Synthesis of nanophase tungsten carbide by electrical discharge machining

Tungsten carbide nanopowders were synthesized successfully by electric discharge machining followed by annealing under a nitrogen atmosphere. The tungsten workpieces were initially melted and evaporated on the working surface during the electric discharge machining process, and then the tungsten powders were reacted with the carbon electrode and the working medium of kerosene to form the nanocrystalline WC_1−x powders. The powders produced were characterized by XRD, SEM, and TEM. When annealing the powders under an N₂ atmosphere, the cubic phases of WC_1−x gradually changed to hexagonal W₂C and then were transformed fully to nanocrystalline hexagonal WC at 1200 °C, with the nanocrystalline tungsten carbide encapsulated in a carbon shell. On the other hand, under an H₂ atmosphere, the WC_1−x phase changed via a W₂C phase to reduced powders of pure tungsten at 1000 °C or were reduced directly from WC_1−x to elemental W.