钢铁表面复合转化膜的制备

为研究一种无磷涂装前金属表面处理技术,提出了以氟锆酸、硝酸锰和KH-792[即N-(2-氨乙基)-3-氨丙基三甲氧基硅烷]为原料在钢铁表面形成复合转化膜的方法。通过单因素实验确定了最佳工艺条件为:氟锆酸5.5 g/L,硝酸锰2.0 g/L,KH-7922.5 g/L,p H 2.5,室温,成膜时间10 min。通过扫描电镜观察到在钢铁表面形成了完整而致密的转化膜,由能谱分析结果推测其化学组成可能为Me ZrF_6·nH_2O·[NH_2(CH_2)_2NH(CH_2)_3SiO_3)]_m(Me)_n(其中Me为Fe或Mn)。该转化膜的单位面积质量为3.152 6 g/m~2,耐3%NaCl溶液浸泡时间为180 min。成膜液的疲劳度优于锌系磷化液和锆化液。     

钢铁件磷化-氧化复合处理工艺及膜层性能

将钢铁件磷化与氧化(双槽)两大工艺结合起来,开发了一种新型转化膜生产工艺。磷化液配方和工艺条件为:磷酸二氢锌30~40 g/L,硝酸锌90~120 g/L,硝酸锰10~20 g/L,总酸80~90点,游离酸2~3点,常温,时间10 min。第一槽氧化液配方和工艺条件为:NaOH 550~600 g/L,NaNO_2 100~150 g/L,温度130~150℃,时间25~35 min。第二槽氧化液配方和工艺条件为:NaOH 600~650 g/L,NaNO_2 150~200 g/L,温度135~140℃,时间25~35 min。该复合转化膜具备磷化膜与氧化膜的优点,平整光滑,厚而耐腐蚀,经过长久磨损后依旧耐腐蚀。     

铝合金无铬化学转化膜工艺研究

以单宁酸和氟钛酸盐为主体原料,加入硝酸铜,在铝合金表面形成化学转化膜,以硫酸铜点滴试验为依据,通过单因素实验优化了铝合金非铬转化膜工艺条件:乙二胺四乙酸二钠0.5 g/L,氟钛酸钾1.0 g/L,氟硼酸铵0.25 g/L,单宁酸0.8 g/L,马日夫盐0.5 g/L,A液(含Cu(NO3)2·3H2O和氟钛酸)25 m L/L,化学转化液的p H 2.5~3.5,温度35°C,浸渍时间15 min。该工艺可在铝合金表面形成完整致密的金黄色非晶态化学转化膜,硫酸铜点滴时间达到6 min,具有较好的抗蚀性能。     

6063铝合金碱性钼酸盐化学转化工艺及膜层性能

采用碱性钼酸盐转化工艺在6063铝合金表面制得耐蚀性良好的转化膜。转化液组成为:钼酸钠10.0g/L,乙二胺四乙酸二钠2.0 g/L,三乙醇胺3.0g/L,氟化钠5.0g/L,含硫无机促进剂2.0 g/L。研究了转化液pH、温度和处理时间对转化膜耐蚀性的影响。结果表明,在pH=11.0、温度50℃的条件下处理6063铝合金6.0 min所得转化膜耐蚀性最优。所得转化膜呈均匀的灰色略泛绿,表面粗糙但无裂纹,厚度达30μm以上,由Al_2O_3、MoO_3、Al_2(MoO_4)_3、Na_3AlF_3等化合物构成。     

装饰用铜合金镧-铈复合化学转化工艺及膜层耐蚀性

对装饰用H62铜合金进行稀土镧-铈复合化学转化。对转化液组成和工艺条件进行正交优化,得到最优参数为:硝酸镧4 g/L,硝酸铈4 g/L,苯并三氮唑15 g/L,钼酸钠2 g/L,柠檬酸13 g/L,磺基水杨酸9 g/L,十二烷基苯磺酸钠0.4 g/L,温度53°C,时间4 min。该条件下所得La–Ce复合转化膜的厚度为6.2μm,耐硝酸点滴时间为23.16 s。中性盐雾试验、静态浸泡腐蚀试验和电化学阻抗谱测试结果均表明,单一镧盐或铈盐转化膜的耐蚀性优于无稀土转化膜,La–Ce复合转化膜的耐蚀性则最优。     

铸铝合金黑色转化膜工艺

介绍了在铸铝表面制备黑色钼酸盐转化膜的工艺条件:3 g/L钼酸铵,3 g/L硫酸钴,1~2 g/L氟化氢铵,pH 4~5,温度55℃,时间20 m in。研究了钼酸铵、硫酸钴、氟化氢铵、黑化液酸度、黑化液温度及时间对膜质量的影响。通过点滴实验测试了膜的耐蚀性为40 s。通过扫描电镜观察了膜的形貌,并探讨了转化膜的形成机理。按此工艺制得的黑色钼酸盐转化膜表面光滑,光泽性好,与基体结合牢固。     

铝合金表面有色转化膜快速成膜工艺

在含有Ti/Zr的处理液中加入单宁酸、有机缓蚀剂和硫酸锰,在铝合金基体上得到了耐蚀性能优异的金黄色转化膜。研究了处理液各组分对转化膜外观以及耐蚀性能的影响,确定了成膜的最佳工艺为:H2TiF6 7 g/L,H2ZrF6 1 g/L,F-3 g/L,单宁酸7 g/L,硫酸锰5 g/L,有机酸缓蚀剂2 g/L,pH 4.9,成膜时间10 min。研究表明,单宁酸和H2TiF6是转化膜着色的关键,二者缺一不可。由最佳工艺得到的转化膜的自腐蚀电流密度是铝合金基体的1.3%,耐蚀性能明显提高。     

钢铁表面氟铁酸钾转化膜技术研究

在钢铁表面制得了氟铁酸钾转化膜,主要工艺流程包括酸洗、钝化、吹干和上漆.钝化液配方及工艺条件为:氟化钾100～130g/L,浓硝酸70～80 mL/L,四价无机钛盐促进剂0.5～1.0 g/L,室温,pH 2～3,时间15～30 min.采用金相显微镜、EDS能谱和硫酸铜点滴试验等方法对膜的表面形貌、元素组成和耐蚀性进行了测试.结果表明,钢铁经此工艺钝化处理后其耐蚀性能及与基体和有机涂层的结合力明显提高.     

铝及铝合金无铬氟锆酸盐化学转化膜

研究了一种适用于铝及铝合金的无铬化学转化工艺,探讨了转化液的主要成分和工艺条件对转化膜质量的影响,得到了较好的工艺条件:氟锆酸钾1.0～2.0 g/L,氢氟酸0.5 ～ 1.5 mL/L,促进剂4～6g/L,氧化剂(硝酸镁)8～12g/L,pH 3.5～4.0,温度40～60℃,氧化时间4～6min.按此工艺制备的转化...     

铝表面自组装成膜工艺的研究

探索出了以KH-460硅烷偶联剂、氟硅酸为主体原料一步法进行铝表面自组装成膜。成膜的最佳条件为:氟硅酸15mL/L,pH值4,镀膜时间15min,温度35℃,KH-460硅烷偶联剂和氟硅酸125mL/L。该工艺适用于涂料涂装前的金属铝表面预处理,自组装膜的综合性能良好,与传统工艺相比具有处理程序简单、槽液稳定、成本低、节能、环保等优点。     

钴基催化剂上氢解反应的研究

制备了一系列不同金属含量的Co/SiO2加氢催化剂,考察了催化剂非原位还原条件、进料空速、氢分压变化对其氢解反应影响。结果发现,钴基催化剂在非原位还原后进行反应时有氢解反应伴随发生。催化剂上金属含量越高、还原温度升高和还原时间延长,氢解反应越明显;较高的进料空速及较高的氢分压有助于抑制氢解反应的发生。     

基于环糊精的纳米功能组装体的研究进展

通过分子自组装形成稳定和结构可控的材料是现在功能材料学、生物学的焦点,构筑纳米尺寸的功能性分子自组装体更是接近生命现象和过程的本质。基于环糊精的超分子组装以其选择性、可调控性和生物相容性等优势引起了广泛关注。本文就近十年来基于环糊精的纳米尺寸的功能组装体的研究进展进行简要综述,包括修饰环糊精的软连接自组装,环糊精轮烷、聚轮烷、纳米线、纳米管、纳米笼的设计、构筑及其更高级组装,以及环糊精与纳米粒子的分子组装和基于环糊精的分子机器。     

Studies on oxidative dehydrogenation of n-butane on bismuth molybdate on alumina

Oslefins and diolefins are important intermediates in the petrochemical industry and the future promises a further substantial increase in demand. While several catalysts have been formulated in the past for the abstraction of hydrogen from butenes and propylene, these catalysts are inefficient in the abstraction of first hydrogen from butane. Bismuth molybdates (β and γ-phases) containing iron oxide and supported on alumina are used as catalysts in the present investigation on the oxidative dehydrogenation of n-butane. Effects of catalyst content, temperature and oxygen: n-butane ratio on conversion and selectivity to butadiene and (C₄H₈ + C₄H₆) are studied in the following ranges of experimental conditions: β-bismuth molybdate/100 mol support I(K), 3–9; γ-bismuth molybdate/100 mol support I(K), 5-20; temperature, 400–500°C; O₂: butane ratio, 0.6:1.7.     

Micro-viscometer based on electrowetting on dielectric

A viscometer used to measure the viscosity of 10 μl of a liquid, must be miniaturized down, and the liquid velocity gradient in the channel used to determine the viscosity coefficient. Two major factors that affect the liquid velocity are the mechanical forces exerted by the mechanical motors and electromagnetic forces. In this study, electrowetting on dielectric (EWOD) is adopted to drive liquids. Variously sized electrodes on a chip, and two shapes of channel are employed to measure the velocity gradient to determine the viscosity coefficient. The device is fabricated by microelectromechanical system (MEMS) technology. The dielectric layer used in EWOD has a high dielectric constant, BST (Ba_0.7Sr_0.3TiO₃), to reduce the required applied voltage; its surface is coated with hydrophobic polymer, polytetrafluoro-ethylene (PTFE, Teflon^® AF DuPont). Experimental results demonstrate that liquids can be pulled at 660 μm/s in linear channels by applying a voltage of 15 V.     

漆酶用于木质纤维板结合的研究

研究了温度和pH值对漆酶酶活以及漆酶处理纤维压制纤维板性能的影响。结果表明,pH较低、温度较高时漆酶酶活较高,压制的纤维板强度性能较好。但温度太高(60～80℃),延长加热时间,漆酶稳定性变差,酶活明显降低,压制纤维板的强度下降。     

表面活性剂对钙指示剂影响的研究

由于钙指示剂（又称NN指示剂）的水溶液不稳定,通常将其配制成固体指示剂使用,但是存在着生成的络合物不够稳定、终点变色不敏锐、准确度不高等问题。研究了固体钙指示剂的最佳使用条件,以及表面活性剂对钙指示剂稳定性、灵敏度的影响等问题。实验结果表明：固体钙指示剂的最佳配比是钙指示剂与氯化钠的质量比为1∶100、液体钙指示剂中钙指示剂-十二烷基硫酸钠,以及钙指示剂-乳化剂OP-10-苦味酸效果最佳,终点变色更加敏锐,精密度以及准确度都有显著提高,体系稳定性好。     

工艺参数对沉降斑影响的实验研究

采用实验方法考察工艺参数对沉降斑的影响。基于一个带凸台的平板模具,采用L27(313)正交矩阵进行实验,研究了几何尺寸、熔体温度、注射时间、保压压力及保压时间对厚度突变处沉降斑形成的影响,同时还考虑了熔体温度和注射时间以及保压压力和注射时间之间的交互作用影响;通过性噪比分析和F检验优化成型工艺条件并对工艺参数的影响进行显著性分析。结果表明,对于厚度突变的平板制品,厚度突变的程度对其沉降斑形成的影响最大,其次为熔体温度,保压压力,保压时间等;采取减小厚度变化,降低熔体温度或增加保压压力和保压时间等措施,可以减小厚度突变处沉降斑,从而减少其对外观质量的影响;因素之间的交互作用对制品沉降斑的形成有一定的影响,熔体温度B和注射时间C之间的交互作用影响较为明显,而保压压力D和注射时间C之间的交互作用对该质量指标的影响最小,可以并入误差。     

株洲化工集团管理改革经验探讨

探讨了株化集团在企业管理及改革等方面的经验。该公司为适应市场经济的变革制订了科学的发展规划、思路和目标;确定了目标管理实施方案和各项制度;强化销售工作和质量管理,加大科技投入,加强科技创新活动;理顺各种关系,做好各项有关工作,使企业的经济效益和对社会的贡献逐年增大。     

基于四氢呋喃聚醚聚氨酯弹性体力学性能的研究

以四氢呋喃聚醚（PTMG）、二异氰酸酯（TDI、或MDI）和扩链剂（MOCA、或BDO）为原料,制备了浇注型和热塑型聚氨酯弹性体。研究了预聚体的NCO基质量份、PTMG的分子量和硬段质量份数对PU弹性体力学性能的影响。结果表明：PU弹性体的硬度和模量随NCO含量和硬段质量份数增加而增加。逐渐提高PTMG的分子量,PU弹性 的拉伸强度降低,而拉断伸长率增加。2000分子量的PTMG－PU弹性体的冲击弹性比1000分子量的PTMG－PU好。     

轮胎滑水特性的CFD分析

以205/50R16子午线轮胎为研究对象,建立带有纵向花纹沟的轮胎有限元模型(FEM)和计算流体动力学(CFD)模型。基于流固耦合的FEM模拟轮胎滑水产生的过程,采用重整规化群和流体体积组分方法的CFD模型得到轮胎接地区域内的水膜流场分布。两种模型计算结果对比表明,CFD模型能够用来分析胎面微花纹沟内流体流动特性。随着水膜厚度的增大,轮胎受到的流体压力也变大,容易出现滑水现象。