添加Zr元素对纳米复相Nd10．5Fe78．4-xCo5ZrxB6．1粘结永磁体结构和磁性能的影响

采用快淬、热处理及模压成形工艺，制备了成分为Nd10．5Fe78．4-xCo5ZrxB6．1（x=0，1．0，1．5，2．0，2．5）的5种粘结永磁体。采用XRD,DTA，TEM等方法对合金的组织结构和晶化行为进行了研究。结果表明：Zr含量的增加可提高材料的非晶形成能力；当Zr添加到一定量时，形成高熔点的Fe2Zr相，产生细化晶粒的作用；添加Zr元素显著地提高了合金的矫顽力，改善了退磁曲线矩形度，从而提高了最大磁能积。Nd10．5Fe78．4-xCo5ZrxB6．1永磁体在x=2时获得最佳磁性能，Br=0．659T，Hcj=628kA／m，Hcb=419kA／m，（BH）m=73kJ／m^3。     

快淬速度对纳米晶复合Nd_(8.5)Dy_1Fe_(76)Co_5Zr_3B_(6.5)永磁材料磁性能和微观结构的影响

采用熔体快淬和随后的退火处理制备了Nd_(8.5)Dy_1Fe_(76)Co_5Zr_3B_(6.5)纳米晶复合永磁合金,研究了快淬速度对合金磁性能和微观结构的影响。随着快淬速度的增加,合金的磁性能呈现先升高再下降的趋势,当快淬速度为15 m/s时,合金有最佳的磁性能,B_r=0.70 T,H_(cj)=706.05 kA/m,(BH)_(max)=74.54 kJ/m~3。透射电镜的分析结果表明:合金的晶粒分布均匀,晶粒尺寸约为20 nm。三维原子探针的结果显示Zr元素在硬磁相Nd_2Fe_(14)B的晶界处富集,起到了抑制晶粒长大、细化晶粒的作用,从而提高了材料的磁性能。     

添加元素对稀土粘结磁体退磁曲线方形度的影响

采用快淬法制备镨基(Nd,Pr)10.5(Fe,Co)83.5-xMxB6(M=Zr,Nb,Ti)系列粘结磁体,研究添加Zr、Nb和Ti等元素对快淬合金显微结构和磁性能的影响.(Nd,Pr)10.5(Fe,Co)83.5B6合金中适量添加Zr、Nb和Ti元素能有效细化合金晶粒,获得细小、均匀的晶粒,平均晶粒尺寸为50～70 nm.添加Zr、Nb和Ti元素的粘结磁体,由于晶粒细化和非磁性相对磁畴畴壁钉扎的共同作用,Hk/Hcj值大幅度增加,退磁曲线方形度得到明显改善,磁性能也显著提高.在Zr、Nb和Ti3种元素中,Zr对细化晶粒和提高磁性能的效果最好.含1％Zr(原子分数)的(Nd,Pr)10.5(Fe,Co)82.5Zr1B6合金薄带晶粒细小、均匀,平均尺寸约为60 nm,其粘结磁体退磁曲线方形度最好,Hk/Hcj值达到了39.9％,剩磁Br为0.675 T,内禀矫顽力Hci为616 kA/m,最大磁能积(BH)m为77 kJ/m3.     

快淬速度对Nd9.5Fe76Zr3Co5B6.5纳米晶复合永磁合金磁性能和微观结构的影响

以Nd9.5Fe76Zr3Co5B6.5合金为研究对象,研究了不同快淬速度(8~65 m/s)对合金的磁性能、交换耦合作用和微观结构的影响。结果表明,快淬速度对合金退火后的微观结构和磁性能具有显著地影响,适当的快淬速度将使合金退火后的晶粒细化、分布均匀,提高软、硬磁性相间的交换耦合作用,进而提高合金的磁性能。当淬速为15 m/s时,合金退火后具有最佳的综合磁性能:Br=0.976 T,Hcj=711.57 kA/m,(BH)max=150.61 kJ/m3。     

Nd含量对高Zr含量纳米双相NdxFe90.5-xZr3.0B6.5合金微结构和磁性能的影响

采用电弧炉快淬和晶化退火工艺制备高性能NdxFe90.5-xZr3.0B6.5（F8．5=11．5）快淬磁体。结果表明，Zr的添加显著提高磁体的磁性能，Nd含量可以明显提高磁体的磁性能，X由8．5增加到10．5时，NdxFe90.5-xZr3.0B6.5磁体的磁能积由75kJ／m^3升高到114kJ／m^3，接近于美国Magnequench公司的MQP-B磁粉性能。     

纳米晶复合Nd_(9.5)Fe_(79-x)Co_5Nb_xB_(6.5)(x=0,1,2,3)永磁合金的微结构和磁性能

利用X射线衍射仪(XRD)、振动样品磁强计(VSM)、透射电子显微镜(TEM)和三维原子探针(3DAP)等研究了Nb元素对纳米晶复合Nd_(9.5)Fe_(79-x)Co_5Nb_xB_(6.5)(x=0,1,2,3)永磁合金微结构和磁性能的影响。结果表明,随着Nb元素的增加,合金的剩磁J _r首先增加,在Nb含量为1 at%时达到最大值0.94 T,继续增加Nb元素后,合金的剩磁开始下降;矫顽力_i H_c则随着Nb元素的增加逐步增加,当Nb含量超过2 at%后,增加幅度变缓;合金的最大磁能积(BH)_(max)随着Nb元素的增加先增加后降低,纳米晶复合Nd_(9.5)Fe_(79-x)Co_5Nb_xB_(6.5)合金具有最优的综合磁性能,即J_r=0.91 T,_i H_c=663k A/m,(BH)_(max)=120 k J/m~3。Nb元素在合金的晶化过程中富集于晶间形成Nb Fe B相,有利于细化晶粒尺寸,从而提高合金的磁性能。     

Ti添加对快淬Pr基永磁合金磁性能与显微结构的影响

采用快淬法制备了Pr基(Nd,Pr)10.5Fe81.5-xTixCo2B6(x=0.0,1.0,2.0,3.0,4.0,5.0)系列粘结磁体,研究了添加Ti元素对快淬合金显微结构和磁性能的影响。Ti元素能有效细化合金的晶粒,添加3at%Ti的合金,晶粒细化到约70nm,且大小均匀;添加量超过3at%,晶粒进一步细化,但均匀性变差。含Ti3at%的(Nd,Pr)10.5Fe78.5Ti3Co2B6合金,粘结磁体磁性能达到最佳值,Br=0.655T,Hci=681kA/m,(BH)m=68kJ/m3。Ti元素低于3at%,合金晶粒粗大,磁性能较低;超过3at%后,富Ti的晶间相加厚,晶粒间的交换作用和剩磁增强效应减弱,且晶粒大小不均匀,合金的内禀矫顽力虽然增加,但剩磁Br和最大磁能积(BH)m降低。     

钛掺杂无氢类金刚石薄膜疏水性能研究

利用X射线衍射分析（XRD）和BH测试仪分别研究了元素Tb、Zr的添加对HD法制备NdFeB永磁体的微结构及磁性能的影响规律。微结构研究表明,元素Tb、Zr添加前后的磁体都主要由四方相Nd2Fe14B（P42/mnm）和微量的富Nd相构成;但Tb和Zr的添加明显改变了永磁体的取向特性和磁性能;采用HORTA法计算表明,Tb和Zr的添加虽然都使永磁体的（004）、（006）、（008）极密度因子减小,但是室温下磁性能测试表明,Zr的添加降低了磁体的矫顽力,而Tb添加后永磁体的矫顽力有了明显的提升,从2038 kA/m提升到2302 kA/m;Kronmüller-Plot关系曲线表明,3种合金的矫顽力机理均为磁畴成核反转机制。     

Preparation of isotropic Sm2Fe17Nx magnetic powders and their bonded magnets

The isotropic Sm2Fe17Nx magnetic powders were prepared by Hydrogenation-Disproportion-Desorption-Recombination (HDDR) process. The phase and microstructure evolutionary process of Sm-Fe alloy during the solidification, homogenization, HDDR and nitration processes were investigated by means of XRD, SEM, EDX and AFM. The results show that the homogeneous Sm2Fe17 alloy wassuccessfully obtained and the impurity phases and residual stress were well removed by heated at 1050 ℃ for 24 h. When heated at 800 ℃ for 1h in H2 of 0.1 Mpa, the alloy turns into SmHx and α-Fe with plenty of nanocrystals. After vacuumized at 800 ℃ for 2h the alloy recombines into Sm2Fe17 with a crystal grain size of about 85 nm.The lattice constant of the alloy increases and the expanding of the crystal cell reaches 6.28% after nitrified at 500 ℃ for 5 h. The magnetic property of isotropic bonded Sm2Fe17Nx magnets is Br=0.6704 T, Hcj = 1015 kA·m-1,( BH )max =73.7 kJ·m-3 with a density of 6.04 g·cm-3 .     

Microstructural characteristics of Nd2Fe14B/α-Fe nanocomposite ribbons bearing Nb element

The effects of Nb on the microstructure and magnetic properties of (Nd0.9Dy0.1)9.5Fe79-xCo5NbxB6.5(x=0, 1) nanocomposite magnets were investigated. A fine and uniform microstructure was achieved for the ribbons annealed at 710℃ for 4min, enhancing the interaction coupling between grains and improving the magnetic properties. The results of three-dimensional atom probe (3DAP) indicated that Fe-Nb-B inter granular phase existed at the grain boundaries, suppressing the grain growth during the crystallization process. The coercivity was improved from 224 to 643 kA/m for the modification of the microstructure.     

Influence of dynamic crystallization on exchange-coupled NdFeB nanocrystalline permanent magnets

Dynamic crystallization was introduced to improve the magnetic properties of NdFeB nanocrystalline permanent magnets by optimizing microstructure. The microstructure was studied by X-ray diffraction (XRD) and transmission electron microscopy (TEM). It has been determined that, compared with the conventional heat treatment, dynamic crystallization can shorten the crystallization time. Moreover, dynamic crystallization can refine grains, enhance the exchange-coupled interaction among grains, and promote the magnetic properties. As a result, the optimal magnetic properties of Nd10.5(FeCoZr)83.4B6.1(Br＝0.685T, Hci ＝732 kA·m -1 , Hcb ＝429 kA·m-1 ,( BH )m=75 kJ·m -3 ) are obtained after dynamic crystallization heat treatment at 700 ℃ for 10 min.     

Effects of Ti and(or) Cu on microstructures and magnetic properties of sintered Nd-Fe-B magnets

1　ＩＮＴＲＯＤＵＣＴＩＯＮＩｔｉｓｗｅｌｌｋｎｏｗｎｔｈａｔｔｈｅｉｎｔｅｒｇｒａｎｕｌａｒｍｉ ｃｒｏｓｔｒｕｃｔｕｒｅｏｆｓｉｎｔｅｒｅｄＮｄ Ｆｅ Ｂｍａｇｎｅｔｓｐｌａｙｓａｋｅｙｒｏｌｅｉｎｄｅｖｅｌｏｐｉｎｇｔｈｅｉｒｃｏｅｒｃｉｖｉｔｙ[1,2 ] .Ｅａｒｌｉｅｒｓｔｕｄｉｅｓｓｈｏｗｅｄｔｈａｔｔｈｅｉｎｔｅｒｇｒａｎｕｌａｒｍｉｃｒｏｓｔｒｕｃｔｕｒｅｉｓｃｏｍ ｐｏｓｅｄｏｆａＮｄ ｒｉｃｈｐｈａｓｅａｎｄａｓｍａｌｌａｍｏｕｎｔｏｆＢ ｒｉｃｈｐｈａｓｅ.Ｉｔｈａｓｂｅｅｎｓｈｏｗｎｔ…     

微量Ga元素对双相纳米晶磁体性能的影响

探讨了微量的Ga替代Fe对Nd2 Fe14 B/Fe3B + (少量 )α Fe永磁材料的晶体结构及磁性能的影响。结果表明 :添加微量的Ga同样可减小晶粒尺寸 ;在Ga含量x <1% (原子百分比 )的范围 ,随着x的增加 ,Br 和 (BH) max随晶化时间变化的曲线由非线性向线性转化 ;矫顽力jHc 下降到一个最小值后 ,又缓慢上升 ;当x =0 2时 ,综合磁性能较好。     

电场烧结法制备纳米复相Nd2Fe14B／α-Fe永磁块体材料

采用电场烧结法制备出纳米复相Nd10．5Dy0．5Fe76．9Nb1Co586．1永磁块体，研究了电场烧结温度对其磁性能和抗压强度的影响，采用XRD，SEM等方法分别对其相结构、显微组织进行了分析。结果表明：非晶合金压制成型后，经823K，300S电场烧结制得的纳米晶永磁块体具有最佳磁性能：Br=0．6498T，Hcj=714kA／m，（BH）max=63kJ／m^3。随着烧结温度的升高，块体的抗压强度增加。     

Dy元素对纳米复合(Nd,Pr)_(10.5-x)Dy_xFe_(83.5)B_6合金磁性能与显微结构的影响（英文）EI北大核心CSCD

采用快淬法制备了镨基(Nd,Pr)10.5-x Dyx Fe83.5B6(x=0.0,0.5,1.0,1.5,2.0,2.5)系列粘结磁体,研究了Dy元素添加对快淬合金显微组织结构、磁性能及快淬薄带热稳定性的影响。与Nd2Fe14B相比,硬磁相Dy2Fe14B具有较高的磁晶各向异性场HA和较低的饱和磁极化强度Js,因此,Dy元素添加能显著提高合金的内禀矫顽力Hcj,但会降低合金的剩磁Br。Dy元素替代Nd/Pr元素,增强了快淬薄带的热稳定性,提高了晶化退火温度。较高的晶化退火温度,使快淬薄带中已经形成的微晶更容易长大,形成一些粗大晶粒,降低了粘结磁体的磁性能。1.0%是较佳的Dy元素添加量,(Nd,Pr)9.5Dy1Fe83.5B6合金快淬粘结磁体的最大磁能积(BH)max为71.6 k J/m3,剩磁Br为0.638 T,内禀矫顽力Hcj为611 k A/m。     

快淬速度对纳米晶复合Nd8.5Fe77.7Nb2Co5Ga0.6B6.2粘结永磁体温度系数的影响

采用熔体快淬法及真空退火工艺制备了不同淬速的Nd8.5Fe77.7Nb2Co5Ga0.6B6.2粘结磁体,研究了不同淬速下磁体的磁性能及温度系数。结果表明,适当的快淬速度有利于合金退火后的晶粒细化,有效地改善了退火后软、硬磁相间的交换耦合作用。快淬速度对磁体的温度系数有显著的影响,矫顽力温度系数β随着淬速的增加而逐渐降低;随着淬速的增加,剩磁温度系数α先降低后升高,这可能与合金中软、硬磁相间的交换耦合作用的变化有密切的关系。     

烧结(Nd,Tb)-Fe-B磁体的元素扩散、反磁化和矫顽力

采用双合金法将两种粉末混合制备烧结永磁体可提高磁体磁性能;但在烧结过程中两种粉末之间存在元素扩散,元素扩散对磁性能的影响程度需要进一步研究。本文将Nd13Fe81B6和TbHx粉末混合制备烧结磁体,Nd13Fe81B6磁体矫顽力为4.5 kOe。当TbHx混合量为3 wt.%,烧结磁体的矫顽力增加至20.0 kOe。通过热激活研究认为,磁畴壁的形核是反磁化需要经过的过程。由于热力学的原因Tb元素更容易扩散进入Nd2Fe14B主相而不是富集在晶间富稀土相。Tb元素进入主相替代Nd可形成具有更高各向异性场的(Nd,Tb)-Fe-B表层,在反磁化过程中晶粒表层磁畴壁的形核场会增加,因此矫顽力增加程度显著。但是,TbHx混合量超过5 wt.%,矫顽力增加幅度降低。对于TbHx混合量7 wt.%的磁体,元素分布显示在主相晶粒内部贫Tb区域明显增少,证实在烧结过程中更多Tb原子从晶粒表层扩散入晶粒内部,这样晶粒表层反磁化形核场的提高程度会减弱,因而磁体矫顽力增加幅度降低。本研究说明要提高双合金Nd-Fe-B磁体磁性能需进一步控制元素扩散并优化磁体的元素分布。     

PrFeBZr纳米复合永磁材料的研究

用振动样品磁强计(VSM)研究了PrxFe94.3-xB5.7Zr1(x=9．4，9．8，10．2，10．6，11，11．4)系列快淬带在淬速V=22m／s的淬态和真空退火态(670℃)样品的磁性能和磁滞回线的变化情况，发现该系列合金在淬速V=20m／s下样品S2(Pr11Fe83.3B5.7Zr1)取得了最好的磁性能为：Jc=0．76T，Hc=977．3kA／m，(BH)max=98．8kJ／m^3；最佳快淬和晶化热处理都可以使软磁相与硬磁相耦合。     

Mo含量对Fe_(40)Co_(40)Zr_((10-x))Mo_xB_9Cu_1(x=0,2,4)合金的微观结构,热性能和磁性能的影响

采用单辊快淬法制备Fe_(40)Co_(40)Zr_((10-x))Mo_xB_9Cu_1(x=0,2,4)系非晶合金,并对3种合金进行不同温度热处理。利用X射线衍射仪(XRD)、透射电镜(TEM)、差热分析仪(DTA)和振动样品磁强计(VSM)对合金的微观结构、热性能和磁性能进行测试分析。结果表明:Fe_(40)Co_(40)Zr_((10-x))Mo_xB_9Cu_1(x=0,2,4)3种合金第1个晶化峰的激活能随Mo含量的增加而减小,Mo的添加不利于合金的热稳定性。Mo含量的增加抑制了ZrCo_3B_2等化合物的析出,细化了结晶相的晶粒尺寸。Fe_(40)Co_(40)Zr_((10-x))Mo_xB_9Cu_1(x=0,2,4)3种非晶合金的矫顽力Hc均随退火温度的升高而逐渐增大。Mo的添加明显降低了合金的矫顽力。     

Magnetic properties of Nd_2Fe_(14)B/α-Fe nanocomposite magnets with yttrium addition

The phase evolution and magnetic properties of Nd9?xYxFe72Ti2Zr2B15 (x = 0,0.5,1,and 2) melt-spun nanocomposite ribbons were studied.It is found that Y addition not only enhances the formability of amorphous phase in the alloy,but also stabilizes the amorphous phase during the annealing treatment.The appropriate content of Y addition effectively enhances the remanence (Jr) of the annealed sample.The residual amorphous intergranular phase in the annealed sample optimizes the squareness of the loop,resulting in an larger maximum energy product (BH)max.The best magnetic properties,Jr = 0.78 T,Hci (coercivity) = 923.4 kA/m,and (BH)max = 98.5 kJ/m3,were obtained from the Nd8YFe72Ti2Zr2B15 ribbon spun at Vs = 4 m/s and annealed at 700°C for 10 min,which is composed of Nd2Fe14B,α-Fe,and amorphous phase.