,阻碍同化反应进行,生成的液相黏度增大.配加8%海砂矿3的烧结矿与配加相同比例海砂矿1相比,还原性提高3.8%,细磨后海砂矿在混合料中分布更加均匀,造成烧结矿中含钛物相质点增多,还原中产生众多微细裂纹,利于还原气体扩散.      

高配比镜铁矿粉混合料烧结性能改善

镜铁矿铁品位高、杂质含量低,是优质炼铁原料,但其制粒性能差,导致透气性差,烧结矿产量和质量下降,因此在烧结生产中的配比(质量分数)一般不超过20%。为了增加镜铁矿在烧结生产中的使用比例,使用烧结杯实验对添加粘结剂改善高配比镜铁矿粉混合料烧结性能进行了研究。结果表明,在镜铁矿粉配比为36%时,添加质量分数为0.65%的膨润土或0.55%的BF复合粘结剂,可使烧结混合料层冷态透气性指数分别提高19.05%和27.98%,热态透气性分别提高21.48%和18.19%,烧结机利用系数分别提高11.67%和7.50%;固体燃耗则分别降低2.82和4.01 kg/t。烧结矿转鼓强度、化学成分和冶金性能均满足高炉冶炼要求。因此,2种粘结剂均能显著改善高配比镜铁矿粉混合料制粒及烧结性能,是提高镜铁矿粉配比的有效措施之一。     

一种新的巴西铁矿粉烧结性能研究

通过对一种新的巴西铁矿粉(BNF)的理化性能、工艺矿物学、高温性能及单矿烧结杯实验研究,对其烧结性能进行了全面评价。结果表明,巴西BNF矿粉基本理化性能产生了较大变化,具有铁品位较高,含硅量偏高,粒度偏细(-0.5 mm占49.01%)等特点;其主要矿物组成为赤铁矿(53%)和镜铁矿(30%),少量针铁矿(8%);粘附粉比表面积大,成球性好;高温性能除同化温度偏高和铁酸钙生成能力较低外,液相流动性好,粘结相自身强度高;单矿烧结性能较好,烧结矿转鼓强度为60.4%,烧结利用系数达到1.73 t/(m~2·h),烧结矿整体呈现中孔、小孔厚壁结构,趋向于以铁酸钙充填于赤铁矿和磁铁矿之间的胶结固结为主,并与硅酸盐液相交织固结,其还原性高,低温还原粉化率低。巴西BNF矿粉能够替代其它铁矿粉用于烧结。     

不同类型进口铁矿粉的烧结基础性能分析

为了探究不同类型铁矿粉的烧结基础性能和区别,采用微型红外烧结炉和扫描电镜对澳大利亚铁矿粉和巴西铁矿粉的烧结基础特性和微观颗粒形貌进行研究,并结合Factsage7.1热力学计算软件对铁矿粉的液相生成能力和黏度进行计算。研究结果表明:不同类型铁矿粉的烧结基础性能差别较大,这主要受铁矿粉种类、化学成分和粒度组成及致密度影响;其中,澳矿粉属于半褐铁矿,结晶水质量分数高,结构疏松,易与CaO反应,矿化过程中易形成多孔网状结构,吸液性强,同化性能优,黏结相强度低,澳矿粉的配加有利于改善烧结矿同化性能,改善矿化过程;巴西矿属于赤铁矿粉,结构致密,反应活性低,同化性能差,黏结相强度高,巴西矿的配加有利于改善烧结矿黏结相性能,提高烧结矿强度。     

烧结优化配矿技术研究

为了改善烧结矿质量、降低炼铁成本,河钢邯钢对8种常用铁矿粉高温特性进行了研究。在此基础上,根据铁矿粉高温特性互补原理,设计了7组配矿方案并进行了烧结杯实验,获得了较好的烧结效果。验证了基于铁矿粉高温特性的烧结优化配矿方法是科学可行性的,为改善烧结矿质量及冶金性能提供了技术依据。     

加拿大某精矿高配比烧结特性

 采用烧结杯试验、冶金性能检测及基础物化性能检测等多种方法研究了产自加拿大的某精矿的配矿烧结性能、烧结矿冶金性能及物化性质,对其烧结特点从物化性质方面进行了分析。结果表明:随精矿配比(质量分数)由24%增加到42%,烧结料层透气性阻力由857 Pa提高到1 150 Pa,垂直烧结速度由21.87 mm/min下降到18.38 mm/min,利用系数从1.14 t/(m2·h)降低到0.93 t/(m2·h),转鼓强度由67.47%下降到64.13%,无烟煤固体燃耗由62.46 kg/t提高到70.42 kg/t,烧结成品矿还原性指数(RI)由82.31%下降到78.76%,低温还原粉化率(RDI＞3.15 mm)由70.71%下降到64.41%,烧结各项指标及烧结矿的冶金性能均出现较大幅度恶化。物化性质分析表明,加拿大精矿的主要矿物组成是镜铁矿和假象赤铁矿,矿物表面亲水性差,且粒度组成不合理,恶化混合料制粒;同时,该精矿的颗粒表面光滑致密,高温反应性能差,软化温度在1 450 ℃以上,烧结过程中难以形成足够液相。加拿大精矿制粒性能差导致烧结料层透气性阻力大造成烧结利用系数低,而较高的软化温度导致随着该矿配比的提高烧结矿转鼓强度降低。     

降低巴西矿配比的试验研究

为进一步降低马钢烧结用矿成本,开展了降低巴西矿配比的烧结试验研究。结果表明,在不增配其他精矿的情况下,巴西矿配比从36%逐步降低至10%,烧结矿转鼓强度明显下降,烧结固体燃耗逐步上升,成品率下降,而烧结矿冶金性能总体改善。通过在烧结配矿中增配10%与巴西矿高温特性指标相近的高品位铁精矿,有效改善了巴西矿配比降低带来的负面影响,并实质性地降低了配矿成本,达到了预期目标。     

齐大山铁矿烧结试验研究

为考察不同SiO2含量对烧结过程以及烧结矿性能的影响规律,对鞍山集团矿业公司齐大山铁矿生产的铁精粉,进行了烧结试验研究。得出随SiO2含量降低,烧结混合料的适宜水分有所升高,烧结料层的垂直烧结速度有减慢的趋势,烧结矿的转鼓强度、成品率有降低趋势,烧结矿的低温还原粉化性能变差,烧结矿的还原度略有降低,烧结矿的软化开始温度升高,软化区间变窄,软化性能改善。综合烧结过程和烧结矿的各项性能指标来看,SiO2含量过低,不利于烧结矿性能的改善。在烧结矿SiO2含量〉5.5%以上时,提铁降硅对烧结生产影响不大,但当SiO2〈5.5%,尤其是SiO2〈5.0%时,随着SiO2含量逐步降低,烧结矿质量明显下降。结合选矿的生产实践,齐大山铁矿合理经济品位的赤铁矿铁精粉中SiO2含量以5.0%-5.5%为宜。     

包钢烧结配加80%(50%)外矿工业应用研究

本文总结了包钢烧结增加外购铁矿的工业试验情况。试验过程中将外购铁矿配比分别提高至 5 0 %和80 %,并将烧结矿碱度由 1 36提高至 1 8,高炉料炉结构定为 75 %烧结矿 +2 5 %球团矿。试验结果表明 :烧结矿转鼓指数提高了 4～ 5个百分点 ,烧结矿粒度组成明显改善 ,其软熔温度提高 30℃以上 ;高炉生产稳定顺行 ,其利用系数突破了 2 0t/m3 ·d ,焦比降低 ,生铁质量明显改善。     

A study of pre-briquetting granulation sintering of the mixtures with high ratio of Brazilian specularite concentrate

In the paper, the pre-treatment of fine Brazilian specularite concentrates with high iron grade and low impurities through pre-briquetting was proposed to improve the granulation and sintering performance of blends comprising some 30% specularite concentrates. The results show that the excellent sintering indexes are attained as follows in pot tests: productivity of 1.64?t?m^?2?h^?1, tumble index of 59.87% and solid fuel consumption of 71.64?kg?t^?1 under the optimal conditions. Compared with traditional sintering process, productivity and tumble index were increased by 13.88 and 3.5%, respectively, and solid fuel consumption decreased by 4.82?kg?t^?1. The RI and RDI_?3.15 reach 83.95 and 35.02%, respectively, which are superior for blast furnace. The mechanism of the pre-treatment of the specularite concentrates was demonstrated that better permeability was achieved by coarsening granule, more calcium ferrite was formed by basicity segregation and separation addition of coke.     

Improvement of sintering performance of sinter mixtures containing high ratio of specularite fines

Although specularite fines possess high iron grade and low impurities, their granulation performance was poor so that the ratio of specularite fines is kept below 20% in sinter ore blends because of low permeability and productivity and weak strength. In order to increase its ratio in sintering, binders were used to improve the granulation performance of sinter blends containing high ratio of specularite fines in sintering pot test. Results show that cold permeability of the sintering bed increases by 19. 05% by adding 0. 65mass% bentonite or by 27. 98% by 0. 55mass% BF composite binder respectively when 36 mass% specularite fines are proportioned in sinter blends. In addition, the hot permeability is also improved by adding bentonite or BF composite binder, respectively, resulting in an increase in the productivity of 11. 67% and 7. 50% as well as an decrease in solid fuel consumption of 2. 82kg/t and 4. 01kg/t, respectively, while the tumble index, chemical composition and metallurgical performance meet the requirement of blast furnace. So using suitable binders is one of effective ways to improve the granulation and sintering performance of sinter ore blends comprising high ratio of specularite fines.     

铁矿石富氧烧结点火试验研究

采用镜铁矿作为铁原料,通过改变天然气流量和氧气过剩系数以及氧气和空气的配比,在实验室进行了一系列点火烧结试验研究,重点考查富氧对烧结点火的影响。研究表明,富氧烧结点火能够降低烧结点火能耗和减少CO2的排放量,同时点火温度上升,烧结料层表面固体燃料的利用率提高,并可获得良好的烧结矿产量、质量指标。当天然气流量为2 m3.h-1,点火时间为1.5 min,助燃风为50%氧气+50%空气(体积分数),氧气过剩系数为1.9的情况下,烧结点火能耗为30.32 MJ.m-2,点火烟气中氧的体积分数为14.28%,所获得的烧结矿成品率和转鼓强度分别为72.32%和65.30%。与助燃风为空气,其它条件不变的情况比较,烟气中氧的体积分数提高了5.17%,烧结矿成品率和转鼓强度分别提高了10.59%和1.97%。     

高品位巴西铁精矿粉在烧结生产中的应用研究

对某巴西精矿的烧结特性和烧结规律进行了试验研究与分析,结果表明:该精矿是1种高铁低硅矿粉,有利于提高烧结矿品位,但其烧结性能较差,对烧结矿转鼓强度、成品率及冶金性能有不利影响。将该精矿配比控制在5%以内,同时将碱度和水分按上限控制,有利于提高烧结矿产量和质量。     

镜铁矿烧结性能试验研究

镜铁矿因成球性和可烧性较差,使得该矿在烧结料中的应用受到了极大限制。本文通过试验对镜铁矿制粒性能、烧结特性及冶金性能的研究,采取优化原料结构技术措施,探索出镜铁矿在烧结中合理使用新途径,为提高其在生产中的配比和改善烧结性能提供指导。     

强化制粒对含铬型钒钛混合料烧结的影响

 含铬型钒钛混合料制粒效率低,料层透气性差,严重影响了其发展低温高料层烧结。在基准方案基础上,通过烧结杯试验研究了生石灰配比、混合料水分、润湿时间和制粒时间对含铬型钒钛混合料烧结的影响,并对强化制粒效果进行了观察。试验结果表明：在碱度为2.15、配碳量为3.2%(质量分数)、混合料配加生石灰为5%、水分为7.5%、消化时间为10 min,制粒时间为8 min时,平均粒径[d]、拟似粒化指数[GI0]、制粒效率[E]、抗粉化指数[B]分别由2.26 mm、66.30%、54.11%、48.15%提高到2.58 mm、80.43%、90.82%、73.53%,烧结速度、成品率、利用系数、转鼓强度分别由16.54 mm/min、70.39%、1.22 t/(m2·h)、55.36%提高到19.70 mm/min、77.94%、1.64 t/(m2·h)、59.36%。含铬型钒钛混合料对水分敏感度高,应严格控制水分波动。采用强化制粒措施,提高料层透气性,增加氧势,可提高烧结矿中铁酸钙质量分数改善其矿物组成与结构,提高产质量。     

建筑用玻璃与可伐合金润湿规律

为实现建筑用玻璃与可伐合金的可靠激光封接,本文针对影响封接质量的主要因素(温度、时间、粗糙度及氧化层)对两者润湿性能的影响开展了研究.当保温温度由800℃提高至900℃,液态玻璃黏度降低致使其在可伐合金表面的流动性增强,润湿角由69.5°降低至31.1°.在850℃下延长保温时间(5~40 min),液态玻璃在低黏度条件下有充分的时间铺展,润湿角降幅为30%.随着可伐合金表面粗糙度的提高,液态玻璃向四周扩散需要克服的势垒增加,当粗糙度值Ra由0.186μm升至0.563μm时,润湿角由46.9°升至69.5°.由于可伐合金表面氧化层可与液体玻璃发生扩散而形成较强离子键,使得两者润湿性能显著提高,润湿角降低幅度达到23.6%.因此,在实际激光封接过程中,增加保温温度和时间、降低钢板表面粗糙度及钢板预氧化处理将有效地提高玻璃与钢板的润湿性能.      

高比例扬迪粉烧结优化试验研究

介绍了扬迪粉(YD粉)烧结配矿优化试验情况及不同硅源对高YD粉配比烧结过程的影响.试验结果表明:用具有高孔隙度的YD矿替代B粉、C粉和E粉后,混合料水分应适当提高,以改善混匀制粒效果.因原料装料密度降低,使原始料层透气性得到改善,烧结生产率得到提高,烧结矿还原性略有改善,T<,D>-T<,S>区间和T<,D>-T<,m...     

分流预成型强化制粒改善镜铁矿粉烧结性能

针对镜铁矿精粉成球性及可烧性差的特点,采用分流预成型强化制粒工艺对进口镜铁矿精粉制粒及烧结性能开展研究.与常规制粒工艺烧结指标相比,采用分流造球强化制粒烧结工艺,焦粉配比从4.85%降至4.20%,利用系数从1.44 t·m-2·h-1提高至1.71 t·m-2·h-1,转鼓强度从57.60%提高至63.80%,固体燃耗从76.46 kg·t-1降至65.24 kg·t-1;采用分流辊压预成型强化制粒烧结工艺,焦粉配加量从4.85%降至4.70%,利用系数从1.44 t·m-2·h-1提高至1.64 t·m-2·h-1,转鼓强度及固体燃耗基本不变.因此,分流预成型强化制粒工艺较常规制粒工艺能显著改善镜铁矿烧结性能.其作用机理为:镜铁精矿经分流预成型后能改善混合料的透气性,降低焦粉配比,提高烧结料层氧位,生成更多的铁酸钙及赤铁矿,所得成品烧结矿结晶完善,矿物之间胶结紧密,内部气孔由不规则大孔变为总体分布较为均匀且大小适中的规则球形,改善了烧结矿的强度和还原性.