Role of Mn doping on magnetic properties of multiferroic NiCr2O4 nanoparticles

The structural and magnetic properties of Mn doped Nickel Chromite (Ni_1-xMn_xCr₂O_4, x = 0, 0.2, 0.3, 0.4, 0.6, 0.8) nanoparticles (NPs) were studied in detail. The X-ray diffraction analysis affirms normal spinel structure for all the samples and average crystallite size was found in the range 31–58 nm. The spinel structure of these nanoparticles was also confirmed by Fourier transform infrared spectroscopy which revealed the formation of tetrahedral and octahedral vibrational bands in the range 607 -628 cm^?1 and 486 - 491 cm^?1, respectively. Transmission electron microscopy images depicts less agglomerated and non-spherical shaped NPs. The temperature dependent zero field cooled and field cooled magnetic measurements revealed a paramagnetic to ferrimagnetic transition T_c at 87 K for NiCr₂O₄ NPs, which is shifted to low temperatures by Mn doping. This effect was attributed to cationic distributions between adjacent sites produced by Mn doping. M ? H loops of Ni_1-xMn_xCr₂O₄ NPs revealed enhanced saturation magnetization with increase in Mn doping which is attributed to a large magnetic moment of Mn ions. Ni_1-xMn_xCr₂O₄ (x = 0.6 and 0.8) NPs show steps in their M ? H loops because of exchange interactions between two sites of these NPs.