镀锌钢板钛盐/硅烷复合膜的耐蚀性研究

研究了镀锌钢板上钛盐钝化膜、硅烷转化膜、钛盐/硅烷复合转化膜的表面形貌和化学成分,并对比了这3种转化膜与普通铬酸盐转化膜的电化学行为和耐盐雾腐蚀性能。结果表明:镀锌钢板钝化后,腐蚀电流密度降低,极化电阻及交流阻抗得到极大提高;钛盐/硅烷复合膜的耐蚀性已经接近普通铬酸盐钝化。SEM和EIS分析表明,硅烷膜是一层物理遮盖膜。     

冷轧钢表面植酸-硅烷双膜复合层的耐蚀性能

为了研究植酸-硅烷复合膜对冷轧钢腐蚀行为的影响,采用浸泡法在冷轧钢板表面分别制备了植酸化学转化膜、硅烷膜层及植酸-硅烷复合膜层。采用扫描电子显微镜观察冷轧钢板表面经植酸转化膜和植酸-硅烷复合膜层处理之后的形貌;运用红外光谱和X-射线光电子能谱方法研究植酸转化膜及植酸-硅烷复合膜层的化学组成;采用极化曲线、电化学阻抗谱、盐雾试验研究植酸-硅烷复合膜层的耐蚀性能及在3.5%氯化钠腐蚀溶液中的稳定性。结果表明:植酸-硅烷复合膜层的耐腐蚀性能及在氯化钠溶液中的稳定性明显高于单一的硅烷膜层。其作用机理在于植酸转化膜一方面可以提高硅烷膜层与金属基体的结合力,另一方面可以与硅烷膜层协同作用提高复合膜的耐腐蚀性能。     

镁合金表面铈盐掺杂硅烷膜的腐蚀电化学行为

目的为进一步提升镁合金表面常规硅烷膜的耐蚀性能。方法在γ-氨丙基三乙氧基硅烷溶液中掺杂0.50 g/L硝酸铈,采用简单化学浸渍处理,在AZ91D镁合金基体表面制备了铈盐掺杂硅烷膜。借助扫描电子显微镜(SEM)观察了铈盐掺杂前后硅烷膜的表面微观形貌,通过开路电位-时间曲线、电化学交流阻抗谱(EIS)和中性盐雾试验(NSS)研究了铈盐掺杂对5%Na Cl溶液中硅烷膜耐蚀性能的影响。结果铈盐掺杂硅烷膜比普通硅烷膜更厚且平整,其致密性、均匀一致性较好,完全覆盖了镁合金基体,已看不到磨痕。铈盐掺杂硅烷膜的稳定电位约为-1.31 V,且需要的稳定时间最长。铈盐掺杂硅烷膜具有更大的低频阻抗数值,有效遏制了侵蚀性粒子向镁合金基体的迁移和扩散,避免了镁合金基体发生阳极溶解反应。结论采用向硅烷溶液中添加硝酸铈的方法,能够在AZ91D镁合金表面制备出铈盐掺杂硅烷膜。由于铈离子在某种程度上修复了硅烷膜层中的微裂纹和缺陷,显著提升了硅烷膜的耐蚀能力。     

镁合金表面微弧氧化/自组装复合膜的耐蚀性能

目的 提高镁合金基体的耐蚀性能.方法 采用微弧氧化工艺对镁合金进行预处理,再通过自组装技术处理,在镁合金表面制备微弧氧化/十六烷基三甲氧基硅烷自组装复合膜层.通过SEM、EDS对复合膜的微观组织结构进行分析,并通过XPS、拉曼光谱分析了复合膜的表面成分,利用电化学阻抗谱、极化曲线、盐雾实验和浸泡实验检测了复合膜层的耐腐蚀性能.结果 复合膜均匀覆盖在镁合金表面,且复合膜较为光滑,主要含有C、O、F、Si等元素.经过自组装处理后,膜层从亲水性转为疏水性,接触角达到145.07°.经电化学性能测试,复合膜的Rct值能达到2.242×106?·cm2,与微弧氧化膜相比,增大了2个数量级;此外,复合膜的腐蚀电流密度为1.314×10-8 A/cm2,与微弧氧化膜相比也降低了2个数量级,具有较好的耐腐蚀性.浸泡120 h后,复合膜的腐蚀电流密度仍有1.061×10-5 A/cm2,盐雾实验进行120 h也没有出现明显的腐蚀现象.结论 自组装技术明显提高了镁合金基体的耐蚀性能,微弧氧化膜在一定程度上增强了自组装膜层对基材的粘附力.由于复合膜的疏水性使得水滴在膜层表面停留的时间减少,所以膜层的耐蚀性会随着疏水性增大而大大提高.     

Mg-Mn-Ce镁合金表面超疏水复合膜层的制备及耐腐蚀性能

采用微弧氧化技术和有机镀膜技术相结合的复合处理方法实现Mg-Mn-Ce镁合金表面改性,获得超疏水复合膜层,研究微弧氧化膜的表面特征、有机镀膜电化学反应过程、复合膜层的润湿特性和耐腐蚀性能。结果表明:镁合金经微弧氧化处理后由于微弧氧化膜表面呈微纳多孔结构,表现为超亲水特性,其蒸馏水的静态接触角接近0°;在微弧氧化膜上经有机镀膜后,其形成的有机薄膜的静态接触角高达173.3°,表现出优良的超疏水特性。镁合金经微弧氧化处理后具有良好的耐腐蚀性能,经有机镀膜超疏水复合处理后,耐腐蚀性能得到进一步提高。复合膜层在3.5%NaCl溶液中,与基体相比动电位极化腐蚀电流密度减小了3个数量级、而电化学阻抗提高了3个数量级,耐腐蚀性能明显改善。微弧氧化与有机镀膜相结合的复合处理使镁合金表面在实现超亲水-超疏水功能转换的同时显著提高镁合金的耐腐蚀性能。     

镁合金黑色微弧氧化膜在NaCl溶液中腐蚀电化学演变

目的 评价镁合金黑色微弧氧化热控膜层在氯离子作用下的腐蚀演变行为.方法 在电解液中添加不同浓度的添加剂制备微弧氧化膜层,分析不同微弧氧化膜试样在0.1 mol/L NaCl溶液中的电化学演变过程.采用电化学极化、电化学交流阻抗表征和拟合,结合扫描电镜等方法,对膜层演变规律及机理进行了探讨.结果 未经微弧氧化的镁合金自腐蚀电流密度为17.7 μA/cm2,自腐蚀电位为-1.464 V;经微弧氧化后,试样自腐蚀电流密度减小至0.09 μA/cm2,自腐蚀电位下降至-1.628 V.添加剂加入后制备的微弧氧化膜相比于镁合金基体,其耐蚀性能提高,且随着添加剂浓度的增加,耐蚀效果呈现先增加、后减弱的趋势,添加剂质量浓度在10 g/L时制备的膜层具有最好的防腐效果.镁合金微弧氧化热控膜层在NaCl溶液中腐蚀过程分为三个阶段:一是腐蚀性离子进入多孔膜层,引起界面熔融层变化;二是MgO与水分子反应造成内层膜更加致密,阻抗有所增加;三是腐蚀溶液接触到部分镁合金基底,发生电化学腐蚀,形成楔形效应,引发裂纹,最终导致局部腐蚀失效.结论 微弧氧化提高了膜层的耐蚀性能,其在0.1 mol/L NaCl溶液中的腐蚀过程可分为介质进入孔内、水合反应和局部腐蚀三个阶段.     

2024铝合金表面无铬钛锆转化膜的制备与性能

采用钛酸盐和锆酸盐为主盐,开发了一种应用于2024铝合金表面的无铬钛锆转化膜。通过扫描电镜 (SEM)、能谱分析 (EDS)、中性盐雾实验、动电位极化曲线和电化学阻抗谱对转化膜的表面形貌、成分及耐蚀性能进行了表征和分析。结果表明：制备的无铬钛锆转化膜由微米级的微小颗粒组成,膜层均匀平整,无明显缺陷;无铬钛锆转化处理后的2024铝合金,经中性盐雾168 h,无明显腐蚀产物产生;钛锆转化膜具有较低的腐蚀电流和一定的钝化能力,可有效的提高铝合金的耐蚀性能。     

AZ31B镁合金钒/硅烷复合转化膜的制备与表征

目的 改善钒酸盐转化膜表面形貌,提高单一钒酸盐转化膜的耐蚀性能。方法 使用偏钒酸盐和硅烷通过两步法在镁合金表面制备钒/硅烷复合转化膜,比较不同硅烷制备的复合膜的耐蚀性能,从而确定使用硅烷的种类,采用扫描电子显微镜(SEM)、X射线能谱(EDS)、X射线光电子能谱(XPS)和傅里叶红外光谱(FT-IR)观察转化膜的微观形貌并分析转化膜的组成和结构,通过交流阻抗测试(EIS)、Tafel极化曲线测试和全浸腐蚀实验评价转化膜的耐蚀性能,并采用划格实验和接触角测试评价转化膜的结合力和疏水性。结果 确定使用BTEPST(双-[3-(三乙氧基硅)丙基]-四硫化物)作为成膜组分,使用偏钒酸钠和BTESPT在镁合金表面成功制备钒/BTESPT复合膜,复合膜表面均匀平整,致密无裂纹,与基体结合力好,具有疏水性,该复合膜的组成元素为Mg、V、C、O、Si和S,且元素分布较均匀,膜层是包含Si—O—S、Si—O—Mg、Si—O—V等共价键的交联结构。交流阻抗测试结果显示,钒/BTESPT复合转化膜的膜层电阻为1.17×10⁵?·cm²,电荷转移电阻为1.076×1...     

钐盐含量对AZ31B镁合金表面铁氰化物转化膜耐蚀性的影响

目的 改善AZ31B镁合金表面单一铁氰化钾转化膜附着力以及提高单一膜层的耐腐蚀性能。方法 选用钐盐对镁合金单一膜层进行处理,着重探讨不同钐盐含量对膜层的影响。利用两步法进行化学浸渍成膜,并且利用扫描电镜(SEM)、X射线衍射仪(XRD)、能谱仪(EDS)和X射线光电子能谱(XPS)对复合膜层表面形貌和组成成分进行表征。采用动电位极化曲线和电化学交流阻抗对复合膜层在3.5%NaCl溶液中的腐蚀行为进行探究。结果 经过钐盐处理的镁合金铁氰化钾转化膜表面生成了新的膜层,该复合膜层主要成分为SmFe(CN)6和Sm(OH)3。其不仅具有比单一膜层更优异的耐蚀性能以及膜层与基体的结合力也有所提高,而且形成的复合膜层也较稳定,可以对基体起到更好的保护作用。另外,钐盐含量为5 g/L时处理的膜层最为致密平整,自腐蚀电流密度最低,为2.129×10^?9 A/cm²,电荷转移电阻和膜层电阻最大,分别为8.164×10⁴ Ω.cm²和1.293×10⁷ Ω.cm²,耐蚀性能最好。结论 使用钐盐对镁合金表面铁氰化钾膜层进行改性,可以进一步提高单一膜层的耐蚀性,并且最佳钐盐含量为5 g/L。     

AZ31B镁合金氧化石墨烯掺杂钇盐转化膜耐蚀性研究

目的研究一种绿色环保的表面处理方法,以提高镁合金的耐蚀性。方法采用化学浸泡法,以硝酸钇为成膜物质,在AZ31B镁合金表面成功制备一种新型稀土盐转化膜,并以氧化石墨烯为阻隔剂对该转化膜进行复合掺杂。采用扫描电镜(SEM)对膜层的表面形貌进行观察,采用析氢实验和电化学测试对不同试样在3.5%Na Cl溶液中的耐蚀性进行了研究。结果镁合金钇盐转化膜表面平整均一,覆盖良好。氧化石墨烯掺杂后的钇盐膜层表面出现了大小不均一的瘤状物质,膜层完整,未出现裂痕。析氢实验结果显示,经过处理的转化膜试样可以极大地抑制腐蚀反应的发生。由极化曲线可知,钇盐转化膜的存在使镁合金的腐蚀电位发生了明显正移,正移了150 m V;而氧化石墨烯掺杂的钇盐膜层的腐蚀电位相对于掺杂前变化不大,但其腐蚀电流密度是掺杂前的1/28。电化学交流阻抗谱的测试结果显示,氧化石墨烯掺杂钇盐转化膜的电荷转移电阻最大,Rct为2485?·cm2;钇盐转化膜的电荷转移电阻次之,Rct为1224?·cm2。两者的电荷转移电阻相对于未经处理的镁合金都有明显提升。结论钇盐转化膜可以明显提高AZ31B镁合金的耐蚀性,氧化石墨烯的加入可以进一步提高转化膜层的耐蚀性。     

Effects of Post-weld Heat Treatment on Microstructure,Mechanical Properties and the Role of Weld Reinforcement in 2219 Aluminum Alloy TIG-Welded Joints

In as-welded state, each region of 2219 aluminum alloy TIG-welded joint shows diff erent microstructure and microhardness due to the diff erent welding heat cycles and the resulting evolution of second phases. After the post-weld heat treatment, both the amount and the size of the eutectic structure or θ phases decreased. Correspondingly, both the Cu content in α-Al matrix and the microhardness increased to a similar level in each region of the joint, and the tensile strength of the entire joint was greatly improved. Post-weld heat treatment played the role of solid solution strengthening and aging strengthening. After the post-weld heat treatment, the weld performance became similar to other regions, but weld reinforcements lost their reinforcing eff ect on the weld and their existence was more of an adverse eff ect. The joint without weld reinforcements after the post-weld heat treatment had the optimal tensile properties, and the specimens randomly crack in the weld zone.     

新型的治疗阿尔茨海默氏症药物(1-二甲基磷酰基-2,2,2-三氯)-乙基-1-醇烟酸醋对体外神经细胞的作用

目的: 观察本实验室合成的一种治疗阿尔茨海默氏症(AD)的药物(1-二甲基磷酰基-2, 2, 2 -三氯)-乙基^-1-醇烟酸醋(NMF),对体外培养的皮层神经细胞活性的影响以及对海人藻酸(KA)所致的神经损伤的保护作用。方法: 采用体外培养皮层神经元的方法,解剖分离 15 d胚胎小鼠皮层神经细胞, 接种于 96孔板,48 h 后加药并培养 72 h,以 MIT 法 观察 NMF 对小鼠皮层神经细胞活性的影响;同时将接种于 24 孔板的细胞预先给予 NMF,d 3 时加或不加KA处理后,以台盼蓝染色鉴别并计数死、活细胞,可得出细胞的存活率。结果: NMF 明显促进胎鼠皮层神经元活性,其中 NMF1、0. 1、10nmol·L^-1促进神经元活性增殖率分别高达 34.7%、37.4%、36. 7%, NMF 明显促进正常胎鼠皮层神经元存活卒,与对照组比较,10nmol·L^-1 NMF 对皮层神经元的存活率分别提高 39.3%、73.5%。 NMF能显著 对抗 KA 所致的神经元损伤,与 KA 损伤组相比, NMF0.1、10、10nmol·L^-1对损伤皮层神经元的保护率分别为 77.30%、80.10%、84.15%。结论: NMF 明 显促进胎鼠皮层神经元的洁性、提高正常皮层神经元,的存活卒,并能有效地保护KA所致的神经元损伤,提示 NMF 是一种很有潜力的治疗 AD 的药物。     

The First Phase of the SRIF Industrialized Base in ＂West Area＂ Has Been Put into Operation

After nearly two years＇ tense construction, the first phase of industrialized base of Shenyang Research Institute of Foundry （SRIF）, located at the Tiexi Casting and Forging Industrial Park in the west of Tiexi District, has now been completed and formally put into operation.     

THERMODYNAMICS STUDY ON THE DECOMPOSITION OF CHROMITE WITH KOH

Institute of Process Engineering, Chinese Academy of Sciences, China, has proposed a method for oxidative leaching of chromite with potassium hydroxide. Understanding the mechanism of chromite decomposition, especially in the potassium hydroxide fusion, is important for the optimization of the operating parameters of the oxidative leaching process. A traditional thermodynamic method is proposed and the thermal decomposition and the reaction decomposition during the oxidative leaching of chromite with KOH and oxygen is discussed, which suggests that chromite is mainly destroyed by reactions with KOH and oxygen. Meanwhile, equilibrium of the main reactions of the above process was calculated at different temperatures and oxygen partial pressures. The stable zones of productions, namely, K2CrO4 and Fe2O3, increase with the decrease of temperature, which indicates that higher temperature is not beneficial to thermodynamic reactions. In addition, a comparison of the general alkali methods is carried out, and it is concluded that the KOH leaching process is thermodynamically superior to the conventional chromate production process.     

INFLUENCE OF HEAT TREATMENT ON DAMPING BEHAVIOUR OF THE MAGNESIUM WROUGHT ALLOY AZ61

The effect of isochronal heat treatments for 1h on variation of damping, hardness and microstructural change of the magnesium wrought alloy AZ61 was investigated. Damping and hardness behaviour could be attributed to the evolution of precipitation process. The influence of precipitation on damping behaviour was explained in the framework of the dislocation string model of Granato and Lücke.     

Theoretical Analysis for the Motion and Temperature of Melt Droplets in Spray Degassing Process

The motion of melt droplets in spray degassing process was analyzed theoretically. The height of the treatment tank in spray degassing process could be determined by the results of theoretical calculation of motion of melt droplets. To know whether the melt droplets would solidify during spraying process, the balance temperature of melt droplets was also theoretically analyzed. Then proof experiments for theoretical results about temperature of melt droplets were carried. In comparison, the experimental results were nearly similar to the calculation results.     

Growth Kinetics of Single Inclusion Particle in Molten Melts

On the basis of the single-particle framework, a new theory on inclusion growth in metallurgical melts is developed to study the kinetics of inclusion growth on account of reaction and collision. The studies show that the early growth of inclusion depends on reaction growth and Brawnian motion collision, and where the former is decisive, the late growth depends on turbulence collision and Stokes＇ collision, and where the former is dominant; collision growth is very quick during the smelting process, lessened in the refining process, but nearly negligible in the continuous casting process.     

Three-Dimensional Growth of Coherent Ferrite in Austenite: A Molecular Dynamics Study

Coherent second phase often exhibits anisotropic morphology with specifi c orientations with respect to both the second and the matrix phases. As a key feature of microstructure, the morphology of the coherent particles is essential for understanding the second-phase strengthening eff ect in various industrial alloys. This letter reports anisotropic growth of coherent ferrite from austenite matrix in pure iron based on molecular dynamics simulation. We found that the ferrite grain tends to grow into an elongated plate-like shape, independent of its initial confi guration. The fi nal shape of the ferrite is closely related to the misfi t between the two phases, with the longest direction and the broad facet of the plate being, respectively, consistent with the best matching direction and the best matching plane calculated via the Burgers vector content(BVC) method. The strain energy calculation in the framework of Eshelby's inclusion theory verifi es that the simulated orientation of the coherent ferrite is energetically favorable. It is anticipated that the BVC method will be applicable in analysis of anisotropic growth and morphology of coherent second phase in other phase transformation systems.     

An Easy Way to Quantify the Adhesion Energy of Nanostructured Cu/X(X=Cr,Ta,Mo,Nb,Zr) Multilayer Films Adherent to Polyimide Substrates

An approach based on film buckling under simple uniaxial tensile testing was utilized in this paper to quantitatively estimate the interfacial energy of the nanostructured multilayer films(NMFs) adherent to flexible substrates. The interfacial energies of polyimide-supported NMFs are determined to be *5.0 J/m2 for Cu/Cr, *4.1 J/m2 for Cu/Ta,*2.8 J/m2 for Cu/Mo, *1.1 J/m2 for Cu/Nb, and *1.2 J/m2 for Cu/Zr NMFs. Furthermore, a linear relationship between the adhesion energy and the interfacial shear strength is clearly demonstrated for the Cu-based NMFs, which is highly indicative of the applicability and reliability of the modified models.     

High-Speed Friction Stir Welding of SiC_p/Al–Mg–Si–Cu Composite

A 17 vol% SiCp/Al–Mg–Si–Cu composite plate with a thickness of 3 mm was successfully friction stir welded(FSWed) at a very high welding speed of 2000 mm/min for the first time. Microstructural observation indicated that the coarsening of the precipitates was greatly inhibited in the heat-affected zone of the FSW joint at high welding speed, due to the significantly reduced peak temperature and duration at high temperature. Therefore, prominent enhancement of the hardness was achieved at the lowest hardness zone of the FSW joint at this high welding speed, which was similar to that of the nugget zone. Furthermore, the ultimate tensile strength of the joint was as high as 369 MPa, which was much higher than that obtained at low welding speed of 100 mm/min(298 MPa). This study provides an effective method to weld aluminum matrix composite with superior quality and high welding efficiency.