奥氏体不锈钢低温离子渗氮工艺研究

对304、316 L奥氏体不锈钢进行了不同温度、不同时间的离子渗氮。研究了渗层的显微组织和耐腐蚀性,测定了渗层的硬度。结果显示,随着渗氮温度的升高,两种钢渗层的表面硬度和深度都增加,而耐蚀性降低。渗氮温度≥400℃时,随着渗氮时间的延长,两种钢渗层的表面硬度变化不大,但深度明显增加,渗层的耐蚀性降低。当渗氮工艺相同时,316 L钢渗氮层的硬度、深度和耐蚀性均比304钢的渗氮层高。     

双相不锈钢低温离子硬化处理工艺

采用低温离子渗氮和氮碳共渗对双相不锈钢进行试验,利用显微硬度计、光学显微镜、X射线衍射仪分别研究了表面硬度、硬度梯度、表面脆性、硬化层横截面显微组织、硬化层结构。结果表明,低温离子渗氮和氮碳共渗后硬化层的性能(表面硬度、硬化层厚度、显微组织、物相结构)变化规律大致相同:随着处理温度的提高或者时间的延长,表面硬度和硬化层厚度不断提高,但最后趋于平缓;表面脆性略有增加。     

低温离子硬化处理对AISI 420不锈钢组织与性能的影响

研究了低温离子渗氮、离子氮碳共渗和离子渗碳硬化处理对AISI 420马氏体不锈钢的显微组织、表面硬度、耐蚀性、耐磨性的影响。结果表明,离子渗氮、氮碳共渗和离子渗碳处理都可提高马氏体不锈钢的表面硬度;经不同工艺处理后的试样,除500 ℃×4 h渗氮工艺外,其他不锈钢试样表面的耐蚀性均未出现明显降低,当渗氮温度过高（500 ℃）时,由于CrN的析出使得渗氮层的耐蚀性显著下降;磨损试验的结果表明,离子渗碳处理后硬化层的耐磨性最佳。     

304 不锈钢低温离子渗氮及氮碳共渗处理

目的研究304不锈钢离子渗氮层和氮碳共渗层的组织、硬度及耐磨、耐蚀性能,并考察渗层的磨损机理。方法利用离子渗氮及氮碳共渗工艺在304不锈钢表面获得硬化层,利用XRD,OM及共聚焦显微镜、显微硬度仪、电化学测试仪,分析处理前后渗层的组织、相结构及渗层的硬度及耐磨耐蚀性能。结果 304不锈钢氮碳共渗和渗氮层主要为S相层,在相同工艺条件下,氮碳共渗工艺获得的渗层为γN+γC的复合渗层,且厚度大于单一渗氮层。渗氮层和氮碳共渗层硬度约为基体硬度的3.5倍。在干滑动摩擦条件下,氮碳共渗层比渗氮层具有更好的耐磨性能;渗氮层的磨损机理为磨粒磨损的犁沟效应和断裂,氮碳共渗层的磨损机理为磨粒磨损的犁沟和微切削。电化学测试表明,渗氮层和氮碳共渗层的耐蚀性能均优于基体。结论 304不锈钢在420℃进行离子渗氮和氮碳共渗处理后,硬度和耐磨性能可大幅提高,且氮碳共渗处理效果更佳。     

304不锈钢双活性屏离子渗氮

目的 考察304不锈钢双活性屏离子渗氮技术的可行性及处理效果.方法 利用双活性屏离子渗氮(DASPN)和普通直流离子渗氮(DCPN)两种技术对304不锈钢进行低温(420℃)硬化处理,对比分析两种工艺所得渗层的组织,对比研究两种工艺所得渗层的相结构、硬度和耐蚀性能.结果 采用DASPN技术可获得比采用DCPN技术更为均匀、致密的渗层,渗层为单一S相层,硬度为763 HV0.25.电化学测试表明,两种渗氮技术相比,DASPN处理获得的渗层耐蚀性能更优.结论 采用DASPN技术对304不锈钢进行低温硬化处理,在试样距双屏的距离为70 mm时能够获得比DCPN更好的渗氮效果.该技术适于工业化推广应用.     

304奥氏体不锈钢低气压离子渗氮组织与性能研究

在400℃、低气压下对304奥氏体不锈钢进行低温低压离子渗氮处理。采用扫描电镜、显微硬度计及万能摩擦试验机对表面改性后的304奥氏体不锈钢渗层组织、硬度及耐磨性进行了测试和分析。结果表明:304奥氏体不锈钢低温低气压渗氮形成了明显的白亮层;低气压对304奥氏体不锈钢离子渗氮具有良好的催渗效果,即渗层厚度随气压的减小而增加,在100 Pa条件下,渗层厚度达到最大值51.7μm;渗氮后试样表面硬度达到最大值1100 HV0.01;低温低气压离子渗氮能够提高304奥氏体不锈钢耐磨性,80 Pa和100 Pa是提高304奥氏体不锈钢耐磨性的最佳气压。     

钛催渗低温离子渗氮对304不锈钢组织性能的影响

目的 在保障304奥氏体不锈钢良好耐蚀性前提下,研发显著改善表层硬度及耐磨性的低温高效离子渗氮技术。方法 低温离子渗氮时,在试样周围均匀放置微量海绵钛,研发304奥氏体不锈钢创新钛催渗低温离子渗氮技术。采用光学显微镜、扫描电子显微镜、能谱分析仪、X射线粉末衍射仪、显微维氏硬度计、摩擦磨损测试仪,以及电化学工作站等设备分别对试样截面显微组织、物相及成分、截面显微硬度、渗层耐磨性能、耐蚀性能等渗层组织性能进行测试与分析。结果 304奥氏体不锈钢在420 ℃/4 h钛催渗离子渗氮处理后,不仅保持了良好耐蚀性,且渗层耐蚀性比常规低温离子渗氮略有提升,同时,表面硬度与耐磨性大幅提高,表面硬度由常规离子渗氮的978HV0.025提升至1350HV0.025。磨损率由20.9 μg/(N.m)降低至7.4 μg/(N.m),下降了约2/3。特别有价值的是,钛催渗低温离子渗氮效率比传统离子渗氮显著提升,渗氮层厚度由常规离子渗氮的11.37 μm增厚到48.32 μm,即渗氮效率提高到常规离子渗氮的4倍以上。结论 本研究研发的钛催渗低温离子渗氮技术在保障304奥氏体不锈钢优良耐蚀性的同时,能够大幅度提升不锈钢表面硬度及耐磨性能,且具有显著的催渗效果。     

离子渗氮工艺对S32205双相不锈钢综合性能的影响

在不同温度下对S32205双相不锈钢进行离子渗氮,利用光学显微镜、显微硬度计、电化学测试仪、XRD等对渗氮层组织性能进行分析。结果表明,400℃离子渗氮4 h工艺条件下,渗氮层由γN相构成,自腐蚀电位由基材的-0.294 V升高至-0.271 V,表面硬度可达到966 HV0.01,为基材表面硬度的2.5倍,渗氮层深为8μm,该温度下离子渗氮可同时提高S32205双相不锈钢耐蚀性和表面硬度。随着渗氮温度升高,在450℃和500℃渗氮时虽然渗氮层深和硬度明显提高,然而由于Cr N的析出,耐蚀性均低于基材。     

温度对AISI304奥氏体不锈钢离子渗氮的影响

对AISI304奥氏体不锈钢进行脉冲电流辉光离子渗氮处理,在不同处理温度(480 ℃、520 ℃、580 ℃)下渗氮8 h后,获得了一定厚度的渗氮层.通过对渗层进行金相分析和硬度测试表明,随着渗氮温度升高,渗层厚度增大,显微硬度先增大后减小.综合温度对渗层厚度与显微硬度的影响,AISI304奥氏体不锈钢卡套辉光离子渗氮温度可采用520 ℃,渗氮后渗层厚度为90 μm,显微硬度为1317 HV0.1.     

奥氏体不锈钢稀土催渗离子渗氮工艺研究

对304、316L奥氏体不锈钢采用不同氮一氢比的气氛,在不同温度和不同保温时间进行了离子渗氮和稀土催渗离子渗氮。结果表明,经580℃在氮一氢比为1：3的气氛中稀土催渗离子渗氮9h,304和316L钢的渗层深度分别为0．12mm和0．112mm,表面硬度达1000HV0．1左右,与常规离子渗氮工艺相比,渗氮时间缩短了1h。     

The wear and corrosion properties of stainless steel nitrided by low-pressure plasma-arc source ion nitriding at low temperatures

Low pressure plasma arc discharge-assisted nitriding of AISI 304 austenitic stainless steel is a process that produces surface layers with useful properties such as a high surface hardness of approximately 1500 Hv_0.1 and a high resistance to frictional wear and corrosion. The phase composition, the thickness, the microstructure and the surface topography of the nitrided layer, as well as its properties, depend essentially on the process parameters. Among them, the processing temperature is the most important factor for forming a hard layer with good wear and corrosion resistance. Nitriding austenitic stainless steel at approximately 420°C for 70 min can produce a thin layer of 7–8 μm with very high hardness and good corrosion resistance on the surface. The microstructure was studied by optical microscopy and both glancing angle and conventional Bragg–Brentano (θ–2θ) symmetric geometry X-ray diffraction (XRD). The formation of expanded austenite was observed. Measurements of the wear depths indicated that the wear resistance of austenitic stainless steel can be improved greatly by nitriding at approximately 420°C using low-pressure plasma-arc source ion nitriding.     

304奥氏体不锈钢氮离子注入层的组织与性能研究

对具有抗磁性的304奥氏体不锈钢进行离子渗氮处理,以提高其硬度和耐磨性.研究了奥氏体不锈钢渗氮前后的金相组织、显微硬度、耐磨性和耐腐蚀性等,并与常用高硬度、高耐磨性GCr15钢进行了对比.结果表明:304奥氏体不锈钢通过一定时间的离子渗氮后,依然具有很好的抗磁性能,且表层硬度约为基体硬度的6倍,耐磨性能大大提高,其性能...     

马氏体不锈钢不同渗氮方法对比试验

采用离子渗氮、液体渗氮及气体渗氮对耐蚀耐热马氏体型热稳定不锈钢1Cr12Ni2WMoVNb进行表面改性,研究了不同渗氮方法下不锈钢的硬度、组织形貌、物相变化及脆性,并对3种渗氮方法下不锈钢的耐蚀性及耐高温磨损性能进行了比较。结果表明:3种渗氮方法均可大幅度提高不锈钢的表面硬度,且不同渗氮处理后不锈钢的渗层组织结构大致相同,但表面物相有所差异,离子渗氮后的表面物相主要为Fe₄N及少量CrN相,液体渗氮后为Fe₃O₄及ε相,气体渗氮后为Fe₃O₄、Fe₄N及少量ε相;3种渗氮方法均可提高不锈钢的耐磨损性能,特别是在500~600 ℃下的高温耐磨性得到了大幅提升,但不锈钢渗氮后的耐蚀性均有所降低。     

Improvement of corrosion and wear resistances of AISI 420 martensitic stainless steel using plasma nitriding at low temperature

The influence of low temperature plasma nitriding on the wear and corrosion resistance of AISI 420 martensitic stainless steel was investigated. Plasma nitriding experiments were carried out with DC-pulsed plasma in 25% N₂ + 75% H₂ atmosphere at 350 °C, 450 °C and 550 °C for 15 h. The composition, microstructure and hardness of the nitrided samples were examined. The wear resistances of plasma nitrided samples were determined with a ball-on-disc wear tester. The corrosion behaviors of plasma nitrided AISI420 stainless steel were evaluated using anodic polarization tests and salt fog spray tests in the simulated industrial environment.The results show that plasma nitriding produces a relatively thick nitrided layer consisting of a compound layer and an adjacent nitrogen diffusion layer on the AISI 420 stainless steel surface. Plasma nitriding not only increases the surface hardness but also improves the wear resistance of the martensitic stainless steel. Furthermore, the anti-wear property of the steel nitrided at 350 °C is much more excellent than that at 550 °C. In addition, the corrosion resistance of AISI420 martensitic stainless steel is considerably improved by 350 °C low temperature plasma nitriding. The improved corrosion resistance is considered to be related to the combined effect of the solid solution of Cr and the high chemical stable phases of ?-Fe₃N and α_N formed on the martensitic stainless steel surface during 350 °C low temperature plasma nitriding. However, plasma nitriding carried out at 450 °C or 550 °C reduces the corrosion resistance of samples, because of the formation of CrN and leading to the depletion of Cr in the solid solution phase of the nitrided layer.     

不锈钢表面含Cu功能梯度复合改性层的制备及抗菌性能

为提高奥氏体不锈钢(ASS)的耐磨性及赋予其抗菌性能,应用改进的活性屏离子渗氮(ASPN)技术,将纯铜冲孔板置于不锈钢冲孔板上面作为活性屏的顶盖,对316奥氏体不锈钢在低温下(430℃)进行表面渗氮处理,在其表面形成由含Cu抗菌沉积层和S相(氮在奥氏体中的过饱和固溶体γ_N)硬质支撑层组成的功能梯度复合改性层。用扫描电镜(SEM)及其所附能谱仪(EDS)、X射线衍射仪(XRD)表征复合改性层的组织形貌、成分及相结构。用显微硬度计和往复摩擦磨损试验机测试了基体和复合改性层的显微硬度和摩擦磨损性能,用金黄色葡萄球菌进行体外抗菌试验评价复合改性层的抗菌性能。结果表明,在偏压达到250 V后,形成了连续分布的硬质S相扩散层和含Cu沉积层组成的复合改性层。改性层表面最高硬度可达928 HV0.05,与Si₃N₄小球对磨时比磨损率较基体降低约57.76%,显著提高了不锈钢的耐磨性。抗菌试验表明,复合改性层与金黄色葡萄球菌接触24 h后,对金黄色葡萄球菌抗菌率提高到98.5%。改进的活性屏离子渗氮技术制备的功能梯度复合改性层可以有效提高...     

Plasma Nitriding of Austenitic Stainless Steel with Severe Surface Deformation Layer

The dc glow discharge plasma nitriding of austenite stainless steel with severe surface deformation layer is used to produce much thicker surface modified layer. This kind of layers has useful properties such as a high surface hardness of about 1500 Hv 0.1 and high resistance to frictional wear. This paper presents the structures and properties of low temperature plasma nitrided austenitic stainless steel with severe surface deformation layer.     

AISI 316L奥氏体不锈钢低温离子-气体渗碳工艺优化

目的将低温离子-气体乙炔渗碳应用于AISI 316L奥氏体不锈钢表面硬化处理,同时探讨其硬化处理的最优工艺参数及优化效果。方法采用离子轰击去除不锈钢表面钝化膜并活化其表面,再进行低温气体乙炔渗碳,实验过程使用脉冲式供气循环处理方式。进行温度梯度实验,寻找渗碳处理的临界温度。并采用正交试验法设计3因素3水平共9组实验,分析气体比例、离子轰击时间、保温压强3个因素对渗碳层硬度和厚度产生的影响,以期得到不锈钢低温离子-气体乙炔渗碳优化工艺。通过对经过最优化工艺处理过后的不锈钢硬化层组织、成分、厚度、硬度、耐磨性、耐蚀性能的研究分析,验证此工艺对AISI 316L奥氏体不锈钢硬化处理的适用性。结果处理温度为540℃时渗碳层有碳的铬化物析出;离子轰击时间对渗碳层硬度影响最大,保温压强对硬化层厚度影响最明显。在硬化处理温度为520℃,V(H2)∶V(C2H2)=1∶1,渗碳压强为-0.02 MPa,离子轰击时间为20 min时,316L奥氏体不锈钢离子-气体乙炔渗碳效果最优。经优化工艺处理后不锈钢硬化层厚度达到30μm左右,表面硬度达到838HV0.05,耐蚀性和耐磨性能等都显著提高。结论低温离子-气体乙炔渗碳硬化处理适用于AISI 316L奥氏体不锈钢,其处理最合适温度为520℃。经优化工艺处理后的不锈钢具有较高的硬度、厚度,良好的硬度梯度,高耐蚀性能及高耐磨性能。     

渗扩时间比对AISI 316不锈钢渗氮层组织与性能的影响

采用真空两段渗氮工艺,在不同的强渗、扩散时间下对AISI 316不锈钢进行渗氮处理,通过X射线衍射(XRD)、扫描电镜(SEM)、光学显微镜(OM)、显微硬度测试和摩擦磨损试验等分析了渗氮层的组织和性能。结果表明,经过12 h的真空渗氮后,AISI 316不锈钢表面形成了一层由γ′-Fe₄N、ε-Fe_2-3N和CrN等相组成的渗氮层,其表面硬度和耐磨性能相较于基体均有明显的提高。其中,渗扩时间比为1∶1(强渗6 h、扩散6 h)时的渗层厚度约为96 μm,表面硬度约为1069 HV0.5,是基体表面硬度的4.5倍,在20 N载荷下的磨损量约为基体的1/3;渗扩时间比为1∶2(强渗4 h、扩散8 h)时的渗层厚度约为120 μm,ε-Fe_2-3N相衍射峰增强,在20 N载荷下的磨损量约为基体的1/30。延长扩散时间能增加渗氮层厚度,改善表面形貌,进一步提高不锈钢的耐磨性。     

Improvement of Mechanical Properties of Martensitic Stainless Steel by Plasma Nitriding at Low Temperature

A series of experiments were carried out to study the influence of low temperature plasma nitriding on the mechanical properties of AISI 420 martensitic stainless steel. Plasma nitriding experiments were carried out for 15 h at 350℃ by means of DC- pulsed plasma in 25%N2＋ 75%H2 atmosphere. The microstructure, phase composition, and residual stresses profiles of the nitrided layers were determined by optical microscopy and X-ray diffraction. The microhardness profiles of the nitridied surfaces were also studied. The fatigue life, sliding wear, and erosion wear loss of the untreated specimens and plasma nitriding specimens were determined on the basis of a rotating bending fatigue tester, a ball-on-disc wear tester, and a solid particle erosion tester. The results show that the 350℃ nitrided surface is dominated by c-Fe3N and ON, which is supersaturated nitrogen solid solution. They have high hardness and chemical stabilities. So the low temperature plasma nitriding not only increases the surface hardness values but also improves the wear and erosion resistance. In addition, the fatigue limit of AISI 420 steel can also be improved by plasma nitriding at 350℃ because plasma nitriding produces residual compressive stress inside the modified layer.