Magnetic properties and magnetic entropy changes of La1-xPrxFe11.5Si1.5 compounds with 0≤x≤ 0.5

Magnetic properties and magnetic entropy changes of La1-xPrxFe11.5Si1.5 compounds with 0≤x≤ 0.5

Magnetic properties and magnetic entropy changes in LaFe$_{11.5}$Si$_{1.5}$ have been investigated by partially substituting Pr by La. It is found that La$_{1 - x}$Pr$_{x}$Fe$_{11.5}$Si$_{1.5}$ compounds remain cubic NaZn$_{13}$-type structures even when the Pr content is increased to 0.5, i.e. $x = 0.5$. Substitution of Pr for La leads to a reduction in both the crystal constant and the Curie temperature. A stepwise magnetic behaviour in the isothermal magnetization curves is observed, indicating that the characteristic of the itinerant electron metamagnetic (IEM) transition above $T_{\rm C}$ becomes more prominent with the Pr content increasing. As a result, the magnetic entropy change is remarkably enhanced from 23.0 to 29.4\,J/kg$\cdot$K as the field changes from 0 to 5\,T, with the value of $x$ increasing from 0 to 0.5. It is more attractive that the magnetic entropy changes for all samples are shaped into high plateaus in a wide range of temperature, which is highly favourable for Ericsson-type magnetic refrigeration.